LUMINESCENCE OF Bi3+ and Eu2+ DOUBLE CENTERS DOPED IN CaS HOST

In this work, double-center.doped luminescent material CaS:Bi³⁺, Eu²⁺ was made via flux NH₄Cl by sintering in excess sulfur environment. The sample had a purplish red net luminescent color. Excitation spectra at both red, 650 nm and blue, 487 nrn were taken. The red emission from Eu²⁺ center was mainly come from the 4f⁶5d¹ absorption in the CaS host. The blue emission from the Bi³⁺ center on the other hand showed no big difference from the singly doped CaS:Bi³⁺ materials in excitation spectrum. Emission spectra were obtained at excitaton of 270nm and 300nm. Stokes shift was moved about 20-30nm, under different point excitation. Emission peaks of both Bi³⁺ and Eu²⁺ centers appeared at 463nm, 642.5nm by 270nm excitation and 487 nm, 620 nm by 300 nm excitation respectively. After-glow decay cures were also obtained and the shapes of decay curves are similar and it is due to the single hole-trap system by lattice defects.     

Bi3+和Eu3+在Ca2SiO4中的发光和能量传递

用高温固态反应合成了Ca2SiO4:Bi3+,Ca2SiO4:Eu3+和Ca2SiO4:Eu3+,Bi3+发光体。讨论了不同掺杂量和掺杂种类时Bi3+对Eu3+的5D0-7F1,5D0-7F2发射的影响规律。实验发现,Ca2SiO4:Bi3+在紫外线激发下发出明亮的蓝色光,Ca2SiO4:Eu3+,Bi3+中的Bi3+能将激发能传递给Eu3+,使Eu3+的5D0-7F1和5D0-7F2两种跃迁都大大加强,同时,Bi3+也发出鲜艳的紫色光。     

Eu3+在硼酸盐玻璃中的发光以及Bi3+对Eu3+的敏化作用

本文研究了单掺和双掺(Eu3+,Bi3+,Fu3++Bi3+)约二十余种不同成份的硼酸盐玻璃,探讨了玻璃成份对Eu3+发光性质的影响和Bi3+对Eu3+的敏化作用.     

Eu2+离子在固体中的发光

Eu2+在发光材料或激光材料中是一种非常有用的激活离子.发光范围可以复盖于紫外到可见的很宽区域.本文综述了Eu2+离子在固体发光中的若干特性及其有关问题,并结合我们的工作讨论了Eu2+激活的某些发光材料的制备及发光性能.     

YAG基质中Ce对Tb3+离子发光特性的影响

实验中发现,在YAG:Tb中加入痕量Ce后,可以使Tb3+离子5D4→7F跃迁显著增强,因而,改变了发射光谱的能量分布,提高了发光亮度,改善了电流和电压特性,揭示了改进和提高商用P53磷光体发光特性的可能性。实验表明,这种增强作用是由于Ce3+→Tb3+离子的能量传递所致。讨论了Ce3+→Tb3+能量传递机理,分析了传递过程。     

ZnS:Eu2+的长余辉发光

Eu2+的5d能级在许多晶体中都低于其4f能级的最低激发态(6P7/2),因此发光呈带状光谱,且发射波长随基质变化很大。由于5L→4f是容许跃迁,所以发光的衰减很快,通常在μs数量级,出人意料的是ZnS:Eu的发光尽管也是Eu2+的5d→4f跃迁,但衰减却极慢,达几十分钟的数量级。弛豫曲线的分析表明,这种长的弛豫是电子陷阱造成的。     

三价铕激活的(Y,La)2O2S二元体系的发光

为了寻找新的荧光粉基质料材,本文研究了在阴极射线、紫外线和X射线激发下,三价铕激活的(Y,La)2O2S二元体系的发光亮度、发射光谱和发光颜色等发光特性随组成变化的规律,并研究了三价铕离子浓度对(Y0.9La0.1)2O2S体系发光性能的影响。     

掺Yb3+双包层光纤激光器的数值分析

本文对976nm激光泵浦掺Yb³⁺双包层光纤激光器进行了数值模拟,分析了泵浦光及激光在光纤中的分布、输出功率与泵浦功率的关系、光纤长度及腔镜反射率对输出激光功率的影响,所得结论与实验现象基本一致.     

CaS∶Eu~(2+),Sm~(3+)的制备与表征

采用湿法工艺在还原气氛下制备了CaS∶Eu2+,Sm3+光存储材料。研究了灼烧温度和灼烧时间对样品性能的影响。XRD图谱表明,样品在700℃—1200℃均形成CaS晶格。光谱分析表明,在紫外光(295nm)激发后,用980nm半导体激光照射样品,具有光激励发光现象,发射光谱峰值波长为649nm。     

Photoluminescence characteristics and energy transfer between Bi3+ and Eu3+ in Gd2O3: Eu3+, Bi3+ nanophosphors

Bi³⁺ and Eu³⁺ codoped cubic Gd₂O₃ nanocrystals were prepared by the Pechini sol-gel method. Their photoluminescent properties were investigated under ultraviolet light excitation. The introduction of Bi³⁺ ions broadened the excitation band of Eu³⁺ emission, of which a new strong band occurred ranging from 320 to 380 nm due to the 6s²→6s6p transition of Bi³⁺ ions, implying a very efficient energy transfer from Bi³⁺ ions to Eu³⁺ ions. Upon 325 and 355 nm light excitation, the luminescent intensity of Eu³⁺ ions was remarkably improved by the incorporation of Bi³⁺ ions. But a significant quenching of Eu³⁺ emission was observed under 266 nm light excitation when Bi³⁺ was codoped. The possible energy transfer processes between Bi³⁺ and Eu³⁺ were discussed. The decay curves of Eu³⁺ emission under the excitation of 266 nm pulsed laser were measured and gave further evidence for our discussion.     

