Tb/Eu 共掺锌硼磷酸盐白光发光玻璃的制备及其发光性能

采用熔体冷却法,通过控制玻璃基质组成及稀土离子添加量,制备了Tb、Eu单掺和Tb/Eu共掺的锌硼磷酸盐低熔点发光玻璃。测试了样品的红外光谱、吸收光谱、激发与发射光谱和荧光寿命,并计算CIE色坐标,研究了材料的微观结构及发光性能。结果表明：样品中部分Eu³⁺被还原为Eu²⁺,在380 nm波长激发下,Tb/Eu共掺发光玻璃同时出现Eu³⁺红光、Tb³⁺绿光和Eu²⁺蓝光的特征发射。增加基体中B₂O₃含量能强化玻璃网络结构,并改变Eu²⁺/Eu³⁺比例。发射光谱和荧光寿命测试表明,共掺的发光玻璃中存在Eu²⁺→Eu³⁺,Eu²⁺→Tb³⁺和Tb³⁺→Eu³⁺的能量传递。改变Tb、Eu的掺杂浓度能够有效改变发光玻璃的发光强度和颜色,最终得到色坐标为（0.318 7,0.286 1）、色温6 480 K的发光玻璃。     

大气环境下合成白光发射的Tb3+/Eu3+共掺杂全无机卤化物钙钛矿量子点

为克服因混合不同卤化物钙钛矿量子点发生阴离子交换反应、不稳定的红光发射卤化物钙钛矿量子点等而导致在获取白光发射方面存在的不足,提出了一种可以在大气环境下合成Tb³⁺,Eu³⁺稀土离子共掺杂全无机卤化物钙钛矿量子点的方法。调节Tb³⁺,Eu³⁺稀土离子的掺杂比例,调控从钙钛矿量子点主晶格到Tb³⁺和Eu³⁺离子的能量转移,获得了单一组分、白光发射的钙钛矿量子点(Tb,Eu):CsPbCl3和(Tb,Eu):CsPb(Cl/Br)3,并对量子点的形貌、结构、发光性能及能量传递机理和稳定性进行了详细研究。研究结果表明:在365nm激光激发下,不同含量Tb³⁺/Eu³⁺离子共掺杂的钙钛矿量子点(Tb,Eu):CsPbCl3发射光谱对应的色坐标位于1931色度图中的白光区域。在进料比PbCl2∶TbCl3∶EuCl3为1∶1.5∶1时,量子产率为3.59%,比纯的CsPbCl3量子点的量子产率(0.57%)提高了6倍。进一步研究发现,该(Tb,Eu):CsPbCl3量子点在空气中储存2个月之后,量子产率几乎保持不变(3.63%),保持了良好的稳定性。此外,研究了采用不同溶剂(正辛烷、十八烯)合成Tb³⁺/Eu³⁺共掺杂钙钛矿量子点的发光特性。Tb³⁺/Eu³⁺离子共掺杂的钙钛矿量子点(Tb,Eu):CsPbCl3可实现单一组分的白光发射,有良好的稳定性,具备一定的应用前景。     

Eu2+/Dy3+共掺SrSiO3透明微晶玻璃的光学性质

在还原气氛中采用高温熔融法制备了Eu2+-Dy3+共掺硅酸盐玻璃,热处理后得到了Eu2+-Dy3+共掺透明SrSiO3微晶玻璃。测试了样品的激发光谱和发射光谱,研究了不同Eu2+-Dy3+物质的量比下微晶玻璃发光的变化并计算了对应的色坐标。研究发现,样品发射光谱范围在400～600nm,其中400～550nm(绿光)的宽发射谱带来自Eu2+的5d→4f跃迁,而位于483nm(蓝光)和575nm(黄光)的尖峰则来自Dy3+的4F9/2→6 H15/2和4F9/2→6 H13/2跃迁;在紫外(UV)光(365nm)激发下通过调控Eu2+-Dy3+物质的量比可得到发白光的微晶玻璃,当Eu2+-Dy3+物质的量比为1∶8时,Eu2+-Dy3+共掺SrSiO3透明微晶玻璃所发白光最佳,对应的色坐标(0.268,0.356)位于CIE标准色坐标图的白光区域且最接近理想白光。结果表明,Eu2+-Dy3+共掺SrSiO3透明微晶玻璃可作为一种潜在的白光发光二极管用基质材料。     

