纳米Al_2O_3对等离子喷涂ZrC-ZrSi_2复合涂层结构与性能的影响

大气等离子喷涂ZrC-ZrSi_2陶瓷涂层的孔隙率高,提高等离子喷涂ZrC-ZrSi_2陶瓷涂层的致密度成为亟待解决的问题。在TC4钛合金表面采用大气等离子喷涂ZrC-ZrSi_2复合粉和ZrC-ZrSi_2-Al_2O_3复合粉分别制备两种复合涂层。研究纳米Al_2O_3对等离子喷涂ZrC-ZrSi_2复合涂层组织结构与性能的影响。结果表明,添加了Al_2O_3的ZrC-ZrSi_2复合涂层的组织结构更为致密,相较于ZrC-ZrSi_2复合涂层具有更优异的力学性能。熔点相对较低的Al_2O_3能够在喷涂焰流中先熔化,熔融态的Al_2O_3能够填充在ZrC-ZrSi_2复合涂层的孔洞处,提高复合涂层的致密度,改善涂层的力学性能。研究成果可为提高大气等离子喷涂制备含高熔点组分复合涂层的致密度提供指导。     

陶瓷颗粒含量对Cr-Al_2O_3复合镀活塞环摩擦磨损性能的影响

为了研究陶瓷颗粒含量对Cr-Al_2O_3复合镀活塞环摩擦磨损性能的影响,采用镀铬活塞环和4种Al_2O_3陶瓷颗粒含量不同的Cr-Al_2O_3活塞环与CuNiCr合金铸铁缸套组成配对副,对其进行摩擦磨损试验,对比各配对副摩擦因数及磨损量。结果表明,镀铬活塞环-缸套配对副摩擦因数较大,约为其它4种含Al_2O_3陶瓷颗粒的Cr-Al_2O_3活塞环-缸套配对副的1.2倍,磨损也比其它4种配对副严重,摩擦副的表面均已经发生严重的粘着磨损现象;其它4种含陶瓷颗粒的Cr-Al_2O_3活塞环-缸套配对副的摩擦因数相近,缸套的磨损量也相近,活塞环的磨损量随着陶瓷含量的增加而先减小后增加。陶瓷颗粒的镶嵌提高了活塞环的耐磨性能,陶瓷含量过少,活塞环表面承载能力不足;陶瓷颗粒含量过多,陶瓷颗粒易脱落,这些都会增大活塞环的磨损量。     

添加CeO_2对MoS_2基复合涂层摩擦学性能的影响

针对MoS_2基复合涂层耐磨性差和承载能力低的问题,以不同含量(质量分数)的CeO_2作为添加剂,采用喷涂法在GCr15钢表面制备MoS_2基复合涂层。利用摩擦磨损试验机和划痕仪分别研究涂层摩擦磨损性能和结合强度,并借助金相显微镜对涂层磨损形貌进行表征。结果表明:添加适量CeO_2可以改善涂层的摩擦磨损性能,其最佳含量为2%,此时摩擦因数和磨损量均最小,分别为0.232和0.011 3 mm~3;同时结合强度从22 N提高到28.29 N。涂层磨损量随载荷的增大而增大;而载荷小于8 N时,涂层的摩擦因数随载荷的增大而减小,当载荷大于8 N时,摩擦因数又有回升趋势。添加稀土后涂层的承载能力有明显提高。未添加稀土时,涂层产生严重剥离,并发生磨粒磨损;添加2%CeO_2后,涂层发生轻微磨粒磨损,耐磨性得到显著提高。     

铝合金表面MoS2/Al2O3复合涂层制备及减摩性能研究

铝合金表面减摩涂层设计和制备是改善铝合金构件摩擦性能的关键技术之一。对于目前铝合金结构件易磨损的问题,本研究采用微弧氧化一步法在6063铝合金表面原位合成纳米MoS2,制备具有减摩作用的MoS2/Al2O3复合陶瓷涂层;讨论了硫盐浓度对涂层成分、形貌及摩擦性能的影响,分析了涂层减摩机理。结果表明：通过微弧氧化在6063铝合金表面成功制备出了含有MoS2的自润滑复合陶瓷涂层;涂层的摩擦系数随着硫盐浓度的升高呈现先下降后上升的趋势,当电解液中硫盐浓度为15g/L时涂层的摩擦系数为0.15,较常规微弧氧化涂层降低了76%。涂层中的MoS2分布在涂层的表面和内部,在与摩擦副接触与挤压的作用下形成均匀分布的MoS2润滑膜,表现出良好的减摩性能。     

