化学沉积法制备Ni-P-SiC复合镀层的研究

研究了在碳钢基材表面进行化学沉积Ni-P-SiC复合镀层的工艺和条件,对镀层的成分进行了扫描分析,对镀层的金相组织进行了观察分析;结果表明SiC硬质纳米粒子嵌入,使Ni-P合金基质产生沉淀强化,使镀层硬度增加.通过对磨实验和腐蚀实验证明,复合镀层可使碳钢零件耐磨性能提高3倍,可使碳钢零件耐蚀性能提高4倍,有效地延长了钢铁零件的使用寿命.     

化学沉积法制备Ni-P-SiC(C)复合镀层的研究

选择廉价的SiC和石C颗粒作为复合镀层添加物，用化学沉积法在碳钢表面制度Ni-P-SiC(C)复合镀层，研究了复合镀层的制备工艺，镀液配方以及复合镀层的性能等，结果显示：风表面开成的复合镀层厚薄均一，SiC和石墨C颗粒在镀层中分布均匀，镀层开成速度理想，表明本文采用的工艺技术合理可行，与单一的Ni-P镀层相比，Ni-P-SiC和Ni-P-C复镀层耐磨性能均有不同程度的提高，而将2种不同性能的SiC和C颗粒同时加入槽液，形成的Ni-P-SiC－C复合镀层具有最优异的耐磨性能。     

Preparation of CoP films by ultrasonic electroless deposition at low initial temperature

Electroless deposition technology has been considered as a kind of common ways to obtain cobalt alloy films. However, in order to get cobalt alloy films, high temperature(353 K) is necessary during the electroless deposition process which will increase costs and energy consumption. Ultrasonic was introduced during electroless plating process to obtain cobalt alloy films at lower initial temperature. It was found that the cobalt thin films could be prepared at lower initial temperature(323 K) with the introduction of ultrasonic. Therefore, different powers of ultrasonic were applied during the electroless deposition process to prepare CoP thin films on copper substrates from an alkaline bath in this investigation. The effects of different powers of ultrasonic on deposition rate, surface morphology, anticorrosion performance and magnetic property of films were studied. It was found that the deposition rate increased gradually with the rise in ultrasonic powers due to cavitation phenomenon. All the CoP films presented the typical spherical nodular structures with the impact of ultrasonic. Smaller and regular shaped structures could be observed when the films were deposited with higher power of ultrasonic which contributed directly to enhancement of anticorrosion performance. Saturation magnetization and coercivity of thin films increased gradually with the rise in ultrasonic powers during the electroless deposition process due to the higher amounts of cobalt.& 2014 Chinese Materials Research Society. Production and hosting by Elsevier B.V. All rights reserved.     

化学镀银聚酯纤维制备及其导电性能研究

 采用化学镀法在聚酯纤维表面镀覆一层导电银层,采用场发射扫描电镜（FE-SEM）、电子能谱仪（EDS）、X射线衍射仪（XRD）分别对聚酯纤维镀银前后的表面形貌、化学元素组成、银结晶结构进行表征.讨论了乙二胺浓度、AgNO₃浓度、施镀时间和镀液温度对化学镀银聚酯纤维增重率及电阻率的影响,测试化学银镀层与纤维基体的结合牢度和耐腐蚀性.结果表明,最佳工艺条件下,电阻率低至2.31Ω·cm^-1;镀层为高纯度的面心立方结构的单质银;银镀层具有良好的与基体的粘结强度和耐化学腐蚀性能.
     

胺基聚氨酯/纳米银复合材料的制备及表征

为制备胺基聚氨酯／纳米银材料并研究胺基聚氨酯和纳米银的作用机理,制备了硬段侧链含胺基的聚氨酯,用硼氢化钠作还原剂在液相中原位合成胺基聚氨酯,纳米银复合物．UV-VIS表明,胺基聚氨酯,纳米银中纳米银的含量高、粒径小并且粒径分布范围小．IR表明聚氨酯硬段的胺基和纳米银有配位作用．     

化学镀银过程硅表面催化性质对镀膜成核的研究

在单晶硅表面用化学镀的方法制备了纳米级的银催化晶籽层,利用开路电位时间曲线(OCP-T)的变化情况监测了硅表面银晶籽的生长过程.研究表明在有Ag 离子存在的溶液中加入HF后的瞬间,银晶籽即在硅表面形成,且在5 s内完全达到覆盖.用OCP-T对刻蚀硅片与银晶籽活化后的硅片在化学镀溶液中的成核情况进行了研究,并结合原子力显微镜与傅立叶红外反射对活化前后的表面经化学镀覆银的情况进行了对比,结果表明用银晶籽层活化的硅片表面具有良好的催化活性,在其上经化学镀银后所得到的薄膜表面平滑度高、致密性好.     

