微量吸附量热研究CuO/γ-Al2O3催化剂的表面酸碱性质

The γ-Al₂O₃ supported CuO samples were studied. XRD results showed that the loading and calcination temperature affected the surface structure. For example， CuO crystallite appeared at the CuO loading of 7% (about 0.82mmol/100m²) on the support. Both CuO crystallite and CuAl₂O₄ spinel were present when the CuO/γ-Al₂O₃ sample was calcined at the same temperature (400℃). Microcalorimetric adsorption of CO₂ and NH₃ revealed that the strength of both the acidity and basicity decreased with the increase of CuO loading for the CuO/γ-Al₂O₃ sample. The increase of calcination temperature further decreased the basicity while the acidity was not affected.     

锐钛矿型TiO2水溶胶的低温制备及其表征

Anatase titanium dioxide hydrosol was prepared at low temperature by a simple method. The title material was characterized by TEM, XRD, FTIR and BET, respectively. The photocatalytic activity of the as-prepared TiO₂ was evaluated by the degradation of methyl orange solution under sunlight and the photocatalytic oxidation of acetone in air. The results showed that the titanium dioxide hydrosol was composed of anatase phase with average grain size of about 7 nm, and the crystallinity became more perfect with the increase of temperature. The BET surface areas were more than 220 m²·g^-1 for these samples. It is found that the photocatalytic activity was much better for the higher heat processing temperature. Especially, the photocatalytic activity of the sample with a heat treatment of 110 ℃ was better than that of P25. In addition, TiO₂ hydrosol also possessed good photocatalytic activity under the sunlight illumination.     

锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.     

纳米二氧化钛粉末的溶胶-凝胶法合成及晶相转化

Nanosized TiO₂ powder with anatase and rutile structures was synthesized by a sol-gel method using TiCl₄ ethanol solution as a precursor.The grain size of TiO₂ powder was about 63nm after the precursor was calcined at 600℃ for 2 hours .The experimental techniques of XRD,TEM and Particle Distribution were used to characterize the synthesized specimens. Various special effects were investigated for their contribution to crystal structure and the size of TiO₂ powder .The formation of anatase as well as the rutile phase of TiO₂ was indicted from the XRD when the reaction temperature was above 30℃ and when the sol was irradiated by infrared rays .However, an anatase TiO₂ powder formed after the heat treatment of the dried gel in a temperature range from 300℃ to 500℃.Under the vacuum drying and with the calcined time below 3hours ,the anatase phase was gained .As well as with the increase of gelatinizing time, the anatase TiO₂ powder was obtained.     

纳米尖晶石LixMn2O4的制备与电化学性能表征

Nano-spinel Li_xMn₂O₄(0.6 ≤x≤ 1.0) was synthesized by two steps of coprecipitation and calcination. The influences of calcination temperature, time and Li/Mn ratio on the crystal structure and the particle size of Li_xMn₂O₄ were investigated. It was shown that the higher the calcination temperature, the more complete the crystal structure, and the larger the particle size. Moreover, the influence of calcination time on the crystal structure was insignificant when it was more than 3h at 700℃. With the increase of x in Li_xMn₂O₄ in the range of 0.6～1.0, the d111 and lattice parameter a increased first and then decreased. The electrochemical properties of nano-spinel LiMn₂O₄ using as cathode material of lithium-ion battery were studied. The low discharge capacity might be due to the irreversible capacity loss brought by the large surface area and lattice vacancies of the nano-spinel.     

有机体系中电合成纳米PbTiO3粉体及表征

The precursor PbTi(OCH₂CH₃)_6-y(acac)_y for the mixed oxide PbTiO₃was synthesized by electrochemical dissolution of Lead and Titanium with a 1∶2 electricity quality in ethanol and acetyl-acetone solution. Nano-sized PbTiO₃powder was prepared by drying and calcining the xerogel from a direct sol-gel hydrolyzation of the precursor solution under pH of 8.5. The FTIR, TG-DTA, XRD and TEM were employed to characterize the structure of the precursor and nano-sized PbTiO₃. The results showed that the optimized conditions for the preparation of nano-sized PbTiO₃ were the electrolysis of the Lead plate and Titanium plate at 50 ℃ and 40 ℃ respectively under 0.03mol·dm^-3Bu₄NBr solution. The nano-sized PbTiO₃prepared by electrolysis exhibited a dispersive structure with an average diameter of 10 to 15 nm.     

