Ce改性TiO2纳米粒子的制备及光催化活性

采用浸渍法制备了Ce/纳米TiO2复合粉体,用XRD对复合粉体的晶体结构进行了表征.以紫外光照下降解甲基橙为目标,研究了Ce掺杂量和焙烧温度对Ce/纳米TiO2复合粉体的光催化能力的影响规律,并分析其机理.结果表明:Ce掺杂能有效地提高纳米TiO2光催化降解甲基橙的能力,在400℃～700℃的焙烧温度下,纳米TiO2为锐钛型晶型结构,0.4%Ce(质量分数,下同)掺杂的复合粉体具有最好的光催化降解甲基橙的能力,其原因在于Ce4+掺杂有利于在TiO2纳米粒子中心和表面之间产生电势差,实现光生电子-空穴对的有效分离,因此存在一个最佳掺杂浓度使得光催化活性最高;焙烧温度对Ce/TiO2纳米复合粉体的影响依赖于Ce的掺杂量,低掺杂量时,较高的焙烧温度降解效果较好;高掺杂量时,较低的焙烧温度降解效果较好.     

Ce改性TiO2纳米粒子的制备及光催化活性

采用浸渍法制备了Ce/纳米TiO2复合粉体,用XRD对复合粉体的晶体结构进行了表征.以紫外光照下降解甲基橙为目标,研究了Ce掺杂量和焙烧温度对Ce/纳米TiO2复合粉体的光催化能力的影响规律,并分析其机理.结果表明Ce掺杂能有效地提高纳米TiO2光催化降解甲基橙的能力,在400℃～700℃的焙烧温度下,纳米TiO2为锐钛型晶型结构,0.4%Ce(质量分数,下同)掺杂的复合粉体具有最好的光催化降解甲基橙的能力,其原因在于Ce4+掺杂有利于在TiO2纳米粒子中心和表面之间产生电势差,实现光生电子-空穴对的有效分离,因此存在一个最佳掺杂浓度使得光催化活性最高;焙烧温度对Ce/TiO2纳米复合粉体的影响依赖于Ce的掺杂量,低掺杂量时,较高的焙烧温度降解效果较好;高掺杂量时,较低的焙烧温度降解效果较好.     

Zr和N共掺杂TiO2的制备、表征及其光催化性能

利用水解沉淀法制备TiO2、N-TiO2、Zr-TiO2以及Zr和N共掺杂的纳米TiO2,用TEM、XRD、XPS和UV-Vis-DRs等方法对光催化剂的结构、元素组成和对可见光的响应等性能进行表征,并以甲基橙为目标降解物,测试其光催化降解效果。结果表明,Zr掺杂能够降低TiO2光催化剂的粒径;Zr和N共掺杂可以起到协同作用,提高样品的光催化活性,同时增强样品在可见光区的响应。Zr和N共掺杂TiO2在高压汞灯光照下比TiO2具有更好的光催化效果,2%Zr和N共掺杂TiO2光照3h后对甲基橙的降解率比纯TiO2提高32%。     

聚乙二醇对TiO2-SiO2粒子的生成及光催化性能影响

以TiCl4为原料,采用自组装技术制备TiO2-SiO2复合粒子,加入聚乙二醇2000（PEG 2000）,探讨聚乙二醇对TiO2-SiO2粒子生成及光催化降解甲基橙的影响。研究发现：随组装次数的增多,复合粒子表面TiO2 的含量增多;随PEG2000的加入,TiO2颗粒间呈现一定的孔隙,使TiO2层粒子的表面积增加;样品经550 ℃煅烧,得到均为锐钛矿与金红石的混合相,且随着PEG2000含量的增加,锐钛矿的相对含量随之增加;光催化实验表明,PEG2000的掺杂使TiO2-SiO2的光催化性能得以提高。     