Al2O3-TiO2复相陶瓷涂层在动态LBE中的耐腐蚀行为

目的分析研究Al_2O_3-TiO_2复相陶瓷涂层在高温流动铅铋合金中的耐腐蚀行为。方法以纯Ti粉末、Fe Al粉末、CrFe粉末为原料制得复合粉末,在CLAM钢基材表面上采用热喷涂-激光原位合成复合工艺制备了Al_2O_3-TiO_2复相陶瓷涂层。试样在500℃,流速为0.3 m/s的液态铅铋合金中进行了时长1000 h的动态腐蚀实验,分别采用X射线衍射仪(XRD)、扫描电镜(SEM)、能谱仪(EDS)等分析测试手段对涂层试样在动态LBE中的耐腐蚀行为进行了研究表征。结果在CLAM钢基材表面制备的Al_2O_3-TiO_2复相陶瓷涂层表面形貌整体较腐蚀前仍保持完好,涂层物相成分保持稳定,截面分析显示铅铋合金在腐蚀过程在涂层中未见渗透;而没有涂层保护的CLAM钢基材在腐蚀后表面发生明显的氧化腐蚀现象,生成结构疏松的Fe3O4氧化层,铅铋合金在氧化层中有扩散分布。结论通过火焰热喷涂-激光原位合成复合工艺在CLAM钢表面制备得到的Al_2O_3-TiO_2复相陶瓷涂层在高温流动的铅铋合金腐蚀条件下组织结构稳定,具有良好的适用性,能有效地阻止高温流动铅铋合金对CLAM钢基体材料的腐蚀。     

Ba(Mg1/3Ta2/3)O3热障涂层的制备及抗热震性能研究

本文以BaCO₃、MgO、Ta₂O₅为原料,采用固相反应法合成了Ba(Mg_1/3Ta_2/3)O₃(简称BMT)陶瓷粉末,利用大气等离子喷涂技术制备了BMT/YSZ双层陶瓷涂层。利用XRD、SEM和金相显微镜检测了BMT粉体及涂层的物相组成和显微结构。采用水淬法考核了涂层的抗热震性能。结果表明：1450℃下煅烧4h可合成出具有复合钙钛矿结构的BMT粉末,粉末具有良好的高温相结构稳定性。等离子喷涂制备的BMT/YSZ涂层组织致密,涂层系统中各界面结合紧密。涂层在室温至1150℃间热震9次后发生片状剥落,剥落位置位于BMT层间,BMT材料低的断裂韧性和第二相Ba₃Ta₅O₁₅的存在是导致涂层失效的主要原因。     

纳米TiO_2含量对等离子喷涂Al_2O_3/TiO_2涂层耐磨性的影响

采用大气等离子喷涂设备在H13热作模具钢表面制备了不同纳米TiO_2含量的Al_2O_3/TiO_2陶瓷复合涂层,并应用扫描电镜(SEM)、X射线衍射仪(XRD)、显微硬度计、摩擦磨损试验机等研究了陶瓷复合涂层的微观形貌、物相组成、显微硬度及摩擦磨损性能。结果表明,不同纳米TiO_2含量的Al_2O_3/TiO_2陶瓷涂层均为层片结构,存在一定的孔隙和裂纹,纳米TiO_2添加可以改善涂层表面质量。XRD图谱显示陶瓷涂层主要由α-Al_2O_3、γ-Al_2O_3和Rutile-TiO_2相组成,Al_2O_3再结晶过程中部分α-Al_2O_3转变为γ-Al_2O_3,且再结晶过程发生晶粒细化。涂层显微硬度平均值为1153 HV0.2。纳米TiO_2添加可以降低涂层摩擦因数,但其含量对涂层耐磨性影响不明显。     

