Cr3+掺杂LiNi0.5Mn1.5O4材料的制备及性能研究

采用高温固相法合成了Cr₃₊掺杂的LiNi_0.5Mn_1.5O₄正极材料,研究了掺杂量对材料物理性能和电化学性能的影响。利用XRD、SEM对材料的结构和形貌进行了表征,结果显示样品具有棱边清晰的尖晶石形貌。讨论了不同Cr₃₊掺杂量对LiCr_xNi_0.5-0.5xMn_1.5-0.5xO₄(x=0,0.05,0.1,0.15,0.2)正极材料性能的影响。充放电测试、循环伏安和交流阻抗测试结果表明：当Cr₃₊的掺杂量为x=0.1时(LiCr_0.1Ni_0.45Mn_1.45O₄)正极材料的性能最好,0.1C、0.5C、1C、2C及5C的首次放电比容量依次为131.54mAh g_-1、126.84mAh g_-1、121.28mAh g_-1、116.49mAh g_-1和96.82mAh g_-1,1C倍率下循环50次,容量保持率仍为96.5%。     

高容量锂离子电池正极材料LiNi0.5Co0.2Mn0.3O2的制备与工艺优化

采用氢氧化物共沉淀法合成前驱体Ni_0.5Cc_0.2Mn_0.3H(OH)₂,进一步用高温固相法与锂源共混煅烧得到LiNi_0.5Co_0.2Mn_0.3O₂。初步探讨了前驱体与锂源在高温煅烧过程中的质量变化及煅烧工艺对材料结构和性能的影响。热重分析(TGA)表明在煅烧过程中750℃后材料质量几乎没有变化。X射线衍射(XRD)对750℃-900℃的材料进行结构分析,结果表明所有材料具有良好的α-NaFeO₂层状结构和较小的阳离子混排度。扫描电镜(SEM)分析表明材料具有表面光滑,分布均匀的球形结构。横流充放电测试结果表明在850℃煅烧的材料具有最好的电学性能,在0.2C,2.5-4.6V测试条件下,其具有193.7mAh/g的首次放电容量,循环30次后的容量保持率为94.2%,并且具有最好的倍率性能。     

Structural characterization of layered LiNi0.85−xMnxCo0.15O2 with x = 0, 0.1, 0.2 and 0.4 oxide electrodes for Li batteries

We report the synthesis of LiNi_0.85−xCo_0.15Mn_xO₂ positive electrode materials from Ni_0.85−xCo_0.15Mn_x(OH)₂ and Li₂CO₃. XRD and XPS are used to study the effect of Mn-doping on the microstructures and oxidation states of the LiNi_0.85−xCo_0.15Mn_xO₂ materials. The analysis shows that Mn-doping promotes the formation of a single phase. With increasing substitution of Mn ions for Ni ions, the lattice parameter a decreases, while the lattice parameters c and c/a increase. XPS revealed that the oxidation states of Ni, Co and Mn in LiNi_0.85−xCo_0.15Mn_xO₂ compounds (where x = 0.1, 0.2 and 0.4) were +2/+3, +3 and +4. The substitution of Mn ions for Ni ions induces a decrease in the average oxidation state of Ni. Because the substitution of Mn for Ni ions is complex, the extent of the changes between the lattice parameter and L_M-O differ. The occupation of Ni in Li sites is affected by the ordering of Mn⁴⁺ with Ni²⁺ and Mn⁴⁺ with Li⁺.     

Synthesis and electrochemical performance of Li(Ni0.8Co0.15Al0.05)0.8(Ni0.5Mn0.5)0.2O2 with core-shell structure as cathode material for Li-ion batteries