由镁、铝醇盐配合物合成纳米粒子MgAl2O4尖晶石

Mg and Al alkoxide complex was synthesized in a cell without battery separator by electrochemical dissolution of aluminum for 6 h and magnesium for 1.8 h at 45 ℃ in ethanol solution of 0.04 mol·dm^-3 (Bu₄N)Br with a current density of 100 mA·cm^-2. IR and Raman spectroscopy were used to characterize the structure of the precursor of MgAl₂O₄. The results show that the current efficiency attains 98.4% and the precursor is MgAl₂(OCH₂CH₃)₅(acac)₃. The acac^- group-containing precursor could prevent it from agglomeration. The xerogel was obtained by drying in vacuum for 24 h and hydrolysis under pH≈8.5 of the precursor, which was heated at 350 ℃ for 2 h to obtain the nano-MgAl₂O₄ powder. XRD and TEM were used to investigate the structure of nano-MgAl₂O₄. The result suggests that the xerogel with an average particle size of 10 nm and the Nano-sized Spinel MgAl₂O₄ Particle of 12 nm thus obtained are with high purity.     

球形Gd2O3∶Eu纳米发光材料的制备

Spherical nanometer Gd₂O₃∶Eu luminescent materials were prepared by homogeneous precipitation method, and the properties were studied also. TG, FTIR and XRD analysis showed that the precursor was carbonate, the cubic Gd₂O₃was obtained after calcination. TEM photographs indicated that the samples were spherical and well dispersed with nanometer and submicrometer size of 200～300 nm which is the nanoparticles’ aggregate. The mechanics of agglomerating growth is also discussed. ED photograph showed that the particle was crystalline. The PL analysis exhibited that CTB band of nanometer Gd₂O₃∶Eu was of 17 nm red shift to bulk materials, and the emission peak was broadened due to the surface and interface effect of nanocrystals.     

La2(CO3)3纳米线的微乳液法制备与表征

La₂(CO₃)₃ nanowires were prepared in the nonionic surfactant microemulsion(Triton X-100/cyclohexane/water)system. Transmission electron microscopy (TEM) and selected area electronic diffraction (SAED) were used to characterize the shape and size of the products. The results showed that the pH value and concentration of mother solution, temperature and aging time all could affect the morphology and size of the La₂(CO₃)₃ nanowires. The lengths of the nanowires were more than 10 μm and the diameters were in the range of 30～200 nm.     

微乳法制备纳米TiO2 /SiO2的结构及光催化研究

Nanosized TiO₂ and TiO₂/SiO₂ particles were prepared by hydrolysis of tetrabutyl titanate (TBOT) and tetraethyl orthosilicate (TEOS) in the TX-100 reverse microemulsion. These particles were characterized by TG-DSC, XRD, FTIR, TEM，N₂ adsorption-desorption. Their photocatalytic activity was tested by degradation of methyl orange. The result shows that TiO₂/SiO₂ nanoparticles are with a monodispersed spherical phase and a uniform size distribution，and TiO₂ particles are dispersed on the surface of SiO₂. The band for Ti-O-Si vibration in FTIR was observed, the Ti-O-Si bond increased the stability of anatase TiO₂, suppressed the phase transformation of titania from anatase to rutile. And due to the addition of SiO₂, the average size of titania decreased from 38 nm in pure TiO₂ to 5 nm in TiO₂/SiO₂. It was found, under UV light irradiation, TiO₂/SiO₂ particles showed higher activity than pure TiO₂, and TiO₂/SiO₂(1/1) particles showed the highest photocatalytic activity on the photocatalytic decomposition of methyl orange, which was influenced by crystal structure, particle size, crystallinity and Surface area Characteristics.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

Ab initio calculation of the intermolecular energy between two hydrogen molecules near the van der Waals minimum

The interaction energy between two hydrogen molecules near the van der Waals minimum is computed as the sum of the SCF interaction energy of the supermolecule and the so-called Hartree-Fock dispersion energy. The most stable configuration is the perpendicular planar one (T configuration), this configuration being stable through the first order term. The energy averaged over the four configurations is in agreement with the available experimental data. The perturbative polarization energy is negligible near the van der Waals minimum but it seems that the charge transfer energy must be taken into account.     

