304奥氏体不锈钢带氧化铁皮直接冷轧技术的研究

结合现场生产实际,通过在试验室对奥氏体不锈钢304黑皮卷直接进行压下率分别为10%,20%,30%的冷轧然后退火酸洗的试验,证明在退火酸洗工艺相同的情况下,通过在热轧后进行一定压下率的直接轧制,可以获得与传统No.1产品相比晶粒尺寸等级相同、表面粗糙度更低、力学性能和耐蚀性相近的2E产品,并且获得更大的热轧产品厚度范围,降低冷轧一个轧程后的产品厚度.因此根据不同客户的要求,可以用2E产品替代No.1产品.     

张力对冷轧304奥氏体不锈钢薄板板形影响的数值模拟

为研究张力对单道次冷轧304奥氏体不锈钢薄板(/%:0.053C、0.55Si、1.50Mn、0.030P、0.002S、17.02Cr、8.01Ni、0.50Cu、0.08Mo)板形的影响,基于显示动力学有限元法,采用ANSYS/LS-DYNA软件对2 mm薄带钢的4辊轧机冷轧过程进行模拟和分析。结果表明,在压下量为0.06 mm,前张力13～40 MPa,后张力1～18MPa的轧制工艺下,轧后板带边部主要受压应力作用,中问部分受拉应力作用,带钢将产生微小的边浪;前张力由15 MPa增大至21 MPa时,带钢沿板宽方向应变值趋于均匀,增大前张力可改善带钢的平直度,后张力增大亦有助于改善板形,其效果较前张力明显。     

不同冷轧压下量对亚稳态奥氏体不锈钢00Cr17Ni7织构的影响

 采用X射线衍射技术(XRD)研究了不同冷轧压下量对亚稳态奥氏体不锈钢00Cr17Ni7织构的影响,分析了亚稳态奥氏体不锈钢00Cr17Ni7中马氏体相和奥氏体相的织构变化情况。研究结果表明,不同冷轧压下量下,00Cr17Ni7中的奥氏体相织构主要由Brass{110}<112>、Goss{110}<001>和少量的Copper{112}<111>、S{123}<634>组成,并且随着压下量的增加Brass和Goss织构强度显著提高;同时马氏体相织构主要以{115}<110>、{112}<110> 、{111}<112>、{332}<113>组成,织构的形成主要归因于“Kurdjumov-Sachs取向关系”和“体心立方金属轧制织构类型演变的特点”共同作用的结果。     

冷变形工艺对SUS301L不锈钢组织性能的影响

对亚稳定奥氏体不锈钢SUS301L进行了不同变形量的冷轧,并分别用X射线衍射仪和MP30铁素体测量仪测出了应变诱导马氏体及其含量.采用金相显微镜观察了试样的组织演变.研究结果表明:形变马氏体在剪切带的交叉点形核,新晶核的不断形成促使了形变马氏体的长大；形变马氏体随着冷轧压下量的增加而增加；另外,抗拉强度和硬度的增加幅度相当；平均抗拉强度与平均显微硬度的比值在2.82～3.17之间.     

固溶处理对冷轧Cr-Mn-N奥氏体不锈钢组织性能的影响

对一种节镍型Cr-Mn-N奥氏体不锈钢(Fe-13.8%Cr-11%Mn-0.35%N)的固溶处理工艺进行研究,设计固溶温度为800~1 100 ℃,保温时间为10、20和30 s,冷却方式为水冷和空冷。结果表明,试验钢经过900 ℃保温30 s水冷后,综合力学性能最佳,其中断后伸长率为47.7％,抗拉强度为1 023 MPa,屈服强度为540 MPa,强塑积为48.8 GPa·%。当固溶温度为800 ℃时,塑性提升并不明显,主要由于该温度仍处于敏化温度区间,导致含铬碳化物析出于奥氏体晶界,这对试样的塑性具有不利影响。根据EBSD的统计结果,经过900 ℃保温30 s后,试样组织中晶粒十分细小且均匀,平均晶粒尺寸约为1.4 μm;而提高固溶温度会导致晶粒粗化,1 000 ℃保温30 s后试样平均晶粒尺寸约为2.1 μm,1 100 ℃保温30 s后平均晶粒尺寸约为9.2 μm。     

