Preparation, microstructure and properties of molybdenum alloys reinforced by in-situ Al2O3 particles

The conventional molybdenum alloys, lacking of hard particles enhancing wear property, have relative poor wear resistance though they are widely used in wear parts. To resolve the above question, Mo alloys reinforced by in-situ Al₂O₃ particles are developed using powder metallurgy method. The in-situ α-Al₂O₃ particles in molybdenum matrix are obtained by the decomposition of aluminum nitrate after liquid-solid incorporation of MoO₂ and Al(NO₃)₃ aqueous solution. The α-Al₂O₃ particles well bonded with molybdenum distribute evenly in matrix of Mo alloys, which refine grains of alloys and increase hardness of alloys. The absolute density of alloy increases firstly and then decreases with the increase of Al₂O₃ content, while the relative density rises continuously. The friction coefficient of alloy, fluctuating around 0.5, is slightly influenced by Al₂O₃. However, the wear resistance of alloy obviously affected by the Al₂O₃ particles rises remarkably with the increasing of Al₂O₃ content. The Al₂O₃ particles can efficiently resist micro-cutting to protect molybdenum matrix, and therefore enhances the wear resistance of Mo alloy.     

Al_2O_3/MoS_2复合涂层的制备及摩擦磨损性能

以大气等离子喷涂工艺制备的Al_2O_3陶瓷涂层为模板,利用陶瓷涂层中存在的孔隙和微裂纹,采用水热反应在其内部原位合成具有润滑特性的MoS_2,制备出Al_2O_3/MoS_2的复合涂层。结果表明,通过水热反应在陶瓷涂层原有的微观缺陷中成功合成了MoS_2,合成的MoS_2固体粉末呈类球形状,并且这球状的粉末是由纳米片层状的MoS_2搭建组成的。摩擦试验结果表明,与纯Al_2O_3涂层相比,复合涂层中由于MoS_2润滑膜的形成,其摩擦因数和磨损率都显著降低,且载荷越大,复合涂层的摩擦性能越好。     

Effect of applied current on the electrodeposited Ni-Al2O3 composite coatings

Nano-sized Al₂O₃ ceramic particles (50 nm) were co-deposited with nickel using electrodeposition technique to develop composite coatings. The coatings were produced in an aqueous nickel bath at different current densities and the research investigated the effect of applied current on microstructure and thickness of the coatings. The variation in some mechanical properties such as hardness, wear resistance, and the adhesive strength of the composite coatings is influenced by the applied current and this was also studied. The morphology of the coatings was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. The hardness, wear resistance, and bond strength of the coatings were evaluated by Vickers micro-hardness test, pin-on-disc test, and tensile test, respectively. Results showed that the Al₂O₃ particles were uniformly distributed in the coatings, and the coatings deposited at a current density of 0.01 A/cm² was most favorable in achieving a maximum current efficiency which causes the co-deposition of a maximum amount of Al₂O₃ particles (4.3 wt.%) in the coatings. The increase in Al₂O₃ particles in the coatings increased the mechanical properties of the Ni-Al₂O₃ composite coatings by grain refining and dispersion strengthening mechanisms.     

Cyclic oxidation behavior and thermal barrier effect of YSZ-(Al2O3/YAG) double-layer TBCs prepared by the composite sol-gel method

Novel YSZ (6 wt.% yttria partially stabilized zirconia)-(Al₂O₃/YAG) (alumina-yttrium aluminum garnet, Y₃Al₅O₁₂) double-layer ceramic coatings were fabricated using the composite sol-gel and pressure filtration microwave sintering (PFMS) technologies. The thin Al₂O₃/YAG layer had good adherence with substrate and thick YSZ top layer, which presented the structure of micro-sized YAG particles embedded in nano-sized α-Al₂O₃ film. Cyclic oxidation tests at 1000 °C indicated that they possessed superior properties to resist oxidation of alloy and improve the spallation resistance. The thermal insulation capability tests at 1000 °C and 1100 °C indicate that the 250 μm coating had better thermal barrier effect than that of the 150 μm coating at different cooling gas rates. These beneficial effects should be mainly attributed to that, the oxidation rate of thermal grown oxides (TGO) scale is decreased by the “sealing effect” of α-Al₂O₃, the “reactive element effect”, and the reduced thermal stresses by means of nano/micro composite structure. This double-layer coating can be considered as a promising TBC.     

