Annealing temperature influence on electrical properties of ion beam sputtered Bi2Te3 thin films

Ion beam sputtering process was used to deposit n-type fine-grained Bi₂Te₃ thin films on BK7 glass substrates at room temperature. In order to enhance the thermoelectric properties, thin films are annealed at the temperatures ranging from 100 to 400 °C. X-ray diffraction (XRD) shows that the films have preferred orientations in the c-axis direction. It is confirmed that grain growth and crystallization along the c-axis are enhanced as the annealing temperature increased. However, broad impurity peaks related to some oxygen traces increase when the annealing temperature reached 400 °C. Thermoelectric properties of Bi₂Te₃ thin films were investigated at room temperature. The Bi₂Te₃ thin films, including as-deposited, exhibit the Seebeck coefficients of −90 to −168 μV K⁻¹ and the electrical conductivities of 3.92×10²-7.20×10² S cm⁻¹ after annealing. The Bi₂Te₃ film with a maximum power factor of 1.10×10⁻³ Wm⁻¹ K⁻² is achieved when annealed at 300 °C. As a result, both structural and transport properties have been found to be strongly affected by annealing treatment. It was considered that the annealing conditions reduce the number of potential scattering sites at grain boundaries and defects, thus improving the thermoelectric properties.     

Epitaxial strain-induced magnetic anisotropy in Sm3Fe5O12 thin films grown by pulsed laser deposition

Sm₃Fe₅O₁₂ thin films of various thicknesses were grown on a (0 0 1)-oriented Gd₃Ga₅O₁₂ substrate by pulsed laser deposition. The crystal structure of the films was strongly dependent on film thickness. The lattice was strained for thinner films due to a lattice mismatch between the film and substrate. This lattice strain was relaxed when the film thickness exceeded a critical thickness of around 660 Å. It is suggested that the epitaxial strain induces uniaxial magnetic anisotropy with an out-of-plane magnetic easy axis.     

Ordering temperature of L10-type FePt films reduced by CuO addition

Effects of addition of CuO layers in L1₀-type FePt thin films are investigated. The ordering temperature of L1₀-type FePt films can be reduced by CuO addition. The coercivities of 0.78 and 0.82 T are achieved in [Pt(10 Å)/Fe(14 Å)/CuO(2 Å)]₁₀ film annealed at 550 °C for 20 min and [Pt(10 Å)/Fe(15 Å)/CuO(3 Å)]₁₀ film annealed at 600 °C for 20 min, respectively, and these values are compared to the coercivity of 0.8 T in [Pt(10 Å)/Fe(13 Å)]₁₀ film annealed at 650 °C. The thickness of Fe and CuO layers strongly influences the ordering temperature of L1₀-type FePt and the magnetic properties of the films. The addition of CuO not only brings microstructure and surface morphology changes of FePt film, but also lowers the ordering temperature.     

Low-frequency alternative-current magnetic susceptibility of amorphous and nanocrystalline Co60Fe20B20 films

This investigation experimentally studies the low-frequency alternating-current magnetic susceptibility (χ_ac) of amorphous and nanocrystalline CoFeB films by measuring the magnetic field established by passing currents of various frequencies through such films of various thicknesses (t_f). A CoFeB film is sputtered onto a glass substrate with t_f from 100 Å to 500 Å under the following conditions: (a) As-deposited films were maintained at room temperature (RT) and (b) films were post-annealed at T_A=150 °C for 1 h. The samples thus obtained are analyzed in a magnetic field that was generated by an alternating current (AC) at various frequencies from 10 Hz to 25,000 Hz. The experimental results demonstrate that the χ_ac declines as the thickness of the as-deposited sample and the post-annealed sample (T_A=150 °C) increases because the lower coercivity (H_c) of thinner CoFeB films is similar to a soft magnetic characteristic and is associated with a higher χ_ac value. The best χ_ac value is obtained at a thickness of 100 Å under both conditions. The χ_ac value of the post-annealed sample exceeds that of the RT sample at thicknesses from 100 Å to 500 Å because the magneto crystalline anisotropy of the post-annealed sample yields the highest χ_ac value at the optimal resonance frequency (f_res), at which the spin sensitivity is maximal. The X-ray diffraction patterns (XRD) of as-deposited CoFeB films reveal their amorphous structure. The XRD results for the post-annealed films include a main peak at 2θ=44.7° from the body-centered cubic (BCC) nanocrystalline CoFe that indicated a (110) textured structure. Post-annealing treatment caused that the amorphous structure to become more crystalline by a thermally driven process, such that the χ_ac value of the post-annealed sample exceeded that of the RT sample. This experimental result demonstrates that the χ_ac value decreased as the thickness of the thin film increased. Finally, the CoFeB thin films had the best χ_ac at low frequency (<50 Hz) following post-annealing treatment. The results obtained under the two conditions indicate that the maximum χ_ac value and the optimal f_res of a 100 Å-thick CoFeB thin film were 1.6 and 30 Hz, respectively, following post-annealing at T_A=150 °C for 1 h, suggesting that a 100 Å-thick CoFeB thin film that has been post-annealed at T_A=150 °C can be utilized as a gage sensor and in transformer applications at low frequencies.     

