Pt/CexZr1-xO2催化剂上丙烷完全氧化性能研究

采用沉淀法制备了ZrO2,CeO2和Ce0.7Zr0.3O2载体,并用浸渍法制备负载型Pt催化剂。考察了500和900℃焙烧催化剂的丙烷完全氧化性能和水汽对丙烷氧化反应的影响。对于500℃焙烧的催化剂,催化剂的丙烷氧化活性顺序为:Pt/ZrO2-500>Pt/CeO2-500>Pt/Ce0.7Zr0.3O2-500;而经900℃焙烧的催化剂活性顺序为:Pt/ZrO2-900>Pt/Ce0.7Zr0.3O2-900>Pt/CeO2-900。反应气氛中水汽的存在对两种Pt/ZrO2催化剂的活性均有抑制作用(T50温度均提高了10~15℃);而对于Pt/CeO2-500催化剂有抑制作用(T50温度提高10℃),但对Pt/CeO2-900催化剂活性有促进作用(T50温度下降25℃);对于两种Pt/Ce0.7Zr0.3O2催化剂活性具有促进作用(T50温度均下降5~25℃)。表征结果表明催化剂的活性与其表面Pt物种价态密切相关,催化剂表面上Pt0物种有利于活性的提高。Pt/Ce0.7Zr0.3O2-500催化剂中只含有氧化态Pt物种(Pt^2+),而Pt/Ce0.7Zr0.3O2-900催化剂中则含有部分金属态Pt物种,因此其活性高于Pt/Ce0.7Zr0.3O2-500催化剂。     

ZrO2及其含量对Pd/ZrO2-Al2O3催化剂加氢脱硫性能的影响

采用浸渍法制备了一系列Pd/ZrO2-Al2O3催化剂,并考察了ZrO2-Al2O3复合载体及其ZrO2含量对Pd基催化剂噻吩加氢脱硫(HDS)性能的影响,运用XRD和NH3-TPD等手段对催化剂进行了表征。结果表明,ZrO2-Al2O3复合载体及其ZrO2含量对Pd基催化剂的HDS性能有较大的影响,其中ZrO2含量为12wt%时Pd/ZrO2-Al2O3催化剂的活性最好。ZrO2-Al2O3复合载体及其ZrO2含量对Pd基催化活性的影响是通过增加Pd的分散度、H吸附量和催化剂的酸量、以及降低活性组分与载体的相互作用来实现。     

Ni／ZrO2-Al2O3制备表征及催化性能的研究

本文采用浸渍沉淀法制备了不同配比的ZrO2-Al2O3复合载体。并通过浸渍法制备Ni/ZrO2-Al2O3催化剂,以苯加氢制环己烷反应为探针,考察了ZrO2与Al2O3的配比对Ni催化剂催化加氢性能的影响;采用X射线衍射(XRD)、程序升温还原(TPR)、程序升温脱附(TPD)等技术考察复合载体对Ni催化剂的体相结构、还原性能以及表面吸附性能的影响。研究结果表明,ZrO2质量分数为20%的复合载体所负载的Ni催化剂有很好的加氢活性,优于单组分载体负载的Ni催化剂;采用浸渍沉淀法制备的ZrO2-Al2O3复合载体中ZrO2以非晶态形式存在,这是由于Al2O3的存在影响了ZrO2的内部结构;该载体负载的Ni催化剂较其他催化剂更容易被还原,吸附中心数量增加。     

助剂对甲烷部分氧化制合成气镍基催化剂性能的影响

考察了添加助剂铈、镧和钙对镍基催化剂反应性能的影响，发现助剂对以α-Al2O3为载体的镍基催化剂的调变作用比以γ-Al2O3为载体的镍基催化剂好，且助剂铈对催化剂的性能改善最好。在此基础上，研究了不同载量的铈对催化剂性能的影响。结果表明，铈的质量分数为1%时对催化剂的性能改善最好。同时采用XRD、XPS、TG等技术，研究了助剂铈对10％Ni/γ-Al2O3催化剂的改性作用。XRD分析表明，铈负载量较低时，催化剂中的CeO2高度分散在催化剂表面，铈负载量较高时，CeO2形成微晶颗粒，降低了催化活性。     

Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟（英文）

以CexZr1-xO2固溶体做载体,制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂（x=1,0.75,0.5,0.25,0）.应用Brunauer-Emmet-Teller（BET）比表面积分析、X射线衍射（XRD）和H2程序升温还原（H2-TPR）等手段对催化剂进行相关表征,并系统研究了催化剂在饮食油烟催化燃烧中的催化活性.BET结果表明催化剂的比表面积随Ce/Zr摩尔比的减小而减小.XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上.H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好.催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧,降低了反应温度.随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化,催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2〉Pt/γ-Al2O3/Ce0.25Zr0.75O2〉Pt/γ-Al2O3/Ce0.75Zr0.25O2〉Pt/γ-Al2O3/CeO2〉Pt/γ-Al2O3/ZrO2.     

Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟

以CexZr1-xO2固溶体做载体,制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂(x=1,0.75,0.5,0.25,0).应用Brunauer-Emmet-Teller(BET)比表面积分析、X射线衍射(XRD)和H2程序升温还原(H2-TPR)等手段对催化剂进行相关表征,并系统研究了催化剂在饮食油烟催化燃烧中的催化活性.BET结果表叫催化剂的比表面积随Ce/Zr摩尔比的减小而减小.XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上.H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好.催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧,降低了反应温度.随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化,催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2＞Pt/γ-Al2O3/Ce0.25Zr0.75O2＞Pt/γ-Al2O3/Ce0.75Zr0.25O2＞Pt/γ-Al2O3/CeO2＞Pt/γ-Al2O3/ZrO2.     

Ce含量对Ni-Ce/Al_2O_3催化剂结构及浆态床CO甲烷化性能的影响

以γ-Al2O3为载体,采用等体积浸渍法制备了不同Ce含量的Ni-Ce/Al2O3催化剂,并考察了其浆态床CO甲烷化反应性能。借助XRD、BET、H2-TPR及CO-TPD等对催化剂进行了表征分析,研究了催化剂的微观结构与甲烷化性能之间的关系。结果表明,助剂Ce的引入能够加强Ni物种与载体之间的相互作用、增强活性组分Ni对CO的吸附能力。随着Ce含量的升高,Ni物种在载体表面的分散度提高、Ni晶粒粒径减小,催化剂的比表面积及与载体相互作用较强的β-NiO相对含量先升后降。催化剂的浆态床甲烷化活性随Ce含量的升高呈现规律性的变化,CO转化率和CH4时空收率先增加后略有下降,当Ce含量为4%(质量分数)时,催化剂甲烷化活性最佳。     

Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟

以CexZr1-xO2固溶体做载体, 制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂(x=1, 0.75, 0.5, 0.25, 0). 应用Brunauer-Emmet-Teller (BET)比表面积分析、X射线衍射(XRD)和H2程序升温还原(H2-TPR)等手段对催化剂进行相关表征, 并系统研究了催化剂在饮食油烟催化燃烧中的催化活性. BET结果表明催化剂的比表面积随Ce/Zr摩尔比的减小而减小. XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上. H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好. 催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧, 降低了反应温度. 随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化, 催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2>Pt/γ-Al2O3/Ce0.25Zr0.75O2>Pt/γ-Al2O3/Ce0.75Zr0.25O2>Pt/γ-Al2O3/CeO2>Pt/γ-Al2O3/ZrO2.     

稀土等碱性助剂对甲烷部分氧化制合成气整体式Ni/γ-Al2O3催化剂性能的影响

制备了整体式Ni/γ-Al2O3和添加稀土等碱性助剂的整体式Ni/γ-Al2O3催化剂. 研究了温度、烷氧比、空速和助剂等因素对甲烷部分氧化反应性能的影响,并利用XRD和TPR对催化剂进行了表征. 结果表明,催化剂活性随着温度的升高而增加;CH4转化率随着烷氧比的增加而降低;当空速为1×105 h-1时,整体式催化剂的催化性能最佳. 添加碱性助剂Ce,La,Na,Sr均有利于改善催化剂的还原性能,提高催化剂的活性. 其中添加稀土Ce,La可使副反应CH4+2 O2→CO2+2H2O 完全被抑制,从而使H2选择性达到100%.     

Zr-Ni/Al2O3催化剂上苯由H2O2氧化直接氨基化制苯胺

用浸渍法制备了Ni／Al2O3和Zr-Ni／Al2O3催化剂，用于以过氧化氢为氧化剂的苯直接氧化胺化制苯胺反应，并对催化剂进行了程序升温还原、室温氧吸附和氢吸附及XRD表征，结果表明，我们所制的Ni基催化剂对苯胺的生成都有活性，加入Zr后，催化剂中Ni物种更分散，低温可还原物种增加，室温吸氧和吸氢能力都增强，反应活性和对目标产物的选择性增大，Zr一方面使Ni物种进一步分散，增大催化剂的吸氢量和表面可还原Ni物种，有利于C-H键的活化；同时Zr与Ni的相互作用，促进了低温可还原物种的生成，使催化剂室温吸氧量增大，有利于苯的氧化，这种Zr和Ni的协同作用提高了催化剂的活性和选择性，催化剂的制备方法影响Zr与Ni的协同作用，使含Zr的两个催化剂的活性和选择性显示出差异。     

Autothermal reforming of methane over Ni catalysts supported over ZrO2-CeO2-Al2O3

