Na2O对MAS系玻璃熔体性质及微晶玻璃结构的影响

利用浇铸法制备了MgO-Al2O3-SiO2微晶玻璃。采用示差扫描量热法(DSC)、X射线衍射(XRD)、扫描电子显微镜(SEM)等分析方法,研究玻璃组成中Na2O对MgO-Al2O3-SiO2(MAS)系统微晶玻璃的高温粘度、结构与析晶性能的影响。结果表明,掺入Na2O后MAS微晶玻璃高温粘度有明显的降低,并且随着掺入量的增加玻璃的粘度逐渐降低。随着Na2O掺入量的增加,玻璃熔体的熔制温度从A0的1 552℃逐步降低到1 494℃。未掺Na2O的MAS微晶玻璃主晶相为颗粒状α-堇青石相,掺入后的微晶玻璃全部析出柱状镁橄榄石相。     

BaO-MgO-Al2O3-SiO2系统微晶玻璃的研究

以MgO-Al2O3-SiO2系统为基础玻璃组成,TiO2为晶核剂,用少量的BaO取代MgO,制备出顽辉石/堇青石基微晶玻璃.采用差热分析、X射线衍射分析、扫描电镜等测试手段研究了BaO对玻璃析晶性能和显微结构等性能的影响,并探讨了不同量的BaO取代MgO对其电导率的影响.结果表明,在1 480℃通过熔融法制备玻璃试样...     

MgO对花岗岩尾矿微晶玻璃析晶和性能的影响

尝试用花岗岩尾矿制备CaO-MgO-Al2O3-SiO2系微晶玻璃,并采用DSC、XRD和SEM等测试手段研究MgO对微晶玻璃析晶和性能的影响。结果表明,随着MgO含量的增加,玻璃转变温度和析晶峰温度逐渐降低,玻璃析晶性能增强。当引入MgO的质量分数为3%时,微晶玻璃的主晶相为钙长石;当MgO质量分数为6%~12%时,主要析出辉石,且质量分数为12%的MgO样品析出的晶体中伴随着部分堇青石。样品的显微硬度随MgO的增加呈现先增大后减小的趋势,质量分数为9%的MgO样品析出晶体的尺寸更均匀,其显微硬度最高,为8.2GPa。     

Fe_2O_3和ZrO_2对花岗岩尾矿微晶玻璃析晶行为的影响

以花岗岩尾矿为主要原料制备CaO-MgO-Al2O3-SiO2系微晶玻璃,用DSC、XRD和SEM等手段研究了Fe2O3和ZrO2对微晶玻璃析晶行为的影响。结果显示,Fe2O3可以降低玻璃转变温度和析晶峰温度,促进玻璃析晶,而ZrO2的作用正好相反,抑制玻璃析晶。不添加任何晶核剂以及分别添加4%ZrO2和4%Fe2O3的样品均以表面析晶为主,析出的主晶相为斜长石。同时添加4%ZrO2和4%Fe2O3的样品在770℃核化,920℃晶化后出现整体析晶,析出的主晶相为透辉石,次晶相为尖晶石和镁黄长石。     

溶胶-凝胶过程影响堇青石结晶行为的因素

为了研究影响堇青石结晶行为的因素,以Mg(NO3)2.6H2O、Al(NO3)3.9H2O、正硅酸乙酯为原料,根据堇青石的化学式2MgO.Al2O3.5SiO2,按照配比制成溶胶,利用溶胶-凝胶法制备堇青石粉末,并利用X射线衍射、差示扫描热量法等测试手段对堇青石粉末进行表征.测试结果表明,煅烧温度和凝胶预处理温度对堇青石的结晶行为有直接的影响,当干凝胶的预处理为500℃,煅烧温度为1 200℃时,出现明显的α-堇青石晶相.     

