La2NiO4 tubular membrane reactor for conversion of methane to syngas

La₂NiO₄ tubular membranes of relative density over 92% were used to separate oxygen from air and facilitate the partial oxidation of methane to H₂ and CO at 900 °C. When methane was fed into a tube of inner surface area 5.11 cm² at a rate of 10.5 ml/min, methane throughput conversion was 89%, CO selectivity 96%, H₂/CO ratio 1.5, and the equivalent oxygen flux was 6.8 ml/min. The surface of the La₂NiO₄ membrane exposed to CH₄ decomposed into La₂O₃ and Ni, while the surface in contact with air remained almost unchanged. It is suggested that the conversion of methane in the membrane reactor involves the reforming of methane by the H₂O and CO₂ catalyzed by nickel.     

NO reduction by CH4 in the presence of O2 over La2O3 supported on Al2O3

Dispersing La₂O₃ on δ- or γ-Al₂O₃ significantly enhances the rate of NO reduction by CH₄ in 1% O₂, compared to unsupported La₂O₃. Typically, no bend-over in activity occurs between 500° and 700°C, and the rate at 700°C is 60% higher than that with a Co/ZSM-5 catalyst. The final activity was dependent upon the La₂O₃ precursor used, the pretreatment, and the La₂O₃ loading. The most active family of catalysts consisted of La₂O₃ on γ-Al₂O₃ prepared with lanthanum acetate and calcined at 750°C for 10 h. A maximum in rate (mol/s/g) and specific activity (mol/s/m²) occurred between the addition of one and two theoretical monolayers of La₂O₃ on the γ-Al₂O₃ surface. The best catalyst, 40% La₂O₃/γ-Al₂O₃, had a turnover frequency at 700°C of 0.05 s⁻¹, based on NO chemisorption at 25°C, which was 15 times higher than that for Co/ZSM-5. These La₂O₃/Al₂O₃ catalysts exhibited stable activity under high conversion conditions as well as high CH₄ selectivity (CH₄ + NO vs. CH₄ + O₂). The addition of Sr to a 20% La₂O₃/γ-Al₂O₃ sample increased activity, and a maximum rate enhancement of 45% was obtained at a SrO loading of 5%. In contrast, addition of SO⁼₄ to the latter Sr-promoted La₂O₃/Al₂O₃ catalyst decreased activity although sulfate increased the activity of Sr-promoted La₂O₃. Dispersing La₂O₃ on SiO₂ produced catalysts with extremely low specific activities, and rates were even lower than with pure La₂O₃. This is presumably due to water sensitivity and silicate formation. The La₂O₃/Al₂O₃ catalysts are anticipated to show sufficient hydrothermal stability to allow their use in certain high-temperature applications.     

Catalytic conversion of methane and CO2 to synthesis gas over a La2O3-modified SiO2 supported Ni catalyst in fluidized-bed reactor

In this contribution, a commercial spherical SiO₂ was modified with different amounts of La₂O₃, and used as the support of Ni catalysts for autothermal reforming of methane in a fluidized-bed reactor. Nitrogen adsorption, XRD and H₂-TPR analysis indicated that La₂O₃-modified SiO₂ had higher surface area, strengthened interaction between Ni and support, and improved dispersion of Ni. CO₂-TPD found that La₂O₃ increased the alkalescence of SiO₂ and improved the activation of CO₂. Coking reaction (via both temperature-programmed surface reaction of CH₄ (CH₄-TPSR) and pulse decomposition of CH₄) disclosed that La₂O₃ reduced the dehydrogenation ability of Ni. CO₂-TPO, O₂-TPO (followed after CH₄-TPSR) confirmed that only part amount of carbon species derived from methane decomposition could be removed by CO₂, and O₂ in feed played a crucial role for the gasification of the inactive surface carbons. Ni/xLa₂O₃-SiO₂ (x = 10, 15, 30) possessed high activity and excellent stability for autothermal reforming of methane in a fluidized-bed reactor.     

