TC4/TNM钎焊接头界面组织及性能

采用Ti-25.65Zr-13.3Cu-12.35Ni-3Co-2Mo(wt.%)非晶箔带钎料在900 ℃~1020 ℃/10 min工艺下真空钎焊连接TC4和TNM合金,并系统研究了TC4/TNM钎焊接头的界面组织和形成机理以及钎焊温度对界面组织和剪切强度的影响规律。结果表明：钎焊温度900～980 ℃时接头的组织为TC4/细小网篮状(α+β)-Ti/γ-(Ti,Zr)2(Cu,Ni) + α-Ti/Ti3Al/TNM,随钎焊温度升高,钎缝中硬脆的γ相减少、韧性的α-Ti增加。钎焊温度1000 ℃和1020 ℃时,接头的界面反应层由三层演变成两层且对应的物相分别是韧性差的粗针状(α+β)-Ti和Ti3Al,粗针状(α+β)-Ti随温度升高进一步粗化。钎焊接头剪切强度随温度升高先增加后减小,钎焊温度980 ℃时剪切强度达到最大值494.83 MPa。剪切测试的钎焊接头均脆性断裂于TNM侧的钎缝中。     

钎焊温度对TC4与Ti3Al-Nb合金钎焊接头组织的影响

采用50Ti-20Zr-20Ni-10Cu粉末钎料对Ti3Al-Nb合金与TC4合金进行真空钎焊,通过SEM、EDS、电子探针及拉伸试验研究不同钎焊温度下钎焊接头的显微组织及性能特征.结果表明,钎焊温度升高钎焊接头强度并不提高;不同温度下钎焊接头中靠近TC4合金基体边界处均生成魏氏体组织,随温度升高魏氏体组织粗化程度加剧;整个钎焊接头中Ti3Al-Nb合金基体与钎料的反应程度弱于TC4合金基体.     

Ti3SiC2陶瓷与TC4合金钎焊接头微观组织及性能

采用接触反应钎焊,以Ti/Ni/Ti为中间层,实现了Ti3SiC2陶瓷与TC4合金的连接。钎焊接头的典型界面组织为：TC4/α-Ti + β-Ti + Ti2Ni/Ti2Ni + Ti3AlC + Ti5Si3Cx + TiC/Ti3SiC2。随着钎焊温度的升高和保温时间的延长,钎缝宽度增加,Ti2Ni相含量减少。钎焊温度为980 ℃时,大量的Ti2Ni相分布于反应区;连接温度为1000 ℃时,钎焊接头抗剪强度最高,达到82 MPa,断裂主要发生在陶瓷母材处;随着钎焊温度的继续提升,在反应区和TC4合金界面处出现明显孔洞,接头力学性能显著降低。此外,分析了钎焊接头的形成机制。     

TiZrNiCu钎料钎焊Ti53311S高温钛合金接头界面结构及性能

采用TiZrNiCu钎料实现了Ti53311S高温钛合金的钎焊连接,通过SEM、EDS、微区XRD等方法分析了接头界面的微观组织结构,重点研究了钎焊温度对接头界面结构及力学性能的影响规律。结果表明,钎焊接头的典型界面结构为:Ti53311S/α+β/(Ti,Zr)2(Cu,Ni)化合物/α+β/Ti53311S;随钎焊温度的升高,(Ti,Zr)2(Cu,Ni)化合物数量不断减少,当钎焊温度超过α+β→β转变温度时,钎缝及钛合金母材均形成片层状α+β组织;接头抗拉强度随钎焊温度升高逐渐增加后趋于稳定,当在1010℃/10 min条件下钎焊时,接头平均抗拉强度最大为912.8 MPa,断口分析表明,断裂发生于钎缝处,为脆性解理断裂。     

钎焊温度对TCA与Ti3Al—Nb合金钎焊接头组织的影响

采用50Ti-20Zr-20Ni-10Cu粉末钎料对Ti，Al—Nh合金与TC4合金进行真空钎焊，通过SEM、EDS、电子探针及拉伸试验研究不同钎焊温度下钎焊接头的显微组织及性能特征。结果表明，钎焊温度升高钎焊接头强度并不提高；不同温度下钎焊接头中靠近TC4合金基体边界处均生成魏氏体组织，随温度升高魏氏体组织粗化程度加剧；整个钎焊接头中Ti3Al-Nb合金基体与钎料的反应程度弱于TCA合金基体。     