Cu-ZrW2O8复合镀层的制备

以ZrO2和WO3为原料,通过两步烧结法制备具有负热膨胀性的钨酸锆（ZrW2O8）粉体,利用X射线衍射（XRD）对合成粉体进行分析。在含ZrW2O8粉体的酸性镀铜溶液中进行复合电镀,就电流密度、电镀时间以及添加剂对复合镀层中ZrW2O8粉体含量的影响进行分析,并利用扫描电镜（SEM）对不同条件下镀层表面的微观形貌进行观察与分析。实验结果表明：电流密度控制在2A／dm^2时,镀层中能获得较高的粉体含量;随着电镀时间延长,粉体在镀层中含量呈峰值变化：镀液中添加十六烷基三甲基溴化氨（CTAB）或十二烷基硫酸钠（SDS）并不利于复合镀层中ZrW2O8粉体含量的提高。     

沉积动力学方程对银快离子玻璃中银沉积的研究

借助电子探针显微分析法,用沉积动力学方程,研究了AgIAg_4P_2O_7、AgIAg_2OB_2O_2、AgIAg_2OP_1O_5B_1O_3银快离子玻璃系统中样品的银沉积问题。发现在电子束轰击下,银计数率随时间的变化实验曲线与理论拟台曲线一致,沉积动力学方程能较好地适合银快离子玻璃。对银快离子玻璃中银的沉积物理过程进行了探讨解释,在电子束注入电子的外电场和试样内离子浓差、局域极化内电场作用下,银离子不断迁移、沉积,达到极限值。     

化学镀法制备电磁屏蔽聚酯织物的研究

为开发具有电磁屏蔽作用的织物,采用化学镀法制备了具有电磁屏蔽性能的聚酯类化纤织物,并研究了化学处理方法——碱减量处理对涤纶织物表面化学镀层的性能及化学镀后织物的电磁屏蔽性能的影响。研究表明,在20g/LNaOH溶液中处理既可使纤维表面形成微观凹坑,增大比表面积,又可改非极性的疏水表面为亲水表面,提高表面活性,提高敏化和活化时金属离子和金属在纤维表面的吸附性,在化学镀过程中使基体与金属形成平整的结合。碱减量处理2～3h有利于提高镀层与织物结合牢度,并使镀层光亮均匀,电磁屏蔽性能更加优异。     

Activator-assisted electroless deposition of copper nanostructured films

This paper showed simple and effective synthesis of copper nanoparticles within controlled diameter using direct electroless deposition on glass substrates, following the sensitization and activation steps. Electroless-deposited metals, such as Cu, Co, Ni, and Ag, and their alloys had many advantages in micro- and nanotechnologies. The structural, morphological, and optical properties of copper deposits were characterized using X-ray diffraction (XRD), atomic force microscopy (AFM), and UV-Vis spectroscopy. The structural data was further analyzed using the Rietveld refinement program. Structural studies reveal that the deposited copper prefers a (111) orientation. AFM studies suggest the deposited materials form compact, uniform, and nanocrystalline phases with a high tendency to self-organize. The data show that the particle size can be controlled by controlling the activator concentration. The absorption spectra of the as-deposited copper nanoparticles reveal that the plasmonic peak broadens and exhibits a blue shift with decreasing particle size.     

化学还原沉积银膜上的SERS光谱的比较研究

用JYU-1000型拉曼光谱仪和新的LABRAMⅠ型技曼光增仪研究了Cu（Ⅱ）NACN和Cu（Ⅱ）NEAE及其与DNA的复合物在化学沉积法制备的银膜上的SERS光增特征．结果表明，化学还原沉积银膜是叶啉的拉曼光谱表面增强活性载体；两种仪器获得的结果具有谱峰一致性，但谱型和峰位略有差异；LABRAMI型拉曼光谱仪有高的激光利用率和快速获诺优势；在化学还原沉积镀膜上Cu（Ⅱ）NEAE部分插入DNA．     

溶胶-凝胶法制备超疏水性OTS-SiO2复合薄膜

以正硅酸乙酯(TEOS)为先驱体,采用酸/碱两步溶胶-凝胶法和自组装技术制备了具有超疏水性的薄膜.利用红外光谱(FT-IR)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)和接触角仪等测试方法对十八烷基三氯硅烷(OTS)修饰前后薄膜的结构、形貌、表面元素组成与润湿等性能进行了表征和分析.结果表明,制备的OTS-SiO2复合薄膜具有良好的超疏水性能,水滴在该薄膜上的最大静态接触角为156°,滚动角小于5°.     

镍-磷/金纳米粒子复合化学镀层的研究

在化学镀镍磷溶液中添加金纳米粒子,在基体钢铁上沉积得到镍-磷/金纳米粒子复合镀层. 金纳米粒子在镀液中的浓度为1.0?μmol•L-1. 用扫描电子显微镜,能谱仪,示差扫描热量分析仪,X 射线衍射仪,显微硬度计等仪器对镀层性能进行了分析. 通过EDS分析表明,Ni P镀层中P的质量分数为9.72%,而Ni P/Au镀层中P质量分数为9.29%,金的质量分数为0.93%. 与镍-磷合金镀层相比,纳米复合镀层具有较高的硬度,并且镀层组织致密,孔隙率小,对基体具有更好的保护作用.     

