含Nb细晶高强IF钢热变形行为的析出热力学

以新型含Nb细晶高强IF钢为研究对象,运用规则溶液亚点阵模型计算了实验钢从均热(1523K)冷却至室温(293K)的各个工艺过程中碳氮化物析出相的平衡体积分数、析出相的组成成分、各组元的平衡质量分数。计算结果表明,从均热到冷却至室温(1523K~293K)的过程中,随着温度的降低,固溶于基体中的Nb、C、N元素的质量分数逐渐减小,析出相平衡体积分数先增大后减小,NbN在析出相中比例逐渐降低,NbC在析出相中比例逐渐增加。至室温(293K)时,Nb和N元素几乎全部析出,碳氮化物不再继续析出。     

IF钢硬化模型试验

目的研究适用于IF钢材料的硬化模型。方法通过对3种不同牌号的IF钢材料进行拉伸试验,基于AUTOFORM软件中4种常用的硬化模型分别对试验数据进行拟合,分析不同硬化模型对试验数据曲线整体拟合效果,并基于曲线重合性均方差最小原则,对比了不同硬化模型的拟合误差。结果 Approximation模型综合了Hockett-Sherby饱和模型和Swift非饱和模型,对应力应变数据拟合效果最好,误差分析显示Ludwick模型拟合误差最大,Swift,Hockett-sherby和Approximation模型拟合误差大致相当,Approximation模型拟合误差最小。结论针对IF钢材料,推荐采用Approximation模型拟合硬化曲线,对提升冲压和回弹仿真精度,具有一定的指导作用。     

连续退火温度对马钢CSP流程IF钢冷轧板屈服强度的影响

采用连续退火工艺方法，研究了以CSP流程热轧卷为基料生产的冷轧卷退火温度对屈服强度的影响。分析了加热温度、缓冷温度和快冷温度对屈服强度影响的显著性，制定了连续退火温度的优化方案。     

240 MPa级高强IF钢的冷轧压下率和退火温度

以工业生产的240MPa级高强IF钢为试验材料,进行了冷轧压下率和退火温度的实验室研究。结果表明:在试验条件下,不同退火温度下,冷轧压下率在75%~85%时,试验钢为完全再结晶组织,卷取温度较高在710℃的试验钢的屈服强度、抗拉强度、伸长率、屈服点伸长率、塑性应变比及应变硬化指数分别在260MPa,445MPa,37.5%,2.14%,0.25,2.0左右;卷取温度较低在670℃的试验钢的上述参数分别为235MPa,369MPa,38.8%,1.73%,0.26,2.1左右。最终提出了试验钢工业生产中退火温度为840℃左右,冷轧压下率为75%左右,为获得高强度和优良成型性能的最佳匹配。     

基于纳米铁碳析出物的钢综合强化机理

简要叙述了关于钢强化机理的研究现状,用化学相分析+X射线小角散射、RTO方法及高分辨透射电镜对薄板坯连铸连轧钛微合金化高强耐候钢中纳米粒子的属性进行了综合分析。发现钛微合金化高强耐候钢中尺寸<36 nm的粒子,除纳米TiC以外,还存在大量的纳米Fe3C,其体积分数为同尺寸TiC体积分数的4.4倍,析出强化作用比纳米TiC粒子大,不可忽略;提出了钢的综合强化机理,指出对不同种类、不同尺寸的纳米析出粒子,应分别根据位错切割和位错绕过机理计算出析出强化贡献,然后与固溶强化和细晶强化贡献加和,求得钢的屈服强度;讨论了细晶强化与位错强化不能加和的原因以及相变对钢强度影响的表现形式,对钛微合金化高强耐候钢屈服强度的理论计算与生产结果相符,实验钢σs=630～676 MPa,实际σs=630～680 MPa。简述了钢综合强化机理的应用情况,指出了有待进一步研究的科学问题。     

