Intermetallics Evolution in Sn-3.5Ag Based Lead-Free Solder Matrix on an OSP Cu Finish

The 0.2Co + 0.1Ni dual additives were used to dope a Sn-3.5Ag solder matrix to modify the alloy microstructure and the solder joint on an organic solderability preservative (OSP) Cu pad. The refined microstructure of the Sn-3.5Ag-0.2Co-0.1Ni solder alloy or the reduced β-Sn size was attributed to the depressed undercooling achieved by the Co-Ni addition. After soldering on the OSP Cu pad, a large Ag₃Sn plate was formed at the Sn-3.5Ag/OSP solder joint, whereas it was absent at the Sn-3.5Ag-0.2Co-0.1Ni/OSP solder joints. With isothermal aging at 150°C, large Ag₃Sn plates formed at the Sn-3.5Ag/OSP solder joint were still observed. A coarsened and dispersed Ag₃Sn phase was found in the solder joints with Co-Ni additions as well. Compared to Cu₆Sn₅, the (Co,Ni)Sn₂ intermetallic compound showed much lower microhardness values. However, (Co,Ni)Sn₂ hardness was comparable to that of the Ag₃Sn phase. Pull strength testing of Sn-3.5Ag-0.2Co-0.1Ni/OSP revealed slightly lower values than for Sn-3.5Ag/OSP during aging. Such results are thought be due to the phase transformation of (Co,Ni)Sn₂ to (Cu,Co,Ni)₆Sn₅.     

Intermetallic reactions in Sn-3.5Ag solder ball grid array packages with Ag/Cu and Au/Ni/Cu pads

During the reflow process of Sn-3.5Ag solder ball grid array (BGA) packages with Ag/Cu and Au/Ni/Cu pads, Ag and Au thin films dissolve rapidly into the liquid solder, and the Cu and Ni layers react with the Sn-3.5Ag solder to form Cu₆Sn₅ and Ni₃Sn₄ intermetallic compounds at the solder/pad interfaces, respectively. The Cu₆Sn₅ intermetallic compounds also appear as clusters in the solder matrix of Ag surface-finished packages accompanied by Ag₃Sn dispersions. In the solder matrix of Au/Ni surface-finished specimens, Ag₃Sn and AuSn₄ intermetallics can be observed, and their coarsening coincides progressively with the aging process. The interfacial Cu₆Sn₅ and Ni₃Sn₄ intermetallic layers grow by a diffusion-controlled mechanism after aging at 100 and 150°C. Ball shear strengths of the reflowed Sn-3.5Ag packages with both surface finishes are similar, displaying the same degradation tendencies as a result of the aging effect.     

Microstructural evolution of a lead-free solder alloy Sn-Bi-Ag-Cu prepared by mechanical alloying during thermal shock and aging

In a previous study, a lead-free solder, Sn-6Bi-2Ag-0.5Cu, was developed by mechanical alloying. The alloy shows great potential as a lead-free solder system. In the present work, the microstructural evolution during thermal shock and aging was examined. In the as-soldered joints small bismuth (1 μm to 2 μm) and Ag₃Sn (1 μm) particles were finely dispersed in a nearly pure tin matrix with a small amount of η-Cu₆Sn₅ phase in the bulk of solder. During thermal shock and aging microstructural evolution occurred with Cu-Sn intermetallic compound (IMC) layer growth at interface, bismuth phase coarsening and Ag₃Sn phase coarsening. The microstructure of the solder appeared to be stable at high temperature. The shear strength of the present solder joint is higher than that of Sn-37Pb and Sn-3.5Ag solders. Shear failure occurred Cu-Sn IMC layer-solder interface and in the bulk of solder.     

