Synthesis and properties of new poly(amide‐imide)s based on 1,3‐bis[4,4'‐(trimellitimido) phenoxy] propane and aromatic diamines

Six new poly(amide‐imide)s 8a–f containing trimethylene moiety in the main chain were synthesized by the polycondensation reactions of 1,3‐bis[4,4'‐(trimellitimido) phenoxy] propane 6 with six different aromatic diamines 7a–f in a medium constituting N‐methyl‐2‐pyrrolidone, triphenylphosphite, CaCl₂, and pyridine as condensing agents. The polycondensation reaction produced a series of novel poly(amide‐imide)s 8a–f in high yields with inherent viscosities between 0.35 and 0.63 dL/g. The resulting poly(amide‐imide)s were characterized by elemental analysis, viscosity measurements, thermal gravimetric analysis (TGA and DTG), solubility tests, and FTIR spectroscopy. 1,3‐Bis[4,4'‐(trimellitimido) phenoxy] propane 6 as a new monomer containing trimethylene moiety was synthesized using a three‐step reaction. At first 1,3‐bis[4,4'‐nitrophenoxy] propane 3 was prepared by the reaction of 4‐nitrophenol 1 with 1,3‐dibromo propane 2 in DMF solution . Then, dinitro 3 was reduced to 1,3‐bis[4,4'‐aminophenoxy] propane 4 by using a solution of sodium sulfite in ethanol. Finally, 1,3‐bis[4,4'‐(trimellitimido) phenoxy] propane 6 was prepared by the reaction of one equivalent diamine 4 with two equivalents of trimellitic anhydride 5 in a mixture of acetic acid‐pyridine (3 : 2). © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Synthesis and properties of poly(amide–imide)s based on N,N′‐bis(4‐carboxyphenyl)‐4,4′‐oxydiphthalimide,p‐aminobenzoic acid and various aromatic diamines

A new diimide–diacid monomer, N,N′‐bis(4‐carboxyphenyl)‐4,4′‐oxydiphthalimide (I), was prepared by azeotropic condensation of 4,4′‐oxydiphthalic anhydride (ODPA) and p‐aminobenzoic acid (p‐ABA) at a 1:2 molar ratio in a polar solvent mixed with toluene. A series of poly(amide–imide)s (PAI, III_a–m) was synthesized from the diimide–diacid I (or I′, diacid chloride of I) and various aromatic diamines by direct polycondensation (or low temperature polycondensation) using triphenyl phosphite and pyridine as condensing agents. It was found that only III_k–m having a meta‐structure at two terminals of the diamine could afford good quality, creasable films by solution‐casting; other PAIs III using diamine with para‐linkage at terminals were insoluble and crystalline; though III_g–i contained the soluble group of the diamine moieties, their solvent‐cast films were brittle. In order to improve their to solubility and film quality, copoly(amide–imide)s (Co‐PAIs) based on I and mixtures of p‐ABA and aromatic diamines were synthesized. When on equimolar of p‐ABA (m = 1) was mixed, most of Co‐PAIs IV had improved solubility and high inherent viscosities in the range 0.9–1.5 dl g^?1; however, their films were still brittle. With m = 3, series V was obtained, and all members exhibited high toughness. The solubility, film‐forming ability, crystallinity, and thermal properties of the resultant poly(amide–imide)s were investigated. © 2002 Society of Chemical Industry     

Microwave‐promoted rapid synthesis of new optically active poly(amide imide)s derived from N,N′‐(pyromellitoyl)‐bis‐L‐isoleucine diacid chloride and aromatic diamines

A pyromellitic dianhydride (benzene‐1,2,4,5‐tetracarboxylic dianhydride) was reacted with L ‐isoleucine in acetic acid, and the resulting imide acid [N,N′‐(pyromellitoyl)‐bis‐L ‐isoleucine] (4) was obtained in a high yield. 4 was converted into N,N′‐(pyromellitoyl)‐bis‐L ‐isoleucine diacid chloride by a reaction with thionyl chloride. The polycondensation reaction of this diacid chloride with several aromatic diamines, including 1,4‐phenylenediamine, 4,4′‐diaminodiphenyl methane, 4,4′‐diaminodiphenylsulfone (4,4′‐sulfonyldianiline), 4,4′‐diaminodiphenylether, 2,4‐diaminotoluene, and 1,3‐phenylenediamine, was developed with two methods. The first method was polymerization under microwave irradiation, and the second method was low‐temperature solution polymerization, with trimethylsilyl chloride used as an activating agent for the diamines. The polymerization reactions proceeded quickly and produced a series of optically active poly(amide imide)s with good yields and moderate inherent viscosities of 0.17–0.25 dL/g. All of the aforementioned polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(amide imide)s are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 951–959, 2004     