The core-shell structure cathode material Li(Ni_0.8Co_0.15Al_0.05)_0.8(Ni_0.5Mn_0.5)_0.2O₂ (LNCANMO) was synthesized via a co-precipitation method. Its applicability as a cathode material for lithium ion batteries was investigated. The core-shell particle consists of LiNi_0.8Co_0.15Al_0.05O₂ (LNCAO) as the core and a LiNi_0.5Mn_0.5O₂ as the shell. The thickness of the LiNi_0.5Mn_0.5O₂ layer is approximately 1.25 μm, as estimated by field emission scanning electron microscopy (FE-SEM). The cycling behavior between 2.8 and 4.3 V at a current rate of 18 mA g⁻¹ shows a reversible capacity of about 195 mAh g⁻¹ with little capacity loss after 50 cycles. High-rate capability testing shows that even at a rate of 5 C, a stable capacity of approximately 127 mAh g⁻¹ is retained. In contrast, the capacity of LNCAO rapidly decreases in cyclic and high rate tests. The observed higher current rate capability and cycle stability of LNCANMO can be attributed to the lower impedance including charge transfer resistance and surface film resistance. Differential scanning calorimetry (DSC) indicates that LNCANMO had a much improved oxygen evolution onset temperature of approximately 251 °C, and a much lower level of exothermic-heat release compared to LNCAO. The improved thermal stability of the LNCANMO can be ascribed to the thermally stable outer shell of LiNi_0.5Mn_0.5O₂, which suppresses oxygen release from the host lattice and not directly come into contact with the electrolyte solution. In particular, LNCANMO is shown to exhibit improved electrochemical performance and is a safe material for use as an electrode for lithium ion batteries.     

Preparation and electrical properties of perovskite ceramics in the system BaBi1−xSbxO3 (0 ≤ x ≤ 0.5)

The effect of the composition on the electrical properties of BaBi_1−xSb_xO₃ (0 ≤ x ≤ 0.5) negative temperature coefficient (NTC) thermistors was studied. Major phases present in the sintered bodies of BaBi_1−xSb_xO₃ (0 < x < 0.5) ceramics were BaBi_0.5Sb_0.5O₃ compounds with a rhombohedral structure and BaBiO₃ compounds with a monoclinal structure. Most pores were located in the grains of BaBiO₃ and BaBi_0.5Sb_0.5O₃ ceramics. It was apparent that the ρ₂₅ and B_25/85 constant of the thermistors increased with increasing Sb content.     

Electrical properties of binder-free thick film BaYxBi1−xO3 NTC thermistors

The microstructure and electrical properties of BaY_xBi_1−xO₃ thick film negative temperature coefficient thermistors, fabricated by screen printing, were investigated. The sintered thick films were the single-phase solid solutions of the BaY_xBi_1−xO₃ compounds with a monoclinic structure. The added Y₂O₃ led to a significant decrease in the grain size of the thermistors. The resistivity and coefficient of temperature sensitivity for the BaY_xBi_1−xO₃ (0 ≤ x ≤ 0.15) thick film NTC thermistors decreased first with increasing x in the range of x < 0.04 and then increased with further increase in x.     

Studies on the power factor of (Ba,Sr)Co2+xRu4−xO11 compounds

We have prepared polycrystalline single-phase ACo_2+xRu_4−xO₁₁ (A = Sr, Ba; 0 ≤ x ≤ 0.5) using the ceramic method and we have studied their structure, electrical resistivity and Seebeck coefficient, in order to estimate their power factor (P.F.). These layered compounds show values of electrical resistivity of the order of 10⁻⁵ Ωm and their Seebeck coefficients are positive and range from 1 μV K⁻¹ (T = 100 K) to 20 μV K⁻¹ (T = 450 K). The maximum power factor at room temperature is displayed by BaCo₂Ru₄O₁₁ (P.F.: 0.20 μW K⁻² cm⁻¹), value that is comparable to that shown by compounds such as SrRuO₃ and Sr₆Co₅O₁₅.     

Thermoelectric properties of Cu1−xPtxFeO2 (0.0 ≤ x ≤ 0.05) delafossite-type transition oxide

The samples of Cu_1−xPt_xFeO₂ (0 ≤ x ≤ 0.05) delafossite were synthesized by solid state reaction method for studying thermoelectric properties. The properties of Seebeck coefficient, electrical conductivity and thermal conductivity were measured in the high temperature ranging from 300 to 960 K. The results of Seebeck coefficient, electrical conductivity and power factor were increased with increasing Pt substitution and temperature. The thermal conductivity was decreased from 5.8 to 3.5 W/mK with increasing the temperature from 300 to 960 K. An important results, the highest value of power factor and ZT is 2.0 × 10⁻⁴ W/mK² and 0.05, respectively, for x = 0.05 at 960 K.     