Influence of Dopant on Growth of Intermetallic Layers in Sn-Ag-Cu Solder Joints

The interfacial interaction between Cu substrates and Sn-3.5Ag-0.7Cu-xSb (x = 0, 0.2, 0.5, 0.8, 1.0, 1.5, and 2.0) solder alloys has been investigated under different isothermal aging temperatures of 100°C, 150°C, and 190°C. Scanning electron microscopy (SEM) was used to measure the thickness of the intermetallic compound (IMC) layer and observe the microstructural evolution of the solder joints. The IMC phases were identified by energy-dispersive x-ray spectroscopy (EDX) and x-ray diffractometry (XRD). The growth of both the Cu₆Sn₅ and Cu₃Sn IMC layers at the interface between the Cu substrate and the solder fits a power-law relationship with the exponent ranging from 0.42 to 0.83, which suggests that the IMC growth is primarily controlled by diffusion but may also be influenced by interface reactions. The activation energies and interdiffusion coefficients of the IMC formation of seven solder alloys were determined. The addition of Sb has a strong influence on the growth of the Cu₆Sn₅ layer, but very little influence on the formation of the Cu₃Sn IMC phase. The thickness of the Cu₃Sn layer rapidly increases with aging time and temperature, whereas the thickness of the Cu₆Sn₅ layer increases slowly. This is probably due to the formation of Cu₃Sn at the interface between two IMC phases, which occurs with consumption of Cu₆Sn₅. Adding antimony to Sn-3.5Ag-0.7Cu solder can evidently increase the activation energy of Cu₆Sn₅ IMC formation, reduce the atomic diffusion rate, and thus inhibit excessive growth of Cu₆Sn₅ IMCs. This study suggests that grain boundary pinning is one of the most important mechanisms for inhibiting the growth of Cu₆Sn₅ IMCs in such solder joints when Sb is added.     

The nanoindentation characteristics of Cu<Subscript>6</Subscript>Sn<Subscript>5</Subscript>, Cu<Subscript>3</Subscript>Sn,and Ni<Subscript>3</Subscript>Sn<Subscript>4</Subscript> intermetallic compounds in the solder bump

In general, formation and growth of intermetallic compounds (IMCs) play a major role in the reliability of the solder joint in electronics packaging and assembly. The formation of Cu-Sn or Ni-Sn IMCs have been observed at the interface of Sn-rich solders reacted with Cu or Ni substrates. In this study, a nanoindentation technique was employed to investigate nanohardness and reduced elastic moduli of Cu₆Sn₅, Cu₃Sn, and Ni₃Sn₄ IMCs in the solder joints. The Sn-3.5Ag and Sn-37Pb solder pastes were placed on a Cu/Ti/Si substrate and Ni foil then annealed at 240°C to fabricate solder joints. In Sn-3.5Ag joints, the magnitude of the hardness of the IMCs was in the order Ni₃Sn₄>Cu₆Sn₅>Cu₃Sn, and the elastic moduli of Cu₆Sn₅, Cu₃Sn, and Ni₃Sn₄ were 125 GPa, 136 GPa, and 142 GPa, respectively. In addition, the elastic modulus of the Cu₆Sn₅ IMC in the Sn-37Pb joint was similar to that for the bulk Cu₆Sn₅ specimen but less than that in the Sn-3.5Ag joint. This might be attributed to the strengthening effect of the dissolved Ag atoms in the Cu₆Sn₅ IMC to enhance the elastic modulus in the Sn-3.5Ag/Cu joint.     

Spreading Kinetics of Liquid Solders over an Intermetallic Solid Surface. Part 2: Lead-Free Solders

This study is devoted to a phenomenological and quantitative investigation of␣the physics of spreading of lead-free solder systems (Sn, Sn-0.7Cu, and Sn-3.5Ag) over Cu₆Sn₅/Cu₃Sn/Cu substrates. Wetting kinetics was studied using real-time in situ monitoring of the triple-line kinetics under a controlled atmosphere. Three different intermetallic (IMC) substrates were used for this investigation. It was found that the grain size of the deposited IMC compound coating has a sizable influence on the triple-line movement of the liquid solders considered. More pronounced spreading of solders on IMC substrates was observed for all lead-free solders over an intermetallic with the smallest grain size. Lead-free solder spreading over IMC surfaces exposed to aging at elevated temperatures, hence featuring larger grain size, did not feature a significant improvement of wettability when compared with the behavior of the same solders on virgin copper substrates.     