铜对奥氏体抗菌不锈钢性能的影响

 研究了不同铜含量的奥氏体抗菌不锈钢的抗菌性能、腐蚀性能和力学性能。样品经过热轧、抗菌热处理、冷轧、退火处理后,进行了抗菌试验、腐蚀试验等。试验结果表明,随着铜含量的增加,抗菌性逐渐提高;其耐点蚀性随着铜含量的增加呈提高的趋势;强度随着铜含量的增加先减后增,塑性先增后减。     

A3钢与奥氏体不锈钢冷轧复合板的固溶氮化

研究了 A 3钢与 1Cr18Ni9Ti钢冷轧复合板的再结晶退火工艺及固溶氮化工艺。实践表明 ,用氨分解气作为保护气氛的再结晶退火使复合板不锈钢一侧发生氮化 ,致使塑性下降 ,冷弯 90°时发生断裂。若将复合板在一定压力下的氮气中进行 10 5 0℃× 2 h固溶氮化后空冷 ,可恢复其塑性同时增加不锈钢的抗点蚀性。 X射线衍射分析表明 :不锈钢一侧发生了固溶氮化。     

脉冲电流对奥氏体不锈钢凝固组织的影响

采用储能电容为 15 0 μF的脉冲电源 ,在 5 2 1V和 2 6 4 7V两种充电电压下 ,对奥氏体不锈钢1Cr18Ni9Ti进行电脉冲处理。结果表明 :脉冲电流能够细化奥氏体不锈钢的凝固组织 ,使奥氏体一次枝晶长度明显缩短 ,二次枝晶间距也有所减小。脉冲电流参数不同 ,其作用机理和效果不同。     

冷轧工艺对443铁素体不锈钢抗皱性能影响

以443铁素体不锈钢为研究对象,研究了冷轧工艺对其表面抗皱性能的影响.结果表明,冷轧采用二轧程的生产工艺可以明显改善表面抗起皱性能;一轧程冷轧板芯部存在明显的晶粒簇,沿着轧向成条状分布,晶粒呈非等轴状,尺寸偏大,而二轧程冷轧板芯部组织分布均匀;一轧程冷轧板表层和芯部除了γ纤维再结晶外还保留强烈的{112}<110>织构...     

Analysis of the microstructure and mechanical properties of 309L austenitic stainless steel

309L is a kind of austenitic stainless steel.This paper discusses 309L,which was smelted and rolled in a lab.Its microstructural characteristics in states of as-cast,hot-rolling,cold-rolling and solid solution were investigated respectively by optical microscope (OM).It is found that 309L is composed of austenite and residual δ-ferrite under these conditions,and the δ-ferrite cannot be eliminated easily by heat-treatment.Its hot plasticity and deformation resistance were investigated in a series of heat simulation tests.Its mechanical properties under different cold reductions were studied.All these provide valuable experimental data for the industrial production.     

Effect of vanadium on the microstructure and properties of metastable austenitic stainless steel AISI 301LN

In this study,the effect of vanadium on the microstructure and properties of the metastable austenitic stainless steel AISI 301LN w as investigated. Results of the study show that the addition of vanadium can refine grains and increase the strength of AISI 301LN by solution treatment. After 60%cold-rolling reduction,the microstructure of the steel w as composed of w ork-hardened austenite bands and deformation-inducedɑ'martensite.Considerable w ork-hardening and phase transformation strengthening occurred. After cold rolling and subsequent annealing,the deformation-inducedɑ'martensite w as reversed into fine-grained austenite. The w orkhardened austenite bands underw ent recrystallization; how ever,the structure of the recrystallized austenite grains w as coarser than that of the reversed ones.Simultaneously,the strength of the experimental steels decreased w ith the increase in annealing temperature. The pinning effect of precipitates of vanadium inhibited the grow th of austenite grains.Thus,the desirable combination of strength and ductility w as obtained by grain refinement.     