热镀锌连续退火工艺对高强IF钢组织和性能的影响

研究了热镀锌连续退火工艺对高强IF钢性能、组织及第二相粒子析出的影响。利用EU AV型热浸镀工艺模拟实验机对热镀锌高强IF钢进行了不同连续退火温度以及在同一温度下分别保温不同时间的连续退火工艺模拟实验。用万能试验机、光学显微镜、透射电子显微镜对样品的性能、组织和第二相粒子进行了检测分析。结果表明:热镀锌连续退火工艺直接影响产品的力学性能、微观组织和第二相粒子的析出,并得出了退火工艺对产品性能、组织和第二相粒子的影响规律。     

不同退火工艺下Ti—IF钢二相料演变的比较

对罩式退火和连续退火过程中Ｔｉ－ＩＦ钢二相粒子的演变规律进行了研究。结果表明：在退火以前形成的二相凿子，ＴｉＮ，ＴｉＳ和Ｔｉ４（ＣＳ）２经过罩式退火和连续退火后，春尺寸，形状和分布无较大的差别，而ＴｉＣ的变化较大；Ｔｉ－ＩＦ钢在连续退火中不形成新的相粒子，而在罩式退火中形成两类新的二相粒子－ＦｅＴｉＰ和（Ｔｉ，Ｍｎ）Ｓ。     

IF钢压薄滚焊接头断裂机理

研究了ＩＦ钢压薄滚焊接头断裂的机理，结果发现，裂纹首先在熔合底部的熔核区以微孔聚合的方式形成，并向粗晶区扩展，然后裂纹在粗晶区内一沿一定的解理面扩展，最后在部分再结昌区以滑移面分离的方式断裂。     

润滑条件对温轧含磷IF钢组织性能的影响

为研究润滑条件对热轧高强钢板的组织和性能的影响机理,对热轧坯料分别进行了润滑和不润滑两种轧制,并对两种轧制条件下的钢板进行了显微组织观察及力学性能测试.结果表明：润滑条件对铁素体区热轧高强IF钢的屈服强度（σs）、抗拉强度（σb）、总延伸率（η）和n值影响不大,但对r值和Δr值有显著的影响.在未润滑条件下轧制的钢板的r...     

加磷高强IF钢的最优冷轧压下率确定

为了确定加磷高强IF钢的最优冷轧压下率,以工业生产的加磷高强IF钢热轧钢板为试验材料,在实验室进行了冷轧试验和盐浴退火试验,研究了冷轧压下率对试验钢显微组织和力学性能的影响。结果表明:在试验条件下,试验钢冷轧压下率为50%～80%,退火温度为820～850℃时,再结晶完成;随着冷轧压下率的增加,晶粒变得细小均匀;冷轧压下率为50%～80%,退火温度为850℃时,屈服强度为160 MPa左右,抗拉强度为345 MPa左右,延伸率为35.0%左右,塑性应变比r值和应变硬化指数n值都较高,r值为1.5左右,n值为0.30左右。最终确定工业生产中最优冷轧压下率为60%～70%。     

ODS钢的抗辐照设计及纳米第二相粒子表征的研究进展

先进裂变反应堆及聚变堆要求材料在高温高压、强中子辐照、长服役周期等苛刻服役环境下具有卓越的结构和性能稳定性。氧化物弥散强化(ODS)钢由于具有优异的耐高温及耐辐照性能成为第四代反应堆包壳及核聚变包层最有希望的候选材料。基于材料的中子辐照损伤特性,主要介绍了ODS钢的抗辐照设计及纳米第二相粒子的表征方面的研究进展。     

合金元素在相变诱发塑性钢中的作用

阐述了相变诱发塑性钢高塑性、高强度的机理和产生原理,合金元素在相变诱发塑性钢中的作用,介绍了我国在相变诱发塑性钢领域研究的现状,指出了相变诱发塑性钢中合金元素今后研究的趋势.     

HREM Observation of Age-Precipitated Particles in Practical Cu-bearing Ultra-Low Carbon Steels

Morphology,distribution and crystal structures of age-precipitated particles in practical Cu-bearing steels with ultra-low carbon were studied by high resolution electron microscopy(HREM).The age-precipitation behavior was explored when poly-microalloying elements Cu,Nb,Cr,Mo and Ni were used and ε-Cu particles coexisted with carbides(carbonitrides) in steels.The fine dispersed ε-Cu particles and carbides of microalloying element Nb,Cr,Mo being about 10 nm only in size were observed in peak aging specimens ...     

