PH13-8Mo钢的离子渗氮工艺

对PH13-8Mo钢离子渗氮工艺参数进行了研究,其中包括渗氮温度、渗氮时间及渗氮件表面粗糙度。结果表明:随渗氮温度的升高、渗氮时间的延长、零件表面粗糙度的降低,PH13-8Mo钢渗氮层厚度增加;渗氮零件表面粗糙度对渗氮层脆性等级影响较大,渗氮零件表面粗糙度为6.3 μm时,其脆性等级达到III级;渗氮时间、渗氮温度及零件表面粗糙度对渗氮层硬度影响甚微。渗氮温度540 ℃,渗氮时间22 h,零件表面粗糙度0.8 μm时,PH13-8Mo钢可获得良好的渗氮层,渗氮层厚度可达197.5 μm,渗氮层硬度可达1083 HV0.2,脆性等级为II级。     

42CrMo钢工件气体渗氮工艺改进

研究了42CrMo钢工件的基体硬度、化学成分及其偏析和渗氮工艺对渗氮层表面硬度和深度的影响.结果表明,42CrMo钢工件的渗氮温度以530℃为宜,提高基体硬度,控制原材料中影响渗氮质量的合金元素含量,均有利于提高42CrMo钢工件渗氮层的表面硬度,获得较为合理的白亮层和扩散层.     

42CrMo钢离子渗氮+后氧化复合处理研究

在脉冲等离子渗氮炉中42CrMo钢进行离子渗氮和后氧化复合处理,离子氧化介质为普通空气。采用金相显微镜、X射线衍射仪、电化学性能分析测试仪对复合渗层的显微组织、物相及耐腐蚀性进行了测试和分析。研究结果表明,复合渗层硬度较单一离子渗氮得到的有不同程度的提高,最大硬度达到760 HV0.05;42CrMo钢离子渗氮后进行氧化处理可在氮化层上形成一层1~2μm厚的氧化层,该氧化层由Fe2O3和Fe3O4组成;后氧化显著提高42CrMo钢的耐蚀性,其中400℃×60 min后氧化获得最佳耐蚀性。     

直流电场对42CrMo钢盐浴渗氮催渗与改性作用

以42CrMo钢为材料,对比研究了传统和直流电场催渗盐浴渗氮技术。利用光学显微镜、显微硬度计和X射线衍射仪对渗层的显微组织、渗层厚度、硬度及物相进行了测试和分析。研究结果表明:直流电场可以显著提高盐浴渗氮速度,降低渗氮温度或缩短渗氮时间;在外加电压7.5 V直流电场条件下,保温时间为80 min时,处理温度530℃获得的化合物层厚度与同样时间常规盐浴渗氮560℃时获得的层深相近,约为6.7μm,处理温度为560℃时化合物层厚度提高到12.1μm。虽然直流电场不改变42CrMo钢盐浴渗氮层的主要物相,均由ε-Fe_3N相、γ'-Fe_4N相和Cr N相构成,但直流电场盐浴渗氮后渗层中硬度较高的γ'-Fe_4N相的相对含量更高。因此,直流电场盐浴渗氮处理后的42CrMo钢的截面显微硬度大幅度的提高,经过575℃×80 min,7.5 V盐浴渗氮后的试样截面显微硬度达到1100 HV0.01,是基体硬度的3倍。同时,施加电场盐浴渗氮使42CrMo钢耐蚀性比常规盐浴渗氮进一步提高。     

42CrMo钢的空气离子后氧化

采用普通空气对离子渗氮的42CrMo钢进行离子后氧化处理。利用光学显微镜、扫描电镜(SEM)、X射线衍射仪、电化学性能分析测试仪对复合渗层的显微组织、厚度、物相、表面形貌及耐蚀性进行了测试和分析。研究结果表明,普通空气可用作42CrMo钢离子后氧化处理的气源;通过离子后氧化处理,在经离子渗氮的42CrMo钢氮化层上形成一层厚度为1~2μm、由Fe2O3和Fe3O4组成的氧化层;随氧化时间延长或温度增高,氮化层化合物相分解,化合物层厚度逐渐减小,后氧化时间和温度对氧化层的Fe2O3和Fe3O4比例起决定作用。同时,离子后氧化能显著改善渗氮42CrMo钢的耐蚀性,其中工艺参数为400℃、氧化60 min获得最佳耐蚀性。     