TC4钛合金钎焊接头的组织与性能

采用Ti-37.5Zr-15Cu-10Ni钎料对TC4钛合金进行了钎焊,钎焊温度为900 ℃,保温时间分别为30、60和90 min。结果表明,在900 ℃时该钎料可润湿TC4母材,润湿角平均值为16.7°。保温时间为90 min时,钎焊界面中心处钎料元素已扩散得较充分,与钎料合金成分相比,Zr元素由37.5%降低至1.79%,Cu和Ni元素分别由15%和10%降低至1.66%和1.64%。TC4钛合金钎焊试样的室温抗拉强度平均值为1007.6 MPa,多数试样断于母材,属于微孔聚合机制导致的断裂失效。     

TiB_w/TC4钛合金与C/C复合材料钎焊接头的界面组织结构

采用活性钎料TiZrNiCu对TiBw/TC4钛合金和C/C复合材料进行了钎焊连接,借助SEM,EDS,XRD等分析手段研究了钎焊工艺参数对接头界面组织结构的影响.结果表明,采用TiZrNiCu钎料可以实现对两种材料的连接,接头典型的界面结构为：C/C复合材料/TiC＋（Ti,Zr）2（Cu,Ni）/Ti（s,s）＋（...     

TiZrNiCu钎料在TA1/TC4异质界面的反应润湿过程

试验采用Ti51ZrNiCu钎料,研究其在TA1/TC4异质界面的反应润湿过程,使用扫描电子显微镜(SEM)、能谱分析仪(EDS)及润湿角测量仪等分析方法研究了不同表面的润湿界面组织结构,并总结了试验参数对组织结构和润湿能力的影响规律。而后进行了填缝试验,用于衡量Ti51ZrNiCu钎料在TA1/TC4异质界面的润湿铺展能力,总结了钎料填充经验公式。结果表明,在试验参数为935℃/3 min的条件下,TiZrNiCu钎料对TA1和TC4母材填充能力可简化为经验公式：h=4 000/a,其中钎缝间隙a的单位为μm,爬升高度h单位为mm。     

TiZrNiCu钎料在TA1/TC4异质界面的反应润湿过程

试验采用Ti51ZrNiCu钎料,研究其在TA1/TC4异质界面的反应润湿过程,使用扫描电子显微镜(SEM)、能谱分析仪(EDS)及润湿角测量仪等分析方法研究了不同表面的润湿界面组织结构,并总结了试验参数对组织结构和润湿能力的影响规律.而后进行了填缝试验,用于衡量Ti51ZrNiCu钎料在TA1/TC4异质界面的润湿铺展能力,总结了钎料填充经验公式.结果表明,在试验参数为935℃/3min的条件下,TiZrNiCu钎料对TA1和TC4母材填充能力可简化为经验公式:h=4 000/α,其中钎缝间隙α的单位为μm,爬升高度h单位为mm.     

AgCu钎料钎焊TC4钛合金与QCr0.8铬青铜接头界面结构及性能

采用AgCu28钎料实现了TC4钛合金与QCr0.8铬青铜的真空钎焊,利用SEM, EDS以及XRD等分析方法确定TC4/AgCu/QCr0.8接头的典型界面结构为TC4钛合金/CuTi +Cu3Ti2 +CuTi2/Ag(s,s) +Cu4Ti/Ag(s,s)+Cu(s,s)/QCr0.8铬青铜. 研究了工艺参数对接头组织和性能的影响. 结果表明,随着钎焊温度和保温时间的增加,钎缝中银铜共晶组织减少,钛铜化合物增多. 接头抗剪强度随钎焊温度的升高先增加后降低,在钎焊工艺参数为890 ℃/0 min时,获得最大抗剪强度449 MPa.保温时间的延长使得接头脆性钛铜化合物增多,接头性能下降,因此随保温时间延长接头抗剪强度显著降低.     