Magnetomechanical properties of epoxy-bonded Sm1−xNdxFe1.55 (0 ≤ x ≤ 0.56) pseudo-1-3 magnetostrictive particulate composites

Pseudo-1-3 magnetostrictive particulate composites consisting of light rare earth (Sm and Nd)-based magnetostrictive Sm_1−xNd_xFe_1.55 particles with the Nd content x of 0-0.56 and randomly distributed sizes of 10-180 μm embedded and aligned in a passive epoxy matrix are fabricated using the particulate volume fraction of 0.5. The quasistatic magnetomechanical properties of the composites are investigated and the results are compared with their monolithic alloys for various x. The composites exhibit similar qualitative trends in properties with the alloys for all x. The Sm_0.92Nd_0.08Fe_1.55 composite shows a large unsaturated magnetostriction λ of −530 ppm at 500 kA/m and a high piezomagnetic coefficient d₃₃ of −2.0 nm/A at 100 kA/m as a result of the magnetocrystalline anisotropy compensation between Sm³⁺ and Nd³⁺ ions in the Sm_0.92Nd_0.08Fe_1.55 alloy.     

过锂量对富锂锰基正极材料Li1.2xNi0.1Co0.2Mn0.5O2结构与电化学性能的影响

采用流变相法合成得到Li_(1.2+x)Ni_(0.1)Co_(0.2)Mn_(0.05)O_2(x=0, 0.036, 0.060, 0.096),探讨过锂量对结构和电化学性能的影响。X射线衍射(XRD)对样品进行结构分析证明所有样品具有典型的α-NaFeO_2结构和较小的阳离子混排度。扫描电镜(SEM)对样品进行表征证明不同过锂量的材料,颗粒相对均匀,表面光滑。电化学性能测试结果表明:最佳过锂量为x=0.036时,正极材料Li_(1.236)Ni_(0.1)Co_(0.2)Mn_(0.5)O_2在0.05C、2～4.8V测试条件下进行电化学性能测试,25和55℃下该材料初始放电容量分别为215.3和297.1 mAh·g-1,首次库伦效率分别为66.6%和84.6%,0.2 C下循环50次后容量保持率分别为89.0%和87.8%,且x=0.036时该材料具有最佳的倍率性能。     

Fabrication and properties of p-type K doped Zn1−xMgxO thin film

A series of K doped Zn_1−xMg_xO thin films have been prepared by pulsed laser deposition (PLD). Hall-effect measurements indicate that the films exhibit stable p-type behavior with duration of at least six months. The band gap of the K doped Zn_1−xMg_xO films undergoes a blueshift due to the Mg incorporation. However, photoluminescence (PL) results reveal that the crystallinity decreased with the increasing of Mg content. The fabricated K doped p-type Zn_0.95Mg_0.05O thin film exhibits good electrical properties, with resistivity of 15.21 Ω cm and hole concentration of 5.54 × 10¹⁸ cm⁻³. Furthermore, a simple ZnO-based p-n heterojunction was prepared by deposition of a K-doped p-type Zn_0.95Mg_0.05O layer on Ga-doped n-type ZnO thin film with low resistivity. The p-n diode heterostructure exhibits typical rectification behavior of p-n junctions.     

Relationships between Zr substitution for Ti and microwave dielectric properties in Mg(ZrxTi1−x)O3 ceramics

The influence of Zr substitution for Ti on the microwave dielectric properties and microstructures of the Mg(Zr_xTi_1−x)O₃(MZ_xT) (0.01 ≤ x ≤ 0.3) ceramics was investigated. The quality factors of Mg(Zr_xTi_1−x)O₃ ceramics with x = 0.01-0.05 were improved because the solid solution of a small amount of Zr⁴⁺ substitution in the B-site could increase density and grain size. An excess of Zr⁴⁺ resulted in the formation of a great deal of secondary phase that declined the microwave dielectric properties of MZ_xT ceramics. The temperature coefficient of resonant frequency (τ_f) of Mg(Zr_xTi_1−x)O₃ ceramics slightly increased with increasing Zr content, and the variation in τ_f was attributed to the formation of secondary phases.     

