Effect of co-deposited SiC nanowires and carbon nanotubes on oxidation resistance for SiC-coated C/C composites

To protect carbon/carbon composites (C/Cs) against oxidation, SiC coating toughened by SiC nanowires (SiCNWs) and carbon nanotubes (CNTs) hybrid nano-reinforcements was prepared on C/Cs by a two-step technique involving electrophoretic co-deposition and reactive melt infiltration. Co-deposited SiCNWs and CNTs with different shapes including straight-line, fusiform, curved and bamboo dispersed uniformly on the surface of C/Cs forming three-dimensional networks, which efficiently refined the SiC grains and meanwhile suppressed the cracking deflection of the coating during the fabrication process. The presence of SiCNWs and CNTs contributed to the formation of continuous glass layer during oxidation, while toughed the coating by introducing toughing methods such as bridging effect, crack deflection and nanowire pull out. Results showed that after oxidation for 45 h at 1773 K, the weight loss percentage of SiC coated specimen was 1.35%, while the weight gain percentage of the SiCNWs/CNTs reinforced SiC coating was 0.03052% due to the formation of continuous glass layer. After being exposed for 100 h, the weight loss percentage of the SiCNWs/CNTs reinforced SiC coating was 1.08%, which is relatively low.     

Oxidation resistance and mechanical properties of LaB6-MoSi2-SiC ceramic coating toughened by SiC nanowires

To improve the high-temperature tolerance of carbon/carbon composites, a compact SiC-nanowires toughened LaB₆-MoSi₂-SiC/SiC (SiCnws-LMS/SiC) coating was designed and fabricated by combination of multiple methods including pack cementation, chemical vapor deposition and supersonic atmospheric plasma spraying. Isothermal oxidation results indicated that the mass loss of LMS/SiC coating decreased from 4.34?±?0.28% to 1.12?±?0.23% after oxidation for 200?h at 1773?K benefit from the addition of SiCnws. Absence of obvious cracks and voids in the coating after oxidation test indicated that the interfaces between various phases and SiCnws could obstruct the crack propagation by releasing the thermal stress in the coating. Meanwhile, after the introduction of SiCnws, the bonding strength and flexural strength of the coating were respectively increased by 54.54% and 59.77% compared to the LMS/SiC coating without SiCnws. The improved mechanical properties could be attributed to the pullout and bridging effects of SiCnws, which created multi-scaled reinforcements, thereby enhancing the load bearing capacity to increase the fracture toughness of the coating.     

Gradient HfB2-SiC multilayer oxidation resistant coating for C/C composites

The gradient HfB₂ modified SiC coating was prepared on the surface of SiC-coated C/C composites by in-situ synthesis. Anti-oxidation behaviors of the coated C/C samples at 1773, 1873 and 1973?K were investigated. The results show that the gradient HfB₂ modified SiC coatings possess excellent oxidation resistance, which can protect C/C substrates from oxidation for 800, 305 and 100?h at 1773, 1873 and 1973?K, respectively. In addition, with the oxidation temperature increasing, the evaporation of the Hf-Si-O glass layer and the active oxidation of SiC were accelerated, which is the reason for the worst oxidation resistance of the sample at 1973?K among the three temperatures.     

SiC nanowire-toughened MoSi2-WSi2-SiC-Si multiphase coating for improved oxidation resistance of C/C composites

To improve the oxidation resistance of carbon/carbon (C/C) composites at high temperature, a SiC nanowire-toughened MoSi₂-WSi₂-SiC-Si multiphase coating was prepared by chemical vapor deposition (CVD) and pack cementation. The microstructure, mechanical properties and oxidation resistance of the coating were investigated. After the introduction of SiC nanowires, the elastic modulus, hardness, and fracture toughness of the MoSi₂-WSi₂-SiC-Si coating were increased by 25.48%, 4.09% and 45.03%, respectively. The weight loss of the coated sample with SiC nanowires was deceased from 4.83–2.08% after thermal shock between 1773 K and room temperature for 30 cycles and the weight loss is only 3.24% after isothermal oxidation at 1773 K in air for 82 h. The good oxidation resistance of the coating is mainly attributed to that SiC nanowires can effectively inhibit the propagation of cracks in the coating by the toughening mechanisms including bridging and pull-out.     

A chromium carbide coating in-situ formed on C/C composites by the novel reactive wetting strategy to enhance oxidation resistance

A chromium carbide (Cr-C) coating in-situ formed on the C/C substrate is successfully prepared by a novel reactive wetting strategy. The interfacial microstructure and oxidation resistance of coated C/C composites are investigated in detail. The as-prepared coating mainly consists of Cr₂₃C₆ and Cr₇C₃, forming a tight joining with the C/C substrate. Compared to uncoated samples, the oxidation weight loss of coated C/C composites is substantially reduced at high temperatures. Furthermore, the hardness of coated C/C composites is significantly increased, enhancing their ability to resist external damage. This reactive wetting strategy can also be used to prepare uniform coatings on C/C composites with complex grooved structure or large size. Surprisingly, coated C/C composites possess a low weight gain of 3.7% due to thin coating (< 10 µm), which can maintain their advantage of low density.     