硼酸盐玻璃中Eu掺杂对Ag纳米颗粒的析出机制及其发光性质研究

采用高温熔融法制备了Eu-Ag共掺的硼酸盐玻璃,利用吸收光谱和发射光谱等研究了玻璃中网络形成体B₂O₃含量变化和Eu离子共掺对于Ag在基质中赋存状态的影响。在Eu-Ag共掺玻璃的吸收光谱中发现,随着B₂O₃含量的增加,Ag纳米颗粒在4 10 nm附近的宽带吸收强度逐渐下降;玻璃在340 nm光源激发下,位于350～600 nm的蓝绿光区出现一个Ag分子团簇的宽带发光,且其发光强度随B₂O₃含量的增加逐渐增强。在Eu或Ag单掺的玻璃中可分别观测到微弱的Eu3+或Ag分子团簇的本征发射,而Eu-Ag共掺样品中Eu3+和Ag分子团簇的发光都得到了显著的增强。并且Eu离子浓度的增加促进了Ag纳米颗粒在410 nm附近的宽带吸收。对Eu离子的添加促进Ag纳米颗粒析出的机理进行了讨论。同时,由于Eu3+的5D₀→7F_J的电子跃迁发射为橙红光,Ag纳米团簇可发射蓝绿光甚至黄光,因此通过玻璃结构的调控和Eu离子掺杂浓度的调节可以实现玻璃的白光发射,这有望成为潜在的白光LED用玻璃照明材料。     

Eu2+掺杂CaSi2O2N2荧光粉发光性能

采用固相反应法合成了组成为Ca_1-xEu_xSi₂O₂N₂的Eu²⁺掺杂CaSi₂O₂N₂荧光粉.通过荧光光谱对样品的发光性能进行了研究,发现Eu²⁺掺杂CaSi₂O₂N₂荧光粉发射光谱为宽波段的单峰结构,主要包含绿光和黄光区,发射峰在556~568 nm.从发射光谱的宽带特征来看,CaSi₂O₂N₂:Eu²⁺的发射主要对应着Eu²⁺离子4f⁶5d→4f⁷跃迁.从激发光谱所覆盖的范围还可以看到,样品可以有效的被UV蓝-光激发,这意味着该类荧光粉在白光LED方面有可能得到广泛的应用.另外,样品的发光性能与激发离子的浓度有着很大关系.激发离子浓度增大时,发射光谱会发生明显红移.利用这一性质,可以通过改变Eu²⁺浓度来调节荧光粉的发光范围,从而满足不同场合的需要.同时,Eu²⁺浓度提高,样品发射光谱的强度也会随之增强,在x=0.06时发射强度达到最大值,之后继续增加Eu²⁺浓度,强度不仅没有增加反而降低,即出现浓度猝灭现象.     

一种新型红色荧光粉CaAl12O19： Eu,Mn的制备及发光性能

固相法制备了碱土金属铝酸盐荧光粉CaAl₁₂O₁₉ : Eu,Mn,测试了样品的XRD及激发与发射光谱,对样品的结构及其发光性能进行了分析,并且考察了灼烧温度及Eu³⁺的浓度对样品发光性能的影响,对Eu³⁺的作用机理进行了探讨。 该荧光粉能被波长短于550 nm的蓝绿光以及紫外和近紫外光激发,其发射光谱峰值在590,615,645,657 nm,其中前两个为Eu³⁺的特征发射,后两个为Mn⁴⁺的²E-⁴ A₂跃迁发射。该荧光粉的最佳烧结温度与时间分别为1 550 ℃和4 h,Eu³⁺的最佳掺杂摩尔分数为0.11%左右。     

稀土离子掺杂LaAlO3:RE3+(RE=Eu,Tb,Sm,Tm)荧光粉的发光性能

采用溶胶凝胶法合成La_1-xAlO₃：xRE³⁺（RE=Eu,Tb,Sm,Tm）荧光粉,对样品进行热重差热（TGA-DTA）、X射线粉末衍射（XRD）、透射电镜（TEM）以及荧光光谱（PL）等表征,探讨样品的合成温度及稀土离子掺杂浓度对样品发光性能的影响。研究结果表明,当煅烧温度为800~1 200℃时,所合成样品为三方晶体结构。在紫外光激发下,掺杂离子均表现出特征的f-f电子跃迁发射,在一定掺杂浓度范围内,当Eu³⁺、Tb³⁺、Sm³⁺和Tm³⁺的掺杂浓度x值分别为0.02,0.04,0.005和0.005时,样品发光强度最大,在一定波长激发下,样品分别发射出红光、绿光、橙黄光和蓝光,Eu³⁺-Tb³⁺、Eu³⁺-Sm³⁺和Eu³⁺-Tm³⁺共掺杂有可能获得白光。     