Synthesis and characterization of novel optically active poly(imide–urethane)s derived from N,N′‐(pyromellitoyl)‐bis‐(L‐leucine) diisocyanate and aromatic diols

N,N′‐(Pyromellitoyl)‐bis‐(L ‐leucine) diacid was reacted with ethyl chloroformate in the presence of triethylamine followed by reaction with activated sodium azide and gave N,N′‐(pyromellitoyl)‐bis‐(L ‐leucine) diacylazide in high yield. This diacylazide was heated in dry benzene and gave the unstable N,N′‐(pyromellitoyl)‐bis‐(L ‐leucine) diisocyanate ( 5 ) in quantitative yield. Thus, diisocyanate 5 was generated in situ and polycondensation reaction of this monomer with several aromatic diols, such as 4,4′‐dihydroxybiphenyl, 1,4‐hydroquinone, bisphenol A, phenolphthalein and 1,4‐dihydroxyanthraquinone, was performed in dry toluene under refluxing in the presence of 1,4‐diazabicyclo[2.2.2]octane (triethylenediamine) as a catalyst. The polymerization reactions proceeded within 48 h, producing a series of optically active poly(imide–urethane)s with good yield and moderate inherent viscosity in the range 0.18–0.28 dl g^?1. All of the above polymers were fully characterized by infrared spectra, elemental analyses and specific rotation. Some structural characterization and physical properties of these optically active poly(imide–urethane)s are reported Copyright © 2003 Society of Chemical Industry     

The preparation of α‐bis and α,ω‐tetrakis aromatic oxazolyl‐ and carboxyl‐functionalized polymers using 1,1‐bis[4‐(2‐(4,4‐dimethyl‐1,3‐oxazolyl))phenyl]ethylene in atom transfer radical polymerization reactions

The preparation of new compounds, 1,1‐bis[4‐(2‐(4,4‐dimethyl‐1,3‐oxazolyl))phenyl]ethanol and a new symmetrically disubstituted 1,1‐diphenylethylene derivative, 1,1‐bis[4‐(2‐(4,4‐dimethyl‐1,3‐oxazolyl))phenyl]ethylene, is described. 1,1‐Bis[4‐(2‐(4,4‐dimethyl‐1,3‐oxazolyl))phenyl]ethylene was utilized as a dioxazolyl initiator precursor for the polymerization of styrene by atom transfer radical polymerization (ATRP) methods to produce α‐bis(oxazolyl) polystyrene. The kinetic study of the polymerization process indicated that the free radical polymerization reaction for the preparation of α‐bis(oxazolyl) polystyrene follows first‐order rate kinetics with respect to monomer consumption. α,ω‐Tetrakis(oxazolyl) polystyrene was prepared by a new, in situ, controlled/living, post‐ATRP chain‐end‐functionalization reaction which involves the direct addition of 1,1‐bis[4‐(2‐(4,4‐dimethyl‐1,3‐oxazolyl))phenyl]ethylene to the ω‐terminus of the α‐bis(oxazolyl) polystyrene derivative, without the isolation and purification of the polymeric precursor. α‐Bis(carboxyl) and α,ω‐tetrakis(carboxyl) polystyrene derivatives were obtained by the quantitative chemical transformation of the oxazoline groups of the respective aromatic oxazolyl chain‐end‐functionalized polystyrene derivatives to the aromatic carboxyl groups. The organic precursor compounds, the dioxazolyl‐functionalized 1,1‐diphenylethylene derivative and the functionalized polymers were characterized using ¹H NMR and ¹³C NMR spectrometry and Fourier transform infrared spectroscopy, size‐exclusion and thin‐layer chromatography and non‐aqueous titration measurements. © 2014 Society of Chemical Industry     