Optical and thermoelectric characterizations of electroplated n-Bi2(Te0.9Se0.1)3

Bismuth selenotelluride (Bi₂(Te_0.9Se_0.1)₃) films were electrodeposited at constant current density from acidic aqueous solutions with Arabic gum in order to produce thin films for miniaturized thermoelectric devices. X-ray fluorescence spectroscopy determined film compositions. X-ray diffraction pattern shows that the films as deposited are polycrystalline, isostructural to Bi₂Te₃ and covered by crystallites. Mueller-matrix analysis reveals that the electroplated layers are optically like an isotropic medium. Their pseudo-dielectric functions were determined using mid-infrared spectroscopic ellipsometry. Tauc-Lorentz combined with Drude dispersion relations were successfully used. The energy band gap E_g was found to be about 0.15 eV. Moreover, the fundamental absorption edge was described by an indirect optical band-to-band transition. From Seebeck coefficient measurement, films exhibit n-type charge carrier and the value of thermoelectric power is about −40 μV/K.     

Annealing effects on the structural and electrical transport properties of n-type Bi2Te2.7Se0.3 thin films deposited by flash evaporation

N-type Bi₂Te_2.7Se_0.3 thermoelectric thin films with thickness 800 nm have been deposited on glass substrates by flash evaporation method at 473 K. Annealing effects on the thermoelectric properties of Bi₂Te_2.7Se_0.3 thin films were examined in the temperature range 373-573 K. The structures, morphology and chemical composition of the thin films were characterized by X-ray diffraction, field emission scanning electron microscope and energy dispersive X-ray spectroscopy, respectively. Thermoelectric properties of the thin films have been evaluated by measurements of the electrical resistivity and Seebeck coefficient at 300 K. The Hall coefficients were measured at room temperature by the Van der Pauw method. The carrier concentration and mobility were calculated from the Hall coefficient. The films thickness of the annealed samples was measured by ellipsometer. When annealed at 473 K, the electrical resistivity and Seebeck coefficient are 2.7 mΩ cm and −180 μV/K, respectively. The maximum of thermoelectric power factor is enhanced to 12 μW/cm K².     

Preparation and properties of spray-deposited ZnIn2Se4 nanocrystalline thin films

Zinc indium selenide (ZnIn₂Se₄) thin films have been deposited onto amorphous and fluorine doped tin oxide (FTO)-coated glass substrates using a spray pyrolysis technique. Aqueous solution containing precursors of Zn, In, and Se has been used to obtain good quality deposits at different substrate temperatures. The preparative parameters such as substrate temperature and concentration of precursors solution have been optimized by photoelectrochemical technique and are found to be 325 °C and 0.025 M, respectively. The X-ray diffraction patterns show that the films are nanocrystalline with rhombohedral crystal structure having lattice parameter a=4.05 Å. The scanning electron microscopy (SEM) studies reveal the compact morphology with large number of single crystals on the surface. From optical absorption data the indirect band gap energy of ZnIn₂Se₄ thin film is found to be 1.41 eV.     