Preparation and characterization of La1−xKxFeO3 (x = 0-1) by self-propagating high-temperature synthesis for use as soot combustion catalyst

This paper proposes La_1−xK_xFeO₃ prepared by self-propagating high-temperature synthesis (SHS) as an alternative to platinum catalysts for promoting diesel soot combustion. The catalytic property of eleven products SHSed with different substitution ratios of potassium (x = 0-1) was experimentally evaluated using a thermobalance. In the mass loss curves of the product, T₅₀ was defined as the temperature at which the weight of the reference soot decreases to half its initial weight. The BET specific surface area of SHSed La_1−xK_xFeO₃ depended on x strongly. All the products showed good oxidation catalytic activity. Despite having the smallest surface area (0.11 m²/g) among the obtained products, La_0.9K_0.1FeO₃ (x = 0.1) was found to be the best catalyst with the lowest T₅₀ (442 °C). T₅₀ of La_1−xK_xFeO₃ decreased with increasing x for x > 0.2. The products with x = 0.6 and 0.8 were the second-best catalysts in terms of their T₅₀. Moreover, average apparent activation energy of La_0.9K_0.1FeO₃ (x = 0.1) calculated by Friedman method using TG was as much as 61 kJ/mol lower than that of Pt/Al₂O₃ catalyst. In conclusion, potassium-substituted SHSed La_1−xK_xFeO₃ can be used as an alternative to Pt/Al₂O₃ for soot combustion.     

Characterization and blood compatibility of TiCxN1 − x hard coating prepared by plasma electrolytic carbonitriding

A novel technique to form Ti(C, N) on titanium, named as plasma electrolytic carbonitriding (PEC/N) on cathode was successful used to prepare TiC_xN_1 − x coating. The structure, composition and morphology of the coating were characterized by XRD, XPS and SEM, respectively. The results indicated that TiC_0.3N_0.7 as a new species appears on the surface of the titanium plate, and the thickness of the coating with porous surface morphology increases with the treated time. The blood compatibility of the TiC_0.3N_0.7 coating was evaluated by haemolysis ratios, dynamic blood clotting test, plasma recalcification time and platelet adhesion. The results indicated that the blood compatibility of the plasma-treated titanium with TiC_xN_1 − x coating is significantly improved as compared to the original titanium. Additionally, the results derived from measurements of hardness and corrosion indicated that the coating has excellent mechanical and corrosion-resistant properties.     

Thermoelectric properties of Bi2SexTe3−x prepared by Bridgman method

Bi₂Se_xTe_3−x crystals with various x values were grown by Bridgman method. The electrical conductivity, σ, was found to decrease with increasing Se content. The highest σ of 1.6 × 10⁵ S m⁻¹ at room temperature was reached at x = 0.12 with a growth rate of 0.8 mm h⁻¹. The Seebeck coefficient, S, was less dependent on Se content, all with positive values showing p-type characteristics, and the highest S was measured to be 240 μV K⁻¹ at x = 0.24. The lowest thermal conductivity, κ, was 0.7 W m⁻¹ K⁻¹ at x = 0.36. The electronic part of κ, κ_el, showed a decrease with increasing Se content, which implies that the hole concentration as the main carriers was reduced by the addition of Se. The highest dimensionless figure of merit, ZT, at room temperature was 1.2 at x = 0.36, which is attributed to the combination of a rather high electrical conductivity and Seebeck coefficient and low thermal conductivity.     