Catalytic behavior of La–Sr–Ce–Fe–O mixed oxidic/perovskitic systems for the NO+CO and NO+CH4+O2 (lean-NOx) reactions

Mixed oxides of the general formula La_0.5Sr_xCe_yFeO_z were prepared by using the nitrate method and characterized by XRD and Mössbauer techniques. The crystal phases detected were perovskites LaFeO₃ and SrFeO_3−x and oxides -Fe₂O₃ and CeO₂ depending on x and y values. The low surface area ceramic materials have been tested for the NO+CO and NO+CH₄+O₂ (“lean-NO_x”) reactions in the temperature range 250–550°C. A noticeable enhancement in NO conversion was achieved by the substitution of La³⁺ cation at A-site with divalent Sr⁺² and tetravalent Ce⁺⁴ cations. Comparison of the activity of the present and other perovskite-type materials has pointed out that the ability of the La_0.5Sr_xCe_yFeO_z materials to reduce NO by CO or by CH₄ under “lean-NO_x” conditions is very satisfying. In particular, for the NO+CO reaction estimation of turnover frequencies (TOFs, s⁻¹) at 300°C (based on NO chemisorption) revealed values comparable to Rh/-Al₂O₃ catalyst. This is an important result considering the current tendency for replacing the very active but expensive Rh and Pt metals. It was found that there is a direct correlation between the percentage of crystal phases containing iron in La_0.5Sr_xCe_yFeO_z solids and their catalytic activity. O₂ TPD (temperature-programmed desorption) and NO TPD studies confirmed that the catalytic activity for both tested reactions is related to the defect positions in the lattice of the catalysts (e.g., oxygen vacancies, cationic defects). Additionally, a remarkable oscillatory behavior during O₂ TPD studies was observed for the La_0.5Sr_0.2Ce_0.3FeO_z and La_0.5Sr_0.5FeO_z solids.     

Role of CeO2 in Ni/CeO2–Al2O3 catalysts for carbon dioxide reforming of methane

Ni catalysts supported on γ-Al₂O₃, CeO₂ and CeO₂–Al₂O₃ systems were tested for catalytic CO₂ reforming of methane into synthesis gas. Ni/CeO₂–Al₂O₃ catalysts showed much better catalytic performance than either CeO₂- or γ-Al₂O₃-supported Ni catalysts. CeO₂ as a support for Ni catalysts produced a strong metal–support interaction (SMSI), which reduced the catalytic activity and carbon deposition. However, CeO₂ had positive effect on catalytic activity, stability, and carbon suppression when used as a promoter in Ni/γ-Al₂O₃ catalysts for this reaction. A weight loading of 1–5 wt% CeO₂ was found to be the optimum. Ni catalysts with CeO₂ promoters reduced the chemical interaction between nickel and support, resulting in an increase in reducibility and stronger dispersion of nickel. The stability and less coking on CeO₂-promoted catalysts are attributed to the oxidative properties of CeO₂.     

Co3O4/CeO2 composite oxides for methane emissions abatement: Relationship between Co3O4–CeO2 interaction and catalytic activity

Co₃O₄/CeO₂ composite oxides with different cobalt loading (5, 15, 30, 50, 70 wt.% as Co₃O₄) were prepared by co-precipitation method and investigated for the oxidation of methane under stoichiometric conditions. Pure oxides, Co₃O₄ and CeO₂ were used as reference. Characterization studies by X-ray diffraction (XRD), BET, temperature programmed reduction/oxidation (TPR/TPO) and X-ray photoelectron spectroscopy (XPS) were carried out.

An improvement of the catalytic activity and thermal stability of the composite oxides was observed with respect to pure Co₃O₄ in correspondence of Co₃O₄–CeO₂ containing 30% by weight of Co₃O₄. The combined effect of cobalt oxide and ceria, at this composition, strongly influences the morphological and redox properties of the composite oxides, by dispersing the Co₃O₄ phase and promoting the efficiency of the Co³⁺–Co²⁺ redox couple. The presence in the sample Co₃O₄(30 wt.%)–CeO₂ of a high relative amount of Ce³⁺/(Ce⁴⁺ + Ce³⁺) as detected by XPS confirms the enhanced oxygen mobility.