应用于白光显示的Tm3+/Ho3+/Yb3+共掺碲酸盐玻璃上转换发光特性研究

用高温熔融法制备了Tm³⁺/Ho³⁺/Yb³⁺共掺碲酸盐玻璃(TeO₂-ZnO-La₂O₃)样品,测试了玻璃样品的吸收光谱和上转换发光光谱,分析了上转换发光机理.结果发现:在975 nm波长激光二极管(LD)激励下,制备的碲酸盐玻璃样品可以观察到强烈的红光(662 nm)、绿光(546 nm)和蓝光(480 nm)三基色上转换发光,红光对应于Tm³⁺离子 关键词： 碲酸盐玻璃 上转换发光 白光 3+/Ho³⁺/Yb³⁺共掺')" href="#">Tm³⁺/Ho³⁺/Yb³⁺共掺     

Eu掺杂GaN薄膜的阴极荧光特性

通过MOCVD方法在蓝宝石衬底上生长GaN薄膜,利用离子注入方法将Eu³⁺离子注入到GaN基质中。X射线衍射结果表明：经过退火处理后,修复了部分离子注入所导致的晶格损伤。利用阴极荧光光谱可得到GaN∶Eu³⁺材料在623 nm处有很强的红光发射,该发射峰来源于Eu³⁺离子的内部4f能级跃迁。另外,Eu³⁺离子注入会在样品中引入电荷转移态,产生408 nm附近的发光。退火处理有助于获得更强的电荷转移态发光和Eu离子特征发光。GaN基质的黄光峰与Eu离子之间存在能量交换,将能量传递给Eu离子,促进Eu离子发光。     

Eu掺杂的高Gd玻璃荧光及闪烁发光性能研究

分别在空气和还原气氛下,采用高温熔融法制备了Eu 掺杂(1 wt%) 的15SiO₂-25B₂O₃-30Al₂O₃-30Gd₂O₃ 氧化物玻璃,对二者的光致发光和闪烁发光性能进行测试. 结果显示：还原气氛下制得的玻璃在395 nm 紫光和X 射线激发下,均可以得到450–550 nm 的Eu²⁺ 蓝绿发光和615 nm 的Eu³⁺ 红光;然而在不同的激发光源下,Eu²⁺ 和Eu³⁺发光强度比存在明显不同,395 nm 紫光激发下,Eu³⁺ 发光强度仅为Eu²⁺ 的0.02 倍,X 射线激发下,Eu³⁺ 发光强度变为Eu²⁺ 强度的1.37 倍. 通过声子边带谱分析,还原后玻璃中Si 形成体附近的Eu³⁺ 全部被还原为Eu²⁺,B 和Al形成体周围的Eu³⁺ 部分被还原为Eu²⁺. 进一步分析闪烁发光的机理表明：Gd 的敏化剂作用以及B 和Al 形成体周围Eu²⁺→Eu³⁺ 的能量传递都增强了还原玻璃中Eu³⁺ 的闪烁发光性能. 关键词： 高Gd玻璃 2+')" href="#">Eu²⁺ 闪烁发光 声子边带谱     

LUMINESCENCE OF Bi3+ and Eu2+ DOUBLE CENTERS DOPED IN CaS HOST

In this work, double-center.doped luminescent material CaS:Bi³⁺, Eu²⁺ was made via flux NH₄Cl by sintering in excess sulfur environment. The sample had a purplish red net luminescent color. Excitation spectra at both red, 650 nm and blue, 487 nrn were taken. The red emission from Eu²⁺ center was mainly come from the 4f⁶5d¹ absorption in the CaS host. The blue emission from the Bi³⁺ center on the other hand showed no big difference from the singly doped CaS:Bi³⁺ materials in excitation spectrum. Emission spectra were obtained at excitaton of 270nm and 300nm. Stokes shift was moved about 20-30nm, under different point excitation. Emission peaks of both Bi³⁺ and Eu²⁺ centers appeared at 463nm, 642.5nm by 270nm excitation and 487 nm, 620 nm by 300 nm excitation respectively. After-glow decay cures were also obtained and the shapes of decay curves are similar and it is due to the single hole-trap system by lattice defects.     

