Functionalized carbon nanotube/polyacrylonitrile composite nanofibers: fabrication and properties

The functionalized multi‐walled carbon nanotubes (f‐MWCNTs) were obtained by Friedel–Crafts acylation, which introduced aromatic amine groups onto the sidewall. And the grafted yield was adjusted by controlling the concentration of the catalyst. The composite solutions containing f‐MWCNTs and polyacrylonitrile (PAN) were then prepared by in‐situ or ex‐situ solution polymerization. The resulting solutions were electrospun into composite nanofibers. In the in‐situ polymerization, morphological observation revealed that f‐MWCNTs was uniformly dispersed along the axes of the nanofibers and increased interfacial adhesion between f‐MWCNTs and PAN. Furthermore, two kinds of f‐MWCNTs/PAN composite nanofibers had a higher degree of crystallization and a larger crystal size than PAN nanofibers had, so the specific tensile strengths and modulus of the composite nanofibers were enhanced. And the thermal stability of f‐MWCNTs/PAN from in‐situ method was higher than that of ex‐situ system. When the f‐MWCNTs content was less than 1 wt%, the specific tensile strengths and modulus of nanofibers were enhanced with increase in the amounts of f‐MWCNTs, and f‐MWCNTs/PAN of in‐situ system provided better mechanical properties than that of ex‐situ system. Copyright © 2010 John Wiley & Sons, Ltd.     

Preparation and characterization of CNTs/PE micro‐nanofibers

Multiwalled carbon nanotubes (CNTs)/polyethylene micro‐nanofibers with content ranging from 0.5 to 10 wt% of CNTs were prepared for the first time by melt extrusion of immiscible blends with cellulose acetate butyrate (CAB) and subsequent removal of CAB matrix. The morphology development of dispersed phase was studied with samples collected at different zones in a twin‐screw extruder. The morphology of the CNTs in PE was found to be in forms of both individual and agglomerations. The average diameters of CNTs/PE nanofibers increased with increasing the CNTs content. The electrical conductivity of CNTs/PE nanofibers was studied and a percolation threshold of about 4 wt% was obtained. In addition, the crystalline structures of the CNTs/PE nanofibers were analyzed, indicating a decrease in the crystallinity with the addition of CNTs. The thermal properties of composite fibrils were also modified. This paper demonstrates a good approach for the preparation of CNTs/TP nanofibers by in situ microfibrillar formation. Copyright © 2011 John Wiley & Sons, Ltd.     

Microstructural evolution and mechanical investigation of hot stretched graphene oxide reinforced polyacrylonitrile nanofiber yarns

To reveal the enhancement effect of graphene oxide (GO) in polymer nanofiber yarns, polyacrylonitrile (PAN)/GO nanofibers with different GO content (0.1‐0.5 wt%) were electrospun. The alignment of PAN chains and GO in nanofibers was enhanced by hot stretching of the yarn in dry conditions. The microstructure of the composite nanofiber yarns was investigated through X‐ray diffraction, polarized Fourier transform infrared spectroscopy and transmission electron microscopy. The results demonstrated that the hot stretching above T_g of PAN precursor lead to the increased orientation‐induced crystallization and alignment of PAN chain and GO. The yarn with 0.1 wt% GO and stretched by 4 times its length obtained the highest strength and modules (310.88 ± 24.68 MPa and 7.24 ± 0.55 GPa), which were 600% and 500% higher than those of the as‐electrospun pure PAN yarn. The most promising tensile properties found in hot stretched yarns with low GO content was because the strong interaction occurred between PAN molecules and oxygen‐containing functional groups. Indirect evidence of GO aggregation was also presented, which adversely affected the mechanical properties at higher GO content. Composite nanofiber yarns were sewable and weavable, and could be used as a new generation of composite reinforcement after pyrolysis.     

