不同煤化程度煤种对飞灰导电特性影响的实验研究

研究了不同煤化程度煤种的导电特性的实验结果表明,高煤化煤种与低煤化煤种的导电特性相差极大。前者比电阻可降至106Ω·cm以下,几十伏电压即发生电击穿。而后者比电阻最高可达10¹²Ω·cm以上,击穿电压超过10kV;高煤化燃煤飞灰的含碳量达到20％时,比电阻发生了陡降,而低煤化燃煤飞灰的含碳量对飞灰导电特性的影响不大,甚至产生负面影响。导致这一结果的机理是不同煤化程度煤种的晶体结构的差异     

双极荷电静电除尘器收集高比电阻微尘的实验

根据粉尘层反电晕现象分析,提出在接地收尘极板上布置芒刺反电晕放电极的双极电晕静电除尘器,这种双极电晕静电除尘器能避免粉尘层的反电晕。在平均场强约3.4kV/cm时,采用粒子图像测速仪(PIV)测得电场内正、负离子风的核心区风速约2m/s。实验表明,离子风对收集微细粉尘有很好的促进作用。在常温常压下,平均场强为3.4kV/cm、气流速度在0.5～2.0m/s的范围内,对质量中位径为0.159μm、比电阻为2.4×1014Ω.cm的硅微粉的电除尘效率测定结果表明,双极荷电静电除尘器的除尘效率高于单极荷电静电除尘器。观察发现,由于接地芒刺的存在,即使对于比电阻高达2.4×1014Ω.cm的硅微粉,沉积在双极荷电静电除尘器收尘极板上的粉饼没有出现反电晕。     

电除尘器对低比电阻粉尘收集的研究

使用电除尘器收集低比电阻粉尘时,由于放电过快,易产生“反弹“,形成“跳跃收集“过程,除尘效率较低。本文研究了电除尘器阳极板涂装后对低比电阻粉尘收集效果,并通过调节断面风速、粉尘浓度、电压、电晕线改善除尘器性能。研究表明:极板涂装对提高电除尘器收集低比电阻粉尘效率影响显著。     

电除尘器对低比电阻粉尘收集的研究

电除尘器收集低比电阻粉尘,由于放电过快,易产生“反弹”,形成“跳跃收集”过程,除尘效率较低。本文论述了电除尘器阳极板涂装后对低比电阻粉尘收集效果,并通过调节断面风速、粉尘浓度、电压、电晕线改善除尘器性能。研究表明：极板涂装对提高电除尘器收集低比电阻粉尘效率影响显著;采用圆形电晕线收尘效率最高,且随着电压的升高而逐渐升高,高于某一电压值后,收尘效率反而下降;进口断面风速控制在0．2m／s到0．3m／s之间,可以取得较高的收尘效率;收尘效率随着入口粉尘浓度的增加而逐渐增加,增加速率逐渐减小。     

SiO2对垃圾焚烧飞灰熔融固化特性的影响

研究了在飞灰中添加不同比例的SiO2对熔融处理的影响,分析了熔融温度、挥发率、重金属固定率的变化规律.研究表明SiO2添加量为1%和10%的飞灰熔融温度相差大约70℃,挥发率相差20.7%;处理温度较高时,大量添加SiO2对挥发量影响很小;飞灰中添加SiO2可以增加重金属Pb的固定率,对Cu和Cd的影响不显著,反而使得Zn的固定率降低.结果表明,在较高的处理温度下,温度是影响重金属固定率的主要因素之一,此时大量添加SiO2既不能增强重金属固化效果,也不能达到减少挥发率的目的.     

CO2对飞灰稳定化效果的影响

用CO2作为化学稳定剂或辅助稳定剂处理三种不同的来自实际垃圾焚烧厂的飞灰，并对处理后的飞样进行浸滤实验来衡量稳定效果。结果表明二氧化碳对飞灰中所含的重金属Pb和Cd具有稳定效果，对飞灰中的Cr有促进溶出的效果。当以磷酸盐和绿矾为稳定剂稳定飞灰中的重金属时，先采用CO2进行预处理基本不影响对Pb和Cd的稳定效果，但对Cr的浸出控制有明显的促进效果。     

转炉烟气含水量对干法除尘效率的影响

随着环境的不断趋于恶化,现阶段在工业生产过程中我国十分注重环境保护以及工业三废的处理,在转炉钢铁冶炼过程中其所产生的烟气非常多,给空气质量带来严重影响作用,而现有的湿法和干法两种不同除尘系统都存在一定的缺陷,本文通过对其中干法除尘系统进行分析不断优化其除尘效率和质量,为工业生产的环保化发展奠定良好基础。     

