纳米Al2O3颗粒对Cu-Al2O3性能的影响

采用溶胶-凝胶法制备纳米Al₂O₃颗粒,通过粉末冶金法制备氧化铝铜（Cu-Al₂O₃）。采用X射线光电子能谱仪、扫描电子显微镜、洛氏硬度仪和涡流计分别测试了Cu-Al₂O₃的结合能、微观组织、硬度和导电率。结果表明：随Al₂O₃颗粒含量的增加,Cu-Al₂O₃的硬度先升高后降低,当Al₂O₃颗粒的质量分数达到0.084%时,Cu-Al₂O₃的硬度达到最大值75.73（HRB）。Cu-Al₂O₃的导电率随着Al₂O₃颗粒含量的增加逐渐下降。Al₂O₃颗粒的质量分数为0.084%时为最佳值,Cu-Al₂O₃的硬度达到最大值,导电率达到69.1% IACS。     

N2分压对抗菌TiN/Cu纳米复合涂层的综合性能影响

人体组织对植入物磨损碎片和腐蚀产物产生的异物反应以及细菌感染是导致植入物失败的主要因素。为了解决这些问题,本文采用电弧离子镀系统通过不同N₂分压的工艺参数设置,在304不锈钢上制备获得一系列抗菌TiN/Cu纳米复合涂层沉积,分别命名为TiN/Cu-x（x = 0.5,1.0,1.5 Pa）。X射线衍射分析、能量色散X射线光谱和扫描电镜分析结果表明,N₂分压决定了TiN/Cu纳米复合涂层的Cu含量、表面缺陷和微晶尺寸,进一步影响了其综合能力。TiN/Cu涂层的硬度和耐磨性随着微晶尺寸的增加而增强。在表面缺陷、微晶尺寸和铜含量的协同作用下,TiN/Cu-1.0和TiN/Cu-1.5涂层具有优异的耐腐蚀性。此外,生物试验证明,所有TiN/Cu涂层均无细胞毒性,抗菌能力强。其中,TiN/Cu-1.5涂层显著促进了细胞增殖,有望成为一种新型抗菌、耐腐蚀、耐磨的医疗植入物表面涂层。     

Ag对Ag-ZnO纳米抗菌涂层微观结构和性能的影响

外固定器作为最常见的固定装置在开放性骨折手术中被大量应用,但其配合使用的螺钉存在易感染的问题。采用射频磁控溅射技术制备Ag-ZnO/Ti纳米复合涂层附着于Ti6Al4V螺钉表面,能够有效减少细菌的粘附。通过调整靶材拼接的比例,探究了不同Ag含量的复合涂层微观形貌对Ti6Al4V螺钉抗菌性能的影响。结果表明,当Ag、ZnO、Ti靶材的拼接体积比为2∶2∶96时,Ag-ZnO/Ti纳米复合涂层中Ag质量分数达到1.85%,其表面粗糙度为4.24 nm,涂层表面平整光滑且具有疏水性,有利于减少细菌的粘附。涂层细胞毒性符合生物安全标准,且抗菌率高达99.62%。     

钛金属表面原位自生K2(Ti8O17)/ TiO2复合生物陶瓷涂层的制备及其生物相容性

采用电化学原位自生方法在钛基体表面成功制备出了K2(Ti₈O₁₇)/ TiO₂复合生物陶瓷涂层，并对涂层的表面形貌、微观结构及相组成等进行了观察分析.通过模拟体液培养对其生物活性进行了评估.结果表明，所制备的K2(Ti₈O₁₇)/ TiO₂复合陶瓷涂层具有良好的生物相容性和生物活性.     