硫化锌中Sm3+的发光中心

本工作研究了Sm3+离子在立方和六角两种结构硫化锌中的光谱。实验上,采用不同激发条件下的高分辨光谱、时间分辨光谱和激发光谱,同时配合低温退火处理实验,鉴别出硫化锌中Sm3+具有两种不同的发光中心。采用发光方法,第一次对稀土离子在硫化锌中的C3v对称发光中心进行分析。在中间耦合自由离子能级基础上利用不可约张量方法和Wigner-Eckart定理进行晶体场计算,得到的晶体场参数实验值和点电荷模型计算的晶体场参数值相符合。     

邻菲绕啉对Tb(Ⅲ)、Eu(Ⅲ)水杨酸二元配合物荧光强度的影响研究

通过分析邻菲绕啉与Tb(Ⅱ)、Eu(Ⅱ)水杨酸二元、三元配合物的多种谱留数据、证实由于邻菲绕啉的最低三重态与Tb(Ⅱ)、Eu(Ⅱ)离子的第一激发态能级差的不同,使得邻菲绕啉够增强Eu(Ⅱ)离子的水杨酸二元配合物的荧光强度而减弱Tb(Ⅱ)离子的水杨酸二元配合物的荧光强度。     

掺Ce3+、Tb3+的M3Y2(BO3)4(M＝Ca,Sr)

采用固相反应的方法;经二次灼烧合成了掺Ce3+、Tb3+的Ca3Y2(BO3)4和Sr3Y2(BO3)4磷光体;分析了合成过程中铈的还原情况.用X-射线衍射分析确定了它们的结构均为正交晶系,空间群P21cn测定了Ce3+和Tb3+在两种基质中的光谱,得到Ce3+波长位移的某些规律,观察到Ce3+对Tb3+的敏化作用.     

水溶液中新型氨羧螯合剂对Eu3+、Tb3+离子的敏化发光性能研究

研究了四种新型氨羧螯合剂在水溶液中自身的荧光及对Eu3+、Tb3+离子的敏化发光性能.考察了浓度、pH值对荧光强度的影响.     

偏硅酸钙中Ce3+的发光性质

制备了Ce3+激活的CaSiO3磷光体。在77K和室温下研究讨论了它们的激发和发射光谱以及荧光寿命等光学性质,分析了结构和电荷补偿剂的影响。在UV或CR激发下,Ce3+发射较强的蓝紫光,峰值为396nm。室温下,Ce3+离子的荧光寿命大约为30ns。     

Eu^3＋掺杂SiO2气凝胶薄膜的时间分辨光谱及发光动力学

气凝胶（ａｅｒｏｇｅｌｓ）是一种新型的轻质纳米多孔性非晶材料,其孔洞率高达８０～９０％,孔洞的典型尺寸为１～１００ｎｍ．已有文献报道利用ＳｉＯ２气凝胶的纳米网络结构制备出以纳米气凝胶为骨架的纳米材料［１～２］．通过溶胶－凝胶方法制得了Ｅｕ３＋掺杂Ｓｉ...     

偏磷酸钛基体中四价铀离子的荧光

本文用蒸发溶液法制备了Th(PO3)4、U(PO3)4及掺杂了U4+的Th(PO3)4:U4+单晶,确定了β-U(PO3)4属于正交晶系Cmca-D2h18点群,α-U(PO3)4和Th(PO3)4都为三斜晶系P1或P1点群,给出了它们的晶格参数.测量了U(PO3)4吸收谱,和Th(PO3)4基体中U4+的激发和荧光谱.在近紫外光激发下,Th(PO3)4:U4+产生一组荧光,对应于U4+离子的6d-5f电子跃迁.270和298nm的荧光寿命约10ns,对应于电偶极跃迁.在波长为553nm绿光激发下,Th(PO3)4:U4+中四价铀的电子产生上转换效应,释放出358和533nm窄带荧光、它们属于U4+的5f-5f电子跃迁,分别对应于3P2-3H4和1I5-3H4。给出了相应的荧光和上转换效应的跃迁能级图.     

Sm3+在玻璃中的发光以及Sb6+、Ce6+、Gd3+对Sm3+发光性质的影响

本文研究了单掺(Sm3+,Ce3+、Gd3+.Sb3+、双掺(Sm3++Ce3+、Sm3++Gd3+,Sm3++Sb3+)和兰掺(Sm3++Gd3++Ce3+)约四十余种不同玻璃的发射谱和激发谱.探讨了玻璃成份和掺杂离子浓度对Sm3+发光性质的影响以及Ce3+,Gd3+、Sb3+、Ce3++Gd3+对Sm3+的敏化作用。     

BaCl2:Eu和BaCl2·2H2O:Eu微晶的发光特性

本文研究了用还原气氛法在箱式炉内制得的BaCl2:Eu2+微晶及进一步处理后得到的BaCl2·2H2O:Eu2+微晶的发光特性,包括发射光谱、激发光谱、热释光、光激励发光(存贮效应)及其温度依赖,就这些特性对BaCl2:Eu与BaCl2·2H2O:Eu进行了比较.根据发光光谱与激发光谱分析了它们具有良好光致发光特性的原因,讨论了这两种材料在热释光性能及光激励发光(存贮效应)上的明显不同,并对BaCl2·2H2O:Eu2+中Eu2+发光的增强提出了可能的解释.