Ni catalysts supported on Al2O3, ZrO2-Al2O3, CeO2-Al2O3 and ZrO2-CeO2-Al2O3 were prepared by coprecipitation method, and their catalytic performances for autothermal reforming of methane to hydrogen were investigated. The Ni-supported catalysts were characterized by XRD, TPR and XPS. The relationship between the structures and catalytic activities of the catalysts was discussed. The results showed that the catalytic activity and stability of the Ni/ZrO2-CeO2-Al2O3 catalyst was better than those of other catalysts with the highest CH4 conversion, H2/CO and H2/COx ratio at 750 ℃. The catalyst showed a little deactivation along the reaction time during its 72 h on stream with the mean deactivation rate of 0.08%/h. The catalytic performance of the Ni/ZrO2-CeO2-Al2O3 catalyst was also affected by reaction temperature, no2 ： nCH4 molar ratio and nH2O ： nCH4 molar ratio. TPR, XRD and XPS measurements indicated that the formation of ZrO2-CeO2 solid solution could improve the dispersion of NiO, and inhibit the formation of NiAl2O3, and thus significantly promoted the catalytic activity of the Ni/ZrO2-CeO2-Al2O3 catalyst.     

焙烧温度对柴油车氧化催化剂Pt-Pd-（x）ZrO2/Ce0.3Zr0.7O2-Al2O3性能的影响

制备了氧化铝、铈锆固溶体复合氧化物负载铂、钯的双金属催化剂Pt-Pd/ Ce0.3Zr0.7O2-Al2O3,并添加3% ZrO2助剂改性,用于柴油车尾气中CO、HC和NO的催化氧化,其中贵金属负载量仅为0.68 wt%。考察了制备过程中焙烧温度对催化剂性能的影响。催化剂活性评价结果表明,与未添加ZrO2的催化剂比较。添加ZrO2明显提高了催化剂的低温氧化活性,而且焙烧温度对催化剂的氧化性能有较大影响。焙烧温度为800 ?C时,CO和C3H6的起燃温度最低,分别为168、189 ?C,焙烧温度为700 ?C时,NO转化为NO2的转化率最高,最大转化率为36%,具有较好的热稳定性。通过XRD、N2吸附-脱附、CO化学吸附、XPS、H2-TPR等表征手段考察了催化剂物理化学性质随焙烧温度的变化情况,并分析了与催化剂活性之间的关系,得到贵金属分散度、表面化学吸附氧含量、催化剂的还原性质对氧化性能有重要影响,发挥协同作用。进而可以通过优化焙烧温度提升柴油车氧化催化剂性能,对提高工业应用柴油车尾气后处理系统的净化效率有重要意义。     

CeO2掺杂RuO2/γ-Al2O3催化剂结构与湿式氧化降解苯酚的活性研究

采用浸渍法制备了RuO2/γ-Al2O3和RuO2-CeO2/γ-Al2O3催化剂,利用XRD,XPS和ESR分析了催化剂的结构,并研究了湿式氧化降解苯酚的活性.结果表明,两种催化剂表面RuO2均有良好的分散性,并且催化剂表面存在氧空位和化学吸附氧,CeO2的掺杂使催化剂表面氧空位和化学吸附氧数量增加.两种催化剂对湿式氧化降解苯酚具有良好的催化活性,当苯酚质量浓度为4200mg/L,在150℃和3MPa下,RuO2/γ-Al2O3催化剂湿式氧化降解苯酚反应150min后,苯酚全部被去除,RuO2-CeO2/γ-Al2O3催化剂反应60min后,苯酚的去除率为96%.     