New poly(amide imide)s containing bis(4‐trimellitimidophenyl) sulfone and hydantoin moieties in the main chain: Synthesis and properties

Several new poly(amide imide)s were synthesized through the polycondensation reactions of bis(4‐trimellitimidophenyl) sulfone [N,N′‐(4,4′‐diphenylsulfone) bistrimellitimide] with a number of hydantoin derivatives in a medium consisting of thionyl chloride, N‐methyl‐2‐pyrrolidone, and pyridine. The polycondensations produced a series of novel poly(amide imide)s in high yields with inherent viscosities of 0.20–0.46 dL/g. The resulting poly(amide imide)s were characterized with elemental analysis, viscosity measurements, thermogravimetric analysis, derivative thermogravimetry, solubility testing, and Fourier transform infrared spectroscopy. All the polymers were soluble at room temperature in polar solvents such as N,N‐dimethylacetamide, N,N‐dimethylformamide, dimethyl sulfoxide, tetrahydrofuran, and N‐methyl‐2‐pyrrolidone. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 1776–1782, 2005     

Synthesis and characterization of novel poly(amide imide)s based on bis(p‐amidobenzoic acid)‐n‐trimellitylimido‐L‐leucine

N‐Trimellitylimido‐L ‐leucine was reacted with thionyl chloride, and N‐trimellitylimido‐L ‐leucine diacid chloride was obtained in a quantitative yield. The reaction of this diacid chloride with p‐aminobenzoic acid was performed in dry tetrahydrofuran, and bis(p‐amidobenzoic acid)‐N‐trimellitylimido‐L ‐leucine (5) was obtained as a novel optically active aromatic imide–amide diacid monomer in a high yield. The direct polycondensation reaction of the monomer imide–amide diacid 5 with 4,4′‐diaminodiphenylsulfone, 4,4′‐diaminodiphenylether, 1,4‐phenylenediamine, 1,3‐phenylenediamine, 2,4‐diaminotoluene, and benzidine (4,4′‐diaminobiphenyl) was carried out in a medium consisting of triphenyl phosphite, N‐methyl‐2‐pyrolidone, pyridine, and calcium chloride. The resulting novel poly(amide imide)s (PAIs), with inherent viscosities of 0.22–0.52 dL g^?1, were obtained in high yields, were optically active, and had moderate thermal stability. All of the compounds were fully characterized with IR spectroscopy, elemental analyses, and specific rotation. Some structural characterization and physical properties of these new optically active PAIs are reported. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 35–43, 2002; DOI 10.1002/app.10181     

Synthesis and characterization of organosoluble poly(arylate‐imide)s prepared from direct polycondensation of bis(trimellitimide)‐diacids and various bisphenols

Three diimide‐diacids, 2,2‐bis[4‐(4‐trimellitimidophenoxy)phenyl]hexafluoropropane ( I‐A ), 2,2‐bis[4‐(4‐trimellitimidophenoxy)phenyl]propane ( I‐B ), and 5,5′‐bis[4‐ (4‐trimellitimidophenoxy)phenyl]hexahydro‐4,7‐methanoindan ( I‐C ), were prepared by the azeotropic condensation of trimellitic anhydride with three analogous diamines. Three series of alternating aromatic poly(arylate‐imide)s, having inherent viscosities of 0.41–0.82 dL/g, were synthesized from these diimide‐diacids ( I‐A , I‐B , and I‐C ) with various bisphenols by direct polycondensation using diphenyl chlorophosphate and pyridine as condensing agents. All of the polymers were readily soluble in a variety of organic solvents such as N‐methyl‐2‐pyrrolidone, N,N‐dimethylacetamide, and even in the less polar tetrahydrofuran. These polymers could be cast into transparent and tough films, which had strength at break values ranging from 73 to 98 MPa, elongation at break from 6 to 11%, and initial modulus from 1.6 to 2.2 GPa. The softening temperatures of the polymers were recorded at 145–248°C. They had 10% weight loss at a temperature above 450°C and left 35–51% residue even at 800°C in nitrogen. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3818–3825, 2003     