一步法合成耐久性水基超疏水TiO2/DTMS涂层

为制备具有优异自清洁功能的耐久性水基超疏水涂层,以十二烷基三甲氧基硅烷(n-dodecyltrimethoxysilane, DTMS)为有机改性物,通过一步法在纳米TiO₂表面嫁接长链烷基官能团得到超疏水TiO₂/DTMS涂层。分析了TiO₂涂层及TiO₂/DTMS涂层的表面润湿性、形貌和化学组成,并对所得超疏水TiO₂/DTMS涂层的自清洁性能、机械及化学稳定性进行了测试。结果表明：超疏水TiO₂/DTMS涂层表面水接触角(water contact angle, WCA)达到159°;以亚甲基蓝粉末作模拟污染物,涂覆有超疏水TiO₂/DTMS涂层的玻璃具有优异的自清洁性能;经机械磨损(10 min)、酸碱液(pH=1、3、5、7、9、11、13)浸泡、高低温(−20、30、60、90、120、150 ℃)处理后超疏水TiO₂/DTMS涂层的WCA仍大于150°,表明其具有优异的机械和化学稳定性,可用于室外防污,如建筑物外墙、玻璃、太阳能电池板等。     

BiOBr/TiO2复合光催化材料的制备及其光催化性能的研究

采用水热法制备了TiO_2、BiOBr、BiOBr/TiO_2复合光催化剂材料,用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、紫外-可见漫反射(UV-Vis)、红外吸收光谱(FTIR)对其进行表征,并以甲基橙为降解物,进行了光催化性能的研究。结果表明:复合材料BiOBr/TiO_2中BiOBr和TiO_2不同的质量比、水热反应温度、水热反应时间、对BiOBr/TiO_2复合光催化剂的光催化性能都有影响,当BiOBr/TiO_2的质量比为1:1、水热反应温度为160℃、水热反应时间12 h,BiOBr/TiO_2复合光催化剂的光催化活性最佳,甲基橙降解率可达97.19%。     

CF4/N2混合物替代SF6/N2的可行性研究

SF6具有良好的绝缘强度,但其全球温室效应指数(GWP)是二氧化碳的23 900倍,因此有必要寻找一种环境友好的绝缘气体替代SF6。从绝缘性能、协同效应和GWP三方面研究了CF_4/N_2混合物替代SF6气体的可行性。研究结果表明:CF_4/N_2混合物的工频击穿电压随气压的升高出现饱和现象;80%CF_4/N_2混合物为最佳混合比例,其绝缘性能约为同条件下纯SF6击穿电压的65%;CF_4/N_2混合物具有协同效应,协同系数在0.2~0.59之间,和SF_6/N_2的协同系数接近;CF_4/N_2混合气体的GWP值随着气体的混合比呈线性关系,80%CF_4/N_2混合物的GWP值比SF_6/N_2低很多。因此,综合考虑绝缘性能、协同效应和GWP,80%CF_4/N_2混合物有希望替代SF_6/N_2气体用于气体绝缘。     

TiO2/SiO2/GQDs双层增透膜的制备及其在太阳能板中的应用

采用溶胶-凝胶法制备了SiO₂ 和TiO₂ 纳米溶胶,采用水热法制备了石墨烯量子点（graphene quantum dots,GQDs）。为进一步提高光伏太阳能板的透光率,设计了一种TiO₂/SiO₂/GQDs双层增透膜结构。探究了薄膜的结构、自清洁性能和增透性能,并进一步讨论了GQDs在增透性中的作用。结果表明,SiO₂-TiO₂/TiO₂-GQDs结构的双层薄膜厚度为120 nm时,太阳能板上的光透过率由未涂敷的85%增加至95%。接触角实验和室外耐环境性能实验测试表明,复合膜层接触角为10°,并具有良好的亲水性和耐环境性能。此外,户外实验结果表明,涂覆该薄膜的太阳能电板发电效率提高6%。由此说明双层增透膜可有效地提高太阳能电池板的光能利用率和使用寿命,可高效地利用太阳能。     