Preparation of porous ultrafine polyacrylonitrile (PAN) fibers by electrospinning

A facile method for the preparation of porous ultrafine nanofibers was demonstrated. The PAN/NaHCO₃ composite nanofibers were electrospun, and then NaHCO₃ was removed by a selective dissolution and reaction with the solution of hydrochloric acid (10 wt%). The obtained PAN fibers showed highly porous surfaces after the extraction of NaHCO₃. The structure and properties of ultrafine PAN nanofibers were characterized by Fourier transform infrared (FT‐IR), X‐ray diffraction (XRD), and thermogravimetry (TG). The results indicated that NaHCO₃ could be introduced into the PAN solution and successfully electrospun. CO₂ is released and pores are formed on the fibers. The morphology image of the fibers was detected by scanning electron microscope (SEM) and showed that many pores aligned the nanofibers. Copyright © 2008 John Wiley & Sons, Ltd.     

静电纺丝法制备聚丙烯腈/聚苯胺复合纳米纤维及其表征

利用静电纺丝技术,以聚丙烯腈(PAN)和苯胺(ANI)为前驱物,用过硫酸胺(APS)溶液在低温下缓慢氧化聚合,制备了PAN/PANI复合纳米纤维,直径约500 nm.通过扫描电子显微镜(SEM)、红外光谱(FTIR)、X射线衍射(XRD)和激光拉曼(RAMAN)光谱仪等测试手段对材料的形貌和结构进行了表征.探讨了材料制备过程中影响纤维形貌、尺寸、均匀度的因素和PANI含量对复合纤维导电性能的影响,结果表明,PAN浓度、ANI的加入量和电压是影响纤维特性的主要因素;PANI在PAN基体中呈纳米尺寸分布,复合纳米纤维具有良好的导电性能,导电率可达10-2S/cm.     

Carbonization of electrospun poly(acrylonitrile) nanofibers containing multiwalled carbon nanotubes observed by transmission electron microscope with in situ heating

Composite nanofibers with 5% w/w multiwalled carbon nanotubes (MWCNTs) in polyacrylonitrile (PAN) were fabricated using the electrospinning technique. Morphological development during the carbonization process was characterized by transmission electron microscopy (TEM) with in situ heating. It was found that the orientation of graphitic layers increases with temperature and does not change significantly with time during our TEM measurement, except the 750 °C. In the heating stage at 750 °C noticeable enhancement of orientation with time was observed. The presence of embedded CNTs enhances the order of the formed graphitic structures even when the CNTs are irregular or entangled. The results indicate that embedded MWCNTs in the PAN nanofibers nucleate the growth of carbon crystals during PAN carbonization. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Preparation and Characterization of Polypyrrole/TiO2 Coaxial Nanocables

Summary: We demonstrate in this communication that large‐scale coaxial nanocables of polypyrrole (PPy)/TiO₂ can be obtained via three steps: (1) synthesis of TiO₂ nanofibers by electrospinning; (2) physical adsorption Fe³⁺ oxidant on the surface of TiO₂ nanofibers; (3) followed by polymerization of pyrrole (from vapor) on the surface of TiO₂ nanofibers. During the synthesis, the PPy formed on TiO₂ nanofibers as a template and formed PPy/TiO₂ coaxial nanocables. TEM image proved that PPy (20 nm thickness) covered the surface of TiO₂ nanofibers. Fourier‐transform infrared (FTIR), X‐ray photoelectron spectra (XPS), and X‐ray diffraction patterns (XRD) characterized the chemical structure of the coaxial nanocables. Surface photovoltage spectroscopy (SPS) revealed the surface properties of the PPy/TiO₂ coaxial nanocables.

TEM image of individual PPy/TiO₂ coaxial nanocable.     