纳米Al2O3改性三聚氰胺-脲醛自修复微胶囊的制备及应用

以纳米Al_2O_3改性三聚氰胺-脲醛树脂(MUF)为壁材,环氧树脂为芯材,采用原位聚合法合成了微胶囊,并采用光学显微镜(OM)、扫描电子显微镜(SEM)、红外光谱仪(FTIR)、X射线光电子能谱分析仪(XPS)、热重分析仪(TGA)等对其表面形貌、结构及热性能等进行了表征和测试;将改性后的微胶囊加入自修复环氧树脂涂层中,并对其热性能、力学性能、自修复性能及电化学性能进行测试。结果表明,当芯壁比为1.5:1、纳米Al_2O_3质量分数为4.5%时,纳米Al_2O_3在壁材中均匀分布,微胶囊的表面粗糙度和热稳定性均增加。当涂层中改性微胶囊质量分数为5%时,涂层的热稳定性提高,且涂层的拉伸强度、弯曲强度、冲击强度及粘结强度分别提高了111.9%、55.1%、10.6%和51.9%;制备的涂层具备较好的自修复性能;涂层的耐腐蚀性能随着微胶囊质量分数的增大而增强。     

Ni2Cr(BO3)O2涂层的制备及其红外发射性能

通过喷雾造粒和高温焙烧制备Ni_2Cr(BO_3)O_2粉末后利用等离子喷涂得到一种高红外发射涂层,并研究了该种涂层的红外发射性能。SEM观察涂层的表面、断面形貌,发现涂层与基体结合紧密、无脱落;XRD对焙烧后的粉末物相组成进行了表征,主要以Ni_2Cr(BO_3)O_2为主。对涂层红外波段发射率的测试表明,在0.76~2.5μm波段的发射率为0.896、2.5~14μm波段发射率为0.925,具有优异的红外发射性能。Ni_2Cr(BO_3)O_2晶胞内的畸变、非对称性以及电子转移跃迁是导致Ni_2Cr(BO_3)O_2这种材料具有高红外发射率的主要原因。Ni_2Cr(BO_3)O_2涂层能够经受37次"900℃~水冷"热震循环。该种涂层由于其高红外发射性能、优异的耐热震性能和热稳定性能而具有较高的实用价值。     

Cu-Al合金薄板内氧化析出相Al_2O_3晶型及分布

Al含量为0.50%(质量分数)的Cu-Al合金薄板在900℃下内氧化25 h制备Cu-Al_2O_3薄板复合材料,并用富集萃取法提取Cu-Al_2O_3复合材料中的Al_2O_3相。利用TEM分析了Cu-Al_2O_3薄板中的Al_2O_3相的种类、分布、与Cu基体的界面关系,用X射线衍射和TEM研究了萃取粉末的组成。结果表明,Cu-Al薄板内氧化法所得的Cu-Al_2O_3复合材料的析出相主要为γ-Al_2O_3,有少量的α-Al_2O_3和θ-Al_2O_3相存在。析出相Al_2O_3颗粒弥散分布在Cu基体上,且析出相γ-Al_2O_3与Cu基体完全共格;Cu-Al_2O_3薄板复合材料从表层至深约0.5 mm处,Al_2O_3颗粒粒径逐渐减小,从14 nm减小到5 nm,颗粒间距逐渐增大,从10 nm增加到15 nm。     

Mechanical and tribological performance of Al2O3-TiO2 coatings elaborated by flame and plasma spraying

Mechanical properties and wear rates of Al₂O₃-13 wt.% TiO₂ (AT-13) and Al₂O₃-43 wt.% TiO₂ (AT-43) coatings obtained by flame and atmospheric plasma spraying were studied. The feed stock was either ceramic cords or powders. Results show that the wear resistance of AT-13 coatings is higher than that of AT-43 and it seems that the effect of hardness on wear resistance is more important than that of toughness. Additionally, it was established that, according to conditions used to elaborate coatings and the sliding tribological test chosen, spray processes do not seem to have an important effect on the wear resistance of these coatings.     