The catalysts stability under reaction conditions was investigated by XRD and XPS analysis of the used samples, paying particular attention to the Co₃O₄ phase decomposition. Methane oxidation tests were performed over fresh (as prepared) and thermal aged samples (after ageing at 750 °C for 7 h, in furnace). The resistance to water vapour poisoning was evaluated for pure Co₃O₄ and Co₃O₄(30 wt.%)–CeO₂, performing the tests in the presence of 5 vol.% H₂O. A methane oxidation test upon hydrothermal ageing (flowing at 600 °C for 16 h a mixture 5 vol.% H₂O + 5 vol.%O₂ in He) of the Co₃O₄(30 wt.%)–CeO₂ sample was also performed. All the results confirm the superiority of this composite oxide.     

ZrO2/SiO2- and La2O3/Al2O3-supported platinum catalysts for CH4/CO2 reforming

Surface-phase ZrO₂ on SiO₂ (SZrOs) and surface-phase La₂O₃ on Al₂O₃ (SLaOs) were prepared with various loadings of ZrO₂ and La₂O₃, characterized and used as supports for preparing Pt/SZrOs and Pt/SLaOs catalysts. CH₄/CO₂ reforming over the Pt/SZrOs and Pt/SLaOs catalysts was examined and compared with Pt/Al₂O₃ and Pt/SiO₂ catalysts. CO₂ or CH₄ pulse reaction/adsorption analysis was employed to elucidate the effects of these surface-phase oxides.

The zirconia can be homogeneously dispersed on SiO₂ to form a stable surface-phase oxide. The lanthana cannot be spread well on Al₂O₃, but it forms a stable amorphous oxide with Al₂O₃. The Pt/SZrOs and Pt/SLaOs catalysts showed higher steady activity than did Pt/SiO₂ and Pt/Al₂O₃ by a factor of three to four. The Pt/SZrOs and Pt/SLaOs catalysts were also much more stable than the Pt/SiO₂ and Pt/Al₂O₃ catalysts for long stream time and for reforming temperatures above 700 °C. These findings were attributed to the activation of CO₂ adsorbed on the basic sites of SZrOs and SLaOs.     

Catalytic performance of Co3O4/CeO2 and Co3O4/CeO2–ZrO2 composite oxides for methane combustion: Influence of catalyst pretreatment temperature and oxygen concentration in the reaction mixture

The influence of catalyst pre-treatment temperature (650 and 750 °C) and oxygen concentration (λ = 8 and 1) on the light-off temperature of methane combustion has been investigated over two composite oxides, Co₃O₄/CeO₂ and Co₃O₄/CeO₂–ZrO₂ containing 30 wt.% of Co₃O₄. The catalytic materials prepared by the co-precipitation method were calcined at 650 °C for 5 h (fresh samples); a portion of them was further treated at 750 °C for 7 h, in a furnace in static air (aged samples).

Tests of methane combustion were carried out on fresh and aged catalysts at two different WHSV values (12 000 and 60 000 mL g⁻¹ h⁻¹). The catalytic performance of Co₃O₄/CeO₂ and Co₃O₄/CeO₂–ZrO₂ were compared with those of two pure Co₃O₄ oxides, a sample obtained by the precipitation method and a commercial reference. Characterization studies by X-ray diffraction (XRD), BET and temperature-programmed reduction (TPR) show that the catalytic activity is related to the dispersion of crystalline phases, Co₃O₄/CeO₂ and Co₃O₄/CeO₂–ZrO₂ as well as to their reducibility. Particular attention was paid to the thermal stability of the Co₃O₄ phase in the temperature range of 750–800 °C, in both static (in a furnace) and dynamic conditions (continuous flow). The results indicate that the thermal stability of the phase Co₃O₄ heated up to 800 °C depends on the size of the cobalt oxide crystallites (fresh or aged samples) and on the oxygen content (excess λ = 8, stoichiometric λ = 1) in the reaction mixture. A stabilizing effect due to the presence of ceria or ceria–zirconia against Co₃O₄ decomposition into CoO was observed.

Moreover, the role of ceria and ceria–zirconia is to maintain a good combustion activity of the cobalt composite oxides by dispersing the active phase Co₃O₄ and by promoting the reduction at low temperature.     