Synthesis of polypyrrole micro/nanofibers via a self-assembly process

Novel polypyrrole (PPy) micro/nanofibers were synthesized via a self-assembly process by using 4-hydroxy-3-[(4-sulfo-1-naphthalenyl) azo]-1-naphthalenesulfonic acid (Acid Red B) as dopant and ferric chloride (FeCl₃) as oxidant. Experimental conditions, including the concentration of the dopant, reaction temperature and stirring state have been investigated for their influences on the morphology of the synthesized PPy micro/nanofibers. The products were characterized by scanning electron microscopy, transmission electron microscopy and Fourier-transform infrared spectroscopy. The formation mechanism of micro/nanofibers was studied. It is believed that the micelles formed by the dopant and pyrrole monomer act as templates during the synthesis process. Two functions of aggregation and synthesis are proposed in the reaction system simultaneously, and the morphologies of micro/nanofibers are the co-operations of these two functions. The maximum conductivity value of the PPy micro/nanofibers was 8.56 S cm^?1     

Electropolymerized composite film of polypyrrole and functionalized multi-walled carbon nanotubes: effect of functionalization time on capacitive performance

The composite film of polypyrrole and functionalized multi-walled carbon nanotubes (PPy/F-MWNTs) was prepared by electropolymerization. MWNTs were functionalized by sonicating with a concentrated solution of H₂SO₄/HNO₃ (3/1, volume ratio) in a water bath for different times. The carbon nanotubes (CNTs) are cut into smaller portions with more functional groups introduced on their surface when the sonicating time (nominated as functionalization time hereafter) is increased. However, the specific capacitance of the composite film reaches a maximum of 240 F g⁻¹ at the scanning rate of 10 mV s⁻¹ when MWNTs are functionalized for 24 h, which is about 205 F g⁻¹, 225 F g⁻¹ and 232 F g⁻¹, respectively, when MWNTs are functionalized for 6 h, 12 h and 48 h. At a current load of 1.0 A g⁻¹, PPy/F-MWNT composite film functionalized for 24 h (PPy/F-MWNTs (24 h)) retains 93.49% of its initial capacitance after 1,000 cycles of galvanostatic charge/discharge, and the discharge efficiency is higher than 98.15% during cycling. High specific capacitance, good rate performance, fast charge/discharge ability and long cycling life are ascribed to the synergistic effect of the two components to form a porous composite film as well as the easy accessibility of counter ions into the film. Therefore, PPy/F-MWNT (24 h) composite film is a kind of promising electrode material for supercapacitors. The mechanism of underfunctionalization and overfunctionalization of carbon nanotubes is also discussed.     

A Simple Method for the Preparation of TiO2/Ag‐AgCl@Polypyrrole Composite and Its Enhanced Visible‐Light Photocatalytic Activity

A novel and facile method was developed to prepare a visible‐light driven TiO₂/Ag‐AgCl@polypyrrole (PPy) photocatalyst with Ag‐AgCl nanoparticles supported on TiO₂ nanofibers and covered by a thin PPy shell. During the synthesis, the PPy shell and Ag‐AgCl nanoparticles were prepared simultaneously onto TiO₂ nanofibers, which simplified the preparation procedure. In addition, because Ag‐AgCl aggregates were fabricated via partly etching the Ag nanoparticles, their size was well controlled at the nanoscale, which was beneficial for improvement of the contact surface area. Compared with reference photocatalysts, the TiO₂/Ag‐AgCl@PPy composite exhibited an enhanced photodegradation activity towards rhodamine B under visible‐light irradiation. The superior photocatalytic property originated from synergistic effects between TiO₂ nanofibers, Ag‐AgCl nanoparticles and the PPy shell. Furthermore, the TiO₂/Ag‐AgCl@PPy composite could be easily separated and recycled without obvious reduction in activity.     

Morphology,rheological and crystallization behavior in non-covalently functionalized carbon nanotube reinforced poly(butylene succinate) nanocomposites with low percolation threshold