MoS2颗粒表面包覆Al2O3及其在镀层中的应用

采用非均匀形核法将Al2O3包覆到MoS2颗粒表面,提高颗粒的亲水性能。研究了溶液pH值、Al(NO3)3的摩尔浓度和预处理工艺对包覆率的影响;采用SEM及EDS分析了包覆前后MoS2颗粒的微观形貌和表面成分;通过测量接触角研究了颗粒表面的亲水性。结果表明,颗粒表面均匀包覆了一层Al(OH)3;溶液pH值对包覆率的影响最大,Al(NO3)3的摩尔浓度次之。最佳工艺为:溶液pH值为5.5,Al(NO3)3浓度为0.15mol/L,预处理过程不添加表面活性剂。随着包覆率的提高,MoS2颗粒的亲水性提高。利用包覆Al2O3的MoS2制得了Ni-P-MoS2化学复合镀层,提高了镀层中沉积粒子的均匀致密性。     

过渡材料对等离子喷涂Al2O3梯度陶瓷涂层性能影响

针对Al2O3陶瓷涂层结合强度低、孔隙率高的实际,选择NiAl金属间化合物和金属铜粉作为过渡材料,利用等离子喷涂制备Al2O3梯度陶瓷涂层,并对梯度涂层进行组织形貌观察,测试结合强度和孔隙率.结果表明,梯度涂层的组织表现出宏观的不均匀性和微观连续性的分布特征,NiAl和Cu是金属基体与Al2O3涂层之间过渡层的理想材料,可以有效地提高涂层的结合强度,而Cu-Al2O3梯度涂层又比NiAl-Al2O3梯度涂层结合强度高;梯度涂层的孔隙率远低于双涂层的孔隙率,在Cu-Al2O3梯度涂层中随Al2O3含量的增加,涂层的孔隙率降低,而且孔隙率低于NiAl-Al2O3梯度涂层.     

Effect of applied current on the electrodeposited Ni-Al2O3 composite coatings

Nano-sized Al₂O₃ ceramic particles (50 nm) were co-deposited with nickel using electrodeposition technique to develop composite coatings. The coatings were produced in an aqueous nickel bath at different current densities and the research investigated the effect of applied current on microstructure and thickness of the coatings. The variation in some mechanical properties such as hardness, wear resistance, and the adhesive strength of the composite coatings is influenced by the applied current and this was also studied. The morphology of the coatings was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. The hardness, wear resistance, and bond strength of the coatings were evaluated by Vickers micro-hardness test, pin-on-disc test, and tensile test, respectively. Results showed that the Al₂O₃ particles were uniformly distributed in the coatings, and the coatings deposited at a current density of 0.01 A/cm² was most favorable in achieving a maximum current efficiency which causes the co-deposition of a maximum amount of Al₂O₃ particles (4.3 wt.%) in the coatings. The increase in Al₂O₃ particles in the coatings increased the mechanical properties of the Ni-Al₂O₃ composite coatings by grain refining and dispersion strengthening mechanisms.     

Tribological properties of Cr- and Ti-doped MoS2 composite coatings under different humidity atmosphere

Solid-lubricant MoS₂ coatings have been successfully applied in high vacuum and aerospace environments. However, these coatings are very sensitive to water vapor and not suitable for applications in moist environments. In this work, Cr- and T-doped MoS₂ composite coatings were developed. The results demonstrated that these composite coatings are promising for applications in high humidity environments.MoS₂-Cr and MoS₂-Ti composite coatings with different Cr or Ti content were deposited on high speed steel substrate by unbalanced magnetron sputtering. The composition, microstructure, and mechanical properties of the as-deposited MoS₂-metal composite coatings were analyzed by energy dispersive analysis of X-ray (EDX), X-ray diffraction (XRD), and nanoindentation experiments. The tribological properties of the coatings were evaluated against an alumina ball under different relative humidity atmosphere using a ball-on-disc tribometer. The MoS₂-Cr and MoS₂-Ti coatings showed a maximum hardness of 7.5 GPa and 8.4 GPa at a dopant content of 16.6 at.% Cr or 20.2 at.% Ti, respectively. The tribological test results showed that, with a small amount of Cr and/or Ti doping, the tribological properties of MoS₂ coatings under humid atmosphere could be significantly improved. The optimum doping level was found to be around 10 at.% for both MoS₂-Cr coatings and MoS₂-Ti coatings to show the best tribological properties, with both the lowest friction coefficient and wear rate. The excellent tribological properties of the MoS₂-Cr and MoS₂-Ti coatings with an appropriate metal doping level in moist atmosphere are found due to their ability to form stable transfer layer on the surface of the counterbody, which supplies lubrication for the contact surface.     