Theoretical study of the triplet excited state of PtPOP and the exciplexes M-PtPOP (M = Tl, Ag) in solution and comparison with ultrafast X-ray scattering results

The [Pt₂(H₂P₂O₅)₄]⁴⁻ ions in the ground and excited states and the excited-state complexes M-[Pt₂(H₂P₂O₅)₄]³⁻ and M₂-[Pt₂(H₂P₂O₅)₄]²⁻ (M = Ag, Tl) were studied in solution with various density functional theory (DFT) functionals from Gaussian 09 and Amsterdam Density Functional (ADF) programs. Calculated results were compared with ultrafast X-ray solution scattering data. Time dependent DFT (TD-DFT) calculations with the B3PW91 functional and unrestricted open shell calculations with the mPBE functional produce good agreement with the experimental results. Compared to gas phase calculations, the surrounding solvent is found to play an important role to shorten the Pt-Pt and M-Pt (M = Ag, Tl) bond lengths, lowering the molecular orbital energies and influences the molecular orbital transitions upon excitation, which stabilizes the excited transient molecules in solution.     

Li2ZrO3材料吸收CO2性能的进一步研究

用不同结构的ZrO₂合成了一系列在高温下吸收CO₂的Li₂ZrO₃材料，并详细的研究了反应物质的物理和化学性质对生成物吸收CO₂性能的影响。采用SEM、XRD以及TG分析法分别进行了材料结构及其吸收CO₂性能的表征，并使用XPS法测定了材料表面的元素组成。实验结果表明，使用不同结构的ZrO₂合成的Li₂ZrO₃，其吸收CO₂的性能明显的不同。用ZrO₂(t)(四方)合成的Li₂ZrO₃吸收CO₂的速度快，在500 ℃下，20% CO₂（80%空气）的气氛中保持3h，其吸收量可达25（±0.6）%（wt），而以ZrO₂(m)(单斜)为原料制备的Li₂ZrO₃在上述吸收条件下重量仅增加9（±0.6）%（wt）。此外，实验结果还表明化学元素的掺杂对用ZrO₂(m)合成的Li₂ZrO₃的CO₂吸收速度及吸收容量影响较大。     

Effect of Zirconia Precursor on the Properties of ZrO2-SiO2 Sol-Gel Oxides

Sol-gel zirconia-silica oxides were synthesized with two zirconium precursors, zirconium n-butoxide and zirconium acetylacetonate, and two different hydrolysis catalysts, HCl and H₂SO₄. The samples prepared with HCl were additionally sulfated with a 1 M solution of H₂SO₄. Characterization was performed with FTIR and ²⁹Si-MAS-NMR spectroscopy, as well as with nitrogen adsorption. Because zirconium and silicon alkoxides have different hydrolysis rates, it was necessary to perform a pre-hydrolysis of the silicon alkoxide before mixing. The atom distribution in the ZrO₂-SiO₂ system depended on the zirconium precursor, which also determined the zirconium incorporation in the silica lattice, which was greater for zirconium acetylacetonate. The zirconium precursor also was responsible for the silanol concentration, which increases when samples were sulfated. Sulfating stabilizes the specific surface area. On sulfate samples calcined at 800°C BET areas larger than 500 m²/g were obtained.     

A study of the compounds present in the three-component system Dy2O3-SeO2-H2O at 100°C

The solubility isotherm of the system Dy₂O₃-SeO₂-H₂O at 100°C was studied and drawn. The selenites present in the system were identified and isolated. A thorough TG, DTG and DTA analysis was made. By modelling the conditions of TG, DTG and DTA analysis, the phases of the thermal decomposition were isolated and identified. The chemistry of the reaction was described.     

High Temperature Reactions in the MoO3-Ag2O System

High-temperature reactions were investigated in the MoO₃-Ag₂O system by means of X-ray, DTA and scanning microscopy methods, and a model was proposed according to which first an Ag₂Mo₄O₁₃ phase was formed at the MoO₃ and Ag₂O (or metallic Ag) interface. Subsequently, at the Ag₂Mo₄O₁₃-Ag₂O contact area a layer of Ag₂Mo₂O₇ appeared. If the amount of silver oxide is sufficiently high, a layer of Ag₂MoO₄ is formed between the Ag₂O and Ag₂Mo₂O₇ phases. This revised version was published online in July 2006 with corrections to the Cover Date.     

Mn-Na2WO4/SiO2催化剂表面活性中心结构的DFT研究

Mn Na2WO4/SiO2 is one of the best catalysts for oxidative coupling of methane.To investigate the nature of active centers and the reaction mechanism,the structure of possible metal sites formed by tungsten and manganese over the silica surface were studied using molecular simulation method and ab initio DFT calculations.Silica support exists in the catalyst as 岐瞔ristobalite and its (111) face exposes preferentially to the surface.The calculated results show that tungsten interacts with the silica surface by three or one bridge oxygen atoms to form tetrahedral [WO4],and manganese interacts with single bridge oxygen to form dispersed [MnO4] or exists as oxide clusters.The nature of the molecular orbitals and the electronic structure suggest that the tetrahedral [WO4] site with single bridge oxygen is the most probable active center responsible for methane activation.     