瓦楞辊的表面强化工艺

研究了经渗氮、碳氮共渗后高频淬火处理后42CrMo及45钢瓦楞辊试样的表面组织和力学性能。结果表明,两种试样经渗氮加高频淬火处理后表层主要为氮化物和回火马氏体组织;碳氮共渗加高频淬火处理后试样表层组织主要为回火马氏体和有少量氮化物。45钢和42CrMo钢试样经过处理表面硬度分别达到740和800 HV0.1,经高频淬火处理后,试样表面硬化层有较好的硬度梯度。     

42CrMo钢离子氮化研究

选用42CrMo钢为实验材料,分别进行普通离子渗氮处理、活性屏离子渗氮处理及预氧化+离子渗氮处理。利用金相显微镜观察离子渗氮层的显微组织;利用XRD分析离子渗氮层中的各种物相;在试验结果的基础上,分析不同的离子渗氮方式及不同的渗氮工艺参数对渗层组织和性能的影响。结果表明:42CrMo钢经离子渗氮处理后由表及里形成明显的白亮层和扩散层;渗层由Fe2-3N和Fe4N组成;离子渗氮后试样的表面硬度得到明显提高;在不同的离子渗氮方式下,渗氮工艺参数对化合物层厚度及扩散层厚度的影响规律存在一定的差异。活性屏对离子渗氮起到一定的促进作用,低温时尤为显著。离子渗氮前进行预氧化处理,可以加速渗氮过程的进行,其中在300℃下预氧化30 min效果最佳。     

42CrMo4钢硼氮离子复合渗与离子渗氮对比研究

目的 为了进一步提高42CrMo4钢离子渗氮层的硬度,研发硼氮离子复合渗创新技术,并与离子渗氮层特性进行对比研究.方法 在520℃、6 h的相同工艺条件下,对42CrMo4钢分别进行硼氮离子复合渗和离子渗氮处理.利用光学显微镜、XRD、显微硬度计、摩擦磨损测试机和电化学工作站对截面显微组织、物相、截面硬度、耐磨性和耐蚀...     

奥氏体不锈钢低温离子渗氮工艺研究

对304、316 L奥氏体不锈钢进行了不同温度、不同时间的离子渗氮。研究了渗层的显微组织和耐腐蚀性,测定了渗层的硬度。结果显示,随着渗氮温度的升高,两种钢渗层的表面硬度和深度都增加,而耐蚀性降低。渗氮温度≥400℃时,随着渗氮时间的延长,两种钢渗层的表面硬度变化不大,但深度明显增加,渗层的耐蚀性降低。当渗氮工艺相同时,316 L钢渗氮层的硬度、深度和耐蚀性均比304钢的渗氮层高。     

渗氮温度对38CrMoAl钢真空感应渗氮层耐磨性能的影响

应用一种新型真空感应渗氮方法对38CrMoAl钢表面制备渗氮层,采用SEM、EDS、自动显微硬度测试、滑动干摩擦试验等测试方法探讨了渗氮温度对38CrMoAl钢渗氮层组织、硬度和耐磨性的影响规律。结果表明:渗氮层表面平整,白亮层、扩散层、基体之间过渡平缓;随着渗氮温度升高,扩散层厚度、渗层硬度、耐磨性均呈现先增加后降低趋势;渗氮温度为560℃时,渗层厚度达到最高值180μm,渗层硬度达到最高值1250 HV0.025;渗氮温度560℃、590℃时的渗层试样在摩擦试验过程中仅有轻微的磨粒磨损,耐磨性能最佳。     