纳米晶镁铝尖晶石透明微晶玻璃的研究

以TiO2、ZrO2为晶核剂,用两步法热处理制备MgO-Al2O3-SiO2(MAS)系统透明微晶玻璃。采用X射线衍射分析(XRD)、扫描电镜(SEM)、场发射环境扫描电镜(FE-ESEM)、紫外-可见光光度计对材料进行了表征。实验结果表明,热处理温度在1 000℃以下时,仅有唯一晶相镁铝尖晶石(MgAl2O4)存在;在1 050℃时,β-石英晶体析出,但尖晶石仍为主晶相。玻璃中晶体的析出使紫外吸收极限向长波方向移动,随着晶化温度的升高,晶粒尺寸增大,微晶玻璃光透过率下降。经830℃核化保温4 h、950℃晶化保温1.5 h得到的微晶玻璃样品平均晶粒尺寸仅为25.6 nm,紫外截止率达100%,可见光透过率为62%。     

熔融法和固相反应法制备堇青石及其性能的对比研究

以石英、铝矾土和轻烧氧化镁为原料,分别利用熔融法和固相反应法两种制备工艺合成堇青石,通过对所制备的样品结构和性能进行表征测试,来探究两种工艺各自的优缺点,并作以比较.结果表明:熔融法在950℃就大量析出α-堇青石相,经过1 000℃、2h晶化处理,热膨胀系数为2.23×10-6℃-1,而固相反应方法在1 300℃时才大量析出α-堇青石相,经过1 350℃、2h晶化处理,热膨胀系数是1.46×10-6℃-1;熔融法合成温度比固相反应法低了近350℃,且合成温度范围宽,但是熔融法的制备工艺比固相反应法复杂,成本偏高.     

TiO_2和Cr_2O_3复合晶核剂对微晶玻璃晶化行为的影响

通过差热分析、X射线衍射分析、偏光显微镜和扫描电镜观察等测试方法 ,研究了TiO2 和Cr2 O3作晶核剂对金属尾矿微晶玻璃晶化行为的影响 .研究表明 :Cr2 O3 和TiO2 复合晶核剂能有效地促进CaO -MgO -Al2 O3-SiO2 系统玻璃在较低温度下即开始晶化 ,且形成以透辉石为主晶相的微晶玻璃 ,晶核剂质量浓度不同对玻璃析晶的影响不同 .     

碱金属氧化物对CaO-MgO-Al_2O_3-SiO_2玻璃黏度和析晶性能的影响

用熔制法制备含不同碱金属氧化物的Ca O-Mg O-Al2O3-Si O2(CMAS)系微晶玻璃,通过旋转黏度仪测试该玻璃黏度,再结合差示扫描量热分析(DSC)、X射线衍射(XRD)、扫描电子显微镜(SEM)等分析方法,研究不同碱金属氧化物对微晶玻璃析晶性能的影响。结果表明:含不同碱金属氧化物的CMAS系微晶玻璃析出的主晶相均为辉石,但玻璃的高温黏度以及显微硬度存在差异。其中含6%Na2O(摩尔分数,下同)试样熔化温度为1 475℃,显微硬度为6.4 GPa。当3%K2O取代3%Na2O时,玻璃的高温黏度降低,熔化温度为1 460℃,析晶能力增强,显微硬度7.6 GPa。当3%Li2O取代3%Na2O时,玻璃高温黏度降低明显,试样熔化温度为1 385℃,析晶能力增强,显微硬度为7.1 GPa。     

CaO—Al_2O_3—SiO_2系统玻璃分相对表面析晶成核影响的差热分析研究

本文利用差热分析(DTA)研究了 CaO—Al_2O_3-SiO_2系统不同温度分相热处理以及未分相玻璃中α—方石英和β—硅灰石的析出情况,发现分相预处理使析晶放热峰开始温度有所下降,下降幅度越大对应分相的(富 SiO_2)液滴相数目越多。分析表明,分相对于表面析晶成核也具有促进作用。     

Bi2Sr2Co2Oy热电材料的制备

为了研究Bi2Sr2Co2Oy热电陶瓷的不同制备方法,实验采用固相反应法和溶胶-凝胶法制备Bi2Sr2Co2Oy陶瓷．用XRD,SEM等表征技术研究了样品的物相及显微组织形貌．结果表明：样品为单相,组织均匀,为层片状结构,且具有明显的c轴择优取向．     

