Effective Ru moment in RuSr2Eu2−xCexCu2O10 from high-temperature magnetic susceptibility

We have made high-temperature (250 K<T<800 K) DC susceptibility measurements in the compounds RuSr₂Eu_2−xCe_xCu₂O₁₀ for x=0.6,0.8, and 1.0 in order to determine the Ru effective magnetic moment. After carefully subtracting all contributions to the magnetic susceptibility except that of the Ru ions, we have been able to fit the Ru susceptibility with a law χ_Ru=χ₀+C_Ru/(T−Θ_Ru). We have found that the Ru effective moment falls between the values expected for Ru⁵⁺ in spin states and . We have also found a dependence of μ_eff(Ru) and Θ_Ru with the Ce content x.     

Tuning the multiferroic properties of Pb(Fe1/2Nb1/2)O3 by cationic substitution

A series of substituted lead iron niobate compounds with the general formula Pb²⁺_(1−x)A^Z_x(Fe_{{(1−(2−Z)x)/2}}Nb_{{(1+(2−Z)x)/2}})O₃ (0<x<0.6 and A=La³⁺, K⁺ or Sr²⁺) were prepared by a modified solid-state synthesis. The relative concentrations of Fe³⁺ and Nb⁵⁺ were adjusted to compensate the charge imbalance due to the aliovalent substitution. The dielectric constant and magnetic susceptibilities were studied as a function of temperature. The temperature of the dielectric maximum, T_M, of the substituted compounds decreased linearly with increasing concentration of the substituent ions. The magnetic measurements showed an antiferromagnetic transition at temperatures T_N1 due to the superexchange interactions mediated by Fe–O–Fe and an additional antiferromagnetic-type transition at T_N2. T_N1 linearly increased with the increasing concentration of Fe³⁺ ion at the B-site of ABO₃-type substituted compounds. T_M is shown to be directly dependent on the concentration of the ferroactive Nb⁵⁺ ions at the B-site and Pb²⁺ ions at the A-site.     

Disruption of antiferromagnetic order in Zn-doped La2CuO4

The magnetic phase diagram of La₂(Cu_1−xZn_x)O₄ has been determined from zero-field muon-spin-rotation (ZF-μSR) data taken at LAMPF for 0 ≤ x ≤ 0.10. Antiferromagnetic onset temperatures follow T_N(x) from susceptibility measurements on the same samples. However, the order becomes long range, as evidenced by a well-defined internal magnetic field, only at temperatures well below T_N. Extrapolation of our results yields T_N → 0 K at x = 0.11 for a single (Cu_1−xZn_x)O₂ plane, and comparison with YBa₂(Cu_1−xZn_x)₃O₆ implies identical disruption of magnetism by Zn doping in the single- and double-plane systems.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Doping effects in the Sr14Cu24O41-type structure: a Raman scattering study

Polarized micro-Raman spectra of different compounds belonging to the Sr₁₄Cu₂₄O₄₁-type structure were studied. In the spectra with parallel polarization along the plane crystal axes of the insulating samples Sr₉R₅Cu₂₄O₄₁ (R = La, Y) a broad peak near 3000 cm⁻¹, similar to the well-known two-magnon peak in the layered cuprates, was observed. In addition to the Raman lines characteristic for this structure, we observed only in the spectra with parallel to the chains numerous lines between 100 and 1200 cm⁻¹, probably originating from Raman-forbidden infrared-active only LO phonons and their combinations. In the spectra of the conducting compounds Sr_14−xCa_xCu₂₄O₄₁ (x = 0,7) these features were very weak or disappeared. We interpret these results as Raman evidence for hole doping of the Cu₂O₃ “spin-ladder” planes and for a redistribution of holes between chains and planes through Ca substitution in the case of the rare-earth-free samples.     

Niobium based tetragonal tungsten bronzes as potential anodes for solid oxide fuel cells: synthesis and electrical characterisation

In this paper we report studies on a range of niobate based tungsten bronzes, with a view to analysing their potential as anode materials in SOFCs. Six systems were studied, (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃, Sr_0.6−xLa_xTi_0.2+xNb_0.8−xO₃, (Sr_0.4−xBa_x)Na_0.2NbO₃, (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃, Ba_0.5−xA_xNbO₃ (A=Ca, Sr), and Ba_0.3NbO_2.8, and the electrical conductivities were examined over a range of oxygen partial pressures (10⁻²⁰–1 bar). All the systems showed good conductivity in low oxygen partial pressures, with values as high as 8 S cm⁻¹ at 930°C (P(O₂)=10⁻²⁰ bar). As the oxygen partial pressure was raised the conductivity dropped showing in most cases an approximate [P(O₂)]^−1/4 dependence and good re-oxidation kinetics. Of all the samples studied the (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃ and (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃ systems appear most promising for potential use as anode materials in SOFCs.     