Microstructure and mechanical properties of Al2O3-Cr2O3 composite coatings produced by atmospheric plasma spraying

Al₂O₃, Al₂O₃-Cr₂O₃ and Cr₂O₃ coatings were deposited by atmospheric plasma spraying. Phase composition of powders and as-sprayed coatings was determined by X-ray diffraction. Electron probe microanalyzer was employed to investigate the polished and fractured surface morphologies of the coatings. Mechanical properties including microhardness, fracture toughness and bending strength were evaluated. The results indicate that the addition of Cr₂O₃ is conducive to the stabilization of α-Al₂O₃. Compared with the pure Al₂O₃ and Cr₂O₃ coatings, Al₂O₃-Cr₂O₃ composite coatings show lower porosities and denser structures. Heterogeneous nucleation of α-Al₂O₃ occurs over the isostructural Cr₂O₃ lamellae and partial solid solution of Al₂O₃ and Cr₂O₃ might be occurring as well. Furthermore, grain refining and solid solution strengthening facilitate the mechanical property enhancement of Al₂O₃-Cr₂O₃ composite coatings.     

MoS2 coated with Al2O3 for Ni-MoS2/Al2O3 composite coatings by pulse electrodeposition

The MoS₂ powders were coated with Al₂O₃ (5 wt.%) through controlling hydrolysis of Al (NO₃)₃·9H₂O. MoS₂ powder coated with Al₂O₃ was written as MoS₂/Al₂O₃ hereinafter. MoS₂/Al₂O₃ powders were put into Ni plating electrolyte bath. Cetyltrimethylammonium bromide (CTAB) — the surfactant was also put into the bath. The experiment proves that MoS₂/Al₂O₃ particles were absorbed onto the Ni plate. The amount of MoS₂/Al₂O₃ deposited on Ni plate rises with the increasing concentration of MoS₂/Al₂O₃ in the bath. The microhardness, micro-surface, phase and the tribological property of the MoS₂/Al₂O₃ multi-plating coating were measured and analyzed. The performances of microhardness and wear resistance of the Ni-MoS₂/Al₂O₃ composite are better than those of Ni-MoS₂ composite.     

等离子喷涂Cu-Al2O3梯度涂层的组织与耐磨性分析

针对纯陶瓷涂层由于结合强度低、孔隙率高、影响涂层耐磨性的实际,用等离子喷涂法制备了Cu-Al2O3梯度涂层,用电子扫描显微镜(SEM)、金相显微镜等手段对涂层进行微观组织和成分分析,用自制销盘式固定磨料磨损试验机,检测了Cu-Al2O3梯度涂层的耐磨料磨损性能.结果表明,采用等离子喷涂法制备的Cu-Al2O3梯度涂层无明显的组织突变和宏观层间界面,涂层的组织表现出宏观不均匀性和微观连续性分布特征;梯度涂层中当Al2O3含量(质量分数,%)达到80%时(GC6),涂层的耐磨性最高,约为基体的3倍,随着Al2O3含量继续增大,纯陶瓷涂层(GC7)的耐磨性有所下降.     

In-situ TiB2 and Al2O3 formation by DC plasma spraying

In-situ plasma spraying (IPS) is a promising process to fabricate composite coatings with in-situ formed thermodynamically stable phases. In the present study, mechanically alloyed Al-12Si, B₂O₃ and TiO₂ powder was deposited onto an aluminum substrate using atmospheric plasma spraying (APS). It has been observed that, during the coating process, TiB₂ and Al₂O₃ are in-situ formed through the reaction between starting powders and finely dispersed in hypereutectic Al-Si matrix alloy. Also, obtained results demonstrate that in-situ reaction intensity strongly depends on spray conditions.