核壳型TiO2/COFe2O4与TiO2/SiO2/COFe2O4光催化剂的制备与性能研究

文章以CoFe2O4纳米颗粒为核,研究了制备核壳型TiO2/CoFe2O4和TiO2/SiO2/CoFe2O4光催化剂的适宜工艺;用XRD和TEM分析了产物的结构组成与形貌;以TNT为目标降解物考察了催化荆的活性.实验结果表明:以非晶CoFe2O4为核时易生成杂相,催化剂及所制备的复合颗粒的活性排序为:TiO2/SiO2/CoFe2O4＞TiO2＞TiO2/CoFe2O4＞SiO2/CoFe2O4.     

BaF2-CaF2-CaCl2三元系熔盐电解体系的物理化学性质

研究了BaF2-CaF2-CaCl2三元系电解质体系的物理化学性质,为熔盐电解法制备Al-Ca合金奠定基础.采用阿基米德法,测定了BaF2-CaF2-CaCl2体系的密度;采用差热-热重分析法,测定了BaF2-CaF2-CaCl2体系初晶温度;采用连续变化电导池常数（CVCC）法,测定了BaF2-CaF2-CaCl2体系的电导率;采用循环伏安法研究了该体系的电化学行为.     

Thermal behavior and lithium ion conductivity of L2O-Al2O3-TiO2-SiO2-P2O5 glass-ceramics

A lithium ion conductive solid electrolyte, L2O-Al2O3-TiO2-SiO2-P2O5 glass with NASICON-type structure have been synthesized and transformed into glass-ceramic through thermal-treatment at various temperatures from 700 to 1 000 ℃ for 12 h. The differential scanning calorimetry (DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM) and complex impedance techniques were employed to characterize the samples. The experimental results indicated that the capability of glass forming in this system is superior to that of L2O-Al2O3-TiO2-P2O5. The glass has an amorphous structure and resultant glass-ceramic mainly consisting of LiTi2(PO4)3 phases. Impurity phases AlPO4, TiO2, TiP2O7 and unidentified phase were observed. With the enhanced heat-treatment temperature, grain grew gradually and lithium ion conductivity of glass-ceramics increased accordingly, the related impedance semicircles were depressed gradually and even disappeared, which could be analytically explained by the coordinate action of the ’Constant phase element’ (CPE) model and the ’Concept of Mismatch and Relaxation’ model (CMR). When the sample is devitrified at 1 000 ℃, the maximum room temperature lithium ion conductivity comes up to 4.1×10-4 S/cm, which is suitable for the application as an electrolyte of all-solid-state lithium batteries.     

Fe~(2+)催化H_2O_2/Na_2S_2O_8氧化降解水中黄腐酸

利用Fe~(2+)催化H_2O_2或Na_2S_2O_8降解水中的黄腐酸,研究了诸因素(处理剂加量、pH和温度)对黄腐酸降解的影响。黄腐酸溶液颜色和TOC的去除,紫外区光吸收强度的降低都表明H_2O_2/Fe~(2+)体系对黄腐酸具有良好的降解效果;在pH=3.0、H_2O_2为400mg·L~(-1)、H_2O_2与Fe~(2+)物质的量的比为10∶1的条件下,处理100mg·L~(-1)黄腐酸溶液120 min,TOC去除率达到88.4%。Na_2S_2O_8/Fe~(2+)降解结果表明:在pH=3.0、Na_2S_2O_8为2 000mg·L~(-1),Fe~(2+)为5mmol·L~(-1),温度为50℃条件下处理100 mg·L~(-1)黄腐酸水样240min,TOC去除率为55.9%。分析降解效果和试剂成本可知,H_2O_2/Fe~(2+)法降解水中黄腐酸优于Na_2S_2O_8/Fe~(2+)法。     

Crystallization Mechanism of Na2O-CaO-Al2O3-SiO2-F Glass Containing Cr2O3

The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1 .5 % (mass fraction) Cr2O3 can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr2O4] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO3 grew epitaxially.     

