Enzymatic Treatment for Shrink-proofing of Wool

Introduction Duetothescalestructureandresiliencyproperties, woolhasatendencytoshrinkundertheinfluencesof moisture,detergentsandagitation.Nowadaysthemost commerciallysuccessfulshrink proofingprocedureistheIWS/CSIROchlorine Hercosetttopprocessasa combinationofsubtractiveandadditivemethods[1,2]. However,apartfromyellowingandresultingasynthetichandle,thisprocessproducesabsorbableorganichalogen compounds(AOX)[1,3],whichcauseseverepressureon environmentallegislation[4,5].Forecologicaland econ…     

羊毛生物酶细化改性工艺研究

采用双氧水预处理并结合蛋白酶—脂肪酶工艺细化羊毛纤维。通过正交试验分别确定了羊毛双氧水预处理的条件和蛋白酶—脂肪酶处理工艺条件,并进行了生物酶细化处理羊毛的对比试验。结果表明采用双氧水预处理并蛋白酶-脂肪酶细化处理羊毛后,羊毛纤维鳞片层受到一定程度的破坏,纤维的直径降低约2.3μm,断裂强力保持率达到94.8%。     

低温等离子体处理对羊毛织物性能的影响

采用空气低温等离子体对羊毛表面进行改性处理,探讨了等离子体处理对羊毛织物抗毡缩性、强力、白度、润湿性、染色性能等的影响.正交试验结果表明:等离子体处理羊毛织物的实验室最佳工艺为时间3min、压强50Pa、功率150W.经空气低温等离子体处理,羊毛织物的毡缩率和白度降低,而润湿性、强力和弱酸性普拉红B染色K/S值提高.单独经过空气等离子体处理的羊毛织物达不到"机可洗"的要求.     

凉爽羊毛/苎麻复合纱的前处理工艺研究

介绍了羊毛与苎麻两种粗纱的前处理工艺。实验证明，高锰酸钾一蛋白酶改性处理后的羊毛纤维能够去除羊毛的鳞片以消除其对人体的刺痒感，并且保持羊毛的强伸性能不发生明显改变。而碱一纤维素酶改性处理后的苎麻纤维不仅对伸长率、结晶度、取向度与刚度等各方面性能都有较大改善，而且对其后道成纱工艺及服用性能也有一定作用，为夏季用羊毛，苎麻复合纱的开发奠定基础。     

羊毛的变性及变性羊毛阳离子染料染色

羊毛经阴离子型活性变性剂处理后，纤维侧基上被引入阴离子型基因，具有和腈纶纤维类似的结构。因而，变性羊毛能够用阳离子染料染色。增大变性剂的分子量、共轭双键数及相对疏水性，变性羊毛用阳离子染料染色时上染速率和上染率均可显著地增大，染色牢度也大为改善，但对酸性染料产生防染作用。从变性羊毛的红外吸收光谱图上可看到，在波数为１１５０～１２６０ｃｍ－１、１０１０～１０８０ｃｍ－１和６００—７００ｃｍ－１处均出现磺酸基的特征吸收峰。变性剂和羊毛间形成共价结合成为纤维侧基的一部分。变性羊毛表面的电性能有较大变化，但其物理机械性能如减溶解度、弹性、断裂强度等基本不受影响。     

羊毛拉伸细化技术综述

阐述了国内外羊毛细化技术的发展过程，并详细介绍了拉伸细化的机理及各种工艺流程，同时列表说明改性后纤维，纱线及织物性质的变化。     

羊毛防毡缩处理工艺的探讨

采用氧化一树脂法对羊毛进行防缩处理，以天然生物材料壳聚糖作为防缩树脂，对比了不同预氧化条件下的防缩效果，选择了最佳的防缩处理条件，对处理后羊毛的毡缩性和强度等指标进行了测定，结果表明，用壳聚糖作为羊毛防缩树脂，必须先进行预氧化才能达到满意的防缩效果，氧化处理采用次氯酸钠和高锰酸钾混合液处理的效果较好，并可降低次氯酸钠的用量。     

拉伸-定型处理对毛发鳞片层改性的异同比较(Herbig反应)

人发及羊毛等角蛋白纤维经拉伸-定型处理后，其漂白性能、染色性能以及反应性等发生一定的变化。通过Herbig反应研究了拉伸-定型处理对毛发纤维鳞片层改性的规律，比较了拉伸-定型处理对人发及羊毛纤维改性作用的不同，从而探讨了拉伸-定型处理对毛发纤维改性的机理。结果表明，拉伸-定型处理对毛发纤维鳞片表层的破坏作用不大，而使表层以下的鳞片层部分发生较大的改性。     

低温氧等离子体处理对羊毛织物性能的影响

为了改善羊毛织物的毡缩、润湿等性能,采用低温氧等离子体对羊毛织物进行改性处理.通过单因素实验,综合评价羊毛织物处理前后的性能变化情况,分析了羊毛织物性能变化与等离子体处理时间、功率和压强变化之间的相互关系;利用原子力显微镜表征了处理前后羊毛纤维鳞片结构的变化情况.实验结果表明,利用低温氧等离子体对羊毛织物进行改性处理,可以获得较好的防毡缩效果,并能改善织物的润湿性能.有效控制处理条件,织物的断裂强力和伸长率不但不会减小,反而可以得到一定程度的增强.     

