大米淀粉及其磷酸酯的理化性质研究

对大米淀粉进行酯化,通过改变温度得到不同取代度的大米淀粉磷酸酯,使用扫描电子显微镜、质构仪、快速黏度分析仪、流变仪对大米淀粉及其不同取代度的淀粉磷酸酯的理化性质进行了测定。结果显示:大米磷酸酯淀粉的硬度、回复性、胶性和咀嚼性要低于大米原淀粉,凝聚性和黏着性要高于原淀粉,取代度越大硬度、回复性、胶性和咀嚼性越小,凝聚性和黏着性越大;大米淀粉磷酸酯的开始糊化温度要小于大米原淀粉,峰值黏度、最低黏度、最终黏度、崩解值、消减值要小于大米原淀粉,取代度增大,开始糊化温度降低,峰值黏度、最低黏度、最终黏度、崩解值、消减值增大。大米淀粉经过磷酸酯变性后,黏度增加了,不易回生,稳定性加强了,凝沉性减弱了,且取代度越高,这些性质越明显;大米淀粉磷酸酯和大米淀粉属于剪切稀化流体,在相同剪切速率下,取代度越大的大米淀粉磷酸酯表观黏度越大。     

几种木薯变性淀粉凝胶化性质的研究

对木薯醋酸酯淀粉、磷酸酯淀粉和氧化淀粉的糊化性质、流变特性和凝胶强度等凝胶化性质进行了比较研究.研究表明:醋酸酯淀粉和磷酸酯淀粉的糊化温度与原淀粉相当,氧化淀粉的糊化温度降低.醋酸酯淀粉和磷酸酯淀粉糊具有剪切稀化特性,属假塑性流体,氧化淀粉糊呈牛顿流体的特征.3种变性淀粉糊的表观粘度受浓度、温度和pH值的影响,与木薯原淀粉相比,变性淀粉糊具有较好的耐热和耐酸碱稳定性.而凝胶强度因变性基团的不同,差异较大.     

木薯淀粉与木薯变性淀粉鱼糜加工性质的影响

本研究比较了木薯淀粉、木薯醋酸酯交联淀粉和木薯磷酸酯交联淀粉对鱼糜加工性质的影响。首先测定了2种木薯醋酸酯交联淀粉、2种木薯磷酸酯交联淀粉以及木薯淀粉的冻融稳定性、透光率、黏性、膨胀度和凝沉性等特性。然后将木薯淀粉和4种变性淀粉分别添加到鱼糜中,测定鱼糜冻融过程中的持水性、白度以及凝胶强度等品质特性。结果表明:木薯变性淀粉因引入了磷酸基、羧甲基等亲水性基团,在透光率、冻融稳定性、黏性和凝沉性等性质方面较木薯淀粉均有提高,添加木薯变性淀粉所得到的鱼糜制品白度、持水性和凝胶强度分别增加了17.7%、10.2%、77.7%。木薯变性淀粉较木薯淀粉更适合用于加工鱼糜。     

复配变性淀粉的性质及在面团中的应用

将冻融稳定性较好的醋酸酯淀粉、羟丙基二淀粉磷酸酯和透明度、黏度较高的羧甲基淀粉进行复配,对比三种变性淀粉和复配变性淀粉的性质,研究其在面团中的应用。结果表明,复配变性淀粉可以综合各变性淀粉的优点,比单一变性淀粉的性质更加全面,其中1:2:1（醋酸酯大米淀粉:羧甲基淀粉:羟丙基二淀粉磷酸酯）组表现最优异,透明度、凝沉性、冻融稳定性、糊化特性、流变性等性质优于其他组。在面团的应用研究中,添加复配变性淀粉可有效改善面团的持水性和质构特性,提高熟面坯的感官品质。复配变性淀粉添加量为5%～7.5%时最好。     

小米淀粉热膨化条件的优化

通过单因素及正交实验以膨化率和脆度为指标确定了小米淀粉热膨化的最佳工艺条件。结果表明,对膨化效果的影响因素次序为水分含量>膨化温度>膨化时间,其中水分含量对膨化效果的影响高度显著(P<0.01)。膨化的最佳条件为水分含量8%,膨化温度310℃,膨化时间50s。此条件下膨化制小米饼的膨化率和脆度分别为8.32及0.254kg·s,脆度优于市售的品牌雪饼(0.424kg·s),感官评价也得到了同样的结论。实验显示以小米为原料制作米雪饼切实可行。     

木薯淀粉与木薯变性淀粉鱼糜加工性质的比较

摘要：本研究比较了木薯淀粉、木薯醋酸酯交联淀粉和木薯磷酸酯交联淀粉对鱼糜加工性质的影响,并测定了二种木薯醋酸酯交联淀粉、二种木薯磷酸酯交联淀粉以及木薯淀粉和鱼糜加工相关的冻融稳定性、透光率、溶解性、膨润度和凝沉性等特性。并将木薯淀粉和四种变性淀粉分别添加到鱼糜中,测定鱼糜冻融过程中的持水性、白度以及凝胶强度等品质特性。结果表明：木薯变性淀粉因引入了磷酸基、羧甲基等亲水性基团,在透光率、冻融稳定性、溶解性和凝沉性等性质方面较木薯淀粉均有提高,添加木薯变性淀粉所得到的鱼糜制品白度、持水性和凝胶强度分别增加了17.7%、10.2%、77.7%。木薯变性淀粉较木薯淀粉更适合用于加工鱼糜。     

