音频法检测铸件的球化级别

介绍了音频法检测铸件球化级别的原理及试验结果。     

钨合金白口铸铁共晶碳化物团球化的研究

针对钨合金白口铸铁脆性大,应用于承受冲击载荷的工况下安全性差,使用范围受到严格限制,探讨了碱金属元素钾、钠对钨合金白口铸铁组织和性能的影响。结果表明:钨合金白口铸铁经钾、钠处理后,共晶碳化物由网状分布变为团块状甚至团球状分布,碳化物明显细化,分布均匀性增大,分析了共晶碳化物团球化的机理。碳化物形态的改善,导致钨合金白口铸铁的冲击韧性和抗冲击磨损能力明显提高。     

Properties of Cross-Rolled Low Alloy White Cast Iron Grinding Ball

Lowalloy white cast iron has high hardness andwear-resistance ;however ,the material has lowduc-tility ,because the carbideinthe structureis distrib-uted in the formof continuous network, which li m-its its application. Therefore , the method to i m-prove the toughness of this material has attractedthe interests of the researchers worldwide . The ex-peri mental results showed that when white cast ironis hot deformed, the network structure of carbidebreaks and becomes independent blocks , which…     

等温球化处理过程中热变形白口铸铁中碳化物的ostwald长大现象

对亚共晶白口铸铁经高温形变后所获得的碳化物在等温球化过程中球化长大进行了研究。结果表明：碳化物是以大粒子吞食小粒子和短棒状碳化物溶断及律端溶解自身球化的方式球化长大的，其特征是碳化物尺寸逐渐增大，数目逐渐减少，碳化物长大速度符合经验公式V＝1．172×10-3／（0．326＋0．0064t）2，而其含量保持不变，长大规律符合ostwald熟化规律。     

铸件中夹杂缺陷成因分析及改进对策

针对铸件中容易发生的缺陷——夹杂，分析其特征、危害以及形成的原因，从而探讨抑制夹杂缺陷的对策。     

球铁,蠕铁和高锰低硅铸铁钢锭模工业试验

一、前言我公司年产钢60多万吨,全部采用模铸工艺,而且至今还一直使用普通灰口铸铁钢锭模。由于这种材质的钢锭模使用寿命短,模耗高,为此我们试制了球墨铸铁、蠕墨铸铁和高锰低硅铸铁三种材质的沸腾钢钢锭     

铸件中夹杂缺陷成因分析及改进对策

针对铸件中容易发生的缺陷——夹杂,分析其特征、危害以及形成的原因,从而探讨抑制夹杂缺陷的对策。     

铸件中缩孔缺陷成因分析

通过对铸铁材料的概述，详细分析了铸件中常见缺陷——缩孔的特征、危害以及形成原因，从而探讨抑制此类缺陷的对策。     

低合金白口铸铁共晶碳化物团球化工艺的研究

低合金白口铸铁是一种耐磨性能优良的铸铁材料,但其组织中共晶碳化物呈连续网状分布,削弱了基体的连续性,导致铸铁脆性过大。我们探讨了复合变质处理和热变形处理对共晶碳化物团球化的影响,同时还研究了共晶碳化物团球化对低合金白口铸铁机械性能和耐磨性的影响,结果表明,共晶碳化物团球化有利于白口铸铁韧性和耐磨性的大幅度提高。