NO decomposition and reduction by CH4 over Sr/La2O3

Both NO decomposition and NO reduction by CH₄ over 4%Sr/La₂O₃ in the absence and presence of O₂ were examined between 773 and 973 K, and N₂O decomposition was also studied. The presence of CH₄ greatly increased the conversion of NO to N₂ and this activity was further enhanced by co-fed O₂. For example, at 773 K and 15 Torr NO the specific activities of NO decomposition, reduction by CH₄ in the absence of O₂, and reduction with 1% O₂ in the feed were 8.3·10⁻⁴, 4.6·10⁻³, and 1.3·10⁻² μmol N₂/s m², respectively. This oxygen-enhanced activity for NO reduction is attributed to the formation of methyl (and/or methylene) species on the oxide surface. NO decomposition on this catalyst occurred with an activation energy of 28 kcal/mol and the reaction order at 923 K with respect to NO was 1.1. The rate of N₂ formation by decomposition was inhibited by O₂ in the feed even though the reaction order in NO remained the same. The rate of NO reduction by CH₄ continuously increased with temperature to 973 K with no bend-over in either the absence or the presence of O₂ with equal activation energies of 26 kcal/mol. The addition of O₂ increased the reaction order in CH₄ at 923 K from 0.19 to 0.87, while it decreased the reaction order in NO from 0.73 to 0.55. The reaction order in O₂ was 0.26 up to 0.5% O₂ during which time the CH₄ concentration was not decreased significantly. N₂O decomposition occurs rapidly on this catalyst with a specific activity of 1.6·10⁻⁴ μmol N₂/s m² at 623 K and 1220 ppm N₂O and an activation energy of 24 kcal/mol. The addition of CH₄ inhibits this decomposition reaction. Finally, the use of either CO or H₂ as the reductant (no O₂) produced specific activities at 773 K that were almost 5 times greater than that with CH₄ and gave activation energies of 21–26 kcal/mol, thus demonstrating the potential of using CO/H₂ to reduce NO to N₂ over these REO catalysts.     

Subsolidus relations in the BaO–La2O3–V2O5 phase diagram

The subsolidus region of the BaO–La₂O₃–V₂O₅ phase diagram has been redetermined. Previously reported binary phases of LaVO₄, La₈V₂O₁₇, La₃VO₇, BaLa₂O₄, Ba₃V₂O₈, Ba₂V₂O₇, Ba₃V₄O₁₃ and BaV₂O₆ have all been confirmed. The ternary phases Ba₂LaV₃O₁₁, Ba₃LaV₃O₁₂ and Ba₃La₄₀V₁₂O₉₃ have also been confirmed. The new phase “BaLa₁₀V₄O₂₆” has been synthesised for the first time and is reported here along with the amended phase diagram. The previously omitted phase of La_1.42V_0.58O_3.58 has also been included and reasons for this are cited. The diagram is shown for two temperatures (1000 and 600 °C) due to the low melting point of V₂O₅-rich compounds.     

An investigation of NO/CO reaction over perovskite-type oxide La0.8Ce0.2B0.4Mn0.6O3 (B = Cu or Ag) catalysts synthesized by reverse microemulsion