工业化超疏水TiO2涂层的简易制备和性能研究

为探究适合工业化生产用超疏水纳米TiO₂的绿色改性工艺,以饱和脂肪酸A、硅烷B、纳米TiO₂（P25）等为原料制备超疏水TiO₂粉末,与环氧树脂混合后利用喷涂法制备出超疏水涂层。采用扫描电子显微镜、X射线衍射仪、傅里叶变换红外光谱仪和接触角分析仪对超疏水粉末和超疏水涂层表面的形貌和疏水性进行了表征。结果表明：超疏水TiO₂粒子表面具有疏水性基团和微-纳米双重粗糙结构,粒子表面的静态水接触角为158°,滚动角为3°;当超疏水TiO₂与环氧树脂的质量比在3.2～3.5时,超疏水涂层既保持超疏水性,又与基底稳固结合,同时具有自清洁性和可修复性。该工艺操作简单方便,成本低,疏水性好,无需特殊设备,工艺环保,适应工业化生产,可用来大面积制备超疏水涂层,拥有较高的商业价值。     

TiO2/CB-NiCo2O4修饰玻碳电极的制备及其对葡萄糖的电化学测定

利用低温下的水化学生长法合成了镍钴氧化物（NiCo₂O₄）纳米针,因其自组装而表现出立方晶相,再用二氧化钛/炭黑（TiO₂/CB）对NiCo₂O₄表面进行了改性,合成了TiO₂/CB-NiCo₂O₄复合纳米材料.用X射线光电子能谱仪（XPS）、扫描电子显微镜（SEM）、能量色散X射线光谱仪（EDX）图谱对材料的形貌进行了表征,运用循环伏安法（CV）、时间-电流（i-t）曲线法考察了TiO₂/CB-NiCo₂O₄修饰玻碳电极的电化学行为.实验发现：TiO₂/CB-NiCo₂O₄修饰电极对葡萄糖的氧化有良好的电催化性能,其线性范围为0.001~1.780 mmol·L^-1,检测限为0.53 μmol·L^-1（信噪比S/N=3）.将该法用于实际样品中葡萄糖的测定,结果令人满意.     

Effect of La2O3 on microstructure, mechanical and tribological properties of Ni-W coatings

In this paper, a Ni-W-La2O3 composite coating was prepared by the electrodeposition method. Microhardness tester and environmental scanning electron microscope equipped energy dispersive spectroscopy were employed to investigate the microhardness and the surface morphology of the composite coatings respectively, and the high temperature friction behavior and corrosion resistance of the coatings against molten glass were investigated by using a high temperature tribometer. The results show that La2O3 can refine the microstructure effectively, and make the element distribution uniform, which leads to the increase of average microhardness. La2O3 particulates can reduce the friction coefficient between the composite coating and glass during the sliding process at about 973 K largely, and the corrosion resistance of the La2O3 added Ni-W coatings is effectively improved compared with that of the non-added one, furthermore the mechanism of friction-reducing and anti-corrosion is also discussed.     

TiO2微粉对Al2O3-MgO-Cr2O3浇注料性能的影响

马克思的市民社会决定国家理论的形成,经历了一个思想交锋、自我批判、绵延提升直至最终导出唯物史观之创建的逻辑进程。马克思立足于《莱茵报》时期的感性经历,先后运用哲学、历史学和政治经济学的方法和知识对黑格尔理性国家观进行系统的理论清算,纠正了黑格尔的市民社会与国家关系的“历史错位”,首次确立了“社会本体论”原则。市民社会决定国家理论的形成是标志着唯物史观开始诞生的第一命题。分析马克思市民社会决定国家理论的发展脉络和演进逻辑,有利于澄清马克思市民社会理论与唯物史观的内在关联,科学评价市民社会理论在历史唯物主义中的历史地位。     

硫化镉/石墨烯/TiO_2纳米棒阵列的光电化学性能

采用水热法在掺氟导电玻璃(FTO)上生长TiO_2纳米棒阵列。通过电化学伏安法将氧化石墨烯还原并沉积在TiO_2纳米棒阵列上,再经过化学水浴沉积硫化镉,形成Cd S/石墨烯/TiO_2阵列复合材料。用X射线衍射仪、扫描电子显微镜及X射线能量色散仪对样品的晶型、形貌以及成分进行分析。通过电化学工作站表征样品交流阻抗、开路电位、光电流响应及光化学能转换效率。结果表明,复合材料的电荷转移电阻约是未修饰的TiO_2纳米棒阵列的1/17,光电流比未修饰的TiO_2纳米棒阵列提高约2.5倍,在外加电压为-0.6 V时可达到2.2%。     