航空不锈钢1Cr11Ni2W2MoV精密薄层气体氮碳共渗

对航空不锈钢1Cr11Ni2W2MoV进行气体氮碳共渗热处理,以获得深度为0.02～0.03 mm的精密薄层,并对不同工艺参数下的渗层深度、硬度和脆性、组织进行了检测和分析。结果表明,在480～560℃共渗温度下,通过控制保温时间,均可得到深度0.02～0.03 mm,硬度≥800 HV0.1的精密渗层。温度越高,保温时间越长,渗层厚度和硬度越大。从工艺控制稳定性和生产效率等方面考虑,520℃温度下渗入速率均匀易控,更适合零件的实际生产。所得渗层脆性达到HB 5022—1994中1～2级的要求,组织符合2级及以上要求。     

6.5 MW核电水泵内齿圈的离子渗氮工艺

为满足核电水泵齿轮箱的大功率、长寿命、高可靠、高精度等要求,在42CrMo钢中硬调质的基体上进行深层可控离子渗氮工艺试验。结果表明,采用氮、氢混合气氛三段离子渗氮,经过工艺优化,工艺总时间为70 h左右,可获得层深为1.05 mm、表面脆性1级、表面为γ′单相组织的渗氮层,渗氮层的残余压应力最大幅值达620 MPa。此工艺应用于模数为12 mm、直径为ø1400 mm的核电站用循环水泵齿轮箱内齿圈深层渗氮,并通过台架试验验证,取代进口产品在我国核电站服役多年。     

Wear and corrosion behavior of CrCN/CrN coatings deposited by cathodic arc evaporation on nitrided 42CrMo4 steel substrates

In the paper, the results of wear and corrosion tests of the CrCN/CrN multilayer coatings, formed by cathodic arc evaporation on 42CrMo4 (AISI 4140) steel substrates are presented. The substrates were subjected to thermo-chemical treatment–nitriding with various nitriding potential. The results of nitriding were determined by XRD and the hardness profile in the samples cross-section. The morphology of thin coatings was examined with SEM. A Vickers FV-700 and Fisherscope HM2000 hardness testers enabled to investigate hardness of steel substrates and CrCN/CrN coatings respectively. A pin-on-disc wear tests were used to determine the hardness and tribological parameters of the coatings: the coefficient of the friction and wear rate. The scratch test and Rockwell test were applied to assess the adhesion of the coatings to the substrates. The corrosion properties of coating–steel substrate systems were investigated using potentiodynamic polarisation tests. Corrosion potential, corrosion current density and polarization resistance were determined. It was found that that the nitriding of steel substrates improves properties of the coating–substrate system. The nitriding 42CrMo4 steel substrate with low nitriding potential enable to obtain substrates without surface “white layer” what favours good adhesion of the coating to the substrate. The CrCN/CrN multilayer coating–steel substrate systems show good mechanical and tribological properties and corrosion resistance.     

低温离子氮碳共渗温度对AerMet100钢摩擦学性能的影响

研究了不同温度对AerMet100钢渗氮层和氮碳共渗层的显微组织、表面硬度、渗层截面硬度梯度以及耐磨性的影响,并考察了渗层的磨损机理。结果表明,氮碳共渗层相较于渗氮层表面生成的化合物更加细小,表面更加平整光滑;离子渗氮、离子氮碳共渗处理都可显著提高AerMet100钢的表面硬度;随着温度的增加,共渗层厚度也明显增加;氮碳共渗层比渗氮层具有更低的摩擦因数,在共渗温度为480 ℃时氮碳共渗试样具有最低摩擦因数和磨损率,表现出最佳的耐磨性。渗氮层的磨损机理为氧化磨损和表面疲劳磨损,氮碳共渗层的磨损机理为氧化磨损、磨粒磨损以及表面疲劳磨损。     

