Enhanced mechanical properties of glass fibre epoxy composites by 2D exfoliated graphene oxide filler

Graphene oxide (GO) received a significant attention in the scientific community due to their excellent mechanical properties identifying themselves as an alternative and combinatory to various other metals and composites. Though GO possess excellent strength, it was observed from the literature that graphene oxide consisting of hydroxyl group elements ensue in poor bonding. Thus reduced functional group density (rFGD) graphene is preferred which has an advantage of good bonding, alongside very small quantity as a filler is required to achieve the enhancement equivalent to graphene oxide which forms the novelty of the current work. In current case, 3, 6 and 9 wt% of rFGD is dispersed into E-glass fibre reinforced composite by traditional hand layup technique. The obtained results revealed that, the tensile, flexural and impact strength have shown superior enhancement with 3 and 6 wt% of rGO than neat E-glass epoxy (0 wt% rGO), whereas an asymptotic decrement is noticed at 9 wt% when tested with ASTM standards except for impact strength. The microstructural studies also indicated the proper adhesion and alignment of fibres without any agglomerations corroborate the enhancement of properties. These overall finding supports the suitability of the developed laminates for potential use in structural applications in aerospace industry.     

Effect of holding time on SiC whiskers growth of SiCw/SiC composites based on SLS technology and their mechanical properties

The in-situ SiC whisker and SiC particle composites were prepared by selective laser sintering (SLS) technology, and the longitudinal and transverse growth rates of crystal nuclei at the liquid-solid interface were calculated and analyzed under the traditional vapor-liquid-solid mechanism. A mathematical model of holding time on the number of in-Situ SiC whisker growth was established, and the prediction rate was 95%. The mechanical properties of in-situ SiC whisker and pure SiC samples with similar volume densities were calculated. The results showed that: The longitudinal growth rate of crystal nuclei at the liquid-solid interface was higher than the transverse growth rate. After precursor infiltration pyrolysis (PIP) four-cycle treatment, the fracture toughness per unit volume density of B-1, B-2, and B-3 specimens increased by 198.66%, 225.00%, and 221.05%, respectively, compared with pure SiC specimens, indicating that this method has a vital role in increasing the toughness of SiC ceramics.     

Fabrication method and mechanical properties of biomimetic Cf/ZrB2-SiC ceramic composites with bouligand structures

Herein, biomimetic C_f/ZrB₂-SiC ceramic composites with bouligand structures are fabricated by combining precursor impregnation, coating, helical assembly and hot-pressing sintering. First, C_f/ZrB₂-SiC ceramic films are achieved through a precursor impregnation method using polycarbosilane (PCS). Second, the PCS-C_f/ZrB₂-SiC ceramic films are coated with ZrB₂ and SiC ceramic layers. Finally, hot-pressing sintering is employed to densify helical assembly C_f/ceramic films with a fixed angle of 30°. The microstructures and carbon fiber content on the mechanical properties of biomimetic C_f/ZrB₂-SiC ceramic composites are analyzed in detail. The results show that the coated ceramic layer on PCS-C_f/ZrB₂-SiC films can heal the cracks formed by pyrolysis of PCS, and the mechanical properties are obviously improved. Meanwhile, the mechanical properties could be tuned by the contents of the carbon fiber. The toughening mechanisms of C_f/ZrB₂-SiC ceramic composites with bouligand structures are mainly zigzag cracks, crack deflection, multiple cracks, carbon fiber pulling out and bridging.     

Effect of Y2O3-stabilized ZrO2 whiskers on the microstructure,mechanical and wear resistance properties of Al2O3 based ceramic composites

The aim of this study was to improve the mechanical properties of Al₂O₃ ceramics by the addition of Y₂O₃-stabilized ZrO₂ whiskers (designated as Al₂O₃/YSZ_W composite) through the flux method and hot-pressing technology. The effect of YSZ_W content on their microstructure, phase composition and transformability, mechanical properties, and wear resistance was systematically investigated. The Al₂O₃/YSZ_W composites containing 10 wt% YSZ_W exhibited the best mechanical performance, including the highest content of YSZ_W tetragonal phase and transformability as well as the largest values in their relative density (99.5%), hardness (1969 HV), fracture toughness (9.57 MPa m^1/2) and flexural strength (855 MPa). The strengthening and toughening of the Al₂O₃/YSZ_W composites were attributed to the YSZ_W tetragonal-monoclinic phase transformation as well as the whiskers reinforcing effect. Furthermore, the Al₂O₃/YSZ_W composites also showed the highest friction and wearing properties.     