掺Ag量对绢云母负载纳米二氧化钛性能的影响

以绢云母为载体,采用水解-沉淀法制备出了绢云母负载纳米TiO2粉体（TiO2/M）,在粉体表面沉积不同量的Ag2CO3,经400℃焙烧,制得不同掺Ag量的绢云母负载TiO2光催化剂,采用TG、XRD、SEM、EDS、UV等手段对样品进行了性能表征;并以日光色镝灯为光源,甲基橙为模拟污染物检测其光催化活性,研究了Ag的掺杂量对粉体中TiO2晶相结构、粒度和光催化性能的影响。结果表明：纳米TiO2均匀负载在绢云母上形成包覆层,Ag的掺杂抑制了TiO2晶粒的长大,减缓锐钛矿向金红石相的转变,同时Ag的掺杂形成新的能级结构,随Ag＋/Ti4＋摩尔比的增加,样品对光的吸收边逐渐红移至440～520 nm,具有明显的可见光响应,当Ag＋/Ti4＋=0.05时,制得样品对甲基橙的光催化降解率是没有掺Ag的样品的1.5倍,相同条件下重复利用4次,该样品60 min对甲基橙的降解率仍然可达34%。     

钕掺杂氧化锌粉末的光性能和光催化性能(英文)

为了提高氧化锌(ZnO)的光催化性能,通过水热法制备了不同钕(Nd)掺杂量的ZnO。X射线衍射分析(XRD)和光电子能谱(XPS)测试说明钕原子成功地掺杂进入了ZnO晶格。XRD图谱还说明了粉末具有各向异性。光致发光(PL)图谱在可见光区域出现较宽范围的强峰。Nd掺杂使得可见光发射强度增强。光催化性能通过降解甲基橙溶液进行测试。研究发现Nd掺杂使得氧化锌的光催化性能得到提高,当掺杂Nd的摩尔分数为3%时,其光催化性能最佳。Nd掺杂引起的电子空穴对的增加以及诱导产生的置换氧缺陷(OZn)和间隙氧缺陷(Oi)使得可见光发射增强和光催化性能得到提高。     

溶胶-凝胶法制备TiO2纳米颗粒及其光催化性能

考察了通过溶胶-凝胶法进行过渡金属(Fe3 、Zn2 、Co2 、Ni2 、Cr3 和Sn4 )和稀土元素(La3 、Pr3 、Nd3 、Ce4 、Sm3 、Tb3 、Eu.3 、Gd3 、Y3 和Dy3 )掺杂的TiO2纳米颗粒的光催化活性,以及通过超声波处理反应过程中的溶胶所制备得到的TiO2纳米颗粒的光催化活性.结果表明:0.5%Sn4 、0.5%La3 、0.5%Y3 和0.5%Eu3 (质量分数)掺杂的TiO2纳米颗粒在降解甲基橙溶液的反应中,其光催化活性提高2%～7%;其它的掺杂则使TiO2纳米颗粒的光催化活性降低0.5%～25%;在TiO2纳米颗粒的制备过程中,对溶胶进行超声辐照可使其光催化活性提高15%以上,这是提高TiO2纳米颗粒光催化活性的一条新途径.     

Mg2+掺杂TiO2薄膜的制备及其光催化性能研究

以钛酸四丁酯和Mg(NO3)2为原料,采用溶胶-凝胶法在较低的热处理温度下制备了Mg2+掺杂的TiO2薄膜,并研究了TiO2薄膜光催化降解甲基橙的情况.采用DTA、XRD、SEM等研究测试手段,发现通过溶胶-凝胶法在TiO2溶胶中加入Mg(NO3)2的方法,可以降低TiO2从无定型到锐钛矿相和锐钛矿相到金红石相的晶型转变温度,并在600C热处理条件下,获得了具有锐钛矿相和金红石相混晶的TiO2薄膜,通过甲基橙水溶液光催化实验表明:其光催化活性高于未掺杂TiO2薄膜的光催化活性.     