Physical characterization and vibrational spectroscopy of Bi(Pb) cuprate 2212 ceramics prepared by sol-gel

Samples of bismuth cuprate with and without lead substitution were prepared by the sol-gel method. The general formula was Bi_2−xPb_xSr₂CaCu₂O_8+δ, where 0≤x≤0.6. The samples were characterized by X-ray diffraction (XRD), electron probe microanalysis (EPMA), magnetic susceptibility, Raman spectroscopy and IR reflectance. Regarding homogeneity, density, purity and superconductivity, optimal behavior was found x = 0.2-0.4. An increase of hole concentration in the CuO₂-planes with Pb²⁺/Bi³⁺ ratio was observed from the optical data. The Raman spectra modifications with lead substitution are discussed. Evidence of the interaction between CuO₂-plane hole continuum and 150 cm⁻¹ IR active modes was found.     

Effects of cation- or oxide ion-defect on conductivities of apatite-type La–Ge–O system ceramics

A series of apatite-type La–Ge–O ceramics were prepared and their cation-defect at the 4f+6h sites and oxide ion-defect at 2a site were investigated. In La_xGe₆O_12+1.5x ceramics of x=6–12, the higher conductivities were obtained in the region of apatite composition, La_x(GeO₄)₆O_1.5x−12 (x=8–9.33), and the highest conductivity was achieved for La₉(GeO₄)₆O_1.5 (x=9), where the number of cation (La³⁺) occupying the 4f+6h sites is 9 and the number of oxide ion occupying the 2a site is 1.5. The ceramics with cation- and oxide ion-defects were La_9−0.66xSr_x(GeO₄)₆O_1.5 (x=0–1), La_9−1.33xZr_x(GeO₄)₆O_1.5 (x=0–1), La_9−xSr_x(GeO₄)₆O_1.5−0.5x (x=0–3), La_9−xZr_x(GeO₄)₆O_1.5+0.5x (x=0–1), La_x(GeO₄)_3x−21(AsO₄)_27−3xO_1.5 (x=0–3), La_x(GeO₄)_33−3x(AlO₄)_3x−27O_1.5 (x=0–3), La₉(GeO₄)_6−x (AlO₄)_xO_1.5−0.5x (x=0–3), La₉(GeO₄)_6−x(AsO₄)_xO_1.5+0.5x (x=0–1), La_9.33−xSr_x(GeO₄)₆O_2−0.5x (x=0–1.2) and La_x(GeO₄)_4.5(AlO₄)_1.5O_1.5x−12.75 (x=8.8–9.83), which were prepared by the partial substitution of La³⁺and GeO₄⁴⁻of the basic apatite La₉(GeO₄)₆O_1.5 with Sr²⁺ or Zr⁴⁺ and AlO₄⁵⁻ or AsO₄³⁻. Such substitutions lowered the conductivity of La₉(GeO₄)₆O_1.5. These results were discussed by the electrostatic interaction between Sr²⁺, Zr⁴⁺, AlO₄⁵⁻ or AsO₄³⁻ and oxide ion as a conductive species.     

Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

A study on the nonstoichiometry of tin oxides by coulometric titration

In this investigation, nonstoichiometries and defect structures of tin oxides were studied between 694 and 990 K by coulometric titration using solid state electrolyte (YSZ) cells. The relationship between nonstoichiometry of the oxide (x) and equilibrium oxygen partial pressure (P_o2) was expressed by the proportionality: xP_O2^−1/6. An intermediate oxide phase, Sn₃O₄ between Sn and SnO₂ was observed in the temperature range of 696–732 K. The standard Gibbs energy of formation of Sn₃O₄ via the reaction; was found to be ΔG^o_Sn3O4 = −1163960+417.36 T (J/mol). The standard Gibbs energy change for the defect formation reaction in SnO_2−x was calculated to be ΔG^o_SnO2−x = 3.05×10⁵−38.97 T (J/mol)).     

Effect of Sn doping on the magnetic and transport properties of LaMnO3+δ

We report the influence of the Sn doping on the magnetotransport properties of the LaMnO_3+δ perovskite. Two series of samples with nominal LaSn_xMn_1−xO_3+δ (I series) and La_{(1−x)/(1+x)}Sn_xMn_1−xO_3+δ (II series) compositions (x=0, 0.025, 0.05 and 0.10) were prepared at T_s=750°C. The M(T) data under 0.01 and 0.5 T for the I series reveal a depressed magnetization as the Sn content increases suggesting the presence of magnetic clusters with a superparamagnetic behavior. Resistivity measurements indicate an insulator material for all Sn content independently of the applied magnetic field. On the contrary, for the II series the M(T) and M(H) data reveal FM behavior and an improvement of the magnetization as Sn increases. These samples show magnetoresistance. The magnetotransport properties are discussed in terms of the presence of A-site cation vacancies.     