Improvement in the properties of nickel by nano-Cr2O3 incorporation

Nano-ceramic composite coatings were prepared by the electrodeposition method using sulphamate electrolyte. Nickel was chosen as the metal matrix and nano-Cr₂O₃ particles were chosen as the reinforcement. The surface morphology and the particle distribution in the coating were analysed using field emission scanning electron microscope (FESEM). The particle content was obtained using energy dispersive X-ray analysis (EDAX). A change in the surface morphology of Ni was seen on the incorporation of Cr₂O₃ particles. The coatings were characterized for their structure and no change in the diffraction pattern was seen between plain Ni and Ni-Cr₂O₃ composite. The mechanical property like microhardness and tribological behaviour of the nano-composite coatings was studied and it was observed that the incorporation of Cr₂O₃ particles enhanced the mechanical properties of Ni matrix. The nano-composites were analysed for their thermal stability and corrosion resistance. An improvement in thermal stability was observed but no change in the corrosion behaviour of Ni was seen on the incorporation of nano chromium oxide particles.     

Microstructural characterization of plasma sprayed Al2O3-40 wt.% TiO2 coatings on high density graphite with different post-treatments

Graphite is one of the candidate materials proposed for application in pyrochemical reprocessing plants involving aggressive molten chloride environment. Post treatments are promising techniques for the improvement of properties of thermal spray coatings for different industrial applications. In the present work, the effect of post treatments like vacuum annealing (VA) and laser melting (LM) on the microstructure and chemical modification of plasma sprayed Al₂O₃-40 wt.% TiO₂ coatings over high density (HD) graphite substrates has been investigated. When compared with sprayed coatings (SC), VA coatings showed cluster morphology and LM coatings exhibited homogenous microstructure. On laser melted surfaces networks of cracks were observed. XRD studies showed that the metastable γ-Al₂O₃ phase present in the SC is transformed to stable α-Al₂O₃ after post treatments. In LM coatings Al₂TiO₅ phase was more predominant in contrast to SC and VA coatings. The microhardness enhancement was observed in case of LM coating compared to the VA and SC. Due to elimination of coating defects in LM samples, there is a considerable reduction in the surface roughness.     

Deposition, microstructure and properties of texture-controlled CVD α-Al2O3 coatings

The influence of nucleation on the microstructure and properties of CVD Al₂O₃ was investigated. The experimental α-Al₂O₃ layers were deposited (a) without nucleation control and (b) with nucleation steps resulting in pronounced , and growth textures. The experimental layers were characterised using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Wear properties of the textured coatings were evaluated in turning. The chemistry of the nucleation surface appeared to be an important factor in pre-determining the phase content and growth textures of the Al₂O₃ layers. Optimised nucleation resulted in substantially improved wear properties and these kinds of α-Al₂O₃ layers were typically composed of relatively small, defect-free grains exhibiting no porosity. The textured α-Al₂O₃ layer showed the best wear resistance.     

TEM and DFT investigation of CVD TiN/κ-Al2O3 multilayer coatings

This paper investigates the interfacial structure in hot-wall CVD TiN/κ-Al₂O₃ multilayer coatings using both HREM and DFT modeling. Two multilayers with different thicknesses of the TiN layers (50 and 600 nm) separating the κ-Al₂O₃ layers are analyzed. The general microstructure of the two multilayers is relatively similar. The TiN layer in the thicker TiN/κ-Al₂O₃ coating is thick enough to be several TiN grains high. This means that epitaxial columns, which are often found in the thinner TiN/κ-Al₂O₃ coatings, are not present. However, the orientation relationships at the TiN/κ-Al₂O₃ interfaces are the same in both multilayers. The HREM investigations show that κ-Al₂O₃ (001) planes can grow directly on flat (111) TiN faces, without any other phases or detectable amounts of impurities, such as sulphur, present. Where the TiN layers are more curved, γ-Al₂O₃ can be grown, at least partly stabilized by the cube-on-cube orientation relationship between γ-Al₂O₃ and the underlying TiN. The DFT calculations show very similar adsorption strengths for an O monolayer positioned on Ti-terminated TiC(111) and TiN(111) surfaces, with preferred adsorption in the fcc site. O adsorption on N-terminated TiN(111) is much weaker, with preferred adsorption in the top site. Calculated elastic-energy contributions yield a higher stability for κ-Al₂O₃ on TiN(111) than on TiC(111) and a higher stability for κ-Al₂O₃ than for α-Al₂O₃ on both TiC and TiN. This indicates that the observed higher stability of κ-Al₂O₃ on TiC(111) than on TiN(111) is not due to the lattice mismatch, while the preferred epitaxial growth of κ-Al₂O₃ over α-Al₂O₃ can be partly attributed to the mismatch.     