Switching phenomenon and optical properties of Se85Te10Bi5 films

Se₈₅Te₁₀Bi₅ films of different thicknesses ranging from 126 to 512 nm have been prepared. Energy-dispersive X-ray (EDX) spectroscopy technique showed that films are nearly stoichiometric. X-ray diffraction (XRD) measurements have showed that the Se₈₅Te₁₀Bi₅ films were amorphous. Electrical conduction activation energy (ΔE_σ) for the obtained films is found to be 0.662 eV independent of thickness in the investigated range. Investigation of the current voltage (I-V) characteristics in amorphous Se₈₅Te₁₀Bi₅ films reveals that it is typical for a memory switch. The switching voltage V_th increases with the increase of the thickness and decreases exponentially with temperature in the range from 298 to 383 K. The switching voltage activation energy (ε) calculated from the temperature dependence of V_th is found to be 0.325 eV. The switching phenomenon in amorphous Se₈₅Te₁₀Bi₅ films is explained according to an electrothermal model for the switching process. The optical constants, the refractive index (n) and the absorption index (k) have been determined from transmittance (T) and reflectance (R) of Se₈₅Te₁₀Bi₅ films. Allowed non-direct transitions with an optical energy gap (E_g^opt) of 1.33 eV have been obtained. ΔE_σ is almost half the obtained value of E_g^opt, which suggested band to band conduction as indicated by Davis and Mott.     

Growth of superconducting FeSe0.5Te0.5 thin films by pulsed-laser deposition

FeSe_0.5Te_0.5 thin films with PbO-type structure are successfully grown on MgO(1 0 0) and LaSrAlO₄(0 0 1) substrates from FeSe_0.5Te_0.5 or FeSe_0.5Te_0.75 polycrystalline targets by pulsed-laser deposition. The film deposited on the MgO substrate (film thickness ∼ 55 nm) shows superconductivity at 10.6 K (onset) and 9.2 K (zero resistivity). On the other hand, the film deposited on the LaSrAlO₄ substrate (film thickness ∼ 250 nm) exhibits superconductivity at 5.4 K (onset) and 2.7 K (zero resistivity). This suggests the strong influence of substrate materials and/or the c-axis length to superconducting properties of FeSe_0.5Te_0.5 thin films.     

Multilayer Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 thin films for tunable microwave applications

Bi_1.5Zn_1.0Nb_1.5O₇/Ba_0.6Sr_0.4TiO₃/Bi_1.5Zn_1.0Nb_1.5O₇ tunable multilayer thin film has been fabricated by pulsed laser ablation and characterized. Phase composition and microstructure of multilayer films were characterized by X-ray diffraction, scanning electron microscopy (SEM) and atomic force microscopy (AFM). The film has very smooth surface with RMS roughness of 1.5-2 nm and grain size of 100-150 nm. Total film thickness has been measure to be 375 nm. The BZN thin films at 300 K, on Pt(1 1 1)/SiO₂/Si substrate showed zero-field dielectric constant of 105 and dielectric loss tangent of 0.002 at frequency of 0.1 MHz. Thin films annealed at 700 °C shows the dielectric tunability of 18% with biasing field 500 kV/cm at 0.1 MHz. The multilayer thin film shows nonferroelectric behavior at room temperature. The good physical and electrical properties of multilayer thin films make them promising candidate for tunable microwave device applications.     

Effect of annealing temperature on the optical and electrical properties of amorphous As45.2Te46.6In8.2 thin films

The optical absorption of the As-prepared and annealed As_45.2Te_46.6In_8.2 thin films are studied. Films annealed at temperatures higher than 453 K show a decrease in the optical energy gap (E_o). The value of E_o increases from 1.9 to 2.43 eV with increasing thickness of the As-prepared films from 60 to 140 nm. The effect of thickness on high frequency dielectric constant (?_∞) and carrier concentration (N) is also studied. The crystalline structures of the As_45.2Te_46.6In_8.2 thin films resulting from heat treatment of the As-prepared film at different elevated temperatures is studied by X-ray diffraction. An amorphous-crystalline transformation is observed after annealing at temperatures higher than 453 K. The electrical conductivity at low temperatures is found due to the electrons transport by hopping among the localized states near the Fermi level. With annealing the films at temperatures higher than 473 K (the crystallization onset temperature) for 1 h, the electrical conductivity increases and the activation energy decreases, which can be attributed to the amorphous-crystalline transformations.     