Cu2O/TiO2/Pt复合薄膜的制备及其性能

为了降解环境污染物,通过磁控溅射的方法在玻璃基底上溅射沉积Cu2O/TiO2/Pt复合薄膜。采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、紫外可见分光光谱仪(UV-vis)和光致发光光谱仪(PL)对复合薄膜的表面形貌和光学性能进行分析。通过可见光下对甲基橙溶液的光催化降解试验研究了薄膜的光催化活性。结果表明:Cu2O/TiO2/Pt复合薄膜共有3层,从下到上依次为Pt层、锐钛矿型TiO2层和Cu2O层。薄膜表面平整致密,由形状规则的球形颗粒组成。Cu2O/TiO2/Pt复合薄膜的光催化活性高于Cu2O/TiO2复合薄膜的和纯TiO2薄膜的光催化活性。光催化活性的提高是由于Pt层的存在进一步抑制了光生电子与空穴的复合,延长了光生载流子的寿命,提高了量子产率,进而有效地改善了薄膜的光催化活性。     

热喷涂法制备的La3+掺杂纳米TiO2粉末的表征

采用等离子热喷涂法以钛酸四丁酯为主要原料制备出稀土离子掺杂的纳米TiO2光催化剂.通过XRD,XPS,TEM,UV-Vis等检测手段对样品进行表征,同时检测了其光催化性能,并分析了掺杂对TiO2的影响机理.结果表明,所制备的La3 掺杂纳米TiO2是锐钛矿相和金红石相混晶结构,粒径分布在10～50nm之间;La3 掺杂能够促进锐钛矿向金红石的转变,同时抑制TiO2晶粒的长大;La3 掺杂使TiO2紫外-可见吸收光谱发生红移;适量La3 掺杂能显著提高TiO2的光催化活性,最佳掺杂浓度为0.5%(与Ti原子摩尔比),甲基橙降解率在90min内可达到82.4%.比纯TiO2高出13.2%.     

Effects of B2O3-SiO2 doping on electrical properties of Ba0. 65 Sr0. 35 TiO3 ceramics

Ba0. 65 Sr0. 35 TiOa ceramics doped with B2O3-SiO2 glass composition were prepared by using conventional solid-state reaction method. The effects of glass dopant on the dielectric and ferroelectric properties were investigated. The results show that the dielectric constant decreases while the dielectric loss increases after doping. And as the glass content increases the dielectric constant decreases while the dielectric loss changes slightly. From the complex impedance analysis the resistance and the relaxation time of the grain and the grain boundary can be calculated.Comparing the P--E hysteresis loop of undoped Ba0.65 Sr0.35 TiO3 ceramics with that of B2O3-SiO2 doped Ba0.65 Sr0.35 TiO3 ceramics, it can be seen that the remanent polarization decreases when the B2O3-SiO2 content is lower than 8% (molar fraction), and the coercive field increases with the increase of B2O3-SiO2 content.     

Optical properties and photocatalytic activity of Nd-doped ZnO powders

To improve the photocatalytic activity of zinc oxides, ZnO powders doped with different neodymium (Nd) concentrations were prepared via hydrothermal method. X-ray diffraction (XRD) together with X-ray photoelectron spectroscopy (XPS) patterns revealed that Nd atoms were successfully incorporated into the ZnO lattice. XRD pattern also showed some anisotropy of the powders. The photoluminescence (PL) spectrum demonstrated a strong and broad peak in the visible light region, and the intensity of visible light emission was enhanced by Nd-doping. The photocatalytic activity was evaluated by the degradation of methyl orange solution. It is shown that doping of Nd into ZnO induces an increase of the photocatalytic activity and it attains to optimum at 3% (mole fraction) doping concentration. The intense visible light emission and the enhanced photocatalytic activity were explained by the increase in electron hole pairs and induced defects like antisite oxygen O_Zn and interstitial oxygen O_i, due to the doping of Nd.     