木薯淀粉及木薯变性淀粉性质比较研究

测定了木薯淀粉、木薯羟丙基淀粉、羟丙基交联淀粉、醋酸酯淀粉、醋酸酯交联淀粉的冻融稳定性、透光率、凝沉、耐盐性、耐酸性、糊化特性等性质.实验结果表明:经过变性的木薯淀粉和原木薯淀粉有很大的不同,经过羟丙基化、羟丙基交联、醋酸酯化、醋酸酯交联后,分别引入了羟丙基、交联键、乙酰基等,使其具有较强的冻融稳定性,具有较高的透明度、耐盐性、耐酸性.据RVA分析,各种变性淀粉糊液性质较原淀粉有较大的提高.经过交联后糊液稳定性较原淀粉、羟丙基及醋酸酯淀粉有较大程度的提高,因此具有更为广阔的应用性.     

不同交联度大米淀粉磷酸酯理化性质研究

以大米淀粉为原料,与三聚磷酸钠反应,制得淀粉磷酸酯;并采用分光光度计、旋转黏度计等现代分析仪器,对生成的淀粉磷酸酯的理化性质进行了较详细的研究。通过流变学分析,测得生成的变性淀粉糊均为非牛顿流体。结果表明,交联度较高时,糊的透明度低,但冻融稳定性较好。     

变性淀粉对面条品质的改良研究

以交联淀粉、醋酸酯淀粉和羟丙基淀粉为面粉改良剂,通过正交实验研究了单一变性淀粉和复合变性淀粉对新鲜面和冷冻面条的改良效果。结果表明:添加1%的马铃薯交联羟丙基淀粉∶1%醋酸酯淀粉∶1.5%磷酸酯淀粉和0.5%的谷朊粉对面条的改良效果最佳。     

不同交联度大米淀粉磷酸酯理化性质研究

以大米淀粉为原料，和三聚磷酸钠反应，并采用分光光度计、旋转粘度计等现代分析仪器，对生成的淀粉磷酸酯的理化性质进行了较详细的研究。通过流变学分析．测得所得变性淀粉糊均为非牛顿流体。结果表明．交联度较高时．糊的透明度低．但冻融稳定性较好。     

不同种木薯变性淀粉对鸡肉肠品质的影响

对比研究了在斩拌过程中添加6%的木薯变性淀粉(醋酸酯淀粉、交酯淀粉和磷酸酯淀粉)和木薯原淀粉对鸡肉肠品质的影响。结果发现:添加变性淀粉的鸡肉肠的产率差异不显著(P>0.05);添加醋酸酯淀粉的鸡肉肠的L*值最大;添加变性淀粉的产品的质构特性要明显好于添加原淀粉的鸡肉肠(P<0.05),其中添加交酯淀粉的产品的硬度、咀嚼性、弹性和凝聚性最高。感官评定结果显示,添加醋酸酯淀粉产品的品质优于添加其它种类变性淀粉的产品。醋酸酯木薯淀粉更适合于肉类产品实际生产中。     

乌冬面专用变性淀粉及其结构表征

采用交联―酯化―预糊化复合变性制备乌冬面专用改性淀粉,并与木薯原淀粉、交联淀粉及交联―酯化淀粉进行比较。结果表明,交联淀粉偏光显微及颗粒形貌没发生明显变化,交联变性并未破坏淀粉结晶结构;交联―酯化淀粉颗粒出现粘连和聚集现象,部分颗粒表面出现凹陷和裂纹现象;红外光谱表明,交联―酯化―预糊化复合变性淀粉在1 728 cm–1、1 247 cm–1附近出现新的吸收峰,分子内引入乙酰基团,X–射线衍射光谱显示,交联―酯化―预糊化复合变性淀粉在5.6°和22°处衍射峰强度减弱,A型特征峰加强,结晶类型由"C"型向"A"型转变;交联―酯化淀粉经预糊化处理后,淀粉颗粒膨胀破裂,结晶结构受到彻底破坏,淀粉偏光十字消失,但预糊化处理未破坏淀粉分子化学键。     

交联羧甲基玉米淀粉和交联酯化木薯淀粉的制备与性质研究

研究了制备交联羧甲基玉米淀粉和交联酯化木薯淀粉的最佳工艺条件及影响取代度的关键因素,并测定了两种复合变性淀粉的冻融稳定性、透光率、膨胀度等特性.结果表明:两种复合变性淀粉的冻融稳定性、膨胀度、透光率等性能均优于原淀粉;交联酯化木薯淀粉具有良好的絮凝效果可用于污水处理.     

