Elastic Modulus of 304 Stainless Steel Coating by Cold Gas Dynamic Spraying

 304 stainless steel coating was deposited on the IF steel substrate by cold gas dynamic spraying (CGDS), and the elastic modulus of the 304 stainless steel coating was studied. The elastic modulus of cold sprayed 304 stainless steel coating was measured using the three-point bend testing and the compound beam theory, and the other mechanic parameters (such as the equivalent flexural rigidity and the moment of inertia of area) of the coatings were also calculated using this compound beam theory. It is found that the calculated results using the above methods are accurate and reliable. The elastic modulus value of the cold sprayed 304 stainless steel coating is 1179×105 MPa, and it is slightly lower than the 304 stainless steel plate (about 2×105 MPa). It indicates that the elastic modulus of the cold sprayed coatings was quite different from the comparable bulk materials. The main reason is that the pores and other defects are existed in the coatings, and the elastic modulus of the coatings also depends on varies parameters such as the feed stock particle size, porosity, and processing parameters.     

Wear Mechanism of Iron-based Alloy Coating by Arc Spraying

The arc spraying technique was adopted to prepare three types of iron-based coatings including 08Mn2Si, 4Cr13,and 65Mn.Meanwhile,the metallurgical microscope and scanning electron microscope (SEM)were used to analyze the microstructure of these coatings.Besides,a DPT-5 dye penetrant was painted on the surface of the coat-ings to simulate the oil fluid,so as to observe its penetration in the pore structures.The MMU-5G end-face high-temperature wear tester was used to carry out wear-resistance tests on these coatings and give comparison with grey cast irons.The experimental results showed that the 4Cr13 coating exhibited the best wear resistance under oil batch lubrication condition.According to the study of these coating structures,it was discovered that three coatings pres-ented topology-like structures due to the accumulation of flat particles on the matrices.Meanwhile,it was found that zonal oxides were mixed in particles with some unmolten particles,pores,and cracks.Besides,the larger pores were mutually connected by gap-like pores.The existence of FeO in the coating and the pore structures keep oil in acted antifriction effects.     

热喷涂Fe基非晶合金涂层的研究现状

综述了超音速火焰喷涂(HVOF),等离子喷涂(PS)技术的性能特征,以及运用热喷涂技术制备Fe基非晶涂层的发展历史与现状。从非晶合金涂层的高硬度、耐磨性及腐蚀性能等方面阐述了非晶合金涂层的优越性,对新型Fe基非晶涂层的形成机理进行研究,探讨采用超音速火焰喷涂技术制备高质量非晶合金涂层的关键因素。并展望了采用热喷涂技术制备非晶合金涂层的未来发展趋势。     

火焰喷涂超高分子聚乙烯涂层工艺及性能研究

以结晶度为衡量指标,通过正交试验确定了火焰喷涂超高分子聚乙烯（UHME-PE）的较优工艺参数,采用氮气侧吹冷却技术使涂层的结晶度降低了13.93%,涂层结合强度提高了16.42%;对UHME-PE涂层耐磨粒冲蚀机理进行了初步探讨。     

Structural and Chemical Microinhomogeneity of the High-Entropy TiVZrNbHfTa Coating

Powder Metallurgy and Metal Ceramics - The structural and chemical microinhomogeneity of the high-entropy TiVZrNbHfTa coating is studied. Electron microprobe analysis shows that the content of...     

等离子喷涂氧化铝涂层的结构与性能研究

采用等离子喷涂技术 ,在 Fe Cr Al RE合金基体表面制备铝钛涂层和氧化铝涂层 ,与浸渍法制备的氧化铝涂层进行比较。利用 XRD、SEM、BET和超声振动等分析测试技术 ,对涂层的微观结构与表面特性进行研究。结果表明 ,加入适量的 Ce O2 、L a2 O3 、Zr O2 、Si O2 后 ,氧化铝喷涂涂层的表面组成相主要保持为 γ- Al2 O3 ,其蜂窝状多孔结构上堆积了大量弥散分布的纳米微粒 ;这种复合结构既保证了涂层与载体牢固的结合 ,表现出优于氧化铝浸渍涂层的抗振性与抗热震性 ,又使得涂层的几何比表面达到 32 .1m2 / g,大大超过铝钛喷涂涂层。因此 ,可用等离子喷涂工艺制备氧化铝涂层 ,作为承载活性组分的分散层 ,用于摩托车的金属载体排气催化剂     

超音速火焰喷涂WC-12Co涂层工艺优化

为了进一步优化JP5000超音速火焰喷涂WC-12Co涂层的制备工艺,本文采用四因素三水平正交实验方法研究了喷涂距离、煤油流量、氧气流量和送粉量等四个主要工艺参数对WC-12Co涂层孔隙率和显微硬度的影响。结果表明:煤油流量是影响涂层孔隙率和显微硬度的最显著因素,氧气流量与喷涂距离次之,送粉量的影响较小;本次试验得到的优化工艺参数为喷涂距离380mm、煤油流量22.5L/h、氧气流量2050SCFH、送粉量5.5r/min。在此工艺参数下制备的WC-12Co涂层,其孔隙率为0.33%,显微硬度为1392HV300。     