The perovskite-type oxides La_0.8Ce_0.2Cu_0.4Mn_0.6O₃ and La_0.8Ce_0.2Ag_0.4Mn_0.6O₃ prepared by reverse microemulsion and sol–gel methods (denoted as R and S, respectively), have been investigated on their catalytic performance for the (NO + CO) reaction, and characterized by means of temperature-programmed desorption (TPD), X-ray diffraction (XRD), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). XRD measurements proved the presence of the perovskite phase with a considerable amount of CeO₂ phase and the formation of CeO₂ phase was restrained with the reverse microemulsion method. TEM investigations revealed that the La_0.8Ce_0.2Cu_0.4Mn_0.6O₃-R nanoparticles were uniform spheres in shape with diameters ranging from 40 to 50 nm, whereas an aggregation of particles was found for the La_0.8Ce_0.2Cu_0.4Mn_0.6O₃-S catalyst. The activity of NO reduction with CO decreased in the order of La_0.8Ce_0.2Cu_0.4Mn_0.6O₃-R > La_0.8Ce_0.2Cu_0.4Mn_0.6O₃-S > La_0.8Ce_0.2Ag_0.4Mn_0.6O₃-R > La_0.8Ce_0.2Ag_0.4Mn_0.6O₃-S. In NO-TPD experiments, the principal desorbed species detected in the effluent was NO with a trace amount of O₂ and N₂O, suggesting that the non-dissociated adsorption of NO on the surface of the perovskite-type oxides was dominant. The XPS results revealed that Ce⁴⁺ and Cu⁺ was the predominant oxidation state for Ce and Cu components in La_0.8Ce_0.2Cu_0.4Mn_0.6O₃ and La_0.8Ce_0.2Ag_0.4Mn_0.6O₃ catalysts. The existence of Cu⁺ ions and its redox reaction (Cu⁺ ↔ Cu²⁺) would benefit the NO adsorption and reduction by CO.     

Sintering of lime doped with La2O3 and CeO2

The sintering of lime doped with up to 2 mol% La₂O₃ as well as CeO₂ was followed on firing at 1400, 1500 and 1600°C. X-ray diffraction and reflected-light microscopy techniques have been used to investigate the phase composition and texture of the fired samples. The load bearing capacity and the rate of hydration of the obtained dense lime samples have also been determined to assess its quality. It is found that doping lime with 0·5–1·0 mol% of either La₂O₃ or CeO₂ and firing up to 1600°C leads to dense and hydration-resistant lime with uniform texture. At this level of the dopant oxides, normal grain growth occurred with the increase in the degree of direct bonding. Doping with less than 0·5 mol% La₂O₃ or CeO₂ is insufficient for inhibiting the discontinuous grain growth of the lime grains. On the other hand, increase in the dopant content above 1·0 mol% showed finer grain sizes at the expense of the degree of direct bonding.     

Decomposition of nitric oxide over perovskite oxide catalysts: effect of CO2, H2O and CH4

Direct nitric oxide decomposition over perovskites is fairly slow and complex, its mechanism changing dramatically with temperature. Previous kinetic study for three representative compositions (La_0.87Sr_0.13Mn_0.2Ni_0.8O_3−δ, La_0.66Sr_0.34Ni_0.3Co_0.7O_3−δ and La_0.8Sr_0.2Cu_0.15Fe_0.85O_3−δ) has shown that depending on the temperature range, the inhibition effect of oxygen either increases or decreases with temperature. This paper deals with the effect of CO₂, H₂O and CH₄ on the nitric oxide decomposition over the same perovskites studied at a steady-state in a plug-flow reactor with 1 g catalyst and total flowrates of 50 or 100 ml/min of 2 or 5% NO. The effect of carbon dioxide (0.5–10%) was evaluated between 873 and 923 K, whereas that of H₂O vapor (1.6 or 2.5%) from 723 to 923 K. Both CO₂ and H₂O inhibit the NO decomposition, but inhibition by CO₂ is considerably stronger. For all three catalysts, these effects increase with temperature. Kinetic parameters for the inhibiting effects of CO₂ and H₂O over the three perovskites were determined. Addition of methane to the feed (NO/CH₄=4) increases conversion of NO to N₂ about two to four times, depending on the initial NO concentration and on temperature. This, however, is still much too low for practical applications. Furthermore, the rates of methane oxidation by nitric oxide over perovskites are substantially slower than those of methane oxidation by oxygen. Thus, perovskites do not seem to be suitable for catalytic selective NO reduction with methane.     