终轧温度对高氮奥氏体钢组织和力学性能的影响

通过加压冶炼、控制轧制方式获得氮质量分数为0.59%的Mn18Cr18N钢板,研究了终轧温度对高氮奥氏体钢组织和力学性能的影响。结果表明,在再结晶区轧制并且终轧温度为970 ℃的钢板,组织为奥氏体等轴晶和部分孪晶,强度较低,塑性、冲击韧性较好;终轧温度为910 ℃的钢板,大部分组织为变形奥氏体晶粒,有少量再结晶晶粒,随着终轧温度降低钢板强度升高,塑性和冲击韧性降低;在未再结晶区轧制并且终轧温度为780 ℃的钢板,组织为变形严重的奥氏体晶粒,强度最高,塑性、韧性最低。所有试验钢有晶界析出的Cr₂N相,降低终轧温度和减缓轧后冷却速度,会增加Cr₂N相的析出。     

冷轧压下率对TRIP钢组织与力学性能的影响

研究了含铝TRIP钢在相同的热处理条件和不同冷轧压下率时的组织和力学性能。结果表明,随着冷轧压下率增加,材料组织细化,屈服强度连续升高;而抗拉强度和伸长率则由于晶粒细化以及TRIP效应,先升高后降低。冷轧压下率74%时材料的综合性能最佳,此时带状组织的危害也有所减轻或消失。     

异步轧制对316L不锈钢组织与性能的影响

研究了形变量分别为50%和80%的异步轧制(速比1.28)对316L不锈钢显微组织与性能的影响.结果表明:异步轧制后显微组织中出现大量机械孪晶;样品表面粗糙度显著降低,硬度明显提高.由于粗糙度降低和孪晶界的贡献,在腐蚀介质(c(H2SO4)=0.05 mol/L, c(NaCl)=0.5 mol/L的水溶液)中,样品表现出良好的耐腐蚀性能.     

Cr-Mn-Ni-N奥氏体不锈钢冷轧退火酸洗工艺

通过实验室模拟退火试验研究了不同退火工艺对Cr-Mn-Ni-N奥氏体不锈钢力学性能的影响,并对退火态的金相组织和晶粒度进行了检测;分析研究了不同酸洗工艺后Cr-Mn-Ni-N奥氏体不锈钢的表面状态。结果表明,退火工艺对Cr-Mn-Ni-N奥氏体不锈钢性能影响不明显,采用中性盐电解后硝酸酸洗和混酸酸洗工艺均能较好地清除钢板表面氧化皮,但需注意酸洗过程中电解电流、酸液浓度、酸温的良好配合和合理控制。     

不锈钢压花板冷轧工艺开发与轧制实践

介绍了宁波宝新不锈钢有限公司在二十辊可逆冷轧机上轧制不锈钢压花板的开发情况,通过对花纹辊制作使用要求、冷轧参数设定、辊形配置以及花纹高度保证等关键工艺的开发优化,成功实现不锈钢压花板的稳定生产,实践表明,在二十辊轧机上轧制的压花板尺寸精确,花纹整齐均匀,立体感强,可满足不同用户需求。     

烧结工艺对316L不锈钢组织与性能的影响

通过研究烧结气氛和烧结温度对冷等静压态316L不锈钢组织和力学性能的影响,探究了烧结的致密化过程,并初步分析了挤压之后不锈钢的组织与性能。发现真空条件下获得的力学性能均比Ar气氛下烧结的好;在N2气氛烧结的不锈钢抗拉强度为803.5 MPa,屈服强度为407.2 MPa,但是断后延伸率仅为33.7%。在真空气氛下进行烧结,随温度的升高,孔隙率下降、孔隙尺寸减小并发生球化;通过对比烧结温度的影响,得出在1 380℃进行烧结获得的力学性能最好,抗拉强度为578.4 MPa,断后伸长率为52.0%,并且晶粒比较细小。经过挤压处理,不锈钢晶粒进一步细化,抗拉强度为675.6 MPa,屈服强度为305.4 MPa,断后伸长率为45.6%。