涤纶纺织品的低温等离子体温敏改性

为制备具有温敏效应的智能型涤纶纺织品．运用低温等离子体引发涤纶织物接枝聚合N-异丙基丙烯酰胺（NIPAAm）凝胶。通过对织物的水通时间、纤维化学结构以及于湿状态织物表面形态的测试．表征了改性前后织物结构及性能的变化．并探讨了改性后织物增重率和“开关效应”的关系。     

等离子体接枝反应对涤纶织物亲水性能的影响

采用氩气辉光放电等离子体处理经聚乙二醇预处理的涤纶织物,以提高织物的亲水性能,采用静电探针测定等离子体处理过程中的电子温度和电子密度,用液态水分管理系统（MMT）测试改性织物的润湿性能。探讨接枝聚合单体及氩等离子体处理条件对涤纶织物亲水性能的影响,分析了涤纶织物亲水改性的反应机制,并讨论了改性效果的耐久性。结果表明,经5%聚乙二醇1000处理后采用氩等离子体处理能显著改善涤纶织物的吸湿性能。氩等离子体最佳处理条件为：功率50W,压强30Pa,时间3min。处理后织物表面润湿时间2.9 s、水分扩散速度为7.2 mm/s,织物表面接触角0°,经多次洗涤显示出良好的耐久性。     

紫外光催化法制备丝胶蛋白改性抗静电涤纶织物

涤纶纤维因缺乏亲水性基团易产生静电,文章由此提出借助丝胶蛋白改善涤纶纤维易产生静电的缺陷。研究中以甲基丙烯酸酐乙烯基化改性的丝胶蛋白和涤纶织物为原料,在紫外光辐照下进行基于自由基反应的催化接枝改性,探究了借助丝胶蛋白整理后涤纶纤维中的双键与甲基丙烯酸酐质量浓度关系及接枝改性效果。结果表明：涤纶织物经2.5 g/L十六烷基三甲基溴化铵和1 g/L氢氧化钠质量浓度预处理能促进其表面乙烯化改性,借助红外光谱和碘液着色法验证了涤纶及丝胶中引入了双键,试样强力损失较退浆织物略有降低;经紫外催化丝胶蛋白接枝后,涤纶表面氮元素含量升至2.41%,织物静电半衰期从33.47 s缩减到8.81s,表明抗静电性有明显提升。紫外光催化丝胶蛋白为涤纶织物抗静电整理提供了新方法。     

大豆蛋白接枝改性PET功能织物的制备及服用性能

用生物酶对涤纶(PET)织物进行改性增强亲水性,然后用交联剂聚乙烯醇缩水甘油醚(PVAGE)将大豆蛋白接枝到织物表面,制备大豆蛋白接枝改性PET功能织物,并对织物进行结构表征及性能测试。大豆蛋白接枝改性的优化工艺:大豆蛋白5%,PVAGE 1.5%,100℃,30 min。结构表征显示制备的大豆蛋白接枝改性PET功能织物纤维表面有一层均匀的大豆蛋白薄膜,改性PET纤维的N从0%增加到2.13%;织物纤维表面出现了氨基和酰胺基的吸收峰,进一步证明大豆蛋白已被成功接枝到PET纤维上。服用性能表明改性织物的亲水性和耐洗性较好,断裂强力显著增强,并很好地保持了原织物的柔软性,广泛应用于各类服装面料的制作。     

涤纶织物表面改性方法研究进展

探讨涤纶织物表面改性方法的研究现状。详细综述了表面氧化法、表面水解法、表面接枝改性法、表面物理处理法等目前主要的表面改性方法,并分别介绍这些方法主要研究进展及其优缺点。认为:涤纶织物改性可为涤纶织物亲水、防静电、抗熔滴等改性及阻燃、抗菌除臭、防紫外、催化、导电等功能化应用奠定基础。低成本、有效的表面化学改性将是以后发展方向。     

阳离子改性阻燃涤纶织物的制备及其性能

为提高阻燃涤纶织物的吸湿、染色和抗菌等性能,以阻燃涤纶织物(FRPET)为基体,利用多巴胺化学辅助的表面引发原子转移自由基聚合(SI-ATRP)技术分别在织物表面接枝不同分子质量的聚(2-(甲基丙烯酰氧基)乙基)二甲基-(3-磺丙基)氢氧化铵(PSBMA)、聚(2-(甲基丙烯酰氧基)乙基)三甲基氯化铵(PMTAC)以及嵌段聚合物PSBMA-b-PMTAC。分别对其表面形貌、吸水、透湿、透气、染色、抗菌和阻燃性能进行表征与测试,研究阻燃涤纶织物改性前后阻燃、透湿、抗菌和染色性能的变化。结果表明：嵌段聚合物PSBMA-b-PMTAC改性的阻燃涤纶织物较原涤纶织物阻燃性能有所提高,热释放速率峰值降低60.7%;改性涤纶织物较原始织物吸水性提高,达到机织类吸湿产品标准;嵌段改性涤纶织物实现了阳离子改性的同时对大肠杆菌的抑菌率提高27%,显示出一定的抗菌性能。     