喷涂工艺对MCrAlY涂层组织影响

采用超音速、爆炸喷涂工艺制备钢铁炉辊用MCrAlY涂层,借助XRD、SEM和EDS等手段分析了涂层组织。结果显示：超音速制备涂层中Cr元素含量比粉末成分偏高,Al、Y元素降低,可能在喷涂过程中元素烧损,形成的氧化物在喷涂沉积过程被吹飞,未沉积到涂层中。XRD分析结果显示涂层由Co基固容体、Al,Co、Cr7C3、TaC等相组成。涂层致密,孔隙率低,显微硬度大,结合强度高。相对超音速工艺制备涂层,爆炸喷涂工艺制备的涂层中除铝元素外,分布较均匀,涂层致密度较低,涂层相对显微硬度较高,结合强度二者一致。     

等离子喷涂FeCrMoSnPBSiC非晶合金涂层的结构和性能

 将软磁非晶合金FeCrMoSnPBSiC粉末作为喷涂材料,用大气等离子喷涂法在Q235钢板表面制备非晶态合金涂层。结果表明,该非晶态合金涂层组织致密均匀,具有较高的硬度,平均显微硬度为HV01 644,涂层与基材结合强度超过25 MPa,而且涂层具有较高的热稳定性和较好的耐腐蚀性能,起始晶化温度约516 ℃,在5%NaCl溶液中具有钝化作用。     

溶胶 - 凝胶法制备 TiO2 及其冷喷涂性能研究

冷喷涂陶瓷涂层的现有研究表明, 大部分商业陶瓷粉末不适合用于冷喷涂, 而实验室制备的纳米团聚粉末 更易于冷喷涂。 溶胶 - 凝胶法是制备纳米 TiO2 最常用的方法之一, 具有工艺简单、 重复性高、 反应易控制等优点, 而且可以通过实验参数的改变从分子水平对反应进行控制, 从而获得结构形态各异的纳米粒子。 本文采用基于钛 酸四正丁酯水解反应的溶胶-凝胶法制备纳米锐钛矿TiO2, 研究粉末的微观结构并考察其冷喷涂性能, 在此基础上, 分析原料粉末性能对其冷喷涂性能的影响。 研究结果表明, 与商业 TiO2 粉末相比, 溶胶 - 凝胶法制备的 TiO2 粉 末具有良好的冷喷涂工艺适应性。 溶胶 - 凝胶法制备的 TiO2 粉末微观结构为不规则形, 经过热处理后由无定形态 转变为锐钛矿相。 冷喷涂 TiO2 涂层晶体结构及涂层内部 TiO2 颗粒的微观形貌均与溶胶 - 凝胶 TiO2 粉末保持一致。 冷喷涂 TiO2 涂层的光催化活性受原始喷涂粉末影响, 当原始喷涂粉末的光催化活性高时, 冷喷涂 TiO2 涂层的光 催化活性也较高。     

Experimental Study on NiCrAl Coating Prepared by Electromagnetically Accelerated Plasma Spraying

Theoretical analysis of the electromagnetically accelerated plasma spraying(EMAPS)by self-developed is carried out.Governing equation of the plasma under dynamic loading conditions is derived.The plasma velocity as a function of time and the length of electrode are also obtained.NiCrAl coating is prepared on medium carbon steel substrate by EMAPS device.Microstructure and hardness of the coating are analyzed with scanning electron microscope(SEM)and hardness tester respectively.     

等离子喷涂NiCrAlYi可磨耗封严涂层的动态应力测试

采用独特的平面应变动态测量方法,在线测量了等离子喷涂NiCrAlY涂层过程中试样的动态残余应变及其分布,获得了喷涂热应力随喷涂次数以及涂层厚度的变化规律.实验结果表明,本试验方法在线测试系统的置信度达到98%;在本实验条件下,随着喷涂循环遍数的增多,涂层厚度的增加,涂层的结合强度在不断减小,而在线测得的涂层动态热应力的累积则有不断增大的趋势,最终将导致涂层脱落.     

FeCrBSiC电弧喷涂层磨损及热腐蚀性能研究

设计开发了一种FeCrBSiC粉芯丝材,采用电弧喷涂技术在Q235钢基体上制备相应涂层,通过XRD、SEM、磨粒磨损试验机及高温箱式电阻炉等对其微观组织结构、磨粒磨损及热腐蚀行为进行表征,同时与工程中广泛应用的NiCrTi涂层进行了对比研究.结果表明,涂层均具有热喷涂典型的层状结构,且较为致密,孔隙率低于3％; Fe基涂层组织更为均匀,其氧化物含量显著低于Ni基涂层.所设计Fe基涂层平均显微硬度约为1107.3HV0.1,其耐磨性也更为优异,达到Ni基涂层4倍以上.两种涂层在650℃时的热腐蚀动力学曲线均呈抛物线形式,表面生成连续致密的氧化膜阻止了腐蚀介质向涂层内部的渗透,能够对基体起到有效的防护作用.     

