选区激光熔化成型GH3536合金的显微组织与拉伸性能

采用选区激光熔化(SLM)成型技术制备了GH3536合金试样,并对其显微组织与拉伸性能进行了分析。结果表明:SLM成型GH3536合金试样的基体显微组织为奥氏体,试样内部存在明显的微裂纹,纵向和横向的显微组织形貌存在明显不同;该试样纵向的拉伸性能优于横向的,相对于热轧Hastelloy X (GH3536)合金,SLM成型GH3536合金试样的强度较好,但塑性较差。     

纳米WC增强选区激光熔化AlSi10Mg显微组织与力学性能EI北大核心CSCD

为了进一步增强选区激光熔化(SLM)成型AlSi10Mg合金的性能,采用物理混合方法混合纳米WC与AlSi10Mg得到WC质量分数为0.1%的WC/AlSi10Mg复合材料,利用选区激光熔化成型机制备试样块。通过对比同种工艺制备的AlSi10Mg试样,探究纳米WC对其微观组织形成、演变规律及其组织对力学性能的影响。结果显示,WC/AlSi10Mg粉末球形度好,粒度分布集中在20~60μm。WC/AlSi10Mg试样致密度达到99%以上,硬度约为158.89HV,相比AlSi10Mg试样增加了14.58%。WC/AlSi10Mg试样组织生长均匀、致密,有明显的熔池线。晶粒内部为α-Al基体,边界为夹杂着WC的共晶Si相。WC/AlSi10Mg试样屈服强度达到337.75 MPa,抗拉强度高达514.00 MPa,伸长率为3.78%,相比同种工艺AlSi10Mg试样分别增加了4.73%,6.25%和35.97%。因此,SLM成型WC/AlSi10Mg纳米复合材料零件相比AlSi10Mg零件具有更好的应用前景。     

轧制温度对Al−4.5Cu−1.5Mg−0.5Zr合金显微组织及性能影响

目的 优化加工工艺,改善合金的组织,提高合金的力学性能。方法 采用金相(OM)观察、拉伸试验和X射线衍射,分析在大应变轧制下冷轧结合T6态处理后板材的成形性能,引入Williamson-Hall模型和Taylor函数,分析合金内部位错密度的变化规律及其对力学性能的影响。结果 随着前期轧制温度从350 ℃升高到400 ℃,合金晶粒得到明显细化,再结晶充分,晶粒尺寸细小,晶界处第二相粗大;冷轧后晶粒破碎严重,晶粒的碎化方向与轧制方向垂直;在350 ℃时,合金内部的位错密度为1.62×10¹⁵ m^?2,位错密度对强度的贡献值为219.5 MPa,其抗拉强度最大为602 MPa、屈服强度为512 MPa、伸长率为12.6%。结论 Al?4.5Cu?1.5Mg?0.5Zr合金的晶粒组织明显细化,其力学性能得到提升。     

热处理工艺对激光选区熔化AM247LC合金组织与性能的影响规律

目的 研究不同热处理制度对激光选区熔化（SLM）AM247LC合金微观组织和力学性能的影响规律。方法 对激光选区熔化制备的AM247LC合金分别进行900℃/16h的直接时效热处理和1 210℃/30 min+1 050℃/30min+950℃/16h的固溶时效热处理,通过OM、SEM、EBSD、XRD等表征手段研究合金热处理前后的晶粒组织、碳化物及析出相等微观组织的变化,并对打印态及不同热处理态样品的室温拉伸性能进行测试,以表征热处理对其力学性能的影响行为。结果 打印态AM247LC合金中存在大量粗大柱状晶和细小晶粒组织;直接时效热处理（900℃/16 h）后的AM247LC合金晶粒组织与打印态类似,但析出了大量γ’强化相;固溶时效热处理（1 210℃/30 min+1 050℃/30 min+950℃/16 h）后,AM247LC合金发生了再结晶,形成大量退火孪晶,并且析出沿晶界分布非连续的微米级碳化物及大量γ’强化相。合金打印态的屈服强度为846.5 MPa,断裂伸长率可达19.6%;直接时效热处理后,合金屈服强度为1 042.8 MPa,断裂伸长率明显降低,仅为11.2%;固溶...     

