Friction stir welding of dissimilar metal joints

Friction stir welding is a solid‐state welding technology, which is suitable for joining dissimilar metals such as aluminium and copper. Because the solidus temperature is typically not exceeded, the formation of intermetallic phases can be reduced when compared to fusion welding processes. In friction stir welding, the intermetallic layer thickness, which determines the seam properties, is influenced by the welding temperature and is formed in correspondence with the Arrhenius law. It is typically in the range of a few hundred nanometers thick. In turn, the process temperature is determined by the process parameters, primarily the rotational speed and the feed rate of the machine tool. In this study, a temperature‐controlled friction stir welding process has been applied to lap joints of aluminium and copper. Welding experiments with various welding speeds and probe lengths were performed in order to assess the effect of the temperature‐time profile near the welding interface. The joints were investigated by tensile shear tests as well as optical microscopy and scanning electron microscopy.     

Effect of pin offset on the mechanical properties of friction stir welded AA 6013 aluminum alloy plates

In this study, AA 6013 aluminum plates were butt‐welded with friction stir welding via pin offset technique. Macrostructural observations revealed that kissing bonds, originated from the broken oxide layers, were found to occur in the welded joints. The fracture location of welded joints after tensile tests was found to be outside the joint area, revealing that kissing bonds which were formed in the stir zone exhibited no detrimental effect on the mechanical properties of joints. Microstructural observations revealed that phases belonging to Mg₂Si, Al₄Cu₂Mg₈Si₇ and Al(MnFe)Si were observed in the x‐ray diffraction pattern of friction stir welded joints. The highest tensile strength with a value of 206 MPa was achieved with the process parameters of 1.5 mm pin offset towards the advancing side and 500 min^?1 tool rotational speed, leading the ratio of tensile strength of joint to ultimate tensile strength of base metal, also known as joint efficiency, to reach 74 %.     

Analysis of dissimilar friction stir welding process for tensile properties of EN AW 2024 and EN AW 5083

The objective of the present study is to analyze the effect of dissimilar friction stir welding process parameters associated with the tool pin profile. Nine different welding experiments were conducted on EN AW 2024 and EN AW 5083 plates. Each of the welded joints was exposed to metallurgical and mechanical tests to determine the effect of the parameters on the welded joint's strength and characteristics. The welding responses or characteristics were analyzed using the statistical tools, grey relational analysis and analysis of variance. Thus, the contribution of each parameter to the process response (ultimate tensile strength and percentage of elongation) was analyzed, and an optimal welding condition was determined. The results of metallurgical analyses showed that the defective joints were mostly in the welded joints fabricated with a conical threaded pin, and the shape of the stir zone was affected by the pin profile and tool rotational speed. The metallurgical results were consistent with the tensile test results. Statistical analyses showed that the most effective parameter on the welded joint strength and elongation is tool rotational speed with 70.3 %. While the tool pin profile affects the stir zone shape, the strength and elongation are not affected. The effect of welding speed (5.6 %) is not significant on strength and elongation.     

Effect of backplate diffusivity on microstructure and mechanical properties of friction stir welded joints

Series of welds were made by friction stir welding (FSW) with various backplates made out of materials ranging from low diffusivity granite to high diffusivity copper in order to reveal the effect of backplate diffusivity on the joint microstructure and properties. The temperature, microstructure, microhardness and tensile properties of joints were compared and discussed. Results show that the backplate with high diffusivity effectively decreases the heat input to the workpiece during FSW. With decreasing the backplate diffusivity the sizes of equiaxed recrystallized grains in the nugget zone increase obviously, while the hardness of the nugget zone also increases a little. The interface between the thermo-mechanically affected zone and nugget zone at the retreating side disappears under the granite backplate. Moreover, the ductility of the joint is more excellent under the copper backplate, but under the granite backplate the failure has mixed fracture characteristics of quasi-cleavage and dimples.     