氧化钽喷涂及涂层熔炼实验

液态铈非常活泼,与很多涂层都发生反应。将钽坩埚表面氧化后熔炼铈已有比较满意的结果,但在石墨坩埚表面喷涂Ta2O5涂层的研究报道却很少。本文总结了石墨坩埚表面等离子及火焰喷涂Ta2O5涂层工艺。在大气中通过热震试验考核了氧化钽涂层相稳定性,在真空感应加热环境下对火焰喷涂氧化钽涂层进行了进一步的热震稳定性考核,采用SEM分析了涂层表面微观形貌,同时采用XRD技术分析了加热前后氧化钽涂层的组成变化,分析表明,火焰喷涂能够制备单一的Ta2O5涂层。石墨坩埚表面Ta2O5涂层熔炼实验表明,液态铈不侵蚀Ta2O5涂层。     

Flame Pyrolysis Spraying of Alumina-Yttria Ceramic Coating

Ｆｉｇ．１Ｓｃｈｅｍａｔｉｃｄｉａｇｒａｍｏｆｔｈｅｔｅｓｔｅｑｕｉｐｍｅｎｔ（１）ｃｏｍｐｒｅｓｅｄａｉｒ；（２）ｅｔｈａｎｏｌｓｏｌｕｔｉｏｎ；（３）ｆｌｏｗｍｅｔｅｒ；（４）ｐｒｅｓｕｒｅｇａｕｇｅ；（５）ｓｐｒａｙｎｏｚｌｅ；（６）ｓｔａｉｎ...     

等离子喷涂La_(0.8)Ca_(0.2)CrO_3高发射率涂层研究

本文以氧化镧、氧化钙、氧化铬为原料,按分子式La0.8Ca0.2Cr O3进行配料,球磨后,采用固相合成法制备原始粉末,再经喷雾干燥处理,将其制备成团聚体粉末,并将粉末粒度分布范围控制在20~60μm,采用等离子喷涂法在高温合金基体表面制备高发射率涂层。采用IRE-2型红外辐射仪对其全波段发射率进行了测试,利用XRD对涂层的相结构进行了分析,并对涂层的金相、结合强度及抗热震性能进行了测试。结果表明,所制备的La0.8Ca0.2Cr O3涂层结合强度为21MPa,孔隙率为14.8%,在600~800℃高温范围内,其全波段发射率可达0.87~0.88,同时,该涂层试样经1100℃~室温水热震10次后没有发生剥落失效现象,涂层具有良好的抗热震性能。     

高耐磨性铁基等离子喷焊涂层的应用研究

针对石油化工等行业中关键部件易磨损的问题,常采用等离子喷焊技术喷焊铁基合金粉末,获得耐磨涂层,从而达到延长零件的使用寿命的目的。本文对4种国产铁基合金粉末喷焊层的表面形貌、硬度和耐磨性进行了比较研究,结果表明,FFe-1160A涂层较其余3种涂层具有更好的耐磨性。     

高速电弧喷涂Fe基涂层的耐磨性能研究

本文通过高速电弧喷涂技术在低碳钢基体上制备Fe基涂层, 采用光学显微镜(OM)、 扫描电子显微镜(SEM)、 白光干涉仪表征涂层的微观结构以及磨痕形貌, 通过维氏硬度计、 摩擦磨损试验机检测涂层的机械性能。 研究结 果显示涂层呈典型的片层状结构, 涂层较为致密, 孔隙率为 1.75±0.22%。 硬质相元素的添加提高了涂层的微观 硬度, 涂层的硬度大约是基体的四倍。 同时, 涂层的磨损量相对基体来说降低了 78.61%, 对磨球切削基体表面 形成较深的犁沟, 而涂层因硬度较大, 形成的沟槽较浅, 并且涂层表层出现脆裂、 剥落现象, 产生大量的磨粒, 使得基体与涂层的磨损机制由粘着磨损向磨料磨损转变     

HVAF喷涂铁基非晶涂层工艺优化

铁基非晶材料具有优异的耐蚀性和耐磨性,空气/丙烷超音速火焰喷涂(HVAF)技术制备铁基非晶涂层近年来引起了广泛关注。由于铁基非晶粉在高温下粘度较大,很容易造成喷枪堵塞,制约了该技术的工程应用。通过在铁基非晶粉末中掺入10 wt.%～20 wt.%的180目白刚玉砂,缓解喷枪堵塞、改善涂层的喷涂稳定性。研究了白刚玉含量、喷涂气体压力、送粉速率、喷涂距离等对涂层沉积效率、抗拉结合强度、孔隙率及粘枪情况的影响规律。结果表明,Fe基粉/白刚玉复合粉喷涂可以实现20 min以上的稳定喷涂,且制备的涂层结合强度达到40 MPa以上,涂层孔隙率<1%,涂层粘枪情况得到显著改善。优化出了适用于铁基非晶粉HVAF喷涂的工艺方法,能够指导该技术的推广应用。     

影响热喷涂层质量的因素分析

分析了试样的表面状态,涂层厚度及喷涂时间对热喷涂层质量的影响。