Interfacial Reactions of Sn-3.5Ag-<Emphasis Type="Italic">x</Emphasis>Zn Solders and Cu Substrate During Liquid-State Aging

The effects of Zn (1 wt.%, 3 wt.%, and 7 wt.%) additions to Sn-3.5Ag solder and various reaction times on the interfacial reactions between Sn-3.5Ag-xZn solders and Cu substrates a during liquid-state aging were investigated in this study. The composition and morphological evolution of interfacial intermetallic compounds (IMCs) changed significantly with the Zn concentration and reaction time. For the Sn-3.5Ag-1Zn/Cu couple, CuZn and Cu₆Sn₅ phases formed at the interface. With increasing aging time, the Cu₆Sn₅ IMC layer grew thicker, while the CuZn IMC layer drifted into the solder and decomposed gradually. Cu₅Zn₈ and Ag₅Zn₈ phases formed at the interfaces of Sn-3.5Ag-3Zn/Cu and Sn-3.5Ag-7Zn/Cu couples. With increasing reaction time, the Cu₅Zn₈ layer grew and Cu atoms diffused from the substrate to the solder, which transformed the Ag₅Zn₈ to (Cu,Ag)₅Zn₈. The Cu₆Sn₅ layer that formed between the Cu₅Zn₈ layer and Cu was much thinner at the Sn-3.5Ag-7Zn/Cu interface than at the Sn-3.5Ag-3Zn/Cu interface. Additionally, we measured the thickness of interfacial IMC layers and found that 3 wt.% Zn addition to the solder was the most effective for suppressing IMC growth at the interfaces.     

Effect of Ag Content and the Minor Alloying Element Fe on the Mechanical Properties and Microstructural Stability of Sn-Ag-Cu Solder Alloy Under High-Temperature Annealing

This study compares the high-Ag-content Sn-3Ag-0.5Cu with the low- Ag-content Sn-1Ag-0.5Cu solder alloy and the three quaternary solder alloys Sn-1Ag-0.5Cu-0.1Fe, Sn-1Ag-0.5Cu-0.3Fe, and Sn-1Ag-0.5Cu-0.5Fe to understand the beneficial effects of Fe on the microstructural stability, mechanical properties, and thermal behavior of the low-Ag-content Sn-1Ag-0.5Cu solder alloy. The results indicate that the Sn-3Ag-0.5Cu solder alloy possesses small primary β-Sn dendrites and wide interdendritic regions consisting of a large number of fine Ag₃Sn intermetallic compound (IMC) particles. However, the Sn-1Ag-0.5Cu solder alloy possesses large primary β-Sn dendrites and narrow interdendritic regions of sparsely distributed Ag₃Sn IMC particles. The Fe-bearing SAC105 solder alloys possess large primary β-Sn dendrites and narrow interdendritic regions of sparsely distributed Ag₃Sn IMC particles containing a small amount of Fe. Moreover, the addition of Fe leads to the formation of large circular FeSn₂ IMC particles located in the interdendritic regions. On the one hand, tensile tests indicate that the elastic modulus, yield strength, and ultimate tensile strength (UTS) increase with increasing Ag content. On the other hand, increasing the Ag content reduces the total elongation. The addition of Fe decreases the elastic modulus, yield strength, and UTS, while the total elongation is still maintained at the Sn-1Ag-0.5Cu level. The effect of aging on the mechanical behavior was studied. After 720 h and 24 h of aging at 100°C and 180°C, respectively, the Sn-1Ag-0.5Cu solder alloy experienced a large degradation in its mechanical properties after both of the aging conditions, whereas the mechanical properties of the Sn-3Ag-0.5Cu solder alloy degraded more dramatically after 24 h of aging at 180°C. However, the Fe-bearing SAC105 solder alloys exhibited only slight changes in their mechanical properties after both aging procedures. The inclusion of Fe in the Ag₃Sn IMC particles suppresses their IMC coarsening, which stabilizes the mechanical properties of the Fe-bearing SAC105 solder alloys after aging. The results from differential scanning calorimetry (DSC) tests indicate that the addition of Fe has a negligible effect on the melting behavior. However, the addition of Fe significantly reduces the solidification onset temperature and consequently increases the degree of undercooling. In addition, fracture surface analysis indicates that the addition of Fe to the Sn-1Ag-0.5Cu alloy does not affect the mode of fracture, and all tested alloys exhibited large ductile dimples on the fracture surface.     