溶胶复合提高WO3气致变色薄膜氢敏特性

本文制备了一种WO3-TiO2-SiO2溶胶,通过浸渍提拉法制备了适用于室温下的光学氢敏薄膜。采用FT-IR, SEM, TEM, AFM,XPS以及紫外-可见-近红外光谱对复合薄膜的结构及气致变色性能进行了表征。尽管TiO2并没有复合到薄膜中,但其在溶胶中引导了新的WO3颗粒的生成。这种颗粒分布在薄膜表面使得其表面粗糙度得到提高。气敏测试显示复合薄膜较未复合薄膜拥有更好的气敏性能。这种提升应当来源于WO3颗粒带来的更高的表面粗糙度。     

La、Nd、Bi共掺杂制备TiO2电致变色薄膜及其性能研究

为了提高TiO2薄膜的光学属性和着色效率,采用溶胶-凝胶工艺,以钛酸丁酯为前驱体在ITO导电玻璃基片表面制备了La、Nd、Bi共掺杂TiO2薄膜。采用XRD、UV-vis和化学工作站等手段研究了TiO2薄膜的结构和表面的光学和电致变色性能。结果表明:在400、500和600℃热处理的二氧化钛干凝胶中形成锐钛矿型二氧化钛,且热处理温度越高,晶体发育越完整。La、Nd、Bi掺杂TiO2增加了TiO2八面体的排列无序性,导致非晶化程度提高。体积分数为12%的钛酸丁酯相应制备的薄膜具有优良的电致变色性能。500℃热处理的TiO2薄膜电致变色性能最为优异。实验进行了La、Nd、Bi单独掺杂TiO2薄膜的性能分析,单独掺杂摩尔分数为8%La、18%Nd、6%Bi的TiO2薄膜具有较优异的变色性能,单独掺杂变色效果的顺序是6%Bi<8%La<18%Nd。La、Nd、Bi共掺杂锐钛矿型TiO2仍然具有很高的非晶化程度,且当掺杂摩尔比La:Nd:Bi=4:10:2时,取得薄膜最佳循环伏安特性,掺杂TiO2非晶化程度最高。     

X-TiO2(X=Ce,Bi)粉体的光电催化性能的研究

采用溶胶-凝胶法制备出纳米X- TiO2(X=Ce,Bi)粉体,并用XRD、UV-Vis DRS对其进行表征,以500W氙灯模拟太阳光,考察改性TiO2粉体的可见光催化活性.采用涂覆法制备出改性TiO2电极,以300W高压汞灯为侧光源,考察了电极的光电催化性能.实验结果表明:改性TiO2粉体均为锐钛矿型晶相,Ce和Bi的加入不同程度地提高了TiO2在可见光区的吸光强度,Bi和Ce最佳摩尔掺杂量均为0.04％.3种电极光电催化性能先后排序为:TiO2电极＜0.04％Bi-TiO2电极＜0.04％Ce-TiO2电极,循环伏安曲线分析表明,金属离子的掺杂提高了TiO2电极的电催化活性,且Ce的掺杂对电极电催化活性的影响大于Bi.HPLC分析表明,金属离子掺杂使得苯环开环加速,促进了苯酚的氧化过程.     

掺杂Y^3＋的纳米TiO2微粒的制备及其光催化性能

在Sol-Gel法制备纳米TiO2微粒的最佳制备条件的基础上，制备了掺杂稀土离子钇(Y^3 )的纳米TiO2复合粒子，并对这二者进行了XRD，TEM和DRS表征及光催化活性检验。结果表明，未经掺杂的TiO2与掺杂稀土Y^3 的TiO2均为锐钛和金红石的混合晶型，锐钛和金红石的比例约为3：1；掺杂抑制了TiO2晶粒的生长，使得TiO2粒径明显变小，其颗粒大小为10nm左右。用DRS表征微粒的光吸收能力和光吸收带边移动情况，发现掺杂导致了TiO2光吸收能力增强及吸收带边红移。通过对苯酚的光催化氧化降解研究，发现当Y^3 掺杂量(按质量)为1．5％时，TiO2光催化活性最高，与未掺杂的TiO2相比，其光催化活性提高约20％。     