Synthesis and characterization of the Aurivillius phases Bi2 − xPbxSr1 − xNdxNb2O9

The n = 2 Aurivillius phase Bi_{2 − x}Pb_xSr_{1 − x}Nd₂O₉ was successfully synthesized as a ceramic material over the whole range of simultaneous, charge compensated substitution x = 0–1.0. Structural investigations were performed by Rietveld refinement applying different space groups Fmmm and A2₁am, and additionally by X-ray absorption spectroscopy (EXAFS) on the Nd L_III-edge, confirming the accommodation of Nd on the atomic sites of Sr, which implies the substitution of Bi³⁺ by the isoelectronic Pb²⁺. The ferroelectric transition temperature T_c = 270 °C of the substituted powders with x = 0.4 and 1.0 is distinctly reduced compared to the unsubstituted sample with T_c = 450 °C. In temperature resolved powder X-ray diffraction patterns no structural phase transition could be detected.     

Magnetic properties of the Bi1.95Sr2.05−xLaxCuOy (Bi-2201) superconducting phase

We have investigated the reversible mixed-state magnetization M of three lanthanum substituted Bi_1.95Sr_2.05−xLa_xCuO_y (Bi-2201) ceramic samples having different critical temperatures T_c ranging from 20.0 to 35.5 K. As for the Bi₂Sr₂CaCu₂O_8+δ (Bi-2212) phase, we found that anisotropy of Bi-2201 is large. A manifestation of this anisotropy is the field independent magnetization M^* observed at a temperature T^*. In the framework of the London model, and including thermal fluctuations of vortices, we found for the temperature dependence of the penetration depth λ_ab(T) = λ_ab(0)[1 − (T/T_c0)ⁿ]^−1/2, with n 1.7 and λ_ab (T = 0) 4000 Å. The estimated upper critical fields μ₀H_c2,c are of the order of 10 T. We observe a peculiar negative slope M/T at low temperature and sufficiently high external magnetic field. This feature seems to be a characteristic of the Bi-2201 phase. However, we do not know whether it is associated with the superconducting mixed-state. A small amount of magnetic impurities could also be responsible for this behavior. Finally, the behavior of the reversible magnetization of the Bi-2201 samples investigated, which are situated at the optimal and in the overdoped region, did not indicate any unusual temperature dependence for the upper critical field H_c2,c.     

A study on the structural–microstructural characterisation and defect structure of Ru based magnetosuperconductor, RuSr2Eu1.6Ce0.4Cu2O10−δ

The structural–microstructural characterization and defect structure of Ru based magnetosuperconductor RuSr₂Eu_1.6Ce_0.4Cu₂O_10−δ has been investigated by selected area electron diffraction pattern and high resolution electron microscopy. Under the present investigations, RuSr₂Eu_1.6Ce_0.4Cu₂O_10−δ magnetosuperconductor shows the presence of both Ru-1222 and Ru-1212 phases. Analysis of the selected area electron diffraction pattern indicates superstructure in Ru-1212 while Ru-1222 phase does not show the presence of superlattice structure. A careful and detailed investigations of the HRTEM image shows the presence of defects like 90° domains, intergrowths, and dislocations.     

Structure, oxygen stoichiometry and electrical conductivity in the system Sr-Ce-Co-O

Mixed oxides in the system S-Ce-Co-O were prepared by solid state reaction and by freeze-drying of precursor compounds followed by thermal treatment. Two types of perovskite oxides exist in the system: Solid solutions of the type Sr_{1 − y}Ce_yCoO_{3 − x} and mixed oxides of the type (1 − y)SrCeO₃ − ySrCoO_{3 − x}. Microstructures and phase compositions were determined by electron microscopy and X-ray diffraction. SrCoO_{3 − x} forms a solid solution of ceria on the A-site in the strontium cobaltite lattice up to 0.15 mol Ce. This solid solution corresponds to the high-temperature structure of pure SrCoO_{3 − x} and is characterized by high oxygen exchange and electrical conductivity. The oxygen deficiency x was measured by solid electrolyte coulometry. The oxygen deficiency of solid solutions Sr_{1 − y}Ce_yCoO_{3 − x} increases with temperature and decreases with pO₂ in the ambient atmosphere and with increasing Ce dopant concentration. The pO₂-T-x diagram of the solid solution was determined. The T, pO₂ and dopant concentration dependencies of electrical conductivity were measured by a four-point d.c. technique. By Ce doping strontium cobaltite becomes a stabilized high-conductive material (maximum conductivity: 500 S cm⁻¹ at 400 °C, E_a = 0.025 eV, p-type). Above this temperature the T-coefficient of the conductivity changes from positive (semiconducting) to negative values.     