Design of a C/SiC functionally graded coating for the oxidation protection of C/C composites

To reduce the residual thermal stress between the carbon fiber-reinforced carbon (C/C) composites and the SiC coating layer, functionally graded materials (FGM) consisting of a C/SiC compositionally graded layer (C/SiC interlayer) were adopted. After designing the compositional distribution of the C/SiC interlayer which can relieve the thermal stress effectively, the deposition conditions of the entire compositional range of the C/SiC composites were determined using a thermodynamic calculation. According to the design and calculation the C/SiC interlayer and the SiC outer layer were deposited on the C/C composites by a low pressure chemical vapor deposition (LPCVD) method at deposition temperatures of 1100 and 1300 °C. The stress calculation and the experimental results suggested that the SiC-rich compositional profile in the FGM layer is the most effective for relieving the thermal stress and increasing the oxidation resistance.     

Dynamic oxidation resistance and residual mechanical strength of ZrB2-CrSi2-SiC-Si/SiC coated C/C composites

To improve oxidation resistance of carbon/carbon (C/C) composites, a multiphase double-layer ZrB₂-CrSi₂-SiC-Si/SiC coating was prepared on the surface of C/C composites by pack cementation. Thermogravimetry analysis showed that the as-prepared coating could provide effective oxidative protection for C/C composites from room temperature to 1490 °C. After thermal cycling between 1500 °C and room temperature, the fracture behaviors of the as-prepared specimens changed and their residual flexural strengths decreased as thermal cycles increased. The specimen after 20 thermal cycles presented pseudo-plastic fracture characteristics and relatively high residual flexural strength (83.1%), while the specimen after 30 thermal cycles failed catastrophically without fiber pullout due to the severe oxidation damage of C/C substrate especially the brittleness of the reinforcement fibers.     

Oxidation behavior of SiC/glaze-precursor coating on carbon/carbon composites

In order to improve the oxidation behavior of carbon/carbon composites in a wide range of temperature, a new SiC/glaze-precursor coating was developed.The SiC layer was produced by slurry and sintering, while the glaze precursor layer was prepared by slurry and drying. The microstructures and phase compositions of the coating were analyzed by SEM and XRD, respectively. The oxidation resistance of the coated composites was investigated using both isothermal and temperature-programmed thermogravimetric analysis in the temperature range from room temperature to 1600 °C. The results showed that the oxidation behavior of the coating was mainly controlled by the diffusion of oxygen during the test.The coating showed excellent oxidation resistance and self-healing ability in a wide range of temperature.     

SiC coating toughened by SiC nanowires to protect C/C composites against oxidation

A dense SiC coating toughened by SiC nanowires was prepared on carbon/carbon (C/C) composites using a two-step technique of chemical vapor deposition (CVD) to protect them against oxidation. The morphologies and crystalline structures of the coatings were characterized by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. SiC nanowires played a role in decreasing the size of the cracks and improving the thermal shock resistance of the coating. The result of thermal shock between 1773 K and room temperature for 21 times indicates that, compared with the SiC coating without SiC nanowires, the average size of the cracks in the SiC coating toughened with SiC nanowires reduced from 5 ± 0.5 to 3 ± 0.5 μm. The weight loss of the SiC coated C/C composites decreased from 9.32 to 4.45% by the introduction of SiC nanowires.     

Ablation resistance of HfC coating reinforced by HfC nanowires in cyclic ablation environment

To improve the ablation resistance of carbon/carbon composites in cyclic ablation environment, SiC/HfC ceramic coating reinforced by HfC nanowires was prepared. The microstructure, bonding strength, coefficient of thermal expansion and cyclic ablation resistance of the as-prepared coating were investigated. After incorporating HfC nanowires, the bonding strength between inner SiC coating and outer HfC coating was increased. HfC nanowires could relieve the coefficient of thermal expansion mismatch between inner and outer coating and improve the toughness of the outer coating. By introducing HfC nanowires, the coated sample’s cyclic ablation resistance was improved. After cyclic ablation under oxyacetylene flame for 60 s × 3, the mass and linear ablation rates of the coated sample with HfC nanowires were only 0.444 mg/s and −0.767 μm/s, respectively.     

Mullite whisker toughened mullite coating to enhance the thermal shock resistance of SiC pre-coated carbon/carbon composites

In order to improve the thermal shock resistance of the coated carbon/carbon (C/C) composites, a mullite whisker toughened mullite coating was fabricated on the surface of SiC pre-coated C/C composites (SiC-C/C) by molten-salt method with a later hot dipping process. The phase compositions, surface and cross-section microstructures, high temperature thermal shock resistance of the as-prepared multi-layer coatings were investigated. Results show that the introduction of mullite whiskers can effectively improve the density of the mullite outer coating and decrease the cracking of the coating during the thermal shock cycle process. After 100 times thermal shock cycles between 1773 K and room temperature, only 1.87 × 10⁻³ g cm⁻² weight loss has been detected, indicating the achievement of the excellent thermal shock resistance.     