Evolution of microstructures and mechanical properties in similar and dissimilar friction stir welding of AA5086 and AA6061

In this work, thermo-mechanical behavior and microstructural evolution in similar and dissimilar friction stir welding of AA6061-T6 and AA5086-O have been investigated. Firstly, the thermo-mechanical behaviors of materials during similar and dissimilar FSW operations have been predicted using three-dimensional finite element software, ABAQUS, then, the mechanical properties and the developed microstructures within the welded samples have been studied with the aid of experimental observations and model predictions. It is found that different strengthening mechanisms in AA5086 and AA6061 result in complex behaviors in hardness of the welded cross section where the hardness variation in similar AA5086-O joints mainly depends on recrystallization and generation of fine grains in weld nugget, however, the hardness variations in the weld zone of AA6061/AA6061 and AA6061/AA5086 joints are affected by subsequent aging phenomenon. Also, both experimental and predicted data illustrate that the peak temperature in FSW of AA6061/AA6061 is the highest compared to the other joints employing the same welding parameters.     

Friction stir welded butt joints optimization

Friction stir welding is an emergent technique that still lacks optimization studies in the literature. Optimum parameters are of prime importance for future investigations, as it will allow for consistent and sound welds. This is of even greater relevance for industrial applications, as for friction stir welding to become a mainstream joining technology. This paper presents an optimization study of friction stir welded butt joints through the Taguchi method. The most influent welding parameters and their trends were identified. The process optimization for the selected aluminium alloy was achieved and the best parameters combination to accomplished quality welds was selected. The parameters combination that lead to higher mechanical stiffness were: 1000 min^–1, 290 mm/min, 0.15 mm from the probe to the root surface and a shoulder/probe diameters ratio of 2 (shoulder diameter of 12 mm). Equations to estimate joint properties were derived by multiregression.     

Application of the hybrid process ultrasound enhanced friction stir welding on dissimilar aluminum/dual‐phase steel and aluminum/magnesium joints

Friction stir welding as a solid‐state joining method with its comparatively low process temperatures is suitable for joining dissimilar materials like aluminum/magnesium or aluminum/steel. Such hybrid joints are of great interest regarding lightweight efforts in different industrial fields like the transportation area. The present work investigates the influence of additionally transmitted power ultrasound during the friction stir welding on the joint properties of EN AC‐48000/AZ91 and EN AW‐6061/DP600. Therefore, conventional friction stir welding was continuously compared to ultrasound enhanced friction stir welding. Light microscopic analysis and nondestructive testing of the joints using x‐ray and high frequency ultrasound show different morphologies of the nugget for the aluminum/magnesium joints as well as differences in the amount and size of steel particles in the nugget of aluminum/steel joints. Scanning electron microcopy proves differences in the thickness of continuous intermetallic layers for the aluminum/steel joints realized with and without power ultrasound. Regarding the tensile strength of the joints the power ultrasound leads to increased joint strengths for EN AC‐48000/AZ91 joints compared to a decrease for EN AW‐6061/DP600 joints. Corrosion investigations show an influence of the ultrasound power on the corrosion properties of EN AC‐48000/AZ91 joints which is attributed to a changed aluminum content in the nugget region. Because of the great potential difference between the magnesium and the nugget phase the transitional area exhibits strong galvanic corrosion. For EN AW‐6061/DP600 joints an increased corrosion caused by galvanic effects is not expected as the potentials of the EN AW‐6061 aluminum alloy and DP600 steel are very similar.     

Effects of peening on mechanical properties in friction stir welded 2195 aluminum alloy joints

The effects of surface treatment techniques like laser and shot peening on the mechanical properties were investigated for friction stir welded 2195 aluminum alloy joints. The loading in the tensile specimens was applied in a direction perpendicular to the weld direction. The peening effects on the local mechanical properties through the different regions of the weld were characterized using a digital image correlation technique assuming an iso-stress condition. This assumption implies that the stress is uniform over the cross-section and is equal to the average stress. The surface strain and average stress were used giving an average stress–strain curve over the region of interest. The extension of the iso-stress assumption to calculate local stress–strain curves in surface treated regions is a novel approach and will help to understand and improve the local behavior at various regions across the weld resulting in a sound welding process. The surface and through-thickness residual stresses were also assessed using the X-ray diffraction and the contour methods. The laser peened samples displayed approximately 60% increase in the yield strength of the material. In contrast, shot peening exhibited only modest improvement to the tensile properties when compared to the unpeened FSW specimens. The result that laser peening is superior to shot peening because of the depth of penetration is original since this superiority has not been presented before regarding mechanical properties performance.     