氩等离子体引发接枝反应赋予涤纶织物亲水性能

本文采用氩气辉光放电等离子体处理经聚乙二醇预处理的涤纶织物,以提高织物的亲水性能,采用静电探针测定等离子体处理过程中的电子温度和电子密度,用液态水分管理系统（MMT）测试改性织物的润湿性能。探讨了接枝聚合单体及氩等离子体处理条件对涤纶织物亲水性能的影响,分析了涤纶织物亲水改性的反应机理,并讨论了改性效果的耐久性。结果表明,经5%聚乙二醇1000处理后采用氩等离子体处理能显著改善涤纶织物的吸湿性能,经多次洗涤显示出良好的耐久性,氩等离子体最佳处理条件为：功率50W,气压30Pa,时间3min。     

涤纶表面亲水改性研究进展及其发展方向

基于涤纶亲水改性的原理和存在问题,结合目前常用的亲水改性方法,介绍了用于涤纶表面亲水改性的几个方面：主要包括表面形态结构改性、表面接枝改性和亲水整理剂的涂覆整理。着重介绍了表面接枝改性方法,尤其是辐射接枝改性,分析了辐照诱导接枝的机理和改善涤纶辐射接枝率的措施。基于对这些改性方法优缺点的分析,指出了目前涤纶表面亲水改性存在的问题和将来的发展方向,认为理想的涤纶亲水改性方法应该具有不损害其原有的优良性能、耐久性好、经济效益高和环境友好等特点。     

等离子体处理对石墨烯/涤纶复合织物结合牢度的影响研究

利用常温常压等离子体对涤纶织物表面进行改性处理,使其表面引入含氮基团,然后将石墨烯通过接枝和浸渍的方式引入到涤纶织物表面,制备成石墨烯/涤纶复合织物。通过试验对比,研究了常温常压等离子体处理后织物表面含氮基团的时效性及石墨烯/涤纶复合织物的结合牢度。等离子体即时处理与处理后放置24 h后织物的氮元素比例由3.73%下降为1.33%,处理24 h后制备的复合织物表面电阻率由0.124 MΩ/cm~2增加到0.259 MΩ/cm~2,说明等离子体处理具有明显的时效性;经等离子体处理复合织物水洗后表面电阻率变化率由99.1%减小到49.2%,说明等离子体处理后的涤纶织物制备的石墨烯/涤纶复合织物结合牢度显著提高。     

新型蜂窝状微孔改性涤纶织物的性能

新型蜂窝状微孔结构改性涤纶纤维的表面和横截面均有微孔结构,为了研究这种改性涤纶纤维及其织物的性能,将蜂窝状微孔改性涤纶纱线和普通涤纶纱线分别与同一种纯棉纱线交织制作成两种织物.对两种交织织物试样进行吸湿性、吸水性、折皱弹性、透气性及手感的测试与分析.结果显示:改性涤纶织物的吸湿性、快干性、透气性及折皱回复性均比普通涤纶织物明显提高,且改性涤纶织物手感柔滑,蓬松性和染色性能均优于涤纶织物.     

化学镀银涤纶织物的制备及其性能

利用化学镀方法制备镀银电磁屏蔽涤纶织物.分别采用场发射电镜( FE-SEM)、电子能谱(EDS)和X射线衍射(XRD)表征镀层的表面形貌、成分和结晶情况;考察了织物的厚度、增重率、耐摩擦色牢度、表面电阻、抗静电性、拉伸断裂强力、断裂伸长率、刚柔性、悬垂性以及透气性.结果表明:镀层为高纯度立方面心结构的单质银;化学镀银后...     

氧化条件对聚苯胺/涤纶导电织物性能的影响

采用浸轧工艺,在织物上进行原位化学氧化聚合,以改善聚苯胺/涤纶导电织物性能。探讨了氧化聚合过程中氧化剂和质子酸浓度、浸液时间、氧化液温度和带液率等因素对导电织物表面电阻率、聚苯胺增重率、颜色深度及均匀性的影响;确定了合适的苯胺氧化聚合条件,即氧化剂浓度0.2mol/L,质子酸浓度0.2mol/L,浸液时间5s以内,氧化液温度40℃以下,带液率120%,从而实现了导电聚苯胺在涤纶织物上的大面积均匀沉积。     

Preparation and characterization of β-cyclodextrin grafted silk fabric

ABSTRACT

Silk fabrics were treated by β-cyclodextrin (β-CD) in the presence of citric acid (CA) as crosslinking agent and sodium hypophosphite (SHP) as catalyst using pad dry cure technique. CA is expected to react with β-CD and hydroxyl groups of silk fibroin via esterification reaction. Four independent factors including curing time, curing temperature, β-cyclodextrin, and citric acid concentrations were selected, and effects of these factors on the weight gain of the samples were examined. Fourier transformed infrared spectrometer (FTIR), weight gain, differential scanning calorimetry (DSC), Thermal gravimetric (TGA) and differential thermal analysis (DTA), and field-emission scanning electron microscope (FE-SEM) were employed to confirm the changes of the silk fabrics. The effect of crosslinking reaction on the color changing of samples was investigated by measurement yellowness index of the treated fabrics. The results revealed that the weight gain could reach up to 22% when fabric was treated with 50 g/L β-CD, 100 g/L CA under 170°С for 3 min. FTIR and thermal analysis demonstrated that β-CD had been grafted onto silk fabric successfully.     