超声波处理对羊毛纤维性能的影响

以未处理、55℃超声波处理和沸水处理的羊毛纤维为研究对象,对比分析两种处理方法对纤维力学性能、表面形态、化学结构的影响,从纤维角度探讨超声波低温染色的机理.试验结果表明,经超声波处理后的羊毛,束纤维强度降低,油脂质量分数减少,纤维表面鳞片张角增大并产生不规则裂纹,部分二硫键断裂,纤维分子有序程度降低,因此,羊毛在染色过程中更易润湿,染料更易进入纤维内部并扩散.     

用离心萃取法从洗毛污水中回收羊毛脂的研究

处理好洗毛污水的关键是最大限度地提净污水中的羊毛脂。本文介绍了一个回收羊毛脂的新方法——离心萃取法。该方法以制药用的ＬＣ—５００型离心萃取机为主机，选用抽余油作萃取溶剂，为防止回收的羊毛脂变黑，工艺中改用降膜减压蒸发。该方法回收率为６０～７０％，比离心分离法高１～２倍。特别适合羊毛脂含量较低的洗毛污水。     

Effect of Stretching - Setting Treatment on Dyeing Behavior of Wool

Changes of dyeing behavior of wool after stretching -setting treatment are studied. Effects of stretching -setting on wool structure are analyzed. It is concluded that stretching - setting treatment not only reduces wool diameter and increases wool length, but also brings about low-temperature dyeing of wool.     

涤纶的酶法改性研究进展

从涤纶纤维自身的特性和其改性研究的现状、理想的涤纶表面改性应满足的要求以及酶在纺织工业中的应用现状等方面出发,综述了涤纶纤维及其织物酶法改性的背景和国内外研究现状,介绍了涤纶酶法改性研究中所用的酶以及酶的筛选方法,探讨了涤纶酶法改性研究中存在的若干问题,并对涤纶酶法改性的前景做了展望.     

优化洗毛加工提高洗净毛质量

讨论洗净毛质量对后道加工及产品质量的影响．以最低成本、最小污染程度获得洁净而松散的洗净毛是洗毛加工优化的目标．对于国产原毛而言，洗毛机械的改进方案为；①加强开毛浸润作用提高土杂去除率；②长短糟结合提高洗涤效率节约用水；③采用加酶洗毛提高洗净毛白度；④多种机械作用并重提高洗净毛松散度；⑤配各相应污水处理设备实现低排放不排放洗毛。     

Comfort of Light-weight Wool and Wool Blend Woven Fabrics

The comfort of the light-weight woven fabrics was investigated by conducting the wear trials under the controlled climatic conditions. The wear trial under the neutral environmental conditions showed that the lightweight wool and wool blend fabrics are generally less comfortable than the silk fabric, cotton poplin and polyester/cotton poplin fabrics tested in this study. The main shortcoming in terms of comfort for these lightweight wool fabrics is the prickle. Besides, the fabric softness was found to be a very important factor influencing the comfort of the clothing worn next to the skin.     

羊毛的变性处理

纯毛粗绒线的原料一般用４８ｓ～５８ｓ半细毛．将４６ｓ羊毛进行变性处理，若在不损伤纤维的情况下，使得羊毛的细度下降约３μｍ，便可用于纺粗绒线．本文优选了羊毛变性处理的最佳工艺，测试了变性羊毛的主要物理机械性质和染色性能，从变性羊毛的表面形态和结构变化，初步探讨羊毛的变性机理．结果表明，用优选工艺进行羊毛变性处理，基本上脱掉了羊毛表面的鳞片，细度下降３μｍ，不损伤羊毛皮质层；变性羊毛手感柔软，光泽增强，具有良好的防毡缩性；羊毛纤维的染色速度加快，得色鲜艳度提高，物理机械性质变化不大．     

羊毛纬平针织物抗起毛起球整理与性能

选用一种低温环保型水性丙烯酸酯共聚乳液,对羊毛纬平针织物进行了抗起毛起球的整理,研究了整理剂质量浓度、浴比、时间、温度4个因子对羊毛纬平针织物整理效果的影响.根据正交实验得出较优工艺参数为:整理剂质量浓度30g/L、浴比1:35、温度50℃、时间30min.经该工艺整理后可提高羊毛纬平针织物的抗起毛起球性能和织物强力.     

羊毛溶解再利用的研究现状

角蛋白质是生物组织结构中一种重要的结构蛋白质，是天然的高分子物。其分子结构又杂不易溶解。现有研究，主要是利用废弃羊毛来制备角蛋白质溶液，希望得到的溶液角蛋白质分子不受或少受破坏，并保持长链结构。虽然已有很多溶解方法，但真正生态、无损溶解较少，溶解对角蛋白分子量影响的解释就更少。通过对已有研究和利用的回顾，以提出存在的问题和研究方向。     

Shrinkage Properties of Wool and Acrylic/Wool Plain Knitted Fabrics Treated with DC109

This paper examines the effects of shrink - resist treatment, washing cycle and fabric tightness on the shrinkage properties of plain knitted fabrics made from 100% wool, acrylic/wool (50/50) and acrylic/wool (70/30). It was found that shrinkages of both treated and untreated wool fabrics were negatively correlated to fabric tightness and exceeded the IWS shrinkage limits (5% in length and 8 % in area) after 2 - 5A washing cycle. The effect of tightness was not as obvious with acrylic/wool (A/W) fabrics, but the shrinkage was seen to increase with stages of washing cycle for untreated A/W fabrics with some exceeding IWS standard. By applying the DC 109 shrink - resist solvent treatment, it was identified that by with higher percentage of acrylic fibre blended with wool, shrinkage could be reduced considerably and within acceptable limits.