Porous Li4Ti5O12 anode material synthesized by one-step solid state method for electrochemical properties enhancement

A porous Li₄Ti₅O₁₂ anode material was successfully synthesized from mixture of LiCl and TiCl₄ with 70 wt% oxalic acid by a modified one-step solid state method. The anode material Li₄Ti₅O₁₂ exhibited a cubic spinel structure and only one voltage plateau occurred around 1.5 V. The initial capacity of porous Li₄Ti₅O₁₂ was 167 and 133 mAh g⁻¹ at 0.5 and 1C charge/discharge rate, respectively, and the capacity retention maintained above 98% after 200 cycles. The porous Li₄Ti₅O₁₂ structure showed promising rate performance with a capacity of 70 mAh g⁻¹ at charge/discharge 10C rate after 200 cycles. It was demonstrated that the porous structure could withstand 50C charge/discharge rate and exhibited excellent cycling stability.     

Preparation and characterization of spinel Li4Ti5O12 anode material from industrial titanyl sulfate solution

Spinel Li₄Ti₅O₁₂ anode material is successfully synthesized by a solid-state method using lithium carbonate and titanium precursors which are prepared by the low cost industrial titanyl sulfate solution. The characters of H₂TiO₃ and TiO₂ precursors are determined by TG/DTA and SEM methods. TG-DAT and EDS methods show that H₂TiO₃ can absorb sulphate ions which can be present as impurities. XRD method shows that the impure phases of Li₂SO₄ and rutile TiO₂ appear in Li₄Ti₅O₁₂ synthesized by H₂TiO₃. The formation of Li₂SO₄ is identified in thermodynamics during the process of calcination. Owing to the formation of Li₂SO₄ impurity, the capacity of the Li₄Ti₅O₁₂ synthesized by H₂TiO₃ is low. One effective way that can tackle this problem is to remove the sulphur by calcining H₂TiO₃, after calcinations, the production will have a thermal treatment with Li₂CO₃. The obtained Li₄Ti₅O₁₂ shows better electrochemical performance. The specific capacities can be increased by 20 mAh g⁻¹ at 0.1, 0.5 and 1C rates.     

Resistivity, thermopower, and thermal conductivity of nickel doped compounds Cr1−xNixSb2 at low temperatures

Substitutional compounds Cr_1−xNi_xSb₂ (0 ≤ x ≤ 0.1) were synthesized, and the effect of Ni substitution on transport and thermoelectric properties of Cr_1−xNi_xSb₂ were investigated at the temperatures from 7 to 310 K. The results indicated that the magnitudes of the resistivity and thermopower of Cr_1−xNi_xSb₂ decreased greatly with increasing Ni content at low temperatures, owing to an increase in electron concentration caused by Ni substitution for Cr. Experiments also showed that the low-temperature lattice thermal conductivity of Cr_1−xNi_xSb₂ decreased substantially with increasing Ni content due to an enhancement of phonon scattering by the increased number of Ni atoms. As a result, the figure of merit, ZT, of lightly doped Cr_0.99Ni_0.01Sb₂ was improved at T > ∼230 K. Specifically, the ZT of Cr_0.99Ni_0.01Sb₂ at 310 K was approximately ∼29% larger than that of CrSb₂, indicating that thermoelectric properties of CrSb₂ can be improved by an appropriate substitution of Ni for Cr.     

Structural, elastic and electronic properties of Mg(Cu1−xZnx)2 alloys calculated by first-principles

The structural, elastic and electronic properties of Mg(Cu_1−xZn_x)₂ alloys (x = 0, 0.25, 0.5,and 0.75) were investigated by means of first-principle calculations within the framework of density functional theory (DFT). The calculation results demonstrated that the partial substitution of Cu with Zn in MgCu₂ leaded to an increase of lattice constants, and the optimized structural parameters were in very good agreement with the available experimental values. From energetic point of view, it was found that with increase of Zn content the structural stability of Mg(Cu_1−xZn_x)₂ alloys decreased apparently. The single-crystal elastic constants were obtained by computing total energy as a function of strain, and then the bulk modulus B, shear modulus G, Young's modulus Y and Poisson's ratio ν of polycrystalline aggregates were derived. The calculated results showed that among the Mg(Cu_1−xZn_x)₂ alloys, MgCuZn exhibited the largest stiffness, while Mg₂Cu₃Zn showed the best ductility. Finally, the electronic density of states (DOSs) and charge density distribution were further studied and discussed.