颗粒增强复合钎料钎焊TiAl合金接头界面结构及性能

采用纳米Si3N4颗粒增强的AgCuTi复合钎料(AgCuTiC)实现了TiAl合金的钎焊连接.利用SEM,EDS及XRD等分析方法确定了TiAl/AgCuTiC/TiAl接头的典型界面结构为TiAl/AlCu2Ti/Ag(s,s)+TiN+ Al4Cu9+Ti5Si3.结果表明,钎焊过程中从TiAl母材溶入液相钎料的活性钛与复合钎料中纳米Si3N4颗粒发生反应,在钎缝中形成了细小的颗粒状TiN,Ti5Si3及Al4Cu9化合物增强的银基复合材料组织.银基复合材料的形成不仅提高了钎缝自身的强度,而且通过降低钎缝的线膨胀系数缓解了接头残余应力,并最终改善了钎焊接头的性能.当采用增强相含量为3％的AgCuTiC钎料在880℃保温5min条件下钎焊时,接头室温平均抗剪强度最高为278 MPa,比采用AgCuTi钎料提高40％.     

Brazing of TiBw/TC4 composite and Ti60 alloy using TiZrNiCu amorphous filler alloy

TiB_w/TC4 composite was brazed to Ti60 alloy successfully using TiZrNiCu amorphous filler alloy, and the interfacial microstructures and mechanical properties were characterized by SEM, EDX, XRD and universal tensile testing machine. The typical interfacial microstructure was TiB_w/TC4 composite/β-Ti + TiB whiskers/(Ti, Zr)₂(Ni, Cu) intermetallic layer/β-Ti/Ti60 alloy when being brazed at 940 °C for 10 min. The interfacial microstructure evolution was influenced strongly by the diffusion and reaction between molten fillers and the substrates. Increasing brazing temperature decreased the thickness of brittle (Ti, Zr)₂(Ni, Cu) intermetallic layer, which disappeared finally when the brazing temperature exceeded 1020 °C. Fracture analyses indicated that cracks were initialized in the brittle intermetallic layer when (Ti, Zr)₂(Ni, Cu) phase existed in the brazing seam. The maximum average shear strength of joints reached 368.6 MPa when brazing was conducted at 1020 °C. Further increasing brazing temperature to 1060 °C, the shear strength was decreased due to the formation of coarse lamellar (α+β)-Ti structure.     

Interfacial microstructure and mechanical properties of tungsten carbide brazed joints using Ag-Cu-Zn + Ni/Mn filler alloy

WC-Co hard metal was furnace brazed by Ag-Cu-Zn+Ni/Mn filler alloy using a tube furnace under high-purity argon at 730 °C. The influence of brazing time and gap size of joints was studied. The results revealed the maximum shear strength of (156±7) MPa for samples with 150 µm gap size at a holding time 15 min. The characterization and microstructure of the brazed joints were characterized by SEM, EDS and XRD. The results showed that increasing the time from 5 to 15 min could provide a better chance for the liquid interlayer to flow towards the base metal. However, the formation of some metallic phases such as Mn₃W₃C at brazing time longer than 15 min resulted in decreased shear strength of the joint.     

Ni-34Ti钎料钎焊TiAl合金接头界面结构及性能

采用Ni-34Ti共晶钎料实现了TiAl合金的钎焊连接,分析了TiAl合金钎焊接头的界面结构,重点研究了钎焊温度对接头组织及性能的影响规律.结果表明,Ni-34Ti共晶钎料主要由TiNi相和TiNi3相组成,钎料熔点为1 120 ℃.不同钎焊温度下获得的接头界面组织均呈现对称特征,无气孔和裂纹等缺陷,接头中主要形成了TiNiAl2,B2,TiNiAl和TiNi2Al四种物相.Al元素在钎缝中的快速扩散,促进了钎缝中Ti-Ni-Al三元化合物的形成.钎焊温度为1 180 ℃保温10 min条件下,TiAl合金接头获得了最大的室温抗剪强度87 MPa.剪切过程中,裂纹容易在富含TiNi2Al相的区域产生和扩展,大量脆性TiNi2Al相的存在对接头的性能是有害的.     

TC4钛合金真空钎焊接头组织与高温性能

采用高钛含量的粉状Ti-Zr-Ni-Cu钎料实现了TC4钛合金的真空钎焊,分析了不同工艺参数对接头高温(600℃)抗拉强度的影响,并借助扫描电镜(SEM)、能谱分析(EDS)和X射线衍射分析等方法研究了钎焊接头界面组织,确定了界面反应产物及其形态分布.结果表明,在界面反应层中生成五种产物:钛基固溶体、Ti₂Ni,Ti₃Al,CuTi₃,Zr₂Ni.随着钎焊温度和加热时间的增加,接头抗拉强度呈现先增大再降低的趋势,当钎焊温度为950℃和保温时间为30 min时,获得最大高温(600℃)抗拉强度为387 MPa的钎焊接头.     