Multi-walled carbon nanotubes (CNTs) were non-covalently functionalized by surface wrapping of poly(sodium 4-styrenesulfonate) (PSS) with the aid of ultrasound. The functionalized CNTs were incorporated into poly(butylene succinate) (PBS) through solution coagulation to fabricate CNTs filled PBS nanocomposites. The morphologies of the PBS/CNT nanocomposites were studied by scanning electron microscope (SEM) and transmission electron microscope (TEM), and the effect of loading of functionalized CNT on the rheological behavior, electrical conductivity and mechanical properties of the nanocomposites was investigated systemically. SEM observation indicates that functionalized CNTs dispersed in PBS matrix without obvious aggregation and showed good interfacial adhesion with the PBS phase. TEM observation reveals that a CNT network was formed when the loading of CNTs increased from 0.1 to 0.3 wt%. Rheological investigation indicates the formation of a CNT network with a percolation threshold of only 0.3 wt%. Significant improvement in electrical conductivity occurred at CNT loading of 0.3 wt%, with the value of electrical conductivity increasing by six orders of magnitude compared to neat PBS. Differential scanning calorimetry indicates that the melt crystallization temperature of PBS was improved by ∼14 °C with addition of only 0.05 wt% functionalized CNTs. Tensile tests indicate that both the yield strength and Young's modulus of PBS were apparently reinforced by incorporation of functionalized CNTs, while the elongation at break was reduced gradually.     

Surface initiated ring-opening polymerization of l-proline N-carboxy anhydride from single and multi walled carbon nanotubes

Ring-opening surface initiated polymerization of l-proline N-carboxyanhydride was performed from amine functionalized single (SWNTs) and multi walled carbon nanotubes (MWNTs). The primary amines were grafted on the surfaces via a well-studied Diels–Alder cycloaddition. The initiator attachment helped the debundling of carbon nanotubes as shown by atomic force microscopy (AFM) studies where only small aggregates were observed. Thermogravimetric analysis revealed high wt% of grafted polyproline on the carbon nanotubes surface after the ring-opening polymerization. AFM studies showed a rather uniform layer of grafted polyproline from both MWNTs and SWNTs. The grafting of PLP on the surface was also verified by FTIR and Raman spectroscopy as well as ¹H NMR in CDCl₃/d-TFA. The polyproline grafted carbon nanotubes (CNTs) were readily dissolved in organic solvents in contrast to the insoluble pristine and amine-functionalized CNTs.     

Nanocomposites based on vapor-grown carbon nanofibers and an epoxy: Functionalization, preparation and characterization

Vapor-grown carbon nanofibers (VGCNF) were functionalized with amine-containing pendants via a Friedel-Crafts acylation reaction with 4-(3-aminophenoxy)benzoic acid. The resulting H₂N-VGCNF was treated with epichlorohydrin, followed by sodium hydroxide solution to afford N,N-diglycidyl-modified VGCNF that is designated as epoxy-VGCNF. Subsequently, epoxy-VGCNF was dispersed in an epoxy resin (Epon 862) with the aid of acetone and sonication. After acetone had been removed under vacuum from the mixture, curing agent “W” was added to epoxy-VGCNF/Epon 862 mixture, which was then poured into molds and cured at 250 °F (121 °C) for 2 h and 350 °F (177 °C) for 2 h to form a series of epoxy/fVGCNF samples; fVGCNF designated for “functionalized VGCNF” was used to denote our belief that all epoxy functions have reacted in the resulting nanocomposites. The VGCNF content was increased from 0.10 to 10.0 wt%. For comparison purposes, the pristine VGCNF or pVGCNF (0.1-5.0 wt%) was also used in the in situ polymerization of Epon 862 and curing agent “W” to afford another series of epoxy/pVGCNF samples. The epoxy-VGCNF showed a better dispersion in the epoxy resin than pVGCNF according to SEM results. Both the tensile moduli and strengths of epoxy/fVGCNF nanocomposites are higher than those of epoxy/pVGCNF. The additive effect of VGCNF on glass-transition (T_g) was discussed in terms of thermal analysis results. The thermal stability of the nanocomposites was investigated by thermogravimetric analysis (TGA).     