Conventional and in situ tensile test of friction stir welded steel – Optimization of processing parameters

In the present investigation, steel plates were joined at different tool traversing speed by friction stir welding keeping other parameters same. Microstructural characterization was carried out with optical and scanning electron microscopes. At weld nugget pearlite and bainite were present within ferrite matrix. Thermo‐mechanically and heat affected zones microstructure consisted of pearlite and ferrite. Second phase area fraction and matrix grain size at different regions were varied depending on welding parameters. Weld nugget exhibited substantial improvement in microhardness with respect to base metal. In this respect heat affected zone revealed minimum microhardness and was below base metal value. Tensile tests were carried out on standard and miniature specimens in scanning electron microscope. Highest joint efficiency to the tune of ～82 % and ～120 % of that of base metal obtained for standard and miniature specimens, respectively machined from weld fabricated at lowest welding speed. With increment in welding speed assembly strength was reduced for both types of specimens. Standard specimens failed from heat affected zone and miniature specimens failed through centre of weld nugget. Apart from matrix grain size and second phase area fraction, precipitation of microalloyed carbide / carbonitride was responsible for altering the joint strength.     

Microstructure and mechanical properties in nano and microscale SiC-included dissimilar friction stir welding of AA6061-AA2024

This work investigates the effect of SiC particles on the microstructure and mechanical properties of dissimilar friction stir welding between AA6061-T6 and AA2024-T351. Two variations in the size of SiC particles, along the joint line, various groove width, and tool offset, were used for the welding. It was found that the joints made by rotational speed of 800?rev?min^?1, travelling speed of 31.5?mm?min^?1, groove width of 0.3?mm, and tool offset of 0.5?mm exhibited the most uniform distribution of particles for both micro- and nano-scale SiC particles. Additionally, the smaller and rounded equiaxed particles result in easier material flow, a more uniform metal matrix composite, the smallest grain size in the stir zone and the highest tensile strength.     

Microstructural evolution and mechanical properties of dissimilar Al–Cu joints produced by friction stir welding

5A02 aluminum alloy and pure copper were joined by friction stir welding (FSW). A defect-free joint was obtained when one of process parameters, i.e. the traverse speed was lowered from 40 mm/min to 20 mm/min. A good mixing of Al and Cu was observed in the weld nugget zone (WNZ). A large amount of fine Cu particles were dispersed in the upper part of the WNZ producing a composite-like structure. In the lower part, nano-scaled intercalations were observed and identified by transmission electron microscopy (TEM). These layered structures were subsequently confirmed as Al₄Cu₉ (γ), Al₂Cu₃ (ε), Al₂Cu (θ), respectively. Formation of these microstructures caused an inhomogeneous hardness profile. Particularly, a distinct rise in hardness was noticed at the Al/Cu interface. Excellent metallurgical bonding between Al and Cu gave rise to good behaviors in the tensile and bending strength.     

Influence of probe offset distance on interfacial microstructure and mechanical properties of friction stir butt welded joint of Ti6Al4V and A6061 dissimilar alloys

Friction stir butt welding of titanium alloy Ti6Al4V and aluminum alloy A6061-T6 with 2 mm thickness was conducted by offsetting probe edge into the titanium alloy at rotation speed of 750 rpm and 1000 rpm and welding speed of 120 mm/min. The effect of probe offset distance on the interfacial microstructure and mechanical properties of the butt joint was investigated. When the probe offset distance is not sufficient, the two alloys cannot be completely joined together, i.e. there exists no bonding or kissing bonding at the root part of joint interface. However, when the probe offset distance is too large, a great amount of intermetallic compounds are formed at the joint interface and its adjacency, leading to fracturing roughly along the joint interface during a tensile test. In a proper range of probe offset distance, sound dissimilar butt joints are produced, which have comparatively high tensile strength and fracture in heat affected zone of the aluminum alloy during a tensile test.     

