薄膜表面等离子体光催化剂Ag@AgBr/CNT/Ni的制备和性能

用复合电沉积技术制备了Ag@AgBr/CNT/Ni表面等离子体薄膜催化剂,以扫描电镜(SEM)、X射线衍射(XRD)、拉曼光谱(Raman Spectra)、X射线光电子能谱(XPS)和紫外-可见漫反射光谱(UV-Vis DRS)对薄膜的表面形貌、晶体结构、化学组成和光谱特性进行了表征,在可见光照射下,用罗丹明B(RhB)作为模拟污染物对薄膜的光催化性质和稳定性进行测定,采用测定薄膜电化学阻抗谱(EIS)和向反应系统中加入活性物种捕获剂的方法对薄膜光催化机制进行探索。结果表明:最优工艺下制备的Ag@AgBr/CNT/Ni薄膜是由少量碳纳米管(CNT)和表面沉积纳米Ag粒子的AgBr晶体构成的复合薄膜。薄膜具有突出的表面等离子体共振效应、优异的光催化活性和良好的催化稳定性。光催化罗丹明B 20 min,Ag@AgBr/CNT/Ni薄膜的降解率是Ag@AgBr/Ni薄膜的1.32倍,是P25 TiO_2/ITO多孔薄膜的21.6倍。在保持光催化性能基本不变的前提下可循环使用5次。CNT的存在使薄膜电荷传导性能和光催化还原溶解氧的性能大幅增加,是所制薄膜相对于Ag@AgBr/Ni薄膜光催化性能提高的主要原因。提出了薄膜光催化罗丹明B的反应机理。     

薄膜表面等离子体光催化剂Ag@AgBr/CNT/Ni的制备和性能

用复合电沉积技术制备了Ag@AgBr/CNT/Ni表面等离子体薄膜催化剂,以扫描电镜（SEM）、X射线衍射（XRD）、拉曼光谱（Raman Spectra）、X射线光电子能谱（XPS）和紫外-可见漫反射光谱（UV-Vis DRS）对薄膜的表面形貌、晶体结构、化学组成和光谱特性进行了表征,在可见光照射下,用罗丹明B（RhB）作为模拟污染物对薄膜的光催化性质和稳定性进行测定,采用测定薄膜电化学阻抗谱（EIS）和向反应系统中加入活性物种捕获剂的方法对薄膜光催化机制进行探索。结果表明：最优工艺下制备的Ag@AgBr/CNT/Ni薄膜是由少量碳纳米管（CNT）和表面沉积纳米Ag粒子的AgBr晶体构成的复合薄膜。薄膜具有突出的表面等离子体共振效应、优异的光催化活性和良好的催化稳定性。光催化罗丹明B 20 min,Ag@AgBr/CNT/Ni薄膜的降解率是Ag@AgBr/Ni薄膜的1.32倍,是P25 TiO₂/ITO多孔薄膜的21.6倍。在保持光催化性能基本不变的前提下可循环使用5次。CNT的存在使薄膜电荷传导性能和光催化还原溶解氧的性能大幅增加,是所制薄膜相对于Ag@AgBr/Ni薄膜光催化性能提高的主要原因。提出了薄膜光催化罗丹明B的反应机理。     

A Simple Method for the Preparation of TiO2/Ag‐AgCl@Polypyrrole Composite and Its Enhanced Visible‐Light Photocatalytic Activity

A novel and facile method was developed to prepare a visible‐light driven TiO₂/Ag‐AgCl@polypyrrole (PPy) photocatalyst with Ag‐AgCl nanoparticles supported on TiO₂ nanofibers and covered by a thin PPy shell. During the synthesis, the PPy shell and Ag‐AgCl nanoparticles were prepared simultaneously onto TiO₂ nanofibers, which simplified the preparation procedure. In addition, because Ag‐AgCl aggregates were fabricated via partly etching the Ag nanoparticles, their size was well controlled at the nanoscale, which was beneficial for improvement of the contact surface area. Compared with reference photocatalysts, the TiO₂/Ag‐AgCl@PPy composite exhibited an enhanced photodegradation activity towards rhodamine B under visible‐light irradiation. The superior photocatalytic property originated from synergistic effects between TiO₂ nanofibers, Ag‐AgCl nanoparticles and the PPy shell. Furthermore, the TiO₂/Ag‐AgCl@PPy composite could be easily separated and recycled without obvious reduction in activity.