染整加工后自卷曲丝结构的变化及其织物弹性

为探究不同PTT/PET自卷曲长丝织物在后整理中的表现及其最终成品的弹性性能,选用3个厂家生产的PTT/PET自卷曲长丝试织织物,并在相同工艺条件下进行染整处理,再与氨纶织物进行对比,得到4种织物的质量损失率、纬向染缩率、弹性伸长率、弹性回复率。结果表明:单丝纤度越大,质量损失率越小,染色率越大;织造密度越大,质量损失率越小;弹性伸长率越大,弹性回复率越小。通过光学显微镜、扫描电镜观察及DSC辅助分析发现,PTT/PET复合丝由于单丝比较细,比表面积大,在染整处理过程中受到碱液腐蚀过大而发生2种组分分离的现象,从而失去了双组分丝应有的高弹性。     

明日叶的保健功能及其产品开发的研究进展

明日叶为一种药食兼用型植物,有利于促进人体健康,日益受到人们关注。本文综述了明日叶查尔酮、香豆素、类黄酮等功能成分,归纳了明日叶“五抗”、“四降”、“三改善”、“二预防”、“一提高”的保健作用及其最新研究进展,并对明日叶保健茶、保健酒、保健饮料、保健胶囊等几种典型产品作了简要介绍,以期为明日叶资源的开发利用提供参考。     

Changes in the Mechanical Properties of Silk Fabrics Modified with Epoxide and Their Relation to the Fabric Construction

An investigation is described in which the mechanical properties of silk fabrics treated with ethyleneglycol diglycidylether (EDGE) were measured in relation to variations in fabric structure in terms of weight gain. Their mechanical behaviour was determined in bending, in-plane shear, and compressional characteristics experiments. An examination of the mechanical properties of silk fabrics treated with EDGE led to the following conclusions. The value of the bending rigidity (B) in the weft direction clearly increased with an increase in weight gain, which suggested hardening of fabric. The value of the shearing stiffness (G) of the fabric in the warp direction remained unchanged in spite of the epoxide treatment, and the values of the shearing hysteresis (2HG) were linearly related to the weight gain. These results suggest that the observed changes in mechanical behaviour can be largely attributed to an increase in the contact pressure between warp and weft yarns.     

碱减量对超细织物染色性能的影响

以纯涤超细织物和涤锦复合超细织物为研究对象,与纯涤常规织物作对照,使用切片摄影和扫描电镜分析不同减量率对涤锦复合超细织物纤维形态结构及开纤的影响,由于开纤和纤维变细的影响大于表面刻蚀的影响,碱减量处理超细织物后的染色表观色深K/S值比未处理时小,相应彩度也较低,这种差异随减量率的提高而增大。     

互穿聚合物网络温敏凝胶对棉织物液态水分传递的影响

为使高分子凝胶在纺织品改性中得到更好的应用,采用互穿聚合物网络（IPN）方法,制备了一种IPN 壳聚糖/聚Ｎ?异丙基丙烯酰胺温敏凝胶;并以戊二醛为交联剂,IPN 凝胶为改性剂,采用二浸二轧法获得改性棉织物,以提高棉织物的液态水分传递能力。研究了不同质量增加率对改性棉织物的透湿性以及液态水分传递能力的影响。结果表明：IPN 凝胶牢固附着在棉纤维表面,且改性棉织物的低临界溶解温度为34.45℃;温度高于低临界溶解温度时,高质量增加率的改性棉织物透湿性显著提高;改性棉织物对液态水分具有较强的单向传递能力,高质量增加率的改性棉织物液态水分传递能力较好;IPN凝胶可显著改善棉织物的透湿和液态水分传递能力。     

涤纶织物葡萄糖和肼化学镀银的研究

采用还原剂为葡萄糖和肼对涤纶织物化学镀银,借助SEM和XRD对镀层的表面形貌进行分析,并测试化学镀银织物的电磁波屏蔽、耐磨性、刚柔性和透气性.结果表明,葡萄糖作还原剂时镀层表面光滑、晶粒较小,电磁波屏蔽及耐磨性能均优于肼镀银织物;两种不同还原剂化学镀银织物的刚柔性基本不变,透气性有所下降.     

有机磷化合物与甲基丙烯酰胺复配阻燃真丝织物

采用有机磷化合物二甲基-2-甲基丙烯酰氧基-乙基磷酸酯(DMMEP)、甲基丙烯酰胺(MAA),以及以上2种物质的共混溶液,分别对真丝织物进行常规接枝,经过单因素分析探讨各自最优的接枝工艺。然后对整理后的丝织物做了接枝率、极限氧指数、炭长的测定,并对接枝织物的表面红外进行了表征,且通过扫描电镜对燃烧后残留炭渣的形态结构进行了分析。结果表明,通过对DMMEP和MAA进行复配,真丝织物能够获得非常好的阻燃性能。