Al2O3纳米粒子环氧涂层对钢筋防护性能的电化学噪声分析

目的研究Al2O3纳米粒子环氧复合涂层对钢筋的防护性能。方法制备Al2O3纳米粒子,将其添加至环氧涂料中,并涂覆在工业钢筋表面成膜。通过XRD和SEM对Al2O3进行表征;利用电化学噪声、交流阻抗谱分析技术,对复合涂层在3.5%(质量分数)NaCl介质中对工业钢筋的防护性能进行测试分析。结果制备的氧化铝纳米粒子的粒径平均为75 nm。通过对电化学噪声测试的有效数据进行时域和频域分析,通过交流阻抗谱分析及数据拟合,认为Al2O3纳米粒子添加量为0.1%(以占环氧树脂质量的百分比计)时,涂层对钢筋的防护性能最好。结论向环氧涂层中添加适量的Al2O3纳米粒子,可以明显提升其对钢筋的防护性能。     

Synthesis and characterization of Y3Al5O12 and ZrO2-Y2O3 thermal barrier coatings by combustion spray pyrolysis

Y₃Al₅O₁₂ and ZrO₂-Y₂O₃ (8 mol% YSZ) coatings for potential application as thermal barrier coatings were prepared by combustion spray pyrolysis. Thermal cycling of as deposited coatings on stainless steel and FeCrAlY bond coat substrates was carried out at 1000 °C and 1200 °C to determine the thermal fatigue response. Structural and morphological studies on Y₃Al₅O₁₂ and 8 mol% YSZ coatings before and after thermal cycling have been carried out. It has been noted that the coatings on FeCrAlY substrates remain intact after 50 cycles between room temperature and 1200 °C, whereas the coatings on stainless steel show some minor damage such as peeling off near the periphery after 50 cycles at 1000 °C. Thermal diffusivity values of Y₃Al₅O₁₂ and 8 mol% YSZ films were measured by using photo thermal deflection spectroscopy and the values are lower than those of coatings produced by conventional techniques such as EBPVD and APS.     

Effects of K2O-Li2O doping on surface and catalytic properties of Fe2O3/Cr2O3 system

The effects of K₂O and Li₂O-doping (0.5, 0.75 and 1.5 mol%) of Fe₂O₃/Cr₂O₃ system on its surface and the catalytic properties were investigated. Pure and differently doped solids were calcined in air at 400-600 °C. The formula of the un-doped calcined solid was 0.85Fe₂O₃:0.15Cr₂O₃. The techniques employed were TGA, DTA, XRD, N₂ adsorption at −196 °C and catalytic oxidation of CO oxidation by O₂ at 200-300 °C. The results revealed that DTA curves of pure mixed solids consisted of one endothermic peak and two exothermic peaks. Pure and doped mixed solids calcined at 400 °C are amorphous in nature and turned to α-Fe₂O₃ upon heating at 500 and 600 °C. K₂O and Li₂O doping conducted at 500 or 600 °C modified the degree of crystallinity and crystallite size of all phases present which consisted of a mixture of nanocrystalline α- and γ-Fe₂O₃ together with K₂FeO₄ and LiFe₅O₈ phases. However, the heavily Li₂O-doped sample consisted only of LiFe₅O₈ phase. The specific surface area of the system investigated decreased to an extent proportional to the amount of K₂O and Li₂O added. On the other hand, the catalytic activity was found to increase by increasing the amount of K₂O and Li₂O added. The maximum increase in the catalytic activity, expressed as the reaction rate constant (k) measured at 200 °C, attained 30.8% and 26.5% for K₂O and Li₂O doping, respectively. The doping process did not modify the activation energy of the catalyzed reaction but rather increased the concentration of the active sites without changing their energetic nature.     