Improving mechanical properties of pinless friction stir spot welded joints by eliminating hook defect

Hook defect (HD) seriously decreases the mechanical properties of friction stir spot welded (FSSW) joints. In this study, two methods were therefore used to eliminate the HD in pinless FSSW joints. The one is changing welding parameters such as rotating speed and dwell time. The other one is FSSW plus subsequent friction stir welding (FSSW-FSW), which is an innovative method proposed in this study. Experimental results showed that the HD in pinless FSSWed AA2024 joints was successfully eliminated by using FSSW-FSW, not by changing process parameters. The joints without HD exhibited a tensile–shear load of as much as 12 kN, which was higher than that of 6.9 kN in the joints with HD. Furthermore, it was proved that the tensile–shear load is not greatly improved only by increasing the nugget zone when HD still existed in the FSSW joints. In addition, the fracture morphology analysis demonstrated that the shear fracture of the FSSW-FSW joints took place along the boundary between the upper and lower sheets through the weld nugget, and the faying surface between the two sheets was completely sheared off.     

Force response characteristics and mechanical properties of friction stir welded AA2024 sheets

Process force and tensile properties in friction stir welding of AA2024 sheets were studied. Results show that the forces present a periodic variation with the same periodicity which is nearly equal to the time of one tool rotation, and thus it only depends on rotation speed. With increasing welding speed the forces increase gradually, while with increasing rotation speed the forces first decrease and then increase. Joints with superior strength-ductility synergy are produced at 900?rev?min^?1–300?mm?min^?1 and 1000?rev?min^?1–350?mm?min^?1. These joints experience nearly the same peak temperature and axial force. As heat input increases the failure initiates from the interface between nugget zone (NZ) and thermo-mechanically affected zone to heat-affected zone continuing to NZ.     

Microstructures and mechanical properties of friction stir welds on 9% Cr reduced activation ferritic/martensitic steel

In this study,the microstructures and mechanical properties of 9%Cr reduced activation ferritic/martensitic(RAFM) steel friction stir welded joints were investigated.When a W-Re tool is used,the recommended welding parameters are 300 rpm rotational speed,60 mm/min welding speed and10 kn axial force.In stir zone(SZ),austenite dynamic recrystallization induced by plastic deformation and the high cooling rates lead to an obvious refinement of prior austenite grains and martensite laths.The microstructure in SZ contains lath martensite with high dislocation density,a lot of nano-sized MX and M_3C phase particles,but almost no M_(23)C_6 precipitates.In thermal mechanically affect zone(TMAZ)and heat affect zone(HAZ),refinement of prior austenite and martensitic laths and partial dissolution of M_(23)C_6 precipitates are obtained at relatively low rotational speed.However,with the increase of heat input,coarsening of martensitic laths,prior austenite grains,and complete dissolution of M_(23)C_6 precipitates are achieved.Impact toughness of SZ at-20?C is slightly lower than that of base material(BM),and exhibits a decreasing trend with the increase of rotational speed.     

Inhomogeneity of microstructure and mechanical properties in the nugget of friction stir welded thick 7075 aluminum alloy joints

In this study, 20 mm thick AA7075-T6 alloy plates were joined by friction stir welding. The microstructure and mechanical properties of the nugget zone along the thickness direction from the top to the bottom was investigated. The results showed that the microstructure including the grain size, the degree of dynamic recrystallization, the misorientation angle distribution and the precipitation phase containing its size, type and content exhibited a gradient distribution along the thickness direction. The testing results of mechanical properties of the slices showed that the nugget was gradually weakened along the depth from the top to the bottom. The maximum ultimate tensile strength, yield strength and elongation of the slice in the nugget top-middle are obtained, which are 415 MPa, 255 MPa and 8.1%, respectively.     