激光选区熔化成形原位自生TiB2/Al-Si复合材料的微观组织和力学性能

利用激光选区熔化（SLM）技术制备了原位自生TiB₂纳米陶瓷颗粒增强Al-Si基复合材料,并对成形后的TiB₂/Al-Si复合材料进行不同的热处理。通过XRD物相分析、SEM微观组织观察、电子背散射衍射（EBSD）、EDS元素扫描分析和力学拉伸试验等对TiB₂/Al-Si复合材料的微观组织进行观察和力学性能测试。研究表明,在原位自生TiB₂纳米陶瓷颗粒和SLM快速凝固特性的共同作用下,SLM成形的原位自生TiB₂/Al-Si复合材料具有超细晶结构,平均晶粒尺寸为1.1 μm;TiB₂/Al-Si复合材料的力学性能优异,屈服强度为262 MPa,抗拉强度为435 MPa,延伸率为11.88%。对比经不同热处理的TiB₂/Al-Si复合材料,直接时效处理（150℃/12 h）的TiB₂/Al-Si复合材料性能最优,抗拉强度达到488 MPa,提高了53 MPa,延伸率降低至7.2%。     

热处理对SLM 18Ni300马氏体时效钢力学性能的影响

为探究热处理对激光选区熔化（Selective Laser Melting,SLM）成形18Ni300马氏体时效钢力学性能的影响,利用激光选区熔化技术制备18Ni300马氏体时效钢试样,分别对成形试样进行时效处理、固溶处理和固溶+时效处理。通过金相显微镜、扫描电镜、硬度计和拉伸试验机,分别测试分析了不同热处理SLM 18Ni300马氏体时效钢的微观组织、显微硬度和拉伸性能。固溶+时效处理后,SLM 18Ni300马氏体时效钢激光熔池消失;组织为均匀致密的板条马氏体,且均有细小析出物弥散分布于晶界和板条间;抗拉强度和硬度显著提高,但延伸率明显下降。此外,固溶+时效处理后材料的强塑积可以得到改善。     

退火态激光选区熔化成形AlSi10Mg合金组织与力学性能

AlSi10Mg合金具有高比强度、高耐磨性等优良特点。由于其成分接近共晶点,成形性能良好,被广泛应用于激光选区熔化技术。然而其热处理制度仍然沿用传统铸态合金的热处理规范,影响了其性能的充分发挥。本工作采用激光选区熔化技术制备了AlSi10Mg合金,并研究了沉积态和后续热处理过程中组织演化规律及其对室温力学性能的影响机制。研究发现：沉积态组织由沿沉积方向生长的α-Al柱状枝晶及枝晶间网状Al-Si共晶组成,具有强烈的〈100〉方向织构,沉积层由三部分组成,分别是细晶区、粗晶区及热影响区,抗拉强度389.5 MPa,伸长率4%。退火过程中,共晶Si破碎、球化,基体中过饱和Si不断析出长大。当退火温度从200 ℃提高到500 ℃时,Si颗粒发生Ostwald熟化,平均尺寸增长了23倍。经过300 ℃和500 ℃退火处理后,试样抗拉强度分别为287.0 MPa和268.0 MPa,但伸长率分别提高到10.3%和17.2%。     

热处理对激光选区熔化成型高速钢组织和力学性能的影响EI北大核心CSCD

基于激光选区熔化(selective laser melting,SLM)技术,采用加热打印基板和低功率慢扫描的打印策略,制备了近全致密、低缺陷的高速钢样品;对比分析了固溶淬火及1~4次高温回火等热处理工艺对高速钢显微组织及力学性能的影响。结果表明:SLM极高的熔融/冷却速率产生了细晶奥氏体组织,解决了高速钢中常见的粗大莱氏体组织和网状碳化物问题。固溶淬火处理后高速钢组织由马氏体和残余奥氏体组成。随后在数次高温回火过程中,高速钢逐渐向回火马氏体转变,并析出大量微米级和纳米级MC型碳化物。在马氏体相变强化和MC型碳化物沉淀强化作用下,固溶淬火+3次回火的Tempered-Ⅲ样品硬度60HRC,抗弯强度3621 MPa,弯曲断裂应变为10.1%,获得硬度、强度和韧性匹配较佳的综合性能。继续增加回火次数则导致部分碳化物长大,使得高速钢弯曲断裂应变有所降低。通过SLM技术结合固溶淬火+高温回火,能够充分发挥细晶强化、相变强化和沉淀强化效果,为高强高韧复杂形状高速钢零件的快速制备提供了新途径。     

Effect of different heat treatments on the microstructure and mechanical properties in selective laser melted INCONEL 718 alloy

The microstructure and tensile properties of selective laser melted (SLM) Inconel 718 alloy were studied in the as-printed and different heat treat conditions. The SLM as-print microstructures exhibited columnar grain structures with very fine dendritic structure with segregation of elements. Apart from the standard heat treatment, three other heat treat cycle variants were carried out in an attempt to remove the extensive segregation of elements and modify the textured grain structure of the SLM as-print microstructure. Increasing the homogenization temperature reduced the segregation and coarsened the grain structure. However, the grains still remained columnar, and the material became softer with reduction in strength. After the ageing treatment, the tensile strength improved significantly for all the heat treated samples, which is typical for precipitation hardening of IN718 alloy. The microstructures of the heat treated samples exhibited the needle shaped δ, carbides, and finely dispersed γ″, γ′ phases.     