过渡材料对等离子喷涂Al2O3梯度陶瓷涂层性能影响

针对Al2O3陶瓷涂层结合强度低、孔隙率高的实际,选择NiAl金属间化合物和金属铜粉作为过渡材料,利用等离子喷涂制备Al2O3梯度陶瓷涂层,并对梯度涂层进行组织形貌观察,测试结合强度和孔隙率.结果表明,梯度涂层的组织表现出宏观的不均匀性和微观连续性的分布特征,NiAl和Cu是金属基体与Al2O3涂层之间过渡层的理想材料,可以有效地提高涂层的结合强度,而Cu-Al2O3梯度涂层又比NiAl-Al2O3梯度涂层结合强度高;梯度涂层的孔隙率远低于双涂层的孔隙率,在Cu-Al2O3梯度涂层中随Al2O3含量的增加,涂层的孔隙率降低,而且孔隙率低于NiAl-Al2O3梯度涂层.     

Preparation of nanostructured Ni/Al2O3 composite coatings in high magnetic field

Ni/Al₂O₃ composite coatings were prepared by a novel method from a modified Watt's type electrolyte containing nano-Al₂O₃ particles, where a high magnetic field was imposed in the direction parallel to an electrolytic current instead of mechanical agitation. Effects of magnetic field on the content of particles, surface morphology, microhardness and wear resistance of plating layer were investigated. It was found that the high magnetic field played an important role in the formation of composite coatings. The amounts of nano-Al₂O₃ particles in the composite coating increased with increasing of magnetic flux density and reached a maximum value at 8 T, then reduced slightly. The microhardness and wear resistance of the nanocomposite coatings also enhanced with increasing of magnetic flux density as compared to that of pure Ni coating fabricated in the absence of magnetic field. That was because the co-deposited nano-Al₂O₃ particles were uniformly distributed in the Ni matrix and contributed to greatly increase the microhardness and wear resistance of the composite coatings. Moreover, the mechanism of action of high magnetic field was discussed preliminarily.     

Investigation on the corrosion and oxidation resistance of Ni-Al2O3 nano-composite coatings prepared by sediment co-deposition

Ni-Al₂O₃ composite coatings were prepared by using sediment co-deposition (SCD) technique from a Watt's type electrolyte containing nano-Al₂O₃ particles. The corrosion resistance and high temperature oxidation resistance of resulting composite coatings were investigated. It was found that the incorporation of nano-Al₂O₃ particles in Ni matrix refined the Ni crystal and changed the preferential orientation of composite coatings. Meanwhile, the corrosion and oxidation resistance were improved after the incorporation of nano-Al₂O₃ particles into Ni matrix. The nano-Al₂O₃ content in deposits plays an important role for improving the corrosion and oxidation protection. The corrosion and oxidation resistance of Ni-Al₂O₃ nano-composite coatings produced via SCD technique are superior to that of CEP technique. Compared to pure Ni and Ni-Al₂O₃ composite coatings fabricated using CEP technique, the Ni-7.58 wt.% Al₂O₃ composite coating obtained by SCD technique exhibits better corrosion resistance and enhanced high temperature oxidation resistance. Moreover, the mechanism of corrosion and high temperature oxidation resistance of Ni-Al₂O₃ nano-composite coatings are discussed.     

In-situ TiB2 and Al2O3 formation by DC plasma spraying

In-situ plasma spraying (IPS) is a promising process to fabricate composite coatings with in-situ formed thermodynamically stable phases. In the present study, mechanically alloyed Al-12Si, B₂O₃ and TiO₂ powder was deposited onto an aluminum substrate using atmospheric plasma spraying (APS). It has been observed that, during the coating process, TiB₂ and Al₂O₃ are in-situ formed through the reaction between starting powders and finely dispersed in hypereutectic Al-Si matrix alloy. Also, obtained results demonstrate that in-situ reaction intensity strongly depends on spray conditions.     

304不锈钢表面Ni-Al2O3复合镀层制备及性能研究

采用复合电沉积法在304奥氏体不锈钢表面制备Ni-Al₂O₃纳米镀层. 研究了Al₂O₃颗粒在复合镀层中的分布情况, 确定了镀液中颗粒的最佳加入量、最佳电流强度和最佳搅拌速度. 用扫描电镜和能谱仪、X射线衍射仪等设备鉴定镀层显微组织与组成. 结果表明, Ni-Al₂O₃纳米复合镀层均匀、致密、晶粒细小; 复合镀层结合强度、耐腐蚀性能优良, 抗高温氧化性能优于纯镍镀层.     