固体超强酸SO4^2-／ZrO2-SiO2的制备及其催化性能的研究

分别以氧氯化锆、硅溶胶和氨水为锆源、硅源和沉淀剂,采用共沉淀法制备Zr(OH)4-Si(OH)4,110 ℃干燥后经硫酸浸渍、干燥和焙烧制得SO2-4/ZrO2-SiO2固体超强酸.XRD和比表面积测定结果表明,SiO2的引入对SO2-4/ZrO2催化剂的结构产生了重要影响,从而使其比表面积明显增大.以所制备的SO2-4/ZrO2-SiO2固体超强酸为催化剂,代替浓硫酸用于丁酸和丁醇的酯化反应,考察了硫酸浸渍液浓度、焙烧温度等制备条件对其催化性能的影响.结果表明,采用硫酸浸渍液浓度为1.0 mol/L,焙烧温度为550 ℃所制备的SO2-4/ZrO2-SiO2催化剂,在丁醇和丁酸的物质的量比为1.2及不添加任何带水剂的条件下,丁酸丁酯的收率高达90%以上,优于SO2-4/TiO2-WO3和TiSiW12O40/TiO2催化剂.     

IR Spectra Analysis of SiO_2-TiO_2-GeO_2 Gel Glass of CO_2 Laser Transmitting Hollow Waveguide

1　ＩｎｔｒｏｄｕｃｔｉｏｎＴｈｅｔｈｅｏｒｙｏｆｈｏｌｌｏｗｗａｖｅｇｕｉｄｅｆｏｒｔｒａｎｓｍｉｔｔｉｎｇＣＯ2ｌａｓｅｒｉｓｂａｓｅｄｏｎｔｈｅａｎｏｍａｌｏｕｓｄｉｓｐｅｒｓｉｏｎｃａｕｓｅｄｂｙｒｅｓｏ ｎａｎｃｅａｂｓｏｒｐｔｉｏｎａｔｔｈｅｗａｖｅｎｕｍｂｅｒｏｆ 94 0ｃｍ- 1[1- 3 ] .Ｈｏｗｅｖｅｒ ,ｔｈｅＩＲａｂｓｏｒｐｔｉｏｎｏｆｔｈｅｓｉｌｉｃａｇｌａｓｓｍａｉｎｌｙｔａｋｅｓｐｌａｃｅａｔｗａｖｅｌｅｎｇｔｈｓｂｅｔｗｅｅｎ 7.6 9ａｎｄ 9.6 2 μｍ ,ａｓａｒｅｓｕｌｔ,ａｌｍｏｓ…     

GeO2-PbF2-ZnF2玻璃的Raman光谱和结构

用Ｒａｍａｎ光谱研究了ＧｅＯ２－ＰｂＦ２－ＺｎＦ２系统玻璃结构。结果表明,这种氟氧混合体系玻璃主要以［ＧｅＯ４－ｘＦｘ］四面体、［ＺｎＦ４］和［ＺｎＯ４］单元共同构成三维网络。网络中非桥氧或［ＧｅＯ４－ｘＦｘ］四面体的数量随Ｆ－／Ｏ２－比例增加而增加,而Ｆ－／Ｏ２－比例一定时,Ｚｎ２＋则能提高［ＧｅＯ４－ｘＦｘ］四面体的聚合度。     

Li_2O、La_2O_3含量对Li_2O-La_2O_3-Ta_2O_5-SiO_2系统玻璃析晶性能的影响

电极玻璃的析晶性能是直接影响电极制作的重要因素 ,本文通过析晶实验 ,利用X射线衍射分析对Li2 O La2 O3 Ta2 O5 SiO2 系统玻璃的析晶性能进行了研究。结果表明 :引入适量的Li2 O、La2 O3能改善该系统玻璃的析晶性能。