Effect of crosslinking reagents and hydroxypropylation levels on dual-modified sago starch properties

Chemical modification is usually carried out to overcome the unstable properties of native sago starch and improve its physical properties during processing. In this study, dual-modification of sago starch was carried out. The first stage of modification was hydroxypropylation, using propylene oxide at levels ranging from 6 to 12%. This was followed by crosslinking, using three different types of crosslinking agents: a mixture of sodium trimetaphosphate (STMP) and sodium tripolyphosphate (STPP), phosphorus oxychloride and epichlorohydrin. Through hydroxypropylation, it was found that there was a significant increase in molar substitution which in turn induces an increase in crosslinking and this was seen from the marked increase in phosphorus content and degree of substitution. This was accompanied by a significant decrease in paste clarity, swelling power and solubility compared to that of the native starch. Starch that was hydroxypropylated with 10–12% propylene oxide and crosslinked by a mixture of 2% STMP and 5% STPP produced modified starch with the most desirable properties in that it exhibited no viscosity breakdown, high acid resistance, high freeze-thaw stability and improved gel texture.     

Relationship between thermomechanical properties and baking expansion of sour cassava starch (Polvilho azedo)

The factors involved in the baking expansion of native and sour cassava starch doughs were compared with those of native corn starch. Unlike corn starch dough, native and sour cassava starch doughs showed expansion properties during baking. The storage modulus E ′ decreased for cassava starch doughs before baking expansion, but remained unchanged for corn starch dough. Expansion during the baking of sour cassava starch was attributed to water vaporisation and the fluidity of starch paste. The fact that temperature and weight loss variations at adequate water contents were significantly greater for cassava than corn starch dough is indicative of the important role played by starch melting in expansion. Expansion ability could be correlated with changes in dough–crumb thermomechanical properties when close to the starch melting temperature. © 2001 Society of Chemical Industry     

季铵醚化改性对磷酸酯淀粉浆料性能的影响

为提高磷酸酯淀粉浆料的使用性能,通过改变3-氯-2羟丙基三甲基氯化铵醚化剂对磷酸酯淀粉的投料比,制备了一系列具有不同季铵醚阳离子取代度的磷酸酯变性淀粉。通过性能对比实验,研究了这种变性淀粉的季铵阳离子化变性对浆液ζ电位、黏度以及黏附性能和浆膜性能的影响。结果表明：随着季铵阳离子取代度的增加,这种变性淀粉浆液的ζ电位升高,黏度明显提高;季铵阳离子化变性能够进一步改善磷酸酯淀粉对棉纤维的黏附性能;随着阳离子取代度的增加,对棉纤维的黏附性能增大,浆膜的断裂伸长率增大。     

酶催化木薯淀粉表面松香酸酯化改性及表征

以木薯淀粉为原料,松香酸为酯化剂,氯仿为溶剂,以液态脂肪酶为催化剂,在两相体系中直接在原木薯淀粉表面进行酯化修饰合成松香淀粉酯(RAS),并利用傅里叶红外光谱(FT-IR)、电子扫描显微镜(SEM)、X-射线衍射(XRD)、热重差分析(TGA)、接触角、乳化能力及乳化稳定性等对RAS的结构及理化性能进行分析。结果表明:与原淀粉相比,FT-IR谱图中RAS在1728 cm-1附近出现羰基特征峰,SEM图中RAS表面的酯化斑点表明木薯淀粉表面成功接上了松香酸基团;XRD和TGA结果显示木薯淀粉经松香酸修饰后结晶度下降;对比原木薯淀粉,RAS(DS=0.0502)的接触角提高了63.40%,乳化能力、乳化稳定性分别由原木薯淀粉的1.53%、1.50%,提高至31.91%、23.08%。且随着DS的升高,RAS疏水性能及乳化性能也随之提高。     

酯化交联淀粉反应及性质的研究(Ⅱ)——糊粘度曲线

测定了三氯氧磷变性木薯淀粉制得的酯化交联淀粉糊的粘度性质 ,如糊的粘度曲线、抗剪切和抗酸碱的特性。变性淀粉的交联度和取代度是影响其糊粘度性质的内在因素     

Influence of prior acid treatment on physicochemical and structural properties of acetylated sorghum starch

Influence of prior acid treatment on acetylation of starch isolated from an Indian sorghum cultivar was investigated. The starch was acid thinned (AT) using 0.1, 0.5, and 1 M HCl for 1.5 h and then acetylated (Ac) with acetic anhydride (8% w/w). The acid thinning and subsequent acetylation appeared to reduce the percentage acetylation as indicated by degree of substitution. Ac‐AT starches exhibited significantly different physicochemical, thermal, pasting, and gel textural properties from those of AT and Ac starches. Starches after dual modification showed higher solubility, lower AM content, gelatinization temperatures, retrogradation, peak viscosity, and gel hardness than native starch. Enthalpy and range of gelatinization were observed to be higher in dual modified starches than native starch. However, no significant changes in granule morphology or crystalline pattern of Ac‐AT starches were observed compared with native starch.