Magnetic properties of Al2O3-Cr2O3 solid solutions

Solid solution ceramics (Al₂O₃)_x(Cr₂O₃)_1−x with different x in the range of 0 < x < 1 were synthesized via traditional ceramic production method. X-ray diffraction results and Rietveld refinements indicated that all samples possessed rhomb-centered structure and continuous solid solutions were synthesized. The samples were composed of irregular grains with several micrometers in diameter. Temperature dependence of magnetization measurements showed monotonous decreasing Néel temperature with increasing x and percolation effect happened with threshold of x = 0.65. As x became higher, weak ferromagnetism was observed in the samples. Field dependence of magnetization measurements further confirmed the weak ferromagnetism in the samples with x = 0.7, 0.8 and 0.9.     

等离子喷涂Cu-Al2O3梯度涂层的组织与耐磨性分析

针对纯陶瓷涂层由于结合强度低、孔隙率高、影响涂层耐磨性的实际,用等离子喷涂法制备了Cu-Al2O3梯度涂层,用电子扫描显微镜(SEM)、金相显微镜等手段对涂层进行微观组织和成分分析,用自制销盘式固定磨料磨损试验机,检测了Cu-Al2O3梯度涂层的耐磨料磨损性能.结果表明,采用等离子喷涂法制备的Cu-Al2O3梯度涂层无明显的组织突变和宏观层间界面,涂层的组织表现出宏观不均匀性和微观连续性分布特征;梯度涂层中当Al2O3含量(质量分数,%)达到80%时(GC6),涂层的耐磨性最高,约为基体的3倍,随着Al2O3含量继续增大,纯陶瓷涂层(GC7)的耐磨性有所下降.     

Synthesis and characterization of Al2O3-Ce0.5Zr0.5O2 powders prepared by chemical coprecipitation method

Al₂O₃-Ce_0.5Zr_0.5O₂ catalytic powders were synthesized by the coprecipitation (ACZ-C) and mechanical mixing (ACZ-M) methods, respectively. As-synthesized powders were characterized by XRD, Raman spectroscopy, surface area and thermogravimetric analyses. It was found that the mixing extent of Al³⁺ ions affected the phase development, texture and oxygen storage capacity (OSC) of the Ce_0.5Zr_0.5O₂ powder. Single phase of ACZ-C could be maintained without phase separation and inhibit α-Al₂O₃ formation up to 1200 °C. The specific surface area value of ACZ-C (81.5 m²/g) was larger than that of ACZ-M (62.1 m²/g) and Ce_0.5Zr_0.5O₂ (17.1 m²/g) powders, which were calcined at 1000 °C. In comparison with ACZ-C and Al₂O₃, which were calcined at high temperature (900–1200 °C), it was found that the degradation rate of specific surface area of ACZ-C was lower than that of Al₂O₃. ACZ-C sample showed a higher thermal stability to resist phase separation and crystallite growth, which enhanced the oxygen storage capacity property for Ce_0.5Zr_0.5O₂ powders.     

BN/Al2O3 复合粉末及其聚合物基复合材料的制备与导热性能

采用固-液相共混法制备了多种BN/Al₂O₃复合粉末,通过冻融法和表面修饰法对BN进行了改性处理,改变表面修饰剂类型和摩尔比得到了前驱体和烧结态BN/Al₂O₃复合粉末,并利用机械混合法制备了聚合物基BN/Al₂O₃复合材料,并测试分析了其导热性能。结果表明,经冻融处理的BN分散性和界面相容性明显优于未经冻融处理的BN。多巴胺对BN的改性效果优于聚乙二醇。采用多巴胺作为表面修饰剂且BN与Al(NO₃)₃的摩尔比为1:1时,能够得到纳米Al₂O₃均匀包覆的微米BN粉末,即BN/Al₂O₃微纳复合粉末,其聚合物基复合材料的导热系数可达0.62 W·m^-1·K^-1,是纯聚合物导热系数的3倍,是采用纯微米BN粉末制备的聚合物基复合材料导热系数的1.5倍。在BN表面附着的Al₂O₃可以形成层状热传导通道,能够有效提高聚合物基BN/Al₂O₃复合材料的热导率。