K-, CeO2-, and Mn-promoted Ni/Al2O3 catalysts for stable CO2 reforming of methane

Reforming of methane with carbon dioxide into syngas over Ni/γ-Al₂O₃ catalysts modified by potassium, MnO and CeO₂ was studied. The catalysts were prepared by impregnation technique and were characterized by N₂ adsorption/desorption isotherm, BET surface area, pore volume, and BJH pore size distribution measurements, and by X-ray diffraction and scanning electron microscopy. The performance of these catalysts was evaluated by conducting the reforming reaction in a fixed bed reactor. The coke content of the catalysts was determined by oxidation conducted in a thermo-gravimetric analyzer. Incorporation of potassium and CeO₂ (or MnO) onto the catalyst significantly reduced the coke formation without significantly affecting the methane conversion and hydrogen yield. The stability and the lower amount of coking on promoted catalysts were attributed to partial coverage of the surface of nickel by patches of promoters and to their increased CO₂ adsorption, forming a surface reactive carbonate species. Addition of CeO₂ or MnO reduced the particle size of nickel, thus increasing Ni dispersion. For Ni–K/CeO₂–Al₂O₃ catalysts, the improved stability was further attributed to the oxidative properties of CeO₂. Results of the investigation suggest that stable Ni/Al₂O₃ catalysts for the carbon dioxide reforming of methane can be prepared by addition of both potassium and CeO₂ (or MnO) as promoters.     

Oxidation behavior of hot-pressed Si3N4 with Re2O3 (Re=Y, Yb, Er, La)

Four different β-Si₃N₄ ceramics with silicon oxynitrides [Y₁₀(SiO₄)₆N₂, Yb₄Si₂N₂O₇, Er₂Si₃N₄O₃, and La₁₀(SiO₄)₆N₂, respectively] as secondary phases have been fabricated by hot-pressing the Si₃N₄–Re₄Si₂N₂O₇ (Re=Y, Yb, Er, and La) compositions at 1820°C for 2 h under a pressure of 25 MPa. The oxidation behavior of the hot-pressed ceramics was characterized and compared with that of the ceramics fabricated from Si₃N₄–Re₂Si₂O₇ compositions. All Si₃N₄ ceramics investigated herein showed a parabolic weight gain with oxidation time at 1400°C and the oxidation products of the ceramics were SiO₂ and Re₂Si₂O₇. The Si₃N₄–Re₄Si₂N₂O₇ compositions showed inferior oxidation resistance to those from Si₃N₄–Re₂Si₂O₇ compositions, owing to the incompatibility of the secondary phases of those ceramics with SiO₂, the oxidation product of Si₃N₄. Si₃N₄ ceramics from a Si₃N₄–Er₄Si ₂N₂O₇ composition showed the best oxidation resistance of 0·198 mg cm⁻² after oxidation at 1400°C for 192 h in air among the compositions investigated herein.     

Effect of rare-earth element oxides (La2O3, Ce2O3) on the structural and physico-chemical characteristics of Pd/Al2O3 monolithic catalysts of nitrogen oxide reduction by methane

It is shown that introduction of additives of rare-earth element oxides (La₂O₃, CeO₂) enables regulating the structural and functional characteristics of Pd/Al₂O₃-catalysts (applied on ceramic monoliths of honeycomb structure) of nitrogen oxide reduction by methane. Modifying additives provide increase of thermal stability of porous structure of both highly dispersed Al₂O₃, as the second support, and the catalyst as a whole.

Contribution of La₂O₃ and CeO₂ in increasing the thermal stability is of an additive nature, and lanthanum oxide shows the higher efficiency than cerium one. According to X-ray phase analysis data, stabilizing action is conditioned by occurrence of rare-earth element oxides into lattice of Al₂O₃, which retards diffusional processes leading to phase transitions of low-temperature crystalline modifications of alumina into high-temperature ones with a low specific surface. For the catalyst samples modified with La₂O₃ an effect of thermal activation is observed, which is revealed by increase in catalytic activity as a result of annealing at 850 °C. Such a phenomenon, as shown by means of X-ray photoelectron spectroscopy technique, can be explained via stabilization of palladium in singly charged state in the form of groups of Pd⁺O₂⁻ and corresponding increase in concentration of active centers.     