Microwave‐assisted synthesis of new optically active poly(ester‐imide)s containing N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine moieties

Pyromellitic dianhydride (benzene‐1,2,4,5‐tetracarboxylic dianhydride) (1) was reacted with L‐phenylalanine (2) in a mixture of acetic acid and pyridine (3 : 2) and the resulting imide‐acid [N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine diacid] (4) was obtained in quantitative yield. The compound (4) was converted to the N,N′‐(pyromellitoyl)‐bis‐L‐phenylalanine diacid chloride (5) by reaction with thionyl chloride. A new facile and rapid polycondensation reaction of this diacid chloride (5) with several aromatic diols such as phenol phthalein (6a), bisphenol‐A (6b), 4,4′‐hydroquinone (6c), 1,8‐dihydroxyanthraquinone (6d), 4,4‐dihydroxy biphenyl (6e), and 2,4‐dihydroxyacetophenone (6f) was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions proceeded rapidly and are completed within 20 min, producing a series of optically active poly(ester‐imide)s with good yield and moderate inherent viscosity of 0.10–0.26 dL/g. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these optically active poly(ester‐imide)s are reported. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 2211–2216, 2002     

Synthesis of novel optically active poly(ester‐imide)s with benzophenone linkages by microwave‐assisted polycondensation

A new simple and rapid polycondensation reaction of 4,4′‐carbonyl‐bis(phthaloyl‐L ‐alanine)diacid chloride [N,N ′‐(4,4′‐carbonyldiphthaloyl)]bisalanine diacid chloride with several diphenols, such as bisphenol‐A, phenolphthalein, 1,8‐dihydroxyanthraquinone, 4,4′‐dihydroxybiphenyl, 1,5‐dihydroxynaphthalene and hydroquinone, in the presence of a small amount of a polar organic medium such as o‐cresol was performed using a domestic microwave oven. The polycondensation reaction proceeded rapidly and was almost complete within 12 min to give a series of poly(ester‐imide)s with inherent viscosities of about 0.35–0.58 dl g⁻¹. The resulting poly(ester‐imide)s were obtained in high yield and are optically active and thermally stable. All the above compounds have been fully characterized by IR spectroscopy, elemental analysis, inherent viscosity (η_inh), solubility test and specific rotation. Thermal properties of the poly(ester‐imide)s have been investigated using thermal gravimetric analysis (TGA). © 2000 Society of Chemical Industry     

Synthesis and characterization of novel optically active poly(amide–imide)s containing N,N′‐(pyromellitoyl)‐bis‐L‐valine diacid chloride and 5,5‐disubstituted hydantoin derivatives under microwave irradiation

Pyromellitic dianhydride (1,2,4,5‐benzenetetracarboxylic acid 1,2,4,5‐dianhydide) was reacted with L ‐valine in a mixture of acetic acid and pyridine (3:2) at room temperature, and then was refluxed at 90–100 °C, N,N′‐(pyromellitoyl)‐bis‐L ‐valine diacid was obtained in quantitative yield. The imide–acid was converted to N,N′‐(pyromellitoyl)‐bis‐L ‐valine diacid chloride by reaction with thionyl chloride. Rapid and highly efficient synthesis of a number of poly(amide–imide)s was achieved under microwave irradiation using a domestic microwave oven by polycondensation of N,N′‐(pyromellitoyl)‐bis‐L ‐valine diacid chloride with six different derivatives of 5,5‐disubstituted hydantoin compounds in the presence of a small amount of a polar organic medium that acts as a primary microwave absorber. A suitable organic medium was o‐cresol. The polycondensation proceeded rapidly, compared with conventional melt polycondensation and solution polycondensation and was almost completed within 8 min, giving a series of poly(amide–imide)s with inherent viscosities in the range 0.15–0.36 dl g^?1. The resulting poly(amide–imide)s were obtained in high yield and are optically active and thermally stable. All of the above compounds were fully characterized by Fourier‐transform infrared (FT‐IR) spectroscopy, elemental analysis, inherent viscosity (η_inh) measurements, solubility testing and specific rotation measurements. The thermal properties of the poly(amide–imide)s were investigated by using thermogravimetric analysis. Copyright © 2004 Society of Chemical Industry     