On Optimizing Batch Annealing for the Production of IF Steels

Batch annealing characterized by a long heating cycle and low heating temperature is widely used to produce sheet steels including interstitial-free (IF) steels. Optimizing batch-annealing conditions would be helpful in cutting lead time and saving energy while keeping the necessary deep drawability; however, little research has been done on it. The effects of batch-annealing parameters on the deep drawability of a Ti-stabilized IF steel and Nb+Ti-stabilized IF steel have been investigated. In general, a slight improvement in r_mvalue was found with the increase of annealing temperature. Because of the higher recrystallization temperatures of Nb+Ti-IF steel, it showed higher sensitivity to annealing temperature than Ti-IF steel. In addition, greater dependency of mechanical properties and deep drawability on soaking time was observed when annealing temperature was lower. Moreover, a heat transfer analysis showed that the annealing time could be reduced by 40% if the temperature decreases from 730°C to 650°C. The industrial production has verified that the analytical results are in good agreement with the recorded annealing temperature curve. Meanwhile, it has been shown that Ti-IF steels annealed at 650°C have very close deep drawability and other tensile properties compared with these annealed at 730°C.     

EBSD Investigation on Oriented Nucleation in IF Steels

The mechanism responsible for the formation of recrystallization texture in cold-rolled Ti bearing interstitial free （IF） steel sheets was investigated using electron back-scatter diffraction （EBSD）. In addition, the origin of nuclei with specific orientations was studied. The formation of recrystallization texture was explained by oriented nucleation. Most nuclei have a high misorientation angle of 25-55° with the surrounding deformed matrices, but no specific orientation of misorientation axis between the nucleus and the surrounding deformed matrix is observed. The stored energy of deformed grains is in the decreasing order of the {111}〈112〉,{111}〈110〉, {112}〈110〉 and {001}〈110〉 orientations. New {111}〈110〉 grains are nucleated within deformed {111}〈112〉 grains and new {111}〈112〉 grains originate in the deformed {111}〈110〉 grains.     

取向电工钢中碳化物在冷变形过程中的行为

用场发射扫描电子显微镜观察了取向电工钢在0-68%冷压加工过程中主要组成为碳化物的第二相粒子的分布状态,统计了不同尺寸粒子面密度的变化。结果表明,冷变形过程造成了碳化物粒子的碎化和回溶行为。粒子碎化到一定程度后其回溶可能是热力学自发过程。这种碎化和回溶有利于促进二次再结晶过程的顺利进行和锋锐Goss织构的生成,也有利于促进一次冷轧板的脱碳过程.     

碳钢及低合金钢海水耐蚀性综合评价

为了分析研究碳钢和低合金钢在海洋环境中的腐蚀行为和规律 ,综合评价材料的耐蚀性能 ,对 1 9种碳钢和低合金钢进行 1、8、1 6a长周期实海暴露挂片试验。采用“极值”统计方法的Gumbel第一类近似函数对一次局部腐蚀数据进行极值概率处理 ,校准局部腐蚀量。将材料的平均腐蚀量和局部腐蚀量进行组合 ,以此综合评价 1 9种钢的耐海水腐蚀性能     

X-荧光能谱法测定合金结构钢标样中五个元素

本文提出X荧光能谱法测定合金结构钢中五个元素含量的方法。本方法采用能谱仪中定量分析软件,选择适当工作条件,测定合金结构钢中五个元素。其准确度,精密度,均能满足分析要求。     

3种船用钢在南海海洋环境中8年的腐蚀行为

研究了３Ｃ（Ｗ ）、１６Ｍｎ、９２１ 三种钢在南海榆林海域全浸、潮差、飞溅环境中暴露８ 年的腐蚀行为。其中,９２１ 钢在飞溅区具有优良的耐蚀性,而在全浸和潮差区耐蚀性不如３Ｃ（Ｗ）钢和１６Ｍｎ 钢的。发现９２１ 钢在全浸区暴露２ 年后发生腐蚀率随时间增加而增大的“逆转”现象。