Effect of boron nitride nanosheets addition on the mechanical and dielectric properties of magnesium oxide ceramics

Boron nitride nanosheets (BNNSs)/magnesium oxide (MgO) composites were prepared via hot pressing. Mechanical properties of MgO ceramics were improved obviously in virtue of adding BNNSs. The bending strength of the 1 wt% BNNSs/MgO composite increased by about 85% than that of the monolithic MgO. The fracture toughness increased by 34% with the addition of 1.5 wt% BNNSs. Microstructural analyzes have shown that the toughening mechanisms are combinations of the pull-out and bridging of BNNSs, crack deflection, and crack bypassing mechanisms. The addition of a small amount of BNNSs don't destroy the excellent dielectric properties of composites. The dielectric constant of the sample doped with 1 wt% BNNSs was about 9.5 in the whole X-band and the vast majority of P-band, and the loss tangent was less than 5 × 10⁻³ in 10–15.8 GHz.     

Combined role of SiC whiskers and graphene nano-platelets on the microstructure of spark plasma sintered ZrB2 ceramics

This research explores the sintering behavior and microstructure of ZrB₂-based materials containing graphene nano-platelets (GNPs) and SiC whiskers (SiC_w). Spark plasma sintering (SPS) process at 1900 °C was implemented to sinter the specimen, leading to a composite with 100% relative density. High-resolution transmission electron microscopy (HRTEM), field emission scanning electron microscopy (FESEM), X-ray photoelectron spectroscopy (XPS), field emission-electron probe microanalyzer (FE-EPMA), and high-resolution X-ray diffractometry (HRXRD) were employed to study the SPSed sample, along with the thermodynamics predictions. According to the HRXRD result and microstructural observations, the sintering process was non-reactive, which was endorsed with the XPS analysis. Furthermore, graphene presented a beneficial role for eradicating the oxide impurities in the sample during the sintering. Such oxide impurities were reduced to the original phases of SiC and ZrB₂, contributing to porosity removal. Nanostructural investigations revealed the formation of ultrathin amorphous interfaces (~10 nm) between ZrB₂/graphene phases, disordered atomic planes in graphene platelets, and dislocations in ZrB₂ grains. One reason for generating crystalline defects in the microstructure was found out to be the mismatches amongst the elastic properties of the available compounds in the system.     

Mechanical,electrical, and thermal properties of graphene nanosheet/aluminum nitride composites

Graphene nanosheet (GNS)/aluminum nitride (AlN) composites were prepared by hot-pressing and effects of GNSs on their microstructural, mechanical, thermal, and electrical properties were investigated. At 1.49 vol% GNSs content, the fracture toughness (5.09 MPa m^1/2) and flexural strength (441 MPa) of the composite were significantly increased by 30.17% and 17.28%, respectively, compared to monolithic AlN. The electrical conductivity of the composites was effectively enhanced with the addition of GNSs, and showed a typical percolation behavior with a low percolation threshold of 2.50±0.4 vol%. The thermal conductivity of the composites decreased with the addition of GNSs.     

Influence of sol-gel derived ZrB2 additions on microstructure and mechanical properties of SiBCN composites

A simple method for introducing ZrB₂ using sol-gel processing into a SiBCN matrix is presented in this paper. Zirconium n-propoxide (ZNP), boric acid and furfuryl alcohol (C₅H₆O₂) (FA) were added as the precursors of zirconia, boron oxide and carbon forming ZrB₂ dispersed in a SiBCN matrix. SiBCN/ZrB₂ composites with different contents of ZrB₂ (5, 10, 15, and 20 wt%) were formed at 2000 °C for 5 min by spark plasma sintering (SPS). The microstructures were carefully studied. TEM analysis showed that the as formed ZrB₂ grains were typically 100–500 nm in size and had uniform distribution. HRTEM revealed clean grain boundaries between ZrB₂ and SiC, however, a separation of C near the SiC boundary was observed. The flexural strength, fracture toughness, Young's modulus and Vicker's hardness of composites all improved with the ZrB₂ contents and SiBCN matrix containing 20 wt% of ZrB₂ could reach 351±18 MPa, 4.5±0.2 MPa m^1/2, 172±8 GPa and 7.2±0.2 GPa, respectively. The improvement in fracture toughness can be attributed to the tortuous crack paths due to the presence of reinforcing particles.     