Intermetallics Characterization of Lead-Free Solder Joints under Isothermal Aging

Solder interconnect reliability is influenced by environmentally imposed loads, solder material properties, and the intermetallics formed within the solder and the metal surfaces to which the solder is bonded. Several lead-free metallurgies are being used for component terminal plating, board pad plating, and solder materials. These metallurgies react together and form intermetallic compounds (IMCs) that affect the metallurgical bond strength and the reliability of solder joint connections. This study evaluates the composition and extent of intermetallic growth in solder joints of ball grid array components for several printed circuit board pad finishes and solder materials. Intermetallic growth during solid state aging at 100°C and 125°C up to 1000 h for two solder alloys, Sn-3.5Ag and Sn-3.0Ag-0.5Cu, was investigated. For Sn-3.5Ag solder, the electroless nickel immersion gold (ENIG) pad finish was found to result in the lowest IMC thickness compared to immersion tin (ImSn), immersion silver (ImAg), and organic solderability preservative (OSP). Due to the brittle nature of the IMC, a lower IMC thickness is generally preferred for optimal solder joint reliability. A lower IMC thickness may make ENIG a desirable finish for long-life applications. Activation energies of IMC growth in solid-state aging were found to be 0.54 ± 0.1 eV for ENIG, 0.91 ± 0.12 eV for ImSn, and 1.03 ± 0.1 eV for ImAg. Cu₃Sn and Cu₆Sn₅ IMCs were found between the solder and the copper pad on boards with the ImSn and ImAg pad finishes. Ternary (Cu,Ni)₆Sn₅ intermetallics were found for the ENIG pad finish on the board side. On the component side, a ternary IMC layer composed of Ni-Cu-Sn was found. Along with intermetallics, microvoids were observed at the interface between the copper pad and solder, which presents some concern if devices are subject to shock and vibration loading.     

Reaction of Liquid Sn-Ag-Cu-Ce Solders with Solid Copper

Small amounts of the rare-earth element Ce were added to the Sn-rich lead-free eutectic solders Sn-3.5Ag-0.7Cu, Sn-0.7Cu, and Sn-3.5Ag to improve their properties. The microstructures of the solders without Ce and with different amounts (0.1 wt.%, 0.2 wt.%, and 0.5 wt.%) of Ce were compared. The microstructure of the solders became finer with increasing Ce content. Deviation from this rule was observed for the Sn-Ag-Cu solder with 0.2 wt.% Ce, and for the Sn-0.7Cu eutectic alloy, which showed the finest microstructure without Ce. The melting temperatures of the solders were not affected. The morphology of intermetallic compounds (IMC) formed at the interface between the liquid solders and a Cu substrate at temperatures about 40°C above the melting point of the solder for dipping times from 2 s to 256 s was studied for the basic solder and for solder with 0.5 wt.% Ce addition. The morphology of the Cu₆Sn₅ IMC layer developed at the interface between the solders and the substrate exhibited the typical scallop-type shape without significant difference between solders with and without Ce for the shortest dipping time. Addition of Ce decreased the thickness of the Cu₆Sn₅ IMC layer only at the Cu/Sn-Ag-Cu solder interface for the 2-s dipping. A different morphology of the IMC layer was observed for the 256-s dipping time: The layers were less continuous and exhibited a broken relief. Massive scallops were not observed. For longer dipping times, Cu₃Sn IMC layers located near the Cu substrate were also observed.     