工艺参数对Al2O3/TC4合金接头界面组织及力学性能的影响

采用Cu＋B钎料分别在钎焊温度890～970℃,保温时间为10min;钎焊温度为930℃,保温时间0～30min条件下,钎焊A120,陶瓷与TCA合金．利用SEM,EDS和压剪试验研究接头界面组织及力学性能．结果表明,随钎焊温度升高或保温时间的延长,Ti2（Cu,Al）2O层增厚,紧邻其侧生成连续并增厚的Ti2（Cu,Al）,Ti2（Cu,Al）含量增加;Ti＋Ti2（Cu,Al）含量增加,尺寸变大,分布范围逐渐变宽并向TC4合金侧迁移,TCA合金侧过共析组织区变宽．钎焊温度低于950℃时,TiB晶须主要分布在Ti2Cu晶界处的AlCu2Ti上;当钎焊温度高于950℃时,AlCu2Ti相逐渐消失,TiB晶须主要分布于Ti2Cu上．当保温时间为10min,钎焊温度为950℃时,接头最大强度为96MPa;而当钎焊温度为930℃,保温时间为20min时,接头最大强度为83MPa．关键词：Al2O3陶瓷;TC4合金;钎焊参数;界面组织;抗剪强度     

TiNi-V共晶钎料钎焊Si3N4陶瓷接头界面结构及性能

采用真空电弧熔炼技术制备了TiNi-V高温共晶钎料合金,研究了该钎料在Si3N4陶瓷表面的铺展行为．随后采用TiNi—V钎料实现了Si3N4陶瓷的钎焊连接,利用SEM,EDS以及XRD等分析方法,确定了接头的典型界面结构为：Si3N4／TiN＋Ti-si化合物／NiV．重点研究了钎焊温度对接头界面结构及力学性能的影响．结果表明,随着钎焊温度的升高,熔融钎料与Si3N4陶瓷反应程度增加,导致钎缝中TiN＋Ti-Si化合物层厚度不断增加,且在接头残余应力的作用下形成了大量显微裂纹,降低了接头性能．当钎焊温度为1200℃,钎焊时间为10min时,接头室温抗剪强度达到最大为28MPa．断口分析显示接头断裂于TiN＋Ti-Si化合物层为脆性断裂．     

TC4/30CrMnSiNi2A钎焊接头组织与力学性能分析

采用Ti-37.5Zr-15Cu-10Ni和 Ag-Cu28两种钎料分别对TC4钛合金/30CrMnSiNi2超高强钢异种材料进行了钎焊,对钎焊界面组织以及接头的力学性能进行了分析。结果表明：Ag基钎料钎焊TC4与30CrMnSiNi2A异种材料时,钎缝界面组织为Ag(s,s)+Ti-Cu系化合物组成;因Ag固溶体的存在,钎缝具有一定的韧性,接头剪切强度较高,剪切断口呈现出韧性断裂特征。Ti基钎料钎焊TC4与30CrMnSiNi2A异种材料时,钎缝界面组织为Ti-Zr固溶体+未完全反应凝固钎料,钎缝显微硬度较高,接头剪切强度较低,呈现出脆性断裂特征。Ag基钎料TC4/30CrMnSiNi2A异种材料钎焊接头力学性能明显优于Ti基钎料结果,在钎焊温度830℃,保温时间15min时,剪切强度为125.52MPa。     

钎焊时间对TZM合金与ZrCp-W复合材料接头界面组织及性能的影响

采用Ti-28Ni（质量分数,%）钎料在1 040℃实现了TZM合金与ZrC_p-W复合材料的真空钎焊连接,分析了钎焊时间对TZM合金与ZrC_p-W复合材料接头界面组织及力学性能的影响.结果表明,钎焊接头的典型界面结构为TZM/Ti（s,s）/Ti₂Ni/（Ti,Zr）C+W（s,s）/ZrC_p-W,钎缝宽度随保温时间的延长而增大,其中Ti（s,s）层的厚度没有变化,Ti₂Ni层厚度略有降低,而扩散层厚度随保温时间的延长稍有增加.当保温时间为10 min时,接头获得最大抗剪强度值120 MPa,接头断裂发生在TZM母材.