Combined role of SiC particles and SiC whiskers on the characteristics of spark plasma sintered ZrB2 ceramics

In this research work, the effects of silicon carbide (SiC) as the most important reinforcement phase on the densification percentage and mechanical characteristics of zirconium diboride (ZrB₂)-matrix composites were studied. In this way, a monolithic ZrB₂ ceramic (as the baseline) and three ZrB₂ matrix specimens each of which contains 25 vol% SiC as reinforcement in various morphologies (SiC particulates, SiC whiskers, and a mixture of SiC particulates/SiC whiskers), have been processed through spark plasma sintering (SPS) technology. The sintering parameters were 1900 °C as sintering temperature, 7 min as the dwell time, and 40 MPa as external pressure in vacuum conditions. After spark plasma sintering, a relative density of ~96% was obtained (using the Archimedes principles and mixture rule for evaluation of relative density) for the unreinforced ZrB₂ specimen, but the porosity of composites containing SiC approached zero. Also, the assessment of sintered materials mechanical properties has shown that the existence of silicon carbide in ZrB₂ matrix ceramics results in fracture toughness and microhardness improvement, compared to those measured for the monolithic one. The simultaneous addition of silicon carbide particulates (SiC_p) and whiskers (SiC_w) showed a synergistic effect on the enhancement of mechanical performance of ZrB₂-based composites.     

Mechanical properties of hybrid multilayer graphene/whisker-reinforced ceramic composites: Simulation and experimental investigation

The trial-and-error method used in ceramics research has certain limitations such as the high blindness of material component design. Moreover, calculations of the toughness of ceramics using the extended finite element method, which is the most broadly applied technique, are complicated. To overcome these issues, in this study, multilayer graphene (MLG)/Si₃N₄ whisker (Si₃N_4w)-reinforced Si₃N₄ ceramics (MWSCs) were used as the model material, and the modeling of MWSCs was conducted using Voronoi tessellation. Additionally, a more concise novel approach was applied for the prediction of the fracture toughness of MWSCs. Furthermore, the optimal MLG and Si₃N_4w contents were predicted, and then they were verified by fabricating MWSCs using spark plasma sintering (SPS). Simulation results indicated that the optimum MLG and Si₃N_4w contents to enable the toughness and hardness to reach the maximum values (9.87 MPa·m^1/2 and 23.19 GPa) were 1 wt% and 3 wt%, which were consistent with the experimental results. Consequently, the effectiveness of the proposed method was verified. Moreover, the experimental values of the maximum fracture toughness and hardness were 11.04 MPa·m^1/2 and 20.29 GPa, which were 47.20% and 12.10% higher than those of Si₃N₄ ceramics reinforced with 1 wt% MLG, respectively. The synergistic toughening effects of MLG and Si₃N_4w were significantly reflected. The load-bearing effect, bridging, and crack deflection induced by MLG and Si₃N_4w were the key reasons for the improvement in the mechanical properties of MWSCs.     

Enhanced mechanical and thermal properties of rigid polyurethane foam composites containing graphene nanosheets and carbon nanotubes

The comparative study of rigid polyurethane foam (RPUF) nanocomposites based on graphene nanosheets (GNSs) and carbon nanotubes (CNTs) has been reported. A GNS content of 0.3 wt% in polyol turns to be optimal for its foamability with the isocyanate component, as verified by rheology measurements. Scanning electron microscopy and transmission electron microscopy observations reveal a homogeneous dispersion of GNSs and CNTs in the RPUF nanocomposites. Only 0.3 wt% loading of GNSs and CNTs led to 36% and 25% improvement respectively in the compressive modulus of the RPUF nanocomposites. Meanwhile, 16 °C and 14 °C improvements in the glass transition temperature confirm the important role of both the nanofillers in the heat resistance of RPUF nanocomposites. These results additionally indicate that GNSs work more effectively than CNTs in mechanical property and heat resistance enhancement of the RPUF nanocomposites. The superiority of GNSs over CNTs can be attributed to their wrinkled surface structure, unique two‐dimensional geometrical morphology and higher specific surface area, which results in stronger interaction and restriction of segmental motion at the interface between the GNSs and the RPUF matrix. In addition, changes in the thermal conductivity of the nanocomposites are negligible, indicating that incorporation of GNSs and CNTs will not hinder the application of RPUF nanocomposites as thermal insulators. On the contrary, the enhancement in mechanical properties and heat resistance will undoubtedly expand the application range of polyurethane foam materials. Copyright © 2012 Society of Chemical Industry     