32Cr2Mo2NiVNb 钢盐浴氮化工艺

目的将盐浴氮化工艺用于32Cr2Mo2NiVNb钢的表面处理。方法采用盐浴氮化工艺处理32Cr2Mo2NiVNb钢,通过对金相组织、力学性能、断口形貌、耐蚀性能、高温耐磨性能等的测试分析,研究该工艺对32Cr2Mo2NiVNb钢组织和性能的影响,验证该工艺对32Cr2Mo2NiVNb钢的适用性。结果32Cr2Mo2NiVNb钢盐浴氮化后,基体组织为均匀的细针状索氏体+少量游离铁素体,渗氮层深度约为0.23 mm,化合物层深度均匀,约为17μm,渗氮层疏松度、氮化物、脆性评级均达到1级;表面硬度为1011HV0.3,较氮化前提高153.4%;抗拉强度、拉伸断口形貌均无明显变化,断后伸长率、断面收缩率、冲击吸收能量仅小幅降低;耐中性盐雾时间为镀硬铬试样的6.3倍;经190 s高温磨损的表面磨痕细小均匀,磨损失重较镀硬铬试样降低62.8%。结论盐浴氮化工艺不损害32Cr2Mo2NiVNb钢组织、强度等,仅使塑性、韧性指标小幅降低,相较于镀硬铬工艺,可显著提高32Cr2Mo2NiVNb钢的耐蚀性、高温耐磨性,对32Cr2Mo2NiVNb钢的工艺适用性良好。     

渗氮温度对40Cr钢QPQ组织与性能的影响

采用光学显微镜(OM)对不同渗氮温度QPQ处理的40Cr钢表面渗氮层显微组织进行观察分析,同时进行维氏硬度试验与销盘摩擦磨损试验,获得渗氮层硬度梯度与磨损失重,并观察分析了磨损表面SEM形貌。结果表明,经不同渗氮温度的QPQ处理后,40Cr钢表面均形成了由氧化膜层、化合物层与扩散层构成的表面渗氮层。但随渗氮温度的升高,其渗氮层厚度呈先增加后减小的变化趋势,4种渗氮温度(580、600、620、640 ℃)下样品有效渗层深度分别为0.14、0.20、0.29、0.26 mm。随渗氮温度的升高,磨损量呈先减小后增大的趋势,在620 ℃下达到最低值。4种渗氮温度下磨损形式均以磨粒磨损与粘着磨损为主,但随着渗氮温度升高带来渗氮层厚度与硬度的变化,磨损程度呈现逐渐减轻的趋势。     

离子渗氮对304L不锈钢组织及高温耐磨性能的影响

以焚烧炉用热电偶304L不锈钢套管为研究对象,开展了不同温度的离子渗氮试验研究。采用光学显微镜、扫描电镜、显微硬度计等分析了304L不锈钢离子渗氮前后的微观结构与力学性能,并研究了其在400 ℃的耐磨损性能。结果表明,304L不锈钢离子渗氮后,可形成硬度1300 HV以上的表面硬化层。随着渗氮温度的提高,表面硬度有所提升,同时硬化层厚度显著增加。离子渗氮可提高304L不锈钢的磨损性能及耐高温氧化性能。     

感应淬火对42CrMo钢曲轴连杆轴颈组织性能的影响

采用OM、SEM、X射线应力分析、力学性能测试等手段,分析了感应淬火处理对42CrMo钢曲轴连杆轴颈截面组织和残余应力的影响,探讨了不同淬火功率对淬硬层形貌、显微组织和力学性能的影响。结果表明,42CrMo钢曲轴连杆轴颈截面由淬硬层、过渡层和基体3部分组成,淬硬层组织为均匀细小的马氏体,过渡层组织为马氏体和回火索氏体的混合组织,基体组织为回火索氏体。经感应淬火处理,42CrMo钢曲轴连杆轴颈表面残余应力由拉应力变为压应力,随着感应淬火功率的增加,淬硬层深度增加,组织不断细化,当感应淬火功率为2500 W,组织最为均匀细小,表面硬度达到了751.3 HV0.1,耐磨性大幅提升;但是淬火功率过高会导致组织粗化,当感应淬火功率为2600 W时,组织有所粗化,硬度也有所降低。