O MAS NMR study of the oxygen local environments in the anionic conductors Y2(B1−xB′x)2O7(B, B′=Sn, Ti, Zr)

The local environments for oxygen in yttrium-containing pyrochlores and fluorites, Y₂(B_1−xB′_x)₂O₇ (B=Ti, B′=Sn, Zr) are investigated by using solid state ¹⁷O MAS NMR spectroscopy. The quadrupolar coupling constants of the nucleus, ¹⁷O are sufficiently small for these ionic oxides, that high-resolution spectra are obtained from the MAS spectra. Different oxygen NMR resonances are observed due to local environments with differing numbers of metal cations (Y³⁺, Sn⁴⁺, Ti⁴⁺ and Zr⁴⁺), allowing the numbers of different local environments to be quantified and cation mixing to be investigated. Evidence for pyrochlore-like local ordering is detected for Y₂Zr₂O₇, which nominally adopts the fluorite structure.     

Phase relations, crystal chemistry, and dielectric properties in sections of the La2O3-CaO-MgO-TiO2 system

Subsolidus phase equilibria and crystal chemistry were studied for the La₂O₃-MgO-TiO₂ system and for the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃ in the quaternary La₂O₃-CaO-MgO-TiO₂ system. Dielectric properties (relative permittivity and temperature coefficient of resonant frequency, τ_f) were measured at 5-10 GHz and mapped onto the phase equilibria relations to reveal the compositions of temperature-stable (τ_f=0) compounds and mixtures. Phase equilibria relations were obtained by X-ray powder diffraction analysis of approximately 80 specimens prepared by solid-state reactions in air at ∼1450°C. Six ternary phases were found to form in the La₂O₃-MgO-TiO₂ system, including the three previously reported compounds LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, and “La₆MgTi₄O₁₈”; and the new phases La₁₀MgTi₉O₃₄, La₉Mg_0.5Ti_8.5O₃₁, and a perovskite-type solid solution (1−x)LaMg_1/2Ti_1/2O₃-xLa_2/3TiO₃ (0?x?0.5). The phase previously reported as “La₆MgTi₄O₁₈” was found to form off-composition, apparently as a point compound, at La₆Mg_0.913Ti_4.04O₁₈. Indexed experimental X-ray powder diffraction patterns are given for LaMg_1/2Ti_1/2O₃, La₅Mg_0.5Ti_3.5O₁₅, La₆Mg_0.913Ti_4.04O₁₈, La₁₀MgTi₉O₃₄, and La₉Mg_0.5Ti_8.5O₃₁. LaMg_1/2Ti_1/2O₃ exhibits a slightly distorted perovskite structure with ordered B-cations (P2₁/n; a=5.5608(2) Å, b=5.5749(3) Å, c=7.8610(5) Å, β=90.034(4)°). La₅Mg_0.5Ti_3.5O₁₅ (Pm1; a=5.5639(1), c=10.9928(5) Å) and La₆Mg_0.913Ti_4.04O₁₈ (R3m; a=5.5665(1), c=39.7354(9) Å) are n=5 and n=6 members, respectively, of the (111) perovskite-slab series A_nB_n−1O_3n. The new phases La₁₀MgTi₉O₃₄ (a=5.5411(2), b=31.3039(9), c=3.9167(1) Å) and La₉Mg_0.5Ti_8.5O₃₁ (a=5.5431(2), b=57.055(1), c=3.9123(1) Å) are n=5 and n=4.5 members, respectively, of the (110) perovskite-slab series A_nB_nO_3n+2, which exhibit orthorhombic subcells; electron diffraction revealed monoclinic superlattices with doubled c-parameters for both compounds. Extensive perovskite-type solid solutions form in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃. The La₂O₃-MgO-TiO₂ system contains two regions of temperature-stable (τ_f=0) compositions. The quaternary La₂O₃-CaO-MgO-TiO₂ system contains an extensive single-phase perovskite-type volume through which passes a surface of temperature-stable compositions with permittivities projected to be in the 40-50 range. Traces of this surface occur as lines of τ_f=0 perovskite-type phases in the ternary sections LaMg_1/2Ti_1/2O₃-CaTiO₃-La₂O₃ and LaMg_1/2Ti_1/2O₃-CaTiO₃-La_0.833Mg_0.25Ti_0.75O₃.