改性纳米碳酸钙制备超疏水涂层

通过油酸改性纳米碳酸钙颗粒使其表面由亲水性变成了疏水性,改性后的纳米颗粒与低表面能的有机硅树脂聚二甲基硅氧烷经过混合陈化固化过程后在玻璃表面形成超疏水涂层.实验通过改性后的纳米粒子在聚合物介质上构造纳米/微米尺度的结构表面.用接触角测量仪和扫描电镜分别检测涂层的疏水性能和涂层的表面形态.实验结果表面涂层有优异的自清洁能力,平均静态水接触角达160°滚,动角为6°,涂层表面成功构造了纳米/微米的双重粗糙结构.该方法简单有效具有很大的应用前景.     

超重力法碳分制备纳米三水合氧化铝的研究

一种超薄六角片状的纳米三水氧化铝（三水铝石）通过超重力碳分的方法被成功制备。文中叙述了实验过程,并讨论了超重力碳分过程中各主要操作参数对产品粒度、形貌和产率等方面的影响,以及水热老化、超重力水洗及干燥过程对产品的影响。采用TEM、XRD、BET和连续等离子光谱分析仪（SPS）对产品的形貌、粒度、晶型、比表面积、钠离子含量进行了分析表征。结果表明其颗粒形貌为超薄六角片状,晶型为Gibbsite类型的三水铝石,根据其比表面积为26.2m²/g,测算其当量粒度为94.24nm,三水铝石中氧化钠质量分数为0.279%。     

Study on antireflection SiO2 coatings fabricated by layer-by-layer deposition

Multifunctional (poly(diallyldimethyl ammonium chloride)/ sodium poly(4-styrene sulfonate)) _n ((PDDA/PSS) _n ) thin films were fabricated by layer-by-layer assembled on the glass substrate. The monolayer silica nanoparticles were prepared on the (PDDA/PSS) _n films. The SiO₂-polyelectrolyte coatings exhibit antireflection properties with low refractive index (as low as 1.22). Interestingly, wavelengths of maximum transmittance could be well tailored by simply changing the particle size of SiO₂. A maximum transmittance of 97.03% in the visible spectral range is achieved for the particle size of 100 nm SiO₂ films. The coatings also show excellent mechanical stability and good adhesion to substrates. The easy availability of the raw materials and simplicity of the fabrication method for such films might make them be potentially useful for various applications.     

还原法制备超细银粉

文章用还原法制备单质银,研究分散剂及还原剂的不同用量对银粒粒径,粒度分布及产率的影响.     

NiTi形状记忆合金表面电化学沉积-碱处理制备HA生物活性涂层

采用电化学沉积-碱处理,在低温条件下从含钙和磷离子的电解水溶液中在NiTi形状记忆合金表面沉积了磷酸钙涂层,经碱处理获得羟基磷灰石(HA)涂层.对涂层的组织形貌和相组成进行了分析,并研究了实验工艺对涂层结构的影响.研究结果表明,电化学沉积涂层CaHPO4*2H2O经碱处理后转变为羟基磷灰石;对试样进行表面处理,同时在电解液中加入有机溶剂得到的涂层更均匀、更致密.     

物理气相沉积法制备TP/TFA纳米薄膜与光致发光特性探究

为了探究有机荧光材料在微纳尺寸上的荧光特性,采用低真空物理气相沉积方法制备了茶碱（TP）和2,3,5,6-四氟对苯二甲酸（TFA）有机纳米薄膜。通过对TP和TFA薄膜的荧光性质进行表征发现：与TP粉末相比薄膜的荧光发射峰由1个增加到4个,发射波长范围拓宽了100 nm,TFA的荧光发射峰之间的相对荧光强度发生了变化,与原料粉末相比在408 nm处的荧光发射峰蓝移了7 nm,362 nm处的荧光发射峰红移了3 nm。另外随着纳米薄膜厚度的逐渐增加,其荧光效率也逐渐增大。通过对TP和TFA纳米薄膜的表面形貌表征发现：随着薄膜厚度的增加,颗粒的聚集形态尺寸逐渐增大,从而验证了荧光效率随膜厚增加而逐渐提升的特性。     

用溶胶——凝胶法制备SrTiO3纳米薄膜材料

为制备具有电容和压敏特性的ＳｒＴｉＯ３双功能器件,以Ｓｒ（ＮＯ３）２,Ｔｉ（ＯＣ４Ｈ９）４为原料,用溶胶－凝胶方法制备ＳｒＴｉＯ３材料,研究了水和醋酸等对ＳｒＴｉＯ３材料的影响机理,并对其进行Ｘ－射线衍射、红外光谱和ＴＥＭ分析,证明该薄膜为纳米晶体结构,晶粒尺寸为１２－２５ｎｍ。