Fe_2O_3纳米粒子对土壤呼吸作用的影响研究

为了解Fe2O3纳米粒子对土壤有机碳分解矿化能力的影响,本研究采用室内培养实验,探讨了Fe2O3纳米粒子对土壤呼吸作用的影响。结果表明,在土壤中添加Fe2O3纳米粒子能够增强土壤呼吸作用,当Fe2O3纳米粒子加入量为10 g·kg-1时,土壤呼吸作用最强。本研究表明Fe2O3纳米粒子具有增强土壤有机碳分解矿化的作用。     

微波诱导催化剂Fe_2O_3/Al_2O_3制备及PEG对其活性影响

以AlCl·36H2O、FeCl·36H2O和CO(NH)22为原料,采用均匀沉淀法制备微波诱导催化剂Fe2O3/Al2O3,用X射线衍射仪(XRD)对其结构进行了表征,研究了加入聚乙二醇(PEG200)作为分散剂对产物的影响。结果表明:加入体积分数为0.05%PEG后,对于20mg/L的甲基橙模拟废水,在微波功率为900W,催化剂投加量为2g/L,处理5min后脱色率可达95.8%。     

粉煤灰对单体直接染料脱色效果的研究

就粉煤灰的投加量、染料的初始浓度、pH值及脱色时间等因素对单体直接染料脱色效果进行了研究，结果表明：在加灰量为0.006g/ml、gH值为2－10、脱色时间为20－30min时，粉煤灰对单体直接染料具有良好的脱色效果。     

粉煤灰资源化特性及路面工程应用技术研究

在实验室对粉煤灰的各项技术参数进行了试验研究 ,揭示出粉煤灰的不同成分和形貌对其资源化特性的影响规律 ;初步完成了消除不利于粉煤灰资源化的有害成分---碳的优化实验工作 ;进行了脱炭粉煤灰混凝土配合比等方面的试验研究 ,并在路面修复工程中应用脱炭粉煤灰完成了试验路修筑工作。结果表明 ,将粉煤灰进行脱炭处理 ,应用于混凝土工程可以明显改善混凝土的工作性能 ,实际道路运营和技术性能符合路面工程的要求 ,具有重大的经济效益和环境效益     

熔融-水热法合成粉煤灰沸石及其吸附性能研究

以粉煤灰为原料，研究了在熔融温度分别为300℃、400℃、500℃，熔融时间分别为1h、2h、3h，水热温度分别为45℃、65℃、85℃，水热时间分别为6h、8h、10h，对合成粉煤灰沸石（FZ）吸附性能的影响。结果表明熔融温度为300℃，熔融保温时间为1h，水热温度为65℃，水热保温时间为6h，产物中有类沸石生成。熔融-水热合成Fz对Cd^2＋吸附率为99．82％，吸附量为0．19964mg／g，略高于活性炭（吸附率99．69％）优于天然沸石（吸附率97．94％）。     

Use of zeolitized coal fly ash in the simultaneous removal of ammonium and phosphate from aqueous solution

Discharge of wastewater containing nitrogen and phosphate can cause eutrophication. Therefore, the development of an efficient material for the immobilization of the nutrients is important. In this study, a low calcium fly ash and high calcium fly ash were converted into zeolite using the hydrothermal method. The removal of ammonium and phosphate that coexist in aqueous solution by the synthesized zeolites were studied. The results showed that zeolitized fly ash could efficiently eliminate ammonium and phosphate at the same time. Saturation of zeolite with Ca²⁺ rather than Na⁺ favored the removal of both ammonium and phosphate because the cation exchange reaction by the NH₄ ⁺ resulted in the release of Ca²⁺ into the solution and precipitation of Ca²⁺ with PO₄ ³⁻ followed. An increase in the temperature elevated the immobilization of phosphate whereas it abated the removal of ammonium. Nearly 60% removal efficiency for ammonium was achieved in the neutral pH range from 5.5 to 10.5, while the increase or decrease in pH out of the neutral range lowered the adsorption. In contrast, the removal of phosphate approached 100% at a pH lower than 5.0 or higher than 9.0, and less phosphate was immobilized at neutral pH. However, there was still a narrow pH range from 9.0 to 10.5 favoring the removal of both ammonium and phosphate. It was concluded that the removal of ammonium was caused by cation exchange; the contribution of NH₃ volatilization to immobilization at alkaline conditions (up to pH level of 11.4) was limited. With respect to phosphate immobilization, the mechanism was mainly the formation of precipitate as Ca₃(PO₄)₂ within the basic pH range or as FePO₄ and AlPO₄ within acidic pH range.     