Eu3+掺杂CaWO4红色荧光粉发光性质的浓度依赖关系研究

采用共沉淀法制备了不同Eu³⁺掺杂浓度的CaWO₄荧光粉材料.通过X射线衍射和场发射扫描电镜技术对样品的结构和形貌进行了表征.测量了各样品的激发光谱、发射光谱和荧光衰减曲线, 计算了各样品的部分Judd-Oflet (J-O)参数和^5D_0 (Eu³⁺)能级量子效率,以及荧光粉的色坐标, 讨论了样品电荷迁移带相对强度、J-O参数、量子效率与掺杂浓度的依赖关系.对Eu³⁺掺杂的CaWO₄ 发光材料的光致发光性质的研究表明,在CaWO₄: Eu³⁺中⁵D₀→⁷F₂跃迁的616~nm 红色发光能被394.5~nm和465~nm的激发光有效激发,具有近紫外(或蓝光)激发效率高和猝灭浓度大的优点, 有潜力成为高效的近紫外(或蓝光)激发白光发光二极管用红色荧光粉材料.     

稀土离子(Eu3+,Tb3+,Ce3+)掺杂ZnAl2O4/SiO2微晶玻璃的制备与发光性能

采用凝胶法分别制备出4.5ZnO-5.5Al₂O₃-90SiO₂(ZAS)以及ZAS[DK]:RE³⁺ (RE=Eu,Tb,Ce) 透明微晶玻璃。利用X射线衍射仪(XRD)、透射电子显微镜(TEM)和荧光光谱仪(PL)等测试手段,研究了稀土离子掺杂浓度对ZAS微晶玻璃的结构和发光性能的影响。XRD结果表明,ZAS[DK]:RE³⁺ (RE=Eu,Tb,Ce)微晶玻璃包含ZnAl₂O₄晶相和SiO₂非晶相,ZnAl₂O₄平均晶粒尺寸约为30 nm,稀土离子的掺杂没有显著改变原来的ZnAl₂O₄晶体结构。TEM结果表明,900 ℃时ZnAl₂O₄从ZAS体系中析出。PL光谱显示,Eu³⁺ 存在 ⁵D₀→⁷F₂跃迁,ZAS[DK]:Eu³⁺在611 nm 处发出强烈的红色光;由于Tb³⁺ 的⁵D₄→⁷F₅ 跃迁,ZAS[DK]:Tb³⁺在541 nm 处发出明亮的绿色光;ZAS[DK]:Ce³⁺ 在381 nm处显示了蓝光发射,对应于Ce³⁺ 的5d→4f 轨道跃迁。ZAS[DK]:RE³⁺ (RE=Eu, Tb, Ce)的PL发射光谱存在着浓度猝灭现象,Eu³⁺、Tb³⁺ 和Ce³⁺的最佳单掺杂摩尔分数分别为20%、20%和3%。CIE色度图表明,ZAS[DK]: RE³⁺ (RE=Eu,Tb,Ce)的色坐标分别位于红光、绿光和蓝光区域。实验结果表明,ZAS:RE³⁺ (RE=Eu,Tb,Ce) 微晶玻璃是一种良好的可用于全色显示的白光LED材料。     

2018年9期电子期刊

采用高温固相法在1 150℃下经二次煅烧合成了双钙钛矿型的红色荧光粉Sr₂ZnTeO₆∶xEu³⁺（x=0.05-0.40）,并进行了相组成、发光性质和热稳定性的研究。结果表明,所合成的Sr₂ZnTeO₆与Sr₂ZnWO₆具有相同的结构,掺杂离子的加入没有改变相结构。样品的激发光谱由电荷迁移带和Eu³⁺离子的特征激发峰组成,主激发峰位于464 nm（⁷F₀→⁵L₆）。样品的发射光谱位于614 nm（⁵D₀→⁷F₂）。Sr₂ZnTeO₆∶xEu³⁺荧光粉的发光强度随着Eu³⁺离子的掺杂,先增大后减小,在x≥0.25时,发生浓度猝灭现象。通过变温荧光发现它具有非常好的热稳定性。由于荧光粉的最佳激发位于464 nm,因而可以用于蓝光激发下的白光LED的红色荧光粉。     