The effect of CeO2 structure on the activity of supported Pd catalysts used for methane steam reforming

Palladium (Pd) supported on CeO₂-promoted γ-Al₂O₃ with various CeO₂ (ceria) crystallinities, were used as catalysts in the methane steam reforming reaction. X-ray diffraction (XRD) analysis, FTIR spectroscopy of adsorbed CO, and X-ray photoelectron spectroscopy (XPS) were employed to characterize the samples in terms of Pd and CeO₂ structure and dispersion on the γ-Al₂O₃ support. These results were correlated with the observed catalytic activity and deactivation process. Arrhenius plots at steady-state conditions are presented as a function of CeO₂ structure. Pd is present on the oxidized CeO₂-promoted catalysts as Pd⁰, Pd⁺ and Pd²⁺, at ratios strongly dependent on CeO₂ structure. XRD measurements indicated that Pd is well dispersed (particles <2 nm) on crystalline CeO₂ and is agglomerated as large clusters (particles in 10–20 nm range) on amorphous CeO₂. FTIR spectra of adsorbed CO revealed that after pre-treatment under H₂ or in the presence of amorphous CeO₂, partial encapsulation of Pd particles occurs. CeO₂ structure influences the CH₄ steam reforming reaction rates. Crystalline CeO₂ and dispersed Pd favor high reaction rates (low activation energy). The presence of CeO₂ as a promoter conferred high catalytic activity to the alumina-supported Pd catalysts. The catalytic activity is significantly lower on Pd/γ-Al₂O₃ or on amorphous (reduced) CeO₂/Al₂O₃ catalysts. The reaction rates are two orders of magnitude higher on Pd/CeO₂/γ-Al₂O₃ than on Pd/γ-Al₂O₃, which is attributed to a catalytic synergism between Pd and CeO₂. The low rates on the reduced Pd/CeO₂/Al₂O₃ catalysts can be correlated with the loss of Pd sites through encapsulation or particle agglomeration, a process found mostly irreversible after catalyst regeneration.     

Photocatalytic conversion of CH4 and CO2 to oxygenated compounds over Cu/CdS–TiO2/SiO2 catalyst

Coupled semiconductor (CS) Cu/CdS–TiO₂/SiO₂ photocatalyst was prepared using a mutli-step impregnation method. Its optical property was characterized by UV–vis spectra. BET, XRD, Raman and IR were used to study the structure of the photocatalyst. Fine CdS was found dispersed over the surface of anatase TiO₂/SiO₂ substrate. Chemisorption and IR analysis showed methane absorbed in the molecular state interacted weakly with the surface of catalyst, and the interaction of CO₂ with CS produced various forms of absorbed CO₂ species that were primarily present in the form of formate, bidentate and linear absorption species. Photocatalytic direct conversion of CH₄ and CO₂ was performed under the operation conditions: 373 K, 1:1 of CO₂/CH₄, 1 atm, space velocity of 200 h⁻¹ and UV intensity of 20.0 mW/cm². The conversion was 1.47% for CH₄ and 0.74% for CO₂ with a selectivity of acetone up to 92.3%. The reaction mechanisms were proposed based on the experimental observations.     

A CO and CO2 tolerating (La0.9Ca0.1)2(Ni0.75Cu0.25)O4+d Ruddlesden-Popper membrane for oxygen separation

A series of novel dense mixed conducting ceramic membranes based on K₂NiF₄-type (La_1–xCa_x)₂ (Ni_0.75Cu_0.25)O_4+δ was successfully prepared through a sol-gel route. Their chemical compatibility, oxygen permeability, CO and CO₂ tolerance, and long-term CO₂ resistance regarding phase composition and crystal structure at different atmospheres were studied. The results show that higher Ca contents in the material lead to the formation of CaCO₃. A constant oxygen permeation flux of about 0.63 mL·min⁻¹·cm⁻² at 1173 K through a 0.65 mm thick membrane was measured for (La_0.9Ca_0.1)₂ (Ni_0.75Cu_0.25)O_4+δ, using either helium or pure CO₂ as sweep gas. Steady oxygen fluxes with no sign of deterioration of this membrane were observed with increasing CO₂ concentration. The membrane showed excellent chemical stability towards CO₂ for more than 1360 h and phase stability in presence of CO for 4 h at high temperature. In addition, this membrane did not deteriorate in a high-energy CO₂ plasma. The present work demonstrates that this (La_0.9Ca_0.1)₂(Ni_0.75Cu_0.25)O_4+δ membrane is a promising chemically robust candidate for oxygen separation applications.