黏土与粉煤灰吸附农村生活垃圾渗滤液的效能及机理

分别以黏土和粉煤灰作为吸附剂,研究单一材料下吸附时间、吸附剂投加量和渗滤液初始pH对农村生活垃圾渗滤液吸附效能的影响及吸附机理。综合考虑去除效果、运行成本及可操作性,选择吸附时间为180 min、吸附剂投加量为50 g/L、渗滤液初始pH为自然值(7.5~8.0)作为实际运行工况。结果表明:黏土对农村生活垃圾渗滤液中化学需氧量(COD_Cr)、氨氮(NH₃-N)、总氮(TN)、总磷(TP)的去除率分别为25.58%、14.87%、41.63%和62.25%,粉煤灰为33.01%、18.18%、22.07%和60.46%;黏土对重金属Cr、As、Cd、Ni和Pb的去除率分别为13.04%、43.34%、60.24%、47.52%和61.77%,粉煤灰为10.53%、31.52%、84.30%、65.73%和68.65%。黏土和粉煤灰对渗滤液中污染物的等温吸附较符合Freundlich模型,化学吸附在多种吸附作用中占主导作用。     

烧结升温方式及气氛对水洗焚烧飞灰晶体演变的影响

为使水洗焚烧飞灰的稳定化处理进一步优化，探讨了热处理的加热过程、气氛条件等对水洗焚烧飞灰晶体成分演变的影响.同时也探讨了3种飞灰：锅炉飞灰（RFA）、CaO/Ca（OH）₂和NaHCO₃分别作为中和剂得到的两种飞灰（CaFA和NaFA）水洗后（RFA-II#、CaFA-II#和NaFA-II#）进行热处理比较.结果发现700℃是个转折点，从这个温度点开始3种水洗飞灰中的晶体成分发生明显变化；原位连续加热模式更容易形成固体溶液因而更适合重金属的稳定；NaFA-II#较之CaFA-II#更易于稳定重金属成分.Factsage的模拟结果与XRD结果一致，而且发现飞灰中氯化物在加热过程中首先释放的是HCl.     

垃圾焚烧飞灰重金属含量与渗滤特性分析

对国内 2种不同的垃圾焚烧炉型———炉排炉与流化床产生的飞灰进行了特性分析 .结果表明 ,飞灰在粒径分布上有相似的规律 .炉排炉飞灰中重金属含量高于流化床飞灰中的含量 .飞灰的渗滤特性表明 ,重金属的渗滤特性受渗滤液的pH影响很大 .     

用偏高岭石、铜矿尾砂、粉煤灰生产土聚水泥试验

以偏高岭石和固体废物铜矿尾砂、粉煤灰为基料,以氢氧化钠、水玻璃等作为激发剂,在室温条件下制备土聚水泥。通过正交试验,研究不同基料配比、激发剂、外加剂的不同加入量等因素对试条抗压强度的影响,并确定最优配方;同时通过SEM观察了土聚水泥的形貌并研究了土壤聚合的反应机理。结果表明:其最佳配方中铜矿尾砂、粉煤灰的质量比之和接近60%,7天抗压强度比标号为P.O42.5的水泥高5%;该土聚水泥呈层状结构,缝隙较小,结构紧密。     

生活垃圾焚烧飞灰差异性特征对脱氯除盐效果影响研究——以重庆和天津飞灰为例

随着生活垃圾焚烧技术的普及,垃圾焚烧飞灰的资源化利用迫在眉睫,然而飞灰中的高浓度氯元素严重阻碍了其资源化进程.水洗技术作为常用的脱氯除盐技术,得到越来越多的应用,但除氯效果受飞灰自身性质特征影响较大.本研究从重庆和天津采集了两种理化性质具有较大差异的垃圾焚烧飞灰,在对其粒径分布、化学组成、矿物组成、pH值和浸出毒性等基本特征进行分析表征的基础上,采用水洗技术和碳酸化水洗技术对两种飞灰进行了脱氯处理.结果表明,重庆飞灰氯元素的赋存形态包括NaCl、KCl等可溶性氯盐,还含有较高浓度的难溶氯盐(如CaClOH、Friedel盐和Ca₆(CO₃)₂(OH)₇Cl),因此,水洗技术难以达到理想的脱氯效果,氯盐去除率最高为88%.在水洗过程中通入CO₂可以显著降低反应体系的pH值,促进难溶盐的转化和溶解,进而提高飞灰氯盐的去除率.重庆飞灰采用加速碳酸化水洗技术,氯盐去除率最高可达94%.天津飞灰中氯元素主要以可溶性氯盐的形式存在,难溶盐占比很少,因此,水洗技术可以达到较高的脱盐率(96%).采用加速碳酸化技术对天津飞灰进行处理,发现氯盐去除率较纯水洗技术反而有所降低,分析其主要原因可能与加速碳酸化过程中碳酸钙等物质的再沉淀对氯盐的裹挟作用有关.由此可知,飞灰自身性特征尤其是氯盐的赋存形态对于脱氯除盐技术的选择有重要影响.因此,实际资源化利用过程中,可根据飞灰性质来决定预处理手段,从而最大化提升效率和节约成本.