微波场作用下La2O2S：Eu荧光粉的快速合成及其发光特性

采用微波法快速合成了La₂O₂S:Eu红色荧光粉,用X射线粉末衍射(XRD)、扫描电镜(SEM)、荧光光谱等对合成产物进行了分析和表征。结果表明:材料的晶体结构为六方晶系,与纯La₂O₂S的结构相同。颗粒的形状不规则,分散性较好,尺寸在2μm左右。La₂O₂S:Eu的激发光谱主要是位于200~450nm范围内的宽带,此宽带激发来源于Eu³⁺的电荷转移态的吸收跃迁。在472nm左右出现一弱的尖锐的吸收峰,属于Eu³⁺的4f→4f跃迁吸收。发射光谱是由512,539,556,583,596,617,627nm的一系列窄带发射峰组成。这些发射峰归属于Eu³⁺从⁵D_J(J=0,1,2)到⁷F_J(J=0,1,2,3,4)的能级跃迁。随着Eu摩尔分数从2%增加到10%,主激发峰从348nm移动到365nm,移动了17nm;位于蓝绿区的发射峰逐渐减弱,627nm处的红光发射明显增强,当Eu的摩尔分数为8%时发光强度达到最大,继续增加Eu的浓度发光强度反而降低。     

Ba3WO6:Eu3+红色荧光粉的结构及其发光特性

以高温固相法成功合成了一系列Eu³⁺离子激活Ba₃WO₆红色荧光粉。分别采用X射线衍射（XRD）和荧光光谱（FL）对样品的晶体结构和发光性能进行了表征。结果表明,样品均具有立方晶系的双钙钛矿结构;Eu³⁺离子的激发谱由一个宽带（包括Eu³⁺-O^2-和W⁶⁺-O^2-电荷转移带）和若干个窄峰（4f-4f电子跃迁）组成,而跃迁⁵D₀→⁷F₁和⁵D₀→⁷F₂则构成了发射谱的主要部分。调整原材料中BaCO₃和WO₃的量的比,XRD的主衍射峰位发生红移至与标准谱完全吻合,发光强度有所提升并分析了原因。Eu³⁺离子的临界摩尔分数为0.05,临界距离（R_c）为1.263 4 nm。在314 nm或394 nm激发光下,样品发出红光（λ_max=596 nm）,色坐标为（0.618,0.342）,在LED照明、显示等领域具备一定潜力。     

Na4Ca3(AlO2)10∶Eu2+,Mn2+荧光粉的发光特性

采用高温固相法,制得一种新型荧光粉Na₄Ca₃(AlO₂)₁₀∶Eu²⁺,Mn²⁺。样品的结构和发光性质分别由X射线衍射谱和荧光光谱来表征。在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺的激发光谱中出现了Eu²⁺的f-d跃迁吸收带;在发射光谱中,出现蓝光发射,峰值位于441 nm。当在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺中掺杂Mn²⁺时,发生了Eu²⁺→Mn²⁺的能量传递,在542 nm处出现了Mn²⁺的发射峰。在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺,Mn²⁺中,随着Mn²⁺浓度的增加,Eu²⁺粒子的发射强度减弱,而Mn²⁺粒子的发射强度增强,且Eu²⁺离子发射的衰减时间缩短,同时色度由蓝光移向白光。     

纳米SrHPO4：RE（RE=Eu3+或Tb3+）磷光体的水热合成与光谱特性

利用水热法合成了α-SrHPO₄：RE（RE=Eu³⁺,Tb³⁺）纳米磷光体,并研究了材料的形貌与光谱特性。α-SrHPO₄纳米粒子为长度90~200 nm的棒状结构,直径为24~36 nm。Eu³⁺和Tb³⁺的掺杂均会降低α-SrHPO₄的结晶度,并减小其长径比。α-Sr_0.97HPO₄：0.03Eu³⁺在395 nm近紫外光的激发下,存在分别由⁵D₀→⁷F₁和⁵D₀→⁷F₁₂跃迁引起的590 nm和614 nm发射峰,最终发射橙红光。α-Sr_0.97HPO₄：0.03Tb³⁺在217 nm近紫外光的激发下,存在由⁵D₄→⁷F₅跃迁引起的543 nm绿光发射。     

Sm3+掺杂对CaMoO4:Eu3+红色荧光粉结构和发光性质的影响

采用共沉淀法制备了CaMoO4:Eu3,Sm3+纳米荧光粉材料.系统研究了Sm3+离子的引入对CaMoO4:Eu3+材料的结构和发光性质的影响.结果表明:纳米材料的尺寸随着Sm3+离子掺杂浓度的增加而变小.Sm3+的引入,可实现Sm3+和Eu3+之间的能量传递,使Eu3+在近紫外405 nm处的激发增强,进而使Eu3+...