Investigation of Dissolution Behavior of Metallic Substrates and Intermetallic Compound in Molten Lead-free Solders

This study investigates the dissolution behavior of the metallic substrates Cu and Ag and the intermetallic compound (IMC)-Ag₃Sn in molten Sn, Sn-3.0Ag-0.5Cu, Sn-58Bi and Sn-9Zn (in wt.%) at 300, 270 and 240°C. The dissolution rates of both Cu and Ag in molten solder follow the order Sn > Sn-3.0Ag-0.5Cu >Sn-58Bi > Sn-9Zn. Planar Cu₃Sn and scalloped Cu₆Sn₅ phases in Cu/solders and the scalloped Ag₃Sn phase in Ag/solders are observed at the metallic substrate/solder interface. The dissolution mechanism is controlled by grain boundary diffusion. The planar Cu₅Zn₈ layer formed in the Sn-9Zn/Cu systems. AgZn₃, Ag5Zn₈ and AgZn phases are found in the Sn-9Zn/Ag system and the dissolution mechanism is controlled by lattice diffusion. Massive Ag₃Sn phases dissolved into the solders and formed during solidification processes in the Ag₃Sn/Sn or Sn-3.0Ag-0.5Cu systems. AgZn₃ and Ag₅Zn₈ phases are formed at the Sn-9Zn/Ag₃Sn interface. Zn atoms diffuse through Ag-Zn IMCs to form (Ag, Zn)Sn₄ and Sn-rich regions between Ag₅Zn₈ and Ag₃Sn.     

Developing a lead-free solder alloy Sn-Bi-Ag-Cu by mechanical alloying

A new lead free alloy, Sn-6Bi-2Ag-0.5Cu, has been developed by mechanical alloying and has great potential as a lead-free solder system. Initial trials on the manufacture of solder joints with this alloy revealed that a high quality bond with copper could be formed. Its melting range of 193.87°C to 209.88°C is slightly higher than that of eutectic tin-lead solder. Examination of the microstructure of the as-soldered joints revealed that it mainly consists of small bismuth (1 μm to 2 μm) and Ag₃Sn (1 μm) particles finely dispersed in a nearly pure tin matrix with a small amount of η-Cu₆Sn₅ particles. The Cu-Sn intermetallic compound (IMC) layer formed at solder-copper interface is the η-Cu₆Sn₅ phase with grain size of 2 μm. The shear strength of the solder joint is higher than that of Sn-37Pb or Sn-3.5Ag. Under shear loading, fracture occurred at IMC layer-solder interface as well as in the bulk of solder.     

Morphology and growth kinetics of intermetallic compounds in solid-state interfacial reaction of electroless Ni-P with Sn-based lead-free solders

A comparative study of solid/solid interfacial reactions of electroless Ni-P (15 at.% P) with lead-free solders, Sn-0.7Cu, Sn-3.5Ag, Sn-3.8Ag-0.7Cu, and pure Sn, was carried out by performing thermal aging at 150°C up to 1000 h. For pure Sn and Sn-3.5Ag solder, three distinctive layers, Ni₃Sn₄, SnNiP, and Ni₃P, were observed in between the solder and electroless Ni-P; while for Sn-0.7Cu and Sn-3.8Ag-0.7Cu solders, two distinctive layers, (CuNi)₆Sn₅ and Ni₃P, were observed. The differences in morphology and growth kinetics of the intermetallic compounds (IMCs) at the interfaces between electroless Ni-P and lead-free solders were investigated, as well as the growth kinetics of the P-enriched layers underneath the interfacial IMC layers. With increasing aging time, the coarsening of interfacial Ni₃Sn₄ IMC grains for pure Sn and Sn-3.5Ag solder was significantly greater than that of the interfacial (CuNi)₆Sn₅ IMC grains for Sn-0.7Cu and Sn-3.8Ag-0.7Cu solders. Furthermore, the Ni content in interfacial (CuNi)₆Sn₅ phase slightly increased during aging. A small addition of Cu (0.7 wt.%) resulted in differences in the type, morphology, and growth kinetics of interfacial IMCs. By comparing the metallurgical aspects and growth kinetics of the interfacial IMCs and the underneath P-enriched layers, the role of initial Cu and Ag in lead-free solders is better understood.     