Oxidation and erosion resistance of multi-layer SiC nanowires reinforced SiC coating prepared by CVD on C/C composites in static and aerodynamic oxidation environments

A multi-layer SiC nanowires reinforced SiC (SiCnws-SiC) coating was prepared in-situ on carbon/carbon (C/C) composites by three chemical vapor deposition (CVD) processes. The microstructure and phase composition of the nanowires fabricated on the first-layer SiCnws-SiC coating and the coatings were examined by SEM, TEM, and XRD. The bamboo-like SiC nanowires with a 50?nm diameter and a length of several tens of micrometers are straight, randomly orientated and distributed like a net on the first-layer SiCnws-SiC coating. The growth direction is [111], and the growth mechanism is VS. The multi-layer SiCnws-SiC coating has three layers: the thickness of the first-layer is roughly 400?µm, and the outer two layers are about 200?µm. Each layer has a sandwich structure. The isothermal oxidation and erosion resistance of the multi-layer SiCnws-SiC coating were investigated in an electrical furnace and a high temperature wind tunnel. The results indicated that the weight loss of the multi-layer SiCnws-SiC coated C/C composites was only 1.8% after oxidation in static air at 1773?K for 361?h. Further, the coated sample failed due to fracture of the coating at the clamping position (i.e. 80?mm) after erosion at 1873?K for 130?h in the wind tunnel. The weight loss of the coated C/C composites occurred due to the formation of penetrating cracks in the coating during the oxidation thermal shock. The maximum bending moment and the larger clamping force caused the coating fracture and resulted in intense oxidation of the substrate and the failure of the specimen.     

Oxidation and defect control of CVD SiC coating on three-dimensional C/SiC composites

Two kinds of multi-layer CVD SiC coatings were prepared on a three-dimensional C/SiC composite. Oxidation behavior of the coating and the composite were studied and the effect of defects in the coating on its oxidation protection property were investigated. Above 1200 °C, thickness of the oxide film formed on the coating was related to oxidation time by the Fick’s first law X(t)²=Bt, the diffusion rate constant increased with oxidation temperature according to the Arrhenius’ relation ln B=−32?483/T+1.4048. Morphology of the interface between the CVD SiC and its oxide film was different after oxidation at temperatures from 1200 to 1500 °C. It was interpreted by consideration of the interfacial stress produced by thermal expansion mismatch and the CO gas pressure produced by interfacial reaction.     

Ablation resistance of HfB2-SiC coating prepared by in-situ reaction method for SiC coated C/C composites

To improve the ablation resistance of SiC coating, HfB₂-SiC coating was prepared on SiC-coated carbon/carbon (C/C) composites by in-situ reaction method. Owing to the penetration of coating powders, there is no clear boundary between SiC coating and HfB₂-SiC coating. After oxyacetylene ablation for 60 s at heat flux of 2400 kW/m², the mass ablation rate and linear ablation rate of the coated C/C composites were only 0.147 mg/s and 0.267 µm/s, reduced by 21.8% and 60.0%, respectively, compared with SiC coated C/C composites. The good ablation resistance was attributed to the formation of multiple Hf-Si-O glassy layer including SiO₂, HfO₂ and HfSiO₄.     

SiC coating with high crack resistance property for carbon/carbon composites

A novel SiC coating with a relatively high crack resistance property (crack extension force (G_C): 12.0 J·m^?2) and outstanding thermal shock resistance was achieved merely by pack cementation. Compared with the conventional SiC coating with Al₂O₃ addition (AOSC2), SiC coating with Al–B–C additions (ABSC2) possesses refined and denser microstructure owing to different effects in promoting SiC densification under different additions. Therefore, the improvement in microstructures results in superior mechanical capabilities, antioxidation performance (900 °C), and thermal shock resistance (between 1500 °C and room temperature).     

Mechanical properties and ablation resistance of HfC nanowire modified carbon/carbon composites

Hafnium carbide nanowires (HfCnws) were in-situ grown in carbon/carbon (C/C) composites, and subsquently the preforms were densified by isothermal chemical vapor infiltration to obtain HfCnws modified carbon/carbon (HfCnws-C/C) composites. Morphology and microstructure of HfCnws were examined, and the effect of HfCnws on the mechanical property and ablation resistance of C/C composites were also investigated. Results show that introducing HfCnws refined the grain size of pyrolytic carbon (PyC). The out-of-plane compression, interlaminar shear and flexual strength of HfCnws-C/C composites increased by 120.80%, 45.60% and 94.65%, respectively compared with pure C/C, and the HfCnws-C/C shows good ablation resistance under oxy-acetylene flame ablation.