Effect of graphene addition on the mechanical and electrical properties of Al2O3-SiCw ceramics

This paper presents a study on graphene-reinforced Al₂O₃-SiCw ceramic composites and the relationship between graphene oxide (GO) loading and the resulting mechanical and electrical properties. Well-dispersed ceramic-GO powders were fabricated using a colloidal processing route. Dense composites were obtained via spark plasma sintering, a technique that has the ability to reduce GO to graphene in situ during the sintering process. The mechanical properties of the sintered composites were investigated. The composite with only a small amount of graphene (0.5 vol.%) showed the highest flexural strength (904 ± 56 MPa), fracture toughness (10.6 ± 0.3 MPa·m^1/2) and hardness (22 ± 0.8 GPa) with an extremely good dispersion of graphene within the ceramic matrix. In addition to these exceptional mechanical properties, the sintered composites also showed high electrical conductivity, which allows the compacts to be machined using electrical discharge machining and thus facilitates the fabrication of ceramic components with sophisticated shapes while reducing machining costs.     

Microstructure,mechanical properties and toughening mechanisms of graphene reinforced Al2O3-WC-TiC composite ceramic tool material

The low fracture toughness of Al₂O₃-based ceramics limited their practical application in cutting tools. In this work, graphene was chosen to reinforce Al₂O₃-WC-TiC composite ceramic tool materials by hot pressing. Microstructure, mechanical properties and toughening mechanisms of the composite ceramic tool materials were investigated. The results indicated that the more refined and denser composite microstructures were obtained with the introduction of graphene. The optimal flexural strength, Vickers hardness, indentation fracture toughness were 646.31?±?20.78?MPa, 24.64?±?0.42?GPa, 9.42?±?0.40?MPa?m^1/2, respectively, at 0.5?vol% of graphene content, which were significantly improved compared to ceramic tool material without graphene. The main toughening mechanisms originated from weak interfaces induced by graphene, and rugged fractured surface, grain refinement, graphene pull-out, crack deflection, crack bridging, micro-crack and surface peeling were responsible for the increase of fracture toughness values.     

Effects of SiC whiskers on the mechanical properties and microstructure of SiC ceramics by reactive sintering

As-received and pre-coated SiC whiskers (SiC_w)/SiC ceramics were prepared by phenolic resin molding and reaction sintering at 1650 °C. The influence of SiC_w on the mechanical behaviors and morphology of the toughened reaction-bonded silicon carbide (RBSC) ceramics was evaluated. The fracture toughness of the composites reinforced with pre-coated SiC_w reached a peak value of 5.6 MPa m^1/2 at 15 wt% whiskers, which is higher than that of the RBSC with as-received SiC_w (fracture toughness of 3.4 MPa m^1/2). The surface of the whiskers was pre-coated with phenolic resin, which could form a SiC coating in situ after carbonization and reactive infiltration sintering. The coating not only protected the SiC whiskers from degradation but also provided moderate interfacial bonding, which is beneficial for whisker pull-out, whisker bridging and crack deflection.     

Sintering behavior and mechanical properties of Ta4HfC5-based composites with ZrB2 additive

Ta₄HfC₅ powder was synthesized using TaCl₅, HfCl₄ and phenolic resin as raw materials. Then, Ta₄HfC₅–10 vol% MoSi₂ ceramics and Ta₄HfC₅–10 vol% MoSi₂ with different proportions of ZrB₂ (10 – 30 vol%) ceramics were sintered by spark plasma sintering. Zr atoms substituted Ta and Hf atoms in Ta₄HfC₅ during the sintering process at 2000 °C. The sintering behavior and microstructure evolution upon the ceramics are discussed. The mechanical properties of the composites were improved compared to the pure Ta₄HfC₅ ceramics. The hardness of Ta₄HfC₅–MoSi₂ with 30 vol% ZrB₂ increased from around 10 GPa to almost 13 GPa, the flexural strength increased from around 245–435 MPa, and the fracture toughness increased from 2.56 ± 0.12 MPa?m^1/2 to 4.46 ± 0.20 MPa?m^1/2.     