稀土Sm_2O_3对Mo_2NiB_2基金属陶瓷微观组织和力学性能的影响

以NiB、Mo、Cr、V、Ni等几种粉末为基本原料,并以稀土Sm_2O_3为添加剂,采用真空液相烧结法制备Mo_2NiB_2基金属陶瓷。利用XRD、SEM、EDS、洛氏硬度计和电子万能试验机等研究添加Sm_2O_3对Mo_2NiB_2基金属陶瓷微观组织和力学性能的影响。结果表明,添加0.3%~0.9%的Sm_2O_3后,金属陶瓷晶粒明显细化,组织分布更加均匀,材料的硬度和抗弯强度也得到提高。当Sm_2O_3添加量为0.6%时,所得试样的晶粒最为细小,晶粒尺寸大致在0.8~3.0μm,材料的力学性能最佳,其硬度和抗弯强度分别达到HRA88.7和1550 MPa。     

Fe2O3/TiO2复合光催化剂的制备及其表征

以硝酸铁为铁源、硫酸钛为钛源,采用微乳液法制备Fe2O3/TiO2复合光催化剂,并用SEM、FTIR、XRD、BET和甲基橙脱色率对复合光催化剂进行表征。结果表明,铁与钛的摩尔比为1∶3、煅烧温度为500℃以及煅烧时间为1.5h时,所制Fe2O3/TiO2复合光催化剂疏松多孔、颗粒细小且热稳定性高,经紫外光照15min后,其对甲基橙的降解率为99.7%,与相同条件下制备的TiO2相比,Fe2O3/TiO2复合光催化剂具有更好的光催化活性和更大的比表面积。     

Preparation and photocatalytic activity of Cu-doped TiO2/SiO2

Cu²⁺-doped nanostructured TiO₂-coated SiO₂ (TiO₂/SiO₂) particles were prepared by the layer-by-layer assembly technique and their photocatalytic property was studied. TiO₂ colloids were synthesized by the sol-gel method using TiOSO₄ as a precursor. The experimental results showed that TiO₂ nanopowders on the surface of SiO₂ particles were well distributed and compact. The amount of TiO₂ increased with the increase in coating layers. The shell structure appeared to be composed of anatase titania nanocrystals at 550°C. The 2-layer coated TiO₂ particles on the surface showed a higher degradation rate compared with all the different-layer samples. The photocatalytic activity of Cu²⁺-doped TiO₂/SiO₂ was higher than that of undoped TiO₂/SiO₂. The optimum dopant content was about 0.10wt%.     

TiO_2-SnO_2异质结纳米棒催化剂高效光降解甲基橙

采用水热法合成SnO_2-TiO_2异质结纳米棒光催化剂,该材料具有独特的纳米棒和异质结结构,可有效阻止光生电子和空穴的复合,通过光电流、X射线光电子能谱(XPS)、X射线衍射(XRD)、透射电子显微镜(TEM)等表征手段证明其异质结功效.该材料作为光催化剂,使用时能大幅提升紫外光降解甲基橙(MO)的效率.     

镀镍碳纳米管对Mo_2FeB_2基金属陶瓷组织与性能的影响

采用化学镀法对碳纳米管进行表面镀镍处理,再利用真空液相烧结法制备出以镀镍碳纳米管为增强体的Mo_2FeB_2基金属陶瓷复合材料,借助SEM、EDS、硬度计等研究了添加镀镍碳纳米管对Mo_2FeB_2基金属陶瓷微观组织及力学性能的影响。结果表明,添加适量镀镍碳纳米管可细化Mo_2FeB_2基金属陶瓷组织并控制其孔洞尺寸及数量,显著提高其硬度及断裂韧性。当镀镍碳纳米管添加量为0.5%时,所得试样的晶粒最为细小,晶粒尺寸大约为1.2μm,材料的力学性能最佳,其硬度和断裂韧性分别达到1228.4HV0.3及15.90MPa·m12,相应增韧机制为裂纹偏转、桥接增韧、撕裂棱增韧和微孔洞增韧。