Double peak behavior of resistivity curves in Cd doped LaMnO3 perovskite systems

The effect of Cd doping on transport, magnetotransport, and magnetic properties has been investigated in the perovskite La_1−xCd_xMnO₃ (0x0.5) systems. The ρ(T) curves exhibit a sharp metal insulator transition (T_p1), which is close to paramagnetic to ferromagnetic transition (T_c) obtained from M−T curves for all samples. In addition, ρ(T) curves for Cd doped samples exhibit another broad transition (T_P2) below T_p1. This transition becomes more prominent and the transition temperature (T_p2) shifts to lower temperature with increasing Cd content. Such double peak behavior in the ρ(T) curve is attributed to the phase separation between the ferromagnetic metallic phases and the ferromagnetic insulating phases induced by the electronic inhomogeneity in the samples.     

Preparation, characterization and oxide ion conductivity in U-substituted Bi4V2O11

A Bi₂V_{1 − x − y}U_xBi_yO_{5.5 + 0.5x − y} solid solution derived from Bi₄V₂O₁₁ has been prepared and characterized with x up to 0.125 for y = 0. Partial substitution of U⁶⁺ for V⁵⁺ in Bi₄V₂O₁₁ leads to the stabilization at room temperature of the high-oxide ion conducting γ-phase, in contrast with other M⁶⁺ dopants which stabilize the β-phase. The lower conductivity in U substituted system compared with BICUVOX.10 is attributed to its higher activation energy. Conductivity values and activation energies of the U substituted phases compare well with Bi₂UO₆.     

Study on the superconducting composite material formation in the system Bi2Sr2CaCu2O8+x/Al-containing phases

Phase evolution in the Bi---Sr---Ca---Cu---Al---O system was studied. Two Al-containing phases BiSr_1.5Ca_0.5Al₂O_z and (Sr_1−xCa_x)₃Al₂O₆ (x = 0.4 − 0.45) were determined to be chemically compatible with Bi_2.18Sr₂CaCu₂O_8+x (Bi-2212) at temperatures of the samples processing. The phase equilibria in the title system were investigated above the solidus temperature. The BiSr_1.5Ca_0.5Al₂O_z was found to be in equilibrium only with the melt and the (Sr_1−xCa_x)₃Al₂O₆ phase. This latter aluminate equilibrated with Ca,Sr cuprates, CaO, the Cu-free phase, and the liquid. The melting and solidification in Bi-2212, doped with the aluminate, corresponded to the reversible reaction Bi-2212 + BiSr_1.5Ca_0.5Al₂O_z ↔ (Sr_1−xCa_x)₃Al₂O₆ + liquid. Two sets of superconducting composite materials with initial compositions Bi-2212 + nBiSr_1.5Ca_0.5Al₂O_z and Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ were prepared by solidification from the partial melt. The former material was composed mostly of large Bi-2212 lamellas separated by the BiSr_1.5Ca_0.5Al₂O_z phase, which destroyed superconducting links between Bi-2212 grains. The latter material consisted of a Bi-2212 polycrystalline matrix with high concentration of small (ca. 3 μm) grains of (Sr_1−xCa_x)₃Al₂O₆ imbedded in Bi-2212 lamellas. The Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ materials displayed a trend to enhance flux pinning at T = 60 K with the increase of aluminate phase content.     

Ramans study of Y1−xPrxBa2Cu3O7−δ and YB2Cu3−xZnxO7−δ single crystals

Single crystals with known T_c values of Y_1−xPr_xBa₂Cu₃O_7−δ (Y---Pr1:2:3) and YBa₂Cu_3−xZn_3−xZn_xO_7−δ (Y---Zn1:2:3) systems are studied by Raman measurements. The Raman spectra for (Y---Pr1:2:3) single crystals show that the frequencies of Ba and O_z modes increase as the Pr content increases. The results are consistent with the hole-localization scheme proposed for the suppression of superconductivity in the polycrystalline Y---Pr1:2:3 systems. On the other hand, in the Y---Zn1:2:3 system, all the Raman modes do not change in frequencies. However, the FWHM of the Cu(2) mode increases with the decrease of T_c, indicating strong scattering of charge carriers by the substituted Zn ions in the CuO₂ planes. The induced disorder in the CuO₂ planes may be related with suppression of T_c in the Y---Zn1:2:3 system. Thus, the suppression mechanism in the Y---Zn1:2:3 systems seems to be different from that in the Y---Pr1:2:3 systems.