FAILURE MODE AND CONSTITUTIVE MODEL OF PLAIN HIGH-STRENGTH HIGH-PERFORMANCE CONCRETE UNDER BIAXIAL COMPRESSION AFTER EXPOSURE TO HIGH TEMPERATURES

An orthotropic constitutive relationship with temperature parameters for plain highstrength high-performance concrete （HSHPC） under biaxial compression is developed. It is based on the experiments performed for characterizing the strength and deformation behavior at two strength levels of HSHPC at 7 different stress ratios including a=σs ： σ3=0.00：-1,-0.20：-1,-0.30 ： -1,-0.40：-1,-0.50：-1,-0.75：-1,-1.00：-1, after the exposure to normal and high temperatures of 20, 200, 300, 400, 500 and 600℃, and using a large static-dynamic true triaxial machine. The biaxial tests were performed on 100 mm×100 mm×100 mm cubic specimens, and friction-reducing pads were used consisting of three layers of plastic membrane with glycerine in-between for the compressive loading plane. Based on the experimental results, failure modes of HSHPC specimens were described. The principal static compressive strengths, strains at the peak stress and stress-strain curves were measured; and the influence of the temperature and stress ratios on them was also analyzed. The experimental results showed that the uniaxial compressive strength of plain HSHPC after exposure to high temperatures does not decrease dramatically with the increase of temperature. The ratio of the biaxial to its uniaxial compressive strength depends on the stress ratios and brittleness-stiffness of HSHPC after exposure to different temperature levels. Comparison of the stress-strain results obtained from the theoretical model and the experimental data indicates good agreement.     

高温静水应力状态下花岗岩稳态蠕变参数研究

高温高压花岗岩钻孔实验表明,温度低于500℃,静水应力低于150MPa 状态下,岩体的钻孔变形均属于稳态蠕变变形阶段. 该文选取了广义开尔文模型来反映其特征,通过拉普拉斯变换及逆变换,详细推演出了钻孔径向位移解析解,并且考虑温度-应力的耦合效应,给出了模型参数随温度及应力变化的关系式. 利用该关系进行拟合计算,说明广义开尔文模型来表达高温高压环境中的花岗岩稳态蠕变变形特性,寻求蠕变参数是合理可靠的. 该文对于高温岩体地热资源开发中的钻孔施工与维护、钻孔变形量预测等方面,具有实际的指导意义.     

高温后高强高性能混凝土双轴压力学性能

利用大型静动真三轴试验机,进行了常温20${^\circ}$C以及200${^\circ}$C$\sim $ 600${^\circ}$C\,6个温度等级高温后高强高性能混凝土在7种应力比双轴压应力状态下的强度与变形试验.测得了双轴主压方向的静态强度、峰值应变与应力应变曲线,剖析了温度和应力比对单、双轴压强度与峰值应变发展趋势的影响规律性以及试件破坏形态. 试验结果表明:随温度的升高,高强高性能混凝土的单轴压减摩强度并不一定降低;双轴压强度相对于单轴压强度的提高倍数取决于应力比、不同温度等级后的高强高性能混凝土``脆硬性'. 提出了带有温度和应力比参数的Kupfer-Gerstle破坏准则公式.