Synthesis and characterization of new cardo poly(ether imide)s derived from 9,9‐bis [4‐(4‐aminophenoxy)phenyl]xanthene

A series of new cardo poly(ether imide)s bearing flexible ether and bulky xanthene pendant groups was prepared from 9,9‐bis[4‐(4‐aminophenoxy)phenyl]xanthene with six commercially available aromatic tetracarboxylic dianhydrides in N,N‐dimethylacetamide (DMAc) via the poly(amic acid) precursors and subsequent thermal or chemical imidization. The intermediate poly(amic acid)s had inherent viscosities between 0.83 and 1.28 dL/g, could be cast from DMAc solutions and thermally converted into transparent, flexible, and tough poly(ether imide) films which were further characterized by X‐ray and mechanical analysis. All of the poly(ether imide)s were amorphous and their films exhibited tensile strengths of 89–108 MPa, elongations at break of 7–9%, and initial moduli of 2.12–2.65 GPa. Three poly(ether imide)s derived from 4,4′‐oxydiphthalic anhydride, 4,4′‐sulfonyldiphthalic anhydride, and 2,2‐bis(3,4‐dicarboxyphenyl))hexafluoropropane anhydride, respectively, exhibited excellent solubility in various solvents such as DMAc, N,N‐dimethylformamide, N‐methyl‐2‐pyrrolidinone, pyridine, and even in tetrahydrofuran at room temperature. The resulting poly(ether imide)s with glass transition temperatures between 286 and 335°C had initial decomposition temperatures above 500°C, 10% weight loss temperatures ranging from 551 to 575°C in nitrogen and 547 to 570°C in air, and char yields of 53–64% at 800°C in nitrogen. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Microwave‐assisted polycondensation of 4,4′‐(hexafluoroisopropylidene)‐N,N′‐bis(phthaloyl‐L‐leucine) diacid chloride with aromatic diols

A new facile and rapid polycondensation reaction of 4,4′‐(hexafluoroisopropylidene)‐N,N′‐bis(phthaloyl‐L ‐leucine) diacid chloride (1) with several aromatic diols such as phenol phthalein (2a), bis phenol‐A (2b), 4,4′‐hydroquinone (2c), 1,4‐dihydroxyanthraquinone (2d), 1,8‐dihydroxyanthraquinone (2e), 1,5‐dihydroxy naphthalene (2f), dihydroxy biphenyl (2g), and 2,4‐dihydroxyacetophenone (2h) was performed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions proceeded rapidly, compared with the conventional solution polycondensation, and was completed within 10 min, producing a series of optically active poly(ester‐imide)s with quantitative yield and high inherent viscosity of 0.50–1.12 dL/g. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of this optically active poly(ester‐imide)s are reported. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 77: 3003–3009, 2000     

Thermal and thermo‐oxidative degradation properties of poly(benzimidazole amide imide) copolymers

In this study, 3,3′‐dinitrobenzidine was first reacted with excess isophthaloyl chloride to form a monomer with dicarboxylic acid end groups. Two types of aromatic dianhydride, [viz., pyromellitic dianhydride (PMDA) and 3,3′,4,4′‐sulfonyldiphthalic anhydride (DSDA)] also were reacted with excess 4,4′‐diphenyl‐ methane diisocyanate (MDI) to form polyimide prepolymers terminated with isocyanate groups. The prepolymers were reacted further with the diacid monomer to form a nitro group–containing aromatic poly(amide imide) copolymers. The nitro groups in these copolymers were hydrogenated to form amine groups and cyclized at 180°C to form the poly(benzimidazole amide imide) copolymers in polyphosphoric acid (PPA), which acts as a cyclization agent. From the viscosity measurements, copolymer appeared to be a reasonably high molecular weight. From the differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) measurements it was shown that the glass transition temperature of copolymers was in the range of ～270–322°C. The 10% weight loss temperatures were in the range of 460 ～ 541°C in nitrogen and ～441–529°C in air, respectively. The activated energy and the integration parameter of degradation temperature of the copolymers were evaluated with the Doyle‐Ozawa method. It indicated that these copolymers have good thermal and thermo‐oxidative stability with the increase in imide content. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2072–2081, 2004     