热工艺对激光选区熔化Hastelloy X合金组织及拉伸性能的影响

采用激光选区熔化技术制备Hastelloy X试样,研究热等静压和固溶处理对Hastelloy X试样显微组织及拉伸性能的影响。结果表明:沉积态组织中可观察到熔池形貌、柱状晶及晶内的胞晶结构,无析出物,其拉伸性能表现出高强度低塑性特点,高温拉伸断口沿激光扫描熔化道断裂。经热等静压后,组织演变为等轴晶,晶界及晶内存在较多的析出物,裂纹愈合,试样拉伸强度降低,塑性提升,尤其是高温屈服强度降低了约48%,高温伸长率提升了约59%。经热等静压+固溶处理后,晶粒尺寸及形貌与热等静压态相比近乎无差异,但晶内析出物明显减少,该状态下的综合拉伸性能最优。     

The effect of laser energy input on the microstructure,physical and mechanical properties of Ti-6Al-4V alloys by selective laser melting

Selective laser melting is an advanced manufacturing process which can control the microstructure evolution and mechanical properties of as-manufactured products via various processing parameters. In this study, the porosity/relative density, surface quality, microstructure and mechanical properties were investigated on the selective laser melted Ti-6Al-4V alloy specimens fabricated with a wide range of laser energy inputs. It was found that the microstructure of selected laser melted Ti-6Al-4V alloys is typical of acicular martensites α′. Quantitative analysis reveals that the relative density, martensitic lath size and microhardness increase with the laser energy input. The surface quality is also substantially affected by the energy input.     

激光选区熔化纳米SiC/AlSi7Mg复合材料微观组织及力学性能EI北大核心CSCD

采用机械混合法制备纳米SiC/AlSi7Mg混合粉末,利用激光选区熔化技术(selective laser melting,SLM)成形纳米SiC颗粒增强AlSi7Mg复合材料,观察和分析试样的相对密度、物相和微观组织,并测试材料的硬度和拉伸性能。结果表明:SLM成形纳米SiC/AlSi7Mg复合材料试样的相对密度随着扫描速度和扫描间距的增大均呈现先增加后减少的趋势,相对密度最高可达99.75%;试样微观组织与SLM成形铝合金相似,Si相呈网状结构均匀嵌入α-Al基体中,且在Al基体中存在与Si分布相似的纳米SiC团聚物及Mg_(2)Si相;与AlSi7Mg相比,复合材料微观组织由柱状晶转化为等轴晶,且晶粒明显细化(平均晶粒尺寸为1.36μm);由于SiC的加入,产生细晶强化和固溶强化,试样的硬度和强度均明显提高,硬度最高达到137.3HV,抗拉强度达到448.3 MPa,屈服强度达到334.7 MPa,但伸长率下降至3.9%,断裂模式主要为脆性断裂。     

退火处理对激光沉积制造TC4钛合金组织及力学性能影响EI北大核心CSCD

以TC4球形粉末为原料,采用激光沉积制造技术制备TC4钛合金厚壁件。通过光学显微镜(OM)、扫描电子显微镜(SEM)、X射线衍射(XRD)等方法研究了退火处理对激光沉积制造TC4显微组织及力学性能的影响。结果表明:试样经α+β两相区退火处理后,显微组织为网篮组织,经β单相区退火后,组织转变为魏氏组织;退火试样力学性能仍存在各向异性:Z向试样强度较低,塑性较好,而XY向试样强度高,塑性较差,退火温度对试样的各向异性具有明显影响;XY向试样拉伸性能存在较明显的分散性;α+β两相区退火处理后两个方向上均为韧性断裂,β单相区退火处理后试样强度与塑性大幅下降,且XY向试样为脆性断裂。     

均匀化处理对Mg-13Gd-3.5Y-2Zn-0.5Zr镁合金组织和力学性能的影响

对Mg-13Gd-3.5Y-2Zn-0.5Zr镁合金铸锭进行均匀化处理,温度为505～525℃,时间为4～24h,并采用光学显微镜(OM)、扫描电子显微镜(SEM)、X射线衍射仪(XRD)和万能材料试验机等检测手段分析均匀化处理前后合金微观组织和力学性能的变化。结果表明:均匀化处理后,原始组织中网状分布共晶化合物转化成晶界处不连续分布的块状LPSO相,离散分布的方块状富稀土相溶解。力学性能测试显示,铸态镁合金的抗拉强度为172.9MPa,伸长率为1.8%,经过均匀化处理后合金的力学性能得到提高,在515℃/16h均匀化制度下,合金室温抗拉强度为212.3MPa,伸长率为3.1%;在200℃下抗拉强度为237.2MPa,伸长率为9.7%,性能达到最佳。断口扫描显示,铸态合金是以撕裂棱与解理台阶为主的解理脆性断裂,均匀化处理后的合金中出现小而浅的韧窝,但仍然是以解理台阶为主的准解理断裂,塑性提高有限,长程有序相可成为裂纹的萌生源。