镍离子掺杂TiO2涂层的制备及亲水性研究

目的 研究不同含量的镍离子掺杂对TiO2纳米涂层亲水性能的影响.方法 采用溶胶-凝胶法制备不同含量Ni2+掺杂TiO2纳米复合溶胶,通过浸渍提拉法在载玻片上成膜,经过热处理后,得到不同含量Ni2+掺杂TiO2复合涂层.通过X射线衍射仪(XRD)、扫描电子显微镜(SEM)、紫外-可见光分光光度计(UV-Vis)、傅里叶变换红外光谱仪(FT-IR)和表面接触角仪,对掺杂不同浓度Ni2+后TiO2的晶型、涂层微观形貌、光吸收性能、结构组成和涂层亲水性等进行表征分析,从而确定最佳Ni2+浓度的复合涂层材料配方.结果 制备的TiO2主要由锐钛矿相和少量金红石相组成,Ni掺杂抑制了锐钛矿相向金红石相的转变.随着Ni含量的增加,TiO2晶粒尺寸逐渐降低.适量掺杂Ni2+制备的TiO2纳米涂层表面形貌光滑,粒子分布致密均匀.掺杂使吸收波长阈值向长波方向偏移,禁带宽度减小,在一定程度上提高了TiO2涂层的亲水性.当Ni2+掺杂质量分数为1.5％时,TiO2涂层亲水性最佳.结论 采用溶胶-凝胶法实现了镍离子掺杂TiO2的改性,掺杂Ni2+后,Ni2+/TiO2复合涂层的亲水性能明显提高.     

TiO_2-SiO_2复合薄膜的常温制备及其性能

采用溶胶-凝胶法合成具有锐钛矿型TiO2晶粒的TiO2-SiO2复合溶胶,通过浸渍提拉工艺常温制备TiO2-SiO2复合薄膜。考察正硅酸乙酯(TEOS)用量对薄膜结构及性能的影响。结果表明:随着TEOS用量的增加,溶胶的稳定性降低,薄膜的透光率及光催化活性先增大后减小。在Si:Ti摩尔比为1:8时,复合溶胶与薄膜的综合性能达到最优;与单一TiO2溶胶相比,TiO2-SiO2复合溶胶的平均粒度从44增大到75nm;与单一TiO2薄膜相比,TiO2-SiO2复合薄膜的表面粗糙度增大,对罗丹明B的分解率从46.1%提高到67.0%,对水接触角由16°下降到3°,透光率显著增强。     

Photocatalysis Performance of Nb-doped TiO2 Film in Situ Growth Prepared by a Micro Plasma Method

采用微等离子体氧化法,在H2SO4溶液为电解液中以钛合金为基体制备原位生长的TiO2薄膜,并以罗丹明B溶液为目标污染物测试其光催化性能。为提高所得TiO2薄膜的光催化性能,向电解液中添加了不同浓度的草酸铌,制备了原位Nb掺杂TiO2薄膜。利用扫描电镜(SEM)和X射线衍射仪(XRD)分别对Nb掺杂前后的TiO2薄膜表面形貌、元素组成和晶体结构进行了分析。结果表明,Nb掺杂能使介孔TiO2晶粒细化,比表面积增大,Nb对TiO2晶相组成影响不大,但对晶胞参数有所影响,Nb掺杂可有效提高TiO2的光催化活性,其中当草酸铌为1.2g/L时,对初始浓度为10 mg/L罗丹明B溶液90min的降解率可达到85%,表现出最强的光降解能力。