Utilization of multiple graphene nanosheets in fuel cells: 2. The effect of oxidation process on the characteristics of graphene nanosheets

Structural properties of graphene nanosheets that will be used as electrode material in fuel cells were investigated at different oxidation times. As the oxidation time was increased, the strong bonding between graphene layers in graphite was reduced and graphene layers started to exfoliate forming clusters with a few number of graphene layers. The variations in interplanar spacings, layer number and percent crystallinity indicated how stepwise chemical procedure influenced the morphology of graphite. It was possible to produce relatively flat graphene clusters with definite number of layers by controlling the oxidation time. Graphene nanosheets were characterized in detail by scanning electron microscopy, atomic force microscopy, X-ray diffraction, Raman spectroscopy, and thermal gravimetric analyzer.     

Mechanical and dielectric properties of functionalized boron nitride nanosheets/silicon nitride composites

Uniformly dispersed boron nitride nanosheets (BNNSs) reinforced silicon nitride (Si₃N₄) composites were prepared by surface modification assisted flocculation combined with SPS sintering. In order to improve the dispersibility of the BNNSs in the composites, the liquid phase stripped BNNSs are surface functionalized by a two-step covalently modification. The amino-modified BNNSs (NH₂-BNNSs) and Si₃N₄ powders have opposite surface potential, mixed evenly by electrostatic interaction during flocculation. The results showed that mechanical properties of Si₃N₄ composites were obviously enhanced by adding NH₂-BNNSs. The fracture toughness and bending strength of Si₃N₄ composites added 0.75 wt% NH₂-BNNSs were increased by 34% and 28%, respectively, compared with monolithic Si₃N₄. Toughening mechanisms are synergistic action of the torn, pull-out or bridging of BNNSs and crack deflection mechanisms with microstructural analyzes. The dielectric properties of the Si₃N₄ ceramics are also improved after the addition of NH₂-BNNSs.     

Effect of Ge on microstructure and mechanical properties of Ti3SiC2/Al2O3 composites

Owing to the good physicochemical compatibility and complementary mechanical properties of Ti₃SiC₂ and Al₂O₃, Ti₃SiC₂/Al₂O₃ composites are considered as ideal structural materials. However, TiC and TiSi₂ typically coexist during the synthesis of Ti₃SiC₂/Al₂O₃ composites through an in-situ reaction, which adversely affects the mechanical properties of the resulting composites. In this study, Ti₃SiC₂/Al₂O₃ composites were prepared via in-situ hot pressing sintering at 1450 °C. Ge, which was used as a sintering aid, improved the purity and mechanical properties of the Ti₃SiC₂/Al₂O₃ composites. This is because Ge replaced some of the Si atoms to compensate the evaporation loss of Si to form Ti₃(Si_1-xGe_x)C₂, which showed a crystal structure similar to that of Ti₃SiC₂. Furthermore, the molten Ge accelerated the diffusion reaction of the raw materials, increasing the overall density of the Ti₃SiC₂/Al₂O₃ composites. The optimum Ge amount for improving the mechanical properties of the composites was found to be 0.3 mol. The flexural strength, fracture toughness, and microhardness of the composite with the optimum Ge amount were 640.2 MPa, 6.57 MPa m^1/2, and 16.21 GPa, respectively. The formation of Ti₃(Si_1-xGe_x)C₂ was confirmed by carrying out X-ray diffraction, energy dispersive spectroscopy, and transmission electron microscopy analyses. A model crystal structure of Ti₃(Si_1-xGe_x)C₂ doped with 0.3 mol Ge was established by calculating the solid solubility of Ge.     

Effects of residual stress and intragranular particles on mechanical properties of hot-pressed Al2O3/SiC ceramic composites

Al₂O₃/SiC ceramic composites with different SiC contents have been prepared by powder metallurgy at 1600 °C for 120 min at 30 MPa pressure. The effect of second phase particles on the microstructure and mechanical properties of composites have been studied. The results show that SiC particle has a significant impact on the matrix subjected to residual stress, and on the microstructure of the composites as well. The average grain size of alumina matrix decreases as the SiC particle content increases. Simultaneously, it has been found that the mechanical properties of the material are significantly enhanced in comparison with monolithic Al₂O₃. The highest strength and toughness are obtained when the SiC content is 15 vol%, and the values are 1237 MPa and 5.68 MPa m^1/2, respectively. The mechanisms of strengthening and toughening have been discussed.