Contact angle measurements of Sn-Ag and Sn-Cu lead-free solders on copper substrates

In this study, the contact angles of four lead-free solders, namely, Sn-3.5Ag, Sn-3.5Ag-4.8Bi, Sn-3.8Ag-0.7Cu, and Sn-0.7Cu (wt.%), were measured on copper substrates at different temperatures. Measurements were performed using the sessile-drop method. Contact angles ranging from 30° to 40° after wetting under vacuum with no fluxes and between 10° and 30° with rosin mildly activated (RMA) and rosin activated (RA) fluxes were obtained. The Sn-3.5Ag-4.8Bi exhibited the lowest contact angles, indicating improved wettability with the addition of bismuth. For all soldering alloys, lower contact angles were observed using RMA flux. Intermetallics formed at the solder/Cu interface were identified as Cu₆Sn₅ adjacent to the solder and Cu₃Sn adjacent to the copper substrate. The Cu₃Sn intermetallic phase was generally not observed when RMA flux was used. The effect of temperature on contact angle was dependent on the type of flux used.     

Microstructure characterization of SnAgCu solder bearing Ce for electronic packaging

The creep-rupture lives of Sn3.8Ag0.7Cu and Sn3.8Ag0.7Cu0.03Ce lead-free solder joints for electronic packaging were investigated, respectively. And the relationship between creep behavior and intermetallic compound (IMC: Ag₃Sn, Cu₆Sn₅, CeSn₃) particles in SnAgCu/SnAgCuCe solder joints has been obtained. Meanwhile, rare earth Ce concentration gradient and retardation effect of Ce on the IMC layer have been observed at the solder/Cu interface. Moreover, aging reaction of Sn and Cu, and the effect mechanism of rare earth Ce on two IMCs (Cu₆Sn₅ and Cu₃Sn) are reported.     

Influence of Lanthanum Additions on the Microstructure and Microhardness of Sn-3.5Ag Solder

This study evaluates the effects of different amounts of lanthanum (La) additions on the microstructure and microhardness of Sn-3.5Ag solders. Sn-3.5Ag-xLa ternary solders were prepared by adding 0 wt.% to 1.0 wt.% La to Sn-3.5Ag alloy. Copper substrates were then dipped in the molten solders and these samples aged at 150°C for up to 625 h. The microstructure and microhardness of the as-solidified solder and the aged solder/copper samples were investigated. The Sn-3.5Ag-xLa solders comprised β-Sn, Ag₃Sn, and LaSn₃ phases, and their microstructure was refined by La additions. As-cast, the addition of La increased the microhardness of the Sn-Ag solder due to the refining effect of Ag₃Sn particles and increased formation of LaSn₃ compounds. As the aging time was increased, the microhardness of the solders decreased and the Ag₃Sn compounds coarsened. However, the coarsening of Ag₃Sn compounds was retarded by La, and the size and amount of LaSn₃ compounds did not change perceptibly with aging time. Therefore, La additions can improve the microhardness and thermal resistance of solder joints.     

Mechanical properties of intermetallic compounds associated with Pb-free solder joints using nanoindentation

Mechanical properties of intermetallic compound (IMC) phases in Pb-free solder joints were obtained using nanoindentation testing (NIT). The elastic modulus and hardness were determined for IMC phases associated with insitu FeSn particle reinforced and mechanically added, Cu particle-reinforced, composite solder joints. The IMC layers that formed around Cu particle reinforcement and at the Cu substrate/solder matrix interface were probed with NIT. Moduli and hardness values obtained by NIT revealed were noticeably higher for Cu-rich Cu₃Sn than those of Cu₆Sn₅. The Ag₃Sn platelets that formed during reflow were also examined for eutectic Sn-Ag solder column joints. The indentation modulus of Ag₃Sn platelets was significantly lower than that of FeSn, SnCuNi, and CuSn IMCs. Indentation creep properties were assessed in localized microstructure regions of the as-cast, eutectic Sn-Ag solder. The stress exponent, n, associated with secondary creep differed widely depending on the microstructure feature probed by the indenter tip.     