X-ray multiple diffraction in the characterization of TiNO and TiO2 thin films grown on Si(0 0 1)

TiO₂ and TiN_xO_y thin films grown by low pressure metal-organic chemical vapor deposition (LP-MOCVD) on top of Si(0 0 1) substrate were characterized by X-ray multiple diffraction. X-ray reflectivity analysis of TiO₂[1 1 0] and TiNO[1 0 0] polycrystalline layers allowed to determine the growth rate (−80 Å/min) of TiO₂ and (−40 Å/min) of TiNO films. X-ray multiple diffraction through the Renninger scans, i.e., ?-scans for (0 0 2)Si substrate primary reflection is used as a non-conventional method to obtain the substrate lattice parameter distortion due to the thin film conventional deposition, from where the information on film strain type is obtained.     

Annealing effect on CdS/SnO2 films grown by chemical bath deposition

The extensive investigation of the annealing effect in nitrogen atmosphere on the structural optical and electrical properties of chemically deposited CdS films on SnO₂ has been performed. The as-deposited film shows 2.45 eV band gap (E_g) and decreases with increasing annealing temperature. The film annealed at 623 K having pure hexagonal phase (a = 4.14 Å, c = 6.71 Å for [1 0 0] plane) and E_g = 2.36 eV shows 10 times higher conductivity for all temperature range, and shows two different activation energies E_a = 0.114 eV and E_a = 0.033 eV for the temperature range 395 K ≤ T ≤ 515 K and 515 K ≤ T ≤ 585 K, respectively. The structural parameters such as dislocation density, strain and optical parameters such as absorption and extinction coefficient are calculated and compared for all the films.     

Growth, structural and optical properties of non-stoichiometric CuIn(S1−xSex)2 thin films deposited by solution growth technique for photovoltaic application

Polycrystalline thin films of p-CuIn(S_1−xSe_x)₂ have been deposited by a solution growth technique. The deposition parameters such as pH, temperature and time have been optimized. In order to achieve uniformity of thin film, triethanolamine (TEA) has been used. As deposited films have been annealed at 450 °C in air for 5 min. The surface morphology, compositional ratio, structural properties have been studied by SEM, EDAX and XRD technique, respectively. It has been found that films have chalcopyrite structure with the lattice parameters a=5.28 Å and c=11.45 Å at composition x=0.5. The grain size of all composition x measured from SEM and XRD is varied in between 450 and 520 nm. The optical transmittance spectra have been recorded in the range 350-1000 nm. The absorption coefficient has been calculated at the absorption edge for each of the composition x and it is in the range of 10⁴ cm⁻¹. The material shows the direct allowed band gap, which varies from 1.07 to 1.44 eV with change in composition (0≤x≤1.0). These parameters are useful for the photovoltaic application.     

Structural and electrical properties of (Na0.85K0.15)0.5Bi0.5TiO3 thin films deposited on LaNiO3 and Pt bottom electrodes

(Na_0.85K_0.15)_0.5Bi_0.5TiO₃ thin films were deposited on LaNiO₃(LNO)/SiO₂/Si(1 0 0) and Pt/Ti/SiO₂/Si(1 0 0) substrates by metal-organic decomposition, and the effects of bottom electrodes LNO and Pt on the ferroelectric, dielectric and piezoelectric properties were investigated by ferroelectric tester, impedance analyzer and scanning probe microscopy, respectively. For the thin films deposited on LNO and Pt electrodes, the remnant polarization 2P_r are about 22.6 and 8.8 μC/cm² under 375 kV/cm, the dielectric constants 238 and 579 at 10 kHz, the dielectric losses 0.06 and 0.30 at 10 kHz, the statistic d_33eff values 95 and 81 pm/V. The improved piezoelectric properties could make (Na_1−xK_x)_0.5Bi_0.5TiO₃ thin film as a promising candidate for piezoelectric thin film devices.     