A novel and convenient preparation of antibacterial polyacrylonitrile nanofibers via post-modification using nitrile click chemistry and electrospinning

An efficient, novel and convenient method for the synthesis of modified polyacrylonitrile (PAN) with antibacterial property is reported. The modification of PAN was prepared by a nitrile click chemistry reaction with sodium azide (NaN₃) and silver nitrate (AgNO₃) as catalyst to yield antibacterial polymeric materials with 5-vinyltetrazole units. The results showed that 5-vinyltetrazole units had coordinated with silver ion (Ag⁺). Through the electrostatic spinning technology, the post-modification PAN nanofibers (PAN–Ag⁺ nanofibers) were prepared and the fibers were tested for their antimicrobial properties by the bacterial infection experiment. Afterwards, the antibacterial and stable performance of different proportions of silver ions in PAN nanofibers has been compared. The PAN–Ag⁺ nanofibers are characterized for mechanical and thermomechanical properties, structural analysis, appearance characteristics, as well as the antibacterial properties. And the nanofibers exhibit marvelous chemical stability according to the thermogravimetric analysis. When at 800 °C, the PAN decomposed about 60%, while the decomposition of the PAN–Ag⁺s was 40%. Based on the bacterial infection experiment, PAN–Ag⁺ nanofibers’ antibacterial properties were stronger with the increase of silver ions, such as the number of bacteria clone was smaller and the bacteriostatic ring was larger. Hence, with combination of silver ions, the final polymers show strong antimicrobial properties.     

Synthesis and characterization of polypyrrole nanofibers with different dopants

Nanostructures of polypyrrole (PPy) were synthesized in the presence of different dopants including hydrochloric acid (HCl), ferric chloride (FeCl₃), p‐toluene sulfonic acid (p‐TSA), camphor sulfonic acid (CSA), and polystyrene sulfonic acid (PSSA), using a simple interfacial oxidative polymerization method. The method is a reliable non‐template approach with relatively simple instrumentation, ease of synthesis, and economic viability for synthesizing PPy nanostructures. Morphology of synthesized PPy structures was investigated using scanning electron microscopy (SEM) and transmission electron microscopy (TEM), which indicate the formation of one‐dimensional (1D) nanofibers with average diameter of 75–180 nm. Energy dispersive spectrum (EDS) of the PPy nanofibers indicates the attachment of the dopants to the PPy backbone; the fact is further confirmed by the Fourier transform infrared (FTIR) spectra of PPy nanostructures. Thermal stabilities of the nanostructures explored using thermal gravimetric analysis (TGA) follow the order PPy‐p‐TSA > CSA > HCl > FeCl₃ > PSSA. It is noticed that the electrical conductivity (EC) of PPy nanostructures depends upon the nature of dopant (PPy‐p‐TSA > CSA > HCl > FeCl₃ > PSSA), PPy‐p‐TSA nanofibers showing the highest EC of 6 × 10^?2 Scm^?1. Copyright © 2009 John Wiley & Sons, Ltd.     

Oxidation of a PPy-modified tantalum electrode

A tantalum electrode on which polypyrrole (PPy) had been previously formed by electropolymerization was galvanostatically electrolyzed in an aqueous solution of 0.01 wt% phosphoric acid. This process contains the irreversible oxidation of a PPy film, the decomposition of solvent, and the formation of Ta₂O₅ by the reaction of OH^? coming through the PPy film, with Ta electrodes. A three layer-structure (PPy/Ta₂O₅/Ta) was confirmed by electron spectroscopy for chemical analysis (ESCA). A PPy film containing CIO₄^? as dopant [PPy(CIO₄^?)] was significantly deteriorated in comparison with PPy(TsO^?) at the electrolysis. Therefore, the (PPy(TsO^?)/Ta₂O₅/Ta) system showed better electrical characteristics as a capacitor than the (PPy(CIO₄^?)/Ta₂O₅/Ta) system showed better electrical characteristics as a capacitor than the (PPy(ClO₄^?)/Ta₂O₅/Ta) system.     

Fabrication of Electrically Conducting Polypyrrole‐Poly(ethylene oxide) Composite Nanofibers

Summary: Electrically conducting polypyrrole‐poly(ethylene oxide) (PPy‐PEO) composite nanofibers are fabricated via a two‐step process. First, FeCl₃‐containing PEO nanofibers are produced by electrospinning. Second, the PEO‐FeCl₃ electrospun fibers are exposed to pyrrole vapor for the synthesis of polypyrrole. The vapor phase polymerization occurs through the diffusion of pyrrole monomer into the nanofibers. The collected non‐woven fiber mat is composed of 96 ± 30 nm diameter PPy‐PEO nanofibers. FT‐IR, XPS, and conductivity measurements confirm polypyrrole synthesis in the nanofiber.