负载型铈基催化剂在NH3-SCR反应中的载体效应

近年来,氨-选择催化还原(NH3-SCR)技术被公认为是控制燃煤烟气和柴油车尾气氮氧化物(NOx)排放的最有效手段之一.V2O5-WO3/TiO2和V2O5-MoO3/TiO2催化剂在300–400°C范围内表现出优异的脱硝性能和抗H2O和SO2中毒性能,因而被广泛用于NH3-SCR过程.然而,钒基催化剂存在一些缺点,如氧化SO2到SO3的活性较高、高温下将部分NH3非选择性地氧化成N2O、V2O5具有生物毒性等.因此,非钒基脱硝催化剂的研制引起人们越来越多的关注.二氧化铈(CeO2)因具有氧化还原性能优异、储/释氧能力强和Ce3+/Ce4+转换容易等优点而广泛用于NH3-SCR反应.然而,单纯CeO2的脱硝性能并不理想.研究表明,将CeO2制备成铈基复合金属氧化物催化剂和负载型铈基催化剂可显著提高其在NH3-SCR反应中的催化性能.尤其是负载型铈基催化剂由于催化性能优异、比表面积大、热稳定性高及活性组分用量少而成为研究热点.众所周知,对于负载型金属氧化物催化剂,载体并不只是惰性材料,它会显著影响表面负载组分的物理化学性质和催化性能.因此,关于载体与组分间相互作用的研究常见诸报道.但是,对于负载型铈基催化剂,具有不同晶相结构的载体对其理化性质和NH3-SCR催化性能的影响规律尚不明晰.此外,SiO2,γ-Al2O3,ZrO2和TiO2是工业上常用的四种催化剂载体,它们具有不同的晶相结构和应用场合,究竟哪一个最适合作为负载型铈基催化剂的载体用于NH3-SCR反应尚无定论.因此,为了阐明负载型铈基催化剂在NH3-SCR反应中的载体效应,筛选出最佳的催化剂载体,我们首先采用溶胶-凝胶法和沉淀法合成了SiO2,γ-Al2O3,ZrO2和TiO2四个载体,再通过浸渍法制备了一系列负载型铈基催化剂(CeO2/SiO2,CeO2/γ-Al2O3,CeO2/ZrO2和CeO2/TiO2)用于NH3-SCR反应.并借助于X射线衍射(XRD)、拉曼光谱(Raman)、比表面积测定(BET)、X射线光电子能谱(XPS)、氢气-程序升温还原(H2-TPR)以及氨气-程序升温脱附(NH3-TPD)等表征手段对上述载体和催化剂进行了较为全面的分析.研究结果表明,这些负载型铈基催化剂的理化性质和脱硝性能强烈地依赖于催化剂载体.首先,CeO2/γ-Al2O3催化剂的表面Ce3+含量明显大于CeO2/SiO2,CeO2/ZrO2和CeO2/TiO2催化剂,有利于氧空位的产生以促进NO分子的解离,进而导致优异的NH3-SCR反应性能.其次,CeO2/γ-Al2O3催化剂具有最佳的还原性能,有利于NO氧化为NO2,进而通过"快速NH3-SCR"途径提升其催化性能.再者,CeO2/γ-Al2O3催化剂表面酸性位最多,能够促进反应物NH3分子的吸附与活化,从而提高脱硝性能.最后,CeO2/γ-Al2O3催化剂在H2O和SO2存在的条件下同样表现出最佳的催化性能,表明其有望用于实际燃煤烟气脱硝.     

Al含量对Pt-S2O82-/ZrO2-Al2O3型固体超强酸催化剂异构化性能的影响

通过向S₂O₈^2-/ZrO₂催化剂中同时引入适量的Pt和Al₂O₃, 制备出了具有较高催化性能和高稳定性的Pt-S₂O₈^2-/ZrO₂-Al₂O₃型固体超强酸催化剂. 以正戊烷异构化反应为探针, 考察了Al含量对催化剂的异构化性能的影响, 并采用XRD, BET, FTIR, TPR, TG-DTA, NH₃-TPD和ICP手段对催化剂进行了表征. 结果表明, Al能够延迟ZrO₂的晶化温度, 抑制硫的分解; Al能够增加催化剂的比表面积, 增强硫氧键的结合, 提高催化剂的还原性能, 增加催化剂的酸强度和酸总量. 当Al₂O₃质量分数为2.5%时, Pt-S₂O₈^2-/ZrO₂-Al₂O₃固体超强酸催化剂的催化活性最高, 正戊烷异构化收率可达60.02%, 选择性在98.2％以上.     

Pt/Ce0.6Zr0.4O2催化剂在水煤气变换反应中的电导研究

采用浸渍法制备了不同载体(Ce0.6Zr0.4O2,CeO2和ZrO2)负载的Pt基水煤气变换反应(WGSR)催化剂, 并对其进行了活性评价. 利用X射线衍射(XRD), 程序升温还原(TPR)和原位电导等技术对样品进行了表征. 结果表明, Ce0.6Zr0.4O2固溶体具有比CeO2更高的氧转移能力, 因此促进了Pt/Ce0.6Zr0.4O2催化剂的WGSR活性.     

CH_4/CO_2重整制合成气Ni/Ce_xZr_(1-x)O_2催化剂性能研究

以水热法合成的介孔铈锆固溶体为载体,采用浸渍法制备了Ni/CexZr1-xO2催化剂,使用X射线衍射(XRD)、程序升温还原(TPR)和热重-差示扫描量热分析(TG-DSC)等测试手段对催化剂进行了表征。通过对比以ZrO2,CeO2,Ce0.6Zr0.4O2和Ce0.33Zr0.67O2为载体的Ni基催化剂性能,发现铈锆固溶体独特的氧化还原性质可以提高活性组分的分散度,增强催化剂的抗积炭性能,从而提高催化剂对甲烷二氧化碳重整制合成气的选择性。