Elevated temperature aging of solder joints based on Sn-Ag-Cu: Effects on joint microstructure and shear strength

The shear strength behavior and microstructural effects after aging for 100 h and 1,000 h at 150°C are reported for near-eutectic Sn-Ag-Cu (SAC) solder joints (joining to Cu) made from Sn-3.5Ag (wt.%) and a set of SAC alloys (including Co- and Fe-modified SAC alloys). All joints in the as-soldered and 100-h aged condition experienced shear failure in a ductile manner by either uniform shear of the solder matrix (in the strongest solders) or by a more localized shear of the solder matrix adjacent to the Cu₆Sn₅ interfacial layer, consistent with other observations. After 1,000 h of aging, a level of embrittlement of the Cu₃Sn/Cu interface can be detected in some solder joints made with all of the SAC alloys and with Sn-3.5Ag, which can lead to partial debonding during shear testing. However, only ductile failure was observed in all solder joints made from the Co- and Fe-modified SAC alloys after aging for 1,000 h. Thus, the strategy of modifying a strong (high Cu content) SAC solder alloy with a substitutional alloy addition for Cu seems to be effective for producing a solder joint that retains both strength and ductility for extended isothermal aging at high temperatures.     

Effects of Ce Addition on the Microstructure and Mechanical Properties of Sn-58Bi Solder Joints

The effects of a rare-earth element on the microstructure, mechanical properties, and whisker growth of Sn-58Bi alloys and solder joints in ball grid array (BGA) packages with Ag/Cu pads have been investigated. Mechanical testing indicated that the elongation of Sn-58Bi alloys doped with Ce increased significantly, and the tensile strength decreased slightly, in compar- ison with undoped Sn-58Bi. In addition, the growth of both fiber- and hillock-shaped tin whiskers on the surface of Sn-58Bi-0.5Ce was retarded in the case of Sn-3Ag-0.5Cu-0.5Ce alloys. The growth of interfacial intermetallic compounds (IMC) in Sn-58Bi-0.5Ce solder joints was slower than that in Sn-58Bi because the activity of Ce atoms at the interface of the Cu₆Sn₅ IMC/solder was reduced. The reflowed Sn-58Bi and Sn-58Bi-0.5Ce BGA packages with Ag/Cu pads had a ball shear strength of 7.91 N and 7.64 N, which decreased to about 7.13 N and 6.87 N after aging at 100°C for 1000 h, respectively. The reflowed and aged solder joints fractured across the solder balls with ductile characteristics after ball shear tests.     

Effect of cooling rate on growth of the intermetallic compound and fracture mode of near-eutectic Sn-Ag-Cu/Cu pad: Before and after aging

Several near-eutectic solders of (1) Sn-3.5Ag, (2) Sn-3.0Ag-0.7Cu, (3) Sn-3.0Ag-1.5Cu, (4) Sn-3.7Ag-0.9Cu, and (5) Sn-6.0Ag-0.5Cu (in wt.% unless specified otherwise) were cooled at different rates after reflow soldering on the Cu pad above 250°C for 60 sec. Three different media of cooling were used to control cooling rates: fast water quenching, medium cooling on an aluminum block, and slow cooling in furnace. Both the solder composition and cooling rate after reflow have a significant effect on the intermetallic compound (IMC) thickness (mainly Cu₆Sn₅). Under fixed cooling condition, alloys (1), (3), and (5) revealed larger IMC thicknesses than that of alloys (2) and (4). Slow cooling produced an IMC buildup of thicker than 10 μm, while medium and fast cooling produced a thickness of thinner than 5 μm. The inverse relationship between IMC thickness and shear strength was confirmed. All the fast- and medium-cooled joints revealed a ductile mode (fracture surface was composed of the β-Sn phase), while the slow-cooled joints were fractured in a brittle mode (fracture surface was composed of Cu₆Sn₅ and Cu₃Sn phases). The effect of isothermal aging at 130°C on the growth of the IMC, shear strength, and fracture mode is also reported.