Ge/Sb2Te3 nanocomposite multilayer films for high data retention phase-change random access memory application

The amorphous-to-crystalline transition of Ge/Sb₂Te₃ nanocomposite multilayer films with various thickness ratios of Ge to Sb₂Te₃ were investigated by utilizing in situ temperature-dependent film resistance measurements. The crystallization temperature and activation energy for the crystallization of the multilayer films increased with the increase in thickness ratio of Ge to Sb₂Te₃. The difference in sheet resistance between amorphous and crystalline states could reach as high as 10⁴ Ω/□. The crystallization temperature and activation energy for the crystallization of Ge/Sb₂Te₃ nanocomposite multilayer films was proved to be larger than that of conventional Ge₂Sb₂Te₅ film, which ensures a better data retention for phase-change random access memory (PCRAM) use. A data retention temperature for 10 years of the amorphous state [Ge (2 nm)/Sb₂Te₃ (3 nm)]₄₀ film was estimated to be 165 °C. Transmission electron microscopy (TEM) images revealed that Ge/Sb₂Te₃ nanocomposite multilayer films had layered structures with clear interfaces.     

Structural and optical properties of In35Sb45Se20−xTex phase-change thin films

Physical properties of In₃₅Sb₄₅Se_20−xTe_x thin films with different compositions (x=2.5, 5, 7.5, 10, 12.5 and 15 at %) prepared by electron beam evaporation method are studied. X-ray diffraction results indicate that the as-evaporated films depend on the Te content and the crystallized compounds consist mainly of Sb₂Se₃ with small amount of Sb₂SeTe₂. Transmittance and reflectance of the films are found to be thickness dependent. Optical-absorption data indicate that the absorption mechanism is direct transition. Optical band gap values decrease with increase in Te content as well as with increase in film thickness.     

The ferroelectric and ferromagnetic characterization of CoFe2O4/Pb(Mg1/3Nb2/3)O3-PbTiO3 multilayered thin films

The multiferroic (PMN-PT/CFO)_n (n = 1,2) multilayered thin films have been prepared on SiO₂/Si(1 0 0) substrate with LNO as buffer layer via a rf magnetron sputtering method. The structure and surface morphology of multilayered thin films were determined by X-ray diffraction (XRD) and atom force microscopy (AFM), respectively. The smooth, dense and crack-free surface shows the excellent crystal quality with root-mean-square (RMS) roughness only 2.9 nm, and average grain size of CFO thin films on the surface is about 44 nm. The influence of the thin films thickness size, periodicity n and crystallite orientation on their properties including ferroelectric, ferromagnetic properties in the (PMN-PT/CFO)_n multilayered thin films were investigated. For multilayered thin films with n = 1 and n = 2, the remanent polarization Pr are 17.9 μC/cm² and 9.9 μC/cm²; the coercivity H_c are 1044 Oe and 660 Oe, respectively. In addition, the relative mechanism are also discussed.     

Laser-induced voltage characteristics of Bi2Sr2Co2Oy thin films on LaAlO3 substrates

We report the laser-induced voltage (LIV) effects in c-axis oriented Bi₂Sr₂Co₂O_y thin films grown on (0 0 1) LaAlO₃ substrates with the title angle α of 0°, 3°, 5° and 10° by a simple chemical solution deposition method. A large open-circuit voltage with the sensitivity of 300 mV/mJ is observed for the film on 10° tilting LaAlO₃ under a 308 nm irradiation with the pulse duration of 25 ns. When the film surface is irradiated by a 355 nm pulsed laser of 25 ps duration, a fast response with the rise time of 700 ps and the full width at half maximum of 1.5 ns is achieved. In addition, the experimental results reveal that the amplitude of the voltage signal is approximately proportional to sin 2α and the signal polarity is reversed when the film is irradiated from the substrate side rather than the film side, which suggests the LIV effects in Bi₂Sr₂Co₂O_y thin films originate from the anisotropic Seebeck coefficient of this material.