Application of microwave irradiation for synthesis of novel optically active poly(amide imides) derived from diacid chloride containing epiclon and L‐isoleucine with aromatic diamines

Epiclon [3a,4,5,7a‐tetrahydro‐7‐methyl‐5‐(tetrahydro‐2,5‐dioxo‐3‐furanyl)‐1,3‐isobenzofurandione] or [5‐(2,5‐dioxotetrahydrofurfuryl)‐3‐methyl‐3‐cyclohexyl‐1,2‐dicarboxylic acid anhydride] (1) was reacted with L ‐isoleucine (2) in acetic acid and the resulting imide acid (3) was obtained in high yield. The diacid chloride (4) was obtained from diacid derivative (3) by reaction with thionyl chloride. The polycondensation reaction of diacid chloride (4) with several aromatic diamines such as 4,4′‐sulfonyldianiline (5a), 4,4′‐diaminodiphenyl methane (5b), 4,4′‐diaminodiphenylether (5c), p‐phenylenediamine (5d), m‐phenylenediamine (5e), 2,4‐diaminotoluene (5f), and 4,4′‐diaminobiphenyl (5g) was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as o‐cresol. The polymerization reactions were also performed in two other different methods: low‐temperature solution polycondensation and reflux conditions. A series of optically active poly(amide imides) with inherent viscosity of 0.12–0.30 dL/g were obtained. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation techniques. Some structural characterizations and physical properties of these optically active poly(amide imides) are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2218–2229, 2004     

Synthesis of new optically active poly(amide‐imide)s containing EPICLON and L‐phenylalanine in the main chain by microwave irradiation and classical heating

EPICLON [3a,4,5,7a‐Tetrahydro‐7‐methyl‐5‐(tetrahydro‐2,5‐dioxo‐3‐furanyl)‐1,3‐isobenzofurandione] or [5‐(2,5‐dioxotetrahydrofurfuryl)‐3‐methyl‐3‐cyclohexyl‐1,2‐dicarboxylic acid anhydride] ( 1 ) was reacted with L ‐phenylalanine ( 2 ) in acetic acid, and the resulting amic acid was refluxed under a Dean‐Stark system with benzene, which produced diacid ( 3 ) in high yield. Compound ( 3 ) was converted to the diacid chloride ( 4 ) by reaction with oxalyl chloride in dry carbon tetrachloride. The polycondensation reaction of this diacid chloride ( 4 ) with several aromatic diamines such as 4,4′‐sulfonyldianiline ( 5a ), 4,4′‐diaminodiphenylmethane ( 5b ), 4,4′‐diaminodiphenylether ( 5c ), 1,4‐phenylenediamine ( 5d ), 1,3‐phenylenediamine ( 5e ), 2,4‐diaminotoluene ( 5f ), and 1,5‐diaminonaphthalene ( 5g ) was developed by using a domestic microwave oven in the presence of a small amount of a polar organic medium such as N‐methylpyrrolidone ( NMP ). The polymerization reactions were also performed under two different classical heating methods: low temperature solution polycondensation in the presence of trimethylsilyl chloride, and high temperature polymerization. A series of optically active poly(amide‐imide)s with moderate yield and inherent viscosity of 0.14–0.22 dL/g were obtained. All of the above polymers were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of this optically active poly(amide‐imide)s are reported. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 91: 3281–3291, 2004     

Synthesis of novel poly(amide‐imide)s containing trimellitylimido‐DL/L‐alanine moieties via direct polycondensation

N‐Trimellitylimido‐DL and L ‐alanine ( 3 ) were prepared from the reaction of trimellitic anhydride ( 1 ) with DL and L ‐alanine ( 2 ) in N,N‐dimethyl formamide (DMF) solution at refluxing temperature. The direct polycondensation reaction of the monomers imide‐diacid ( 3 ) with 4,4′‐diaminodiphenylsulfone ( 4a ), 4,4′‐diaminodiphenylmethane ( 4b ), 1,4‐phenylenediamine ( 4c ), 1,3‐phenylenediamine ( 4d ), 2,4‐diaminotoluene ( 4e ), and 4,4′‐diaminodiphenylether ( 4f ) was carried out in a medium consisting of triphenyl phosphite, N‐methyl‐2‐pyrolidone (NMP), pyridine, and calcium chloride. The resulting poly(amide‐imide)s PAIs, with inherent viscosities 0.32–0.66 dL/g, were obtained in high yield. All of the above‐mentioned compounds were fully characterized by IR, elemental analyses, and specific rotation. Some structural characterization and physical properties of these new optically active PAI s are reported. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 80: 1312–1318, 2001     