An SEM image of the PPy‐PEO composite nanofibers. The scale bar in the image is 500 nm.     

Preparation of amidoxime-modified polyacrylonitrile (PAN-oxime) nanofibers and their applications to metal ions adsorption

Polyacrylonitrile (PAN) nanofibers were applied to metal adsorption. PAN nanofibers (prepared by an electrospinning technique) were chemically modified with amidoxime groups, which are suitable for metal adsorption due to their high adsorption affinity for metal ions. The adsorption of the amidoxime-modified PAN (PAN-oxime) (25% conversion) nanofibers followed Langmuir isotherm. The saturation adsorption capacities for Cu(II) and Pb(II) of 52.70 and 263.45 mg/g (0.83 and 1.27 mmol/g), respectively, indicating that the monolayer adsorption occurred on the nanofiber mats. In addition, over 90% of metals were recovered from the metal-loaded PAN-oxime nanofibers in a 1 mol/L HNO₃ solution after 1 h.     

Water effect on the gelation behavior of polyacrylonitrile/dimethyl sulfoxide solution

The gelation behavior of polyacrylonitrile (PAN)/dimethyl sulfoxide (DMSO) solution containing different amounts of water has been investigated using various methods. The ternary phase diagram of PAN/DMSO/water system indicated that water enhanced the temperature at which phase separation of PAN/DMSO solution occurred. Intrinsic viscosities [η] of dilute PAN/DMSO solution and PAN/DMSO/water solution at varied temperatures were measured to examine the influence of water on the phase behavior of PAN/DMSO solution. The presence of water in the solution gave rise to elevated critical temperature T_c. The gelation temperature T_g obtained by measuring the loss tangent tan δ at different oscillation frequencies in a cooling process was found to increase with increased water content in the solution. The critical relaxation exponent n value, however, changed little with varied concentration. During the aging process, the gelation rate of PAN/DMSO solution increases with the water level. The n values of the PAN/DMSO solutions with 2 wt% and 4 wt% water were a little larger than that of the solution without water, which may be explained by the turbid gel resulted from phase separation. The n values obtained in the aging process were larger than those obtained in the cooling process for the same three solutions, ascribed to the weaker gel with less cross-linking points formed in long time. Water led to the formation of denser gel structure. The coarser gel surface can also be attributed to the phase separation promoted by water.     

NiSe2 nanoparticles encapsulated in CNTs covered and N-doped TiN/carbon nanofibers as a binder-free anode for advanced sodium-ion batteries

Metal selenides are promising anodes for sodium-ion batteries (SIBs) due to the high theoretical capacity through conversion reaction mechanism. However, developing metal selenides with superior electrochemical sodium-ion storage performance is still a great challenge. In this work, a novel composite material of free-standing NiSe₂ nanoparticles encapsulated in N-doped TiN/carbon composite nanofibers with carbon nanotubes (CNTs) in-situ grown on the surface (NiSe₂@N-TCF/CNTs) is prepared by electrospinning and pyrolysis technique. In this composite materials, NiSe₂ nanoparticles on the surface of carbon nanofibers were encapsulated into CNTs, thus avoiding aggregation. The in-situ grown CNTs not only improve the conductivity but also act as a buffer to accommodate the volume expansion. TiN inside the nanofibers further enhances the conductivity and structural stability of carbon-based nanofibers. When directly used as anode for SIBs, the NiSe₂@N-TCF/CNT electrode delivered a reversible capacity of 392.1 mAh/g after 1000 cycles and still maintained 334.4 mAh/g even at a high rate of 2 A/g. The excellent sodium-ion storage performance can be attributed to the fast Na⁺ diffusion and transfer rate and the pseudocapacitance dominated charge storage mechanism, as is evidenced by kinetic analysis. The work provides a novel approach to the fabrication of high-performance anode materials for other batteries.