Weld zone representation methods during the stretching of friction stir welded blanks with dissimilar sheet thickness: A study using numerical simulations

In this work, the validity of weld zone representation as single zone or double zone under varied weld conditions of friction stir welded (FSW) blanks with dissimilar thicknesses sheets is explored. During LDH test simulations, representative base material of 1.5 mm and 1.1 mm thickness is considered. It is observed that modeling FSW blanks with double zone assumption plays a vital role for accurate formability prediction. There are possibilities of obtaining multiple domains of weld conditions for the single zone and double zone assumption validity. The failure locations also affect the weld zone representation along with the critical error percentage difference between reference model (single zone) and double zone model FSW blanks. The number of single zone models has increased in transverse weld orientation and number of double zone models has increased in longitudinal weld orientation in the case of FSW blanks with dissimilar thickness as compared to similar thickness FSW blanks. A comparison is done between the limit strain values for single zone and double zone assumptions with reference model. The pattern that is observed in the load‐punch stroke behavior is also seen in limit strain comparison for weld zone representation.     

Application and exploration of friction stir welding/processing in plastics industry

Friction stir welding (FSW) is a green, pollution-free, low-energy technology with high manoeuvrability. Thermoplastic plastics have extensive applications in the present industry because they offer excellent physical and corrosion properties, high degree freedom of processing and design. In this paper, the current state of FSW/P in plastics industry, including tool improvement, welding methods, process parameters optimisation, metal and polymer joining as well as composites fabrication, has been addressed. Although it presents a major challenge, FSW/P has a great potential to produce defect-free joint and fabricate composites in polymer materials.     

Fracture and fatigue crack growth behaviour of PMMC friction stir welded butt joints

The paper is focused on the evaluation of the fracture and Fatigue Crack Growth (FCG) properties of butt joints of particulate metal-matrix composite (PMMC) obtained by friction stir welding (FSW). The materials considered are two aluminum alloy matrix/alumina particle PMMCs (AA6061/Al₂O₃/20p and AA7005/Al₂O₃/10p). Tests were conducted on unwelded and welded PMMCs using CT and Extended CT (ECT) specimen geometries, respectively. The crack growth rate was monitored by means of compliance with a strain gage attached on the back of the specimen. FCG experiments were carried out both at the centre and in the Thermo-Mechanically Altered Zone (TMAZ) at the side of the weld. The comparison between unwelded and welded PMMCs showed that FSW influences fracture toughness and FCG rate in a different fashion depending on the material. In particular, the FSW AA6061/Al₂O₃/20p butt joint exhibited comparable fracture toughness and higher FCG threshold with respect to the unwelded material, while in the case of AA7005/Al₂O₃/10p the behaviour is the opposite. The interpretation of this trend has been carried out by optical analysis of the crack path roughness and its correlation with the FCG rate. The dynamic recrystallization of the aluminum matrix and particle shaping operated by the FSW tool are at the ground of the explanation.     

Influences of joint geometry on defects and mechanical properties of friction stir welded AA6061-T4 T-joints

In this paper, AA6061-T4 T-joints with three different joint geometries of T-lap/T-butt-lap/T-butt were fabricated successfully by friction stir welding. The distributions and formation mechanisms of defects in friction stir welded (FSWed) T-joints were discussed through macro and micro-observations, respectively. Hardness profiles of the as-welded samples were also measured to evaluate the softening effect during the process. What’s more, influences of joint geometry and the traverse speed on the tensile properties of FSWed T-joints were investigated. All the experimental results indicate that tunnel defects and kissing bond are easily formed and vary significantly in T-joints of the three joint geometries. Defects are moderated to a large extent with decreasing the traverse speed, but the specific relationship to tensile properties is complicated. T-lap joints present the superior tensile properties along the skin direction among the three geometries, the same as T-butt joints along the stringer direction. All the as-welded samples almost fractured in the locations of softening zones and bonding surfaces.