Synthesis and characterization of novel optically active poly(amide‐imide)s

4,4′‐(Hexafluoroisopropylidene)‐bis‐(phthalic anhydride) (1) was reacted with L ‐leucine (2) in toluene solution at refluxing temperature in the presence of triethylamine and the resulting imide‐acid (4) was obtained in quantitative yield. The compound (4) was converted to the diacid chloride (5) by reaction with thionyl chloride. The polymerization reaction of the imide‐acid chloride (5) with 1,6‐hexamethylenediamine (6a) , benzidine (6b) , 4,4′‐diaminodiphenylmethane (6c) , 1,5‐diaminoanthraquinone (6d) , 4,4′‐sulfonyldianiline (6e) , 3,3′‐diaminobenzophenone (6f) , p‐phenylenediamine (6g) and 2,6‐diaminopyridine (6h) was carried out in chloroform/DMAc solution. The resulting poly(amide‐imide)s were obtained in high yield and are optically active and thermally stable. All of the above compounds were fully characterized by IR, elemental analyses and specific rotation. Some structural characterization and physical properties of those optically active poly(amide‐imide)s are reported. © 1999 Society of Chemical Industry     

Effects of addition orders on the properties of fluorine‐containing copolyimides

A series of fluorine‐containing copolyimides were synthesized by three different orders of addition of monomers. The fluorine‐containing copolyimides were prepared by the reaction of 4,4′‐diaminodiphenylmethane (DDM) with 2,2′‐bis(3,4‐dicarboxyphenyl) hexafluoropropane dianhydride (6FDA), and pyromellitic dianhydride (PMDA). The synthesis reactions of the copoly(amic acid)s (PA) were carried out by three different orders of addition of the monomers with different molar ratios of 6FDA to PMDA. The viscosity of the PA solution obtained by DDM–(6FDA+PMDA), that is, 6FDA and PMDA added simultaneously to DDM in N‐methyl‐2‐pyrrolidinone (NMP), was higher than the other two addition orders (i.e., DDM–6FDA–PMDA and DDM–PMDA–6FDA). The viscosity decreased as the relative amount of 6FDA to PMDA increased. The copolyimides formed by different addition orders but the same 6FDA‐to‐PMDA molar ratios contained different properties, such as dielectric constant, moisture absorption, contact angle, and optical transparency. All of these copolyimides were insoluble in common organic solvents, such as NMP and tetrahydrofuran. Thermogravimetric analysis showed that the onset temperature of 8% weight loss decreased slightly as [6FDA] : [PMDA] increased. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 77: 3252–3258, 2000     

Synthesis of new poly(amide–imide)s derived from trimellitylimido‐L‐phenylalanine

N‐Trimellitylimido‐L ‐phenylalanine was prepared from the reaction of 1,2,4‐benzenetricarboxylic anhydride with L ‐phenylalanine in N,N‐dimethylformamide solution at refluxing temperature. The direct polycondensation reaction of the monomer imide‐diacid with 4,4′‐diaminodiphenylsulfone, 4,4′‐diaminodiphenylmethane, 1,4‐phenylenediamine, 1,3‐phenylenediamine, 2,4‐diaminotoluene, 4,4′‐diaminodiphenylether and benzidine was carried out in a medium consisting of triphenyl phosphite, N‐methyl‐2‐pyrrolidone, pyridine and calcium chloride. The resulting poly(amide–imide)s, PAIs, having inherent viscosities of 0.21–0.45 dlg^?1 were obtained in high yield. All of the above compounds were fully characterized by IR spectroscopy and elemental analyses. The optical rotation of all PAIs has also been measured. Some structural characterization and physical properties of these new optically active PAIs are reported. © 2001 Society of Chemical Industry