玻璃纤维增强复材条带与钢纤维砂浆加固损伤柱轴心受压试验研究

通过对1根未加固混凝土(RC)柱和4根加固损伤混凝土(RC)柱进行轴压试验,研究了玻璃纤维增强复材(GFRP)条带及钢纤维砂浆复合加固不同损伤程度RC方柱的轴压性能.分析了同等损伤情况下,GFRP条带对钢纤维砂浆加固损伤RC柱的约束作用;不同损伤情况下,复合加固RC柱的承载力、刚度、延性.结果表明:GFRP条带可以显著...     

GFRP加固RC柱应变滞后试验分析

本文在试验的基础上 ,详细地分析了GFRP加固RC柱子的时候由于不同工况的存在 ,导致GFRP相对RC柱表面混凝土应变的滞后。从而带来GFRP加固承载力不足的RC柱子时候 ,因为应变滞后而不同程度地降低GFRP对RC柱的约束     

钢筋网水泥复合砂浆加固 RC偏心受压柱的试验研究

在对9根近似足尺偏心受压柱(包括小偏心受压和大偏心受压柱)的试验研究中,通过用一种薄壁型的钢筋网水泥 复合砂浆(简称CMMR)片加固的偏心受压柱与未加固的偏心受压柱的对比试验,发现被加固的偏压柱其承载力有了较大 幅度的提高,在相同的加固条件下,小偏心受压柱加固后承载力提高幅度大于大偏心受压柱;较低强度等级的偏压柱比较 高强度等级偏压柱的加固效果更好。被加固柱的延性得到了明显改善,变形能力和耗能能力有显著增强。本文先对试验结 果进行了描述,然后分析了这种加固层对加固偏压柱的极限承载力、破坏形态、荷载.挠度曲线及裂缝分布形态等的影响 机理和作用规律。研究结果证明这是一种加固效果显著,加固后柱各种工作性能优良、施工方便且投资节省的柱加固方 法。     

高性能GFRP包裹RC方柱的轴心受压试验研究

结合具体工程实践，分析了高性能GFRP条带等间距包裹钢筋混凝土方柱的强度、层数影响和轴压比导致的应变滞后情况。结果表明。随着层数的增加，强度有所增加但有限值，GFRP应变滞后程度随轴压比的增大而严重。并给出GFRP条带等间距包裹RC方柱的承载力计算公式。     

GFRP加固实心黏土砖轴心受压短柱的试验研究

通过对7组粘贴玻璃纤维布(GFRP)的实心黏土砖轴心受压短柱及1组对比柱在单倚载作用下的试验研究,比较分析了不同长细比和不同FRP加固量等参数对加固砖柱的承载力、延性和破坏形态的影响.试验表明:横向粘贴GFRP布能有效地提高轴心受压短柱的承载力,柱的延性得到显著改善.     

钢筋钢丝网砂浆加固混凝土柱轴压试验研究

目前常用的三种钢筋混凝土柱加固方法有加大截面法、外包钢法和纤维复合材料法,都有各自的不足,本文试图提出钢筋（大直径）钢丝网砂浆加固混凝土柱的新方法,并对该方法加固的混凝土柱进行了轴压试验研究.     

GFRP管钢筋混凝土短柱力学性能研究

为研究GFRP管钢筋混凝土短柱的力学性能,对14根GFRP管钢筋混凝土短柱和2根无套管短柱进行轴压试验,通过试验,分析了影响套管钢筋混凝土短柱的部分因素,试验结果表明：对于在不同受力方式下的试件,其承载力与变形能力都基本相同;GFRP管有很强的约束能力,由于GFRP管的约束,使得混凝土的强度得到明显的提高,变形能力也得到明显的增加;对于配置有纵筋的试件,既可以提高试件的承载力,又可以避免核心混凝土发生剪切破坏。     

复合砂浆钢筋网加固RC足尺梁受弯试验研究

通过对6根RC足尺梁受弯试验,研究不同强度等级RC足尺梁采用高性能复合砂浆钢筋网加固后的受弯性能。主要分析原构件混凝土强度和加固砂浆强度匹配对加固梁受弯承载力、刚度及抗裂性能影响。依据平截面假定和试验结果,提出梁的受弯承载力、刚度计算公式。依据建立的公式计算受弯极限承载力和挠度值与试验值吻合较好,可为实际加固工程设计提供理论参考。     

玻璃纤维管再生混凝土柱轴心重复受压试验研究

为研究玻璃纤维管再生混凝土柱的轴压性能,对7根不同直径的圆形截面玻璃纤维管再生混凝土柱进行了轴向重复受压试验,分析了其破坏过程及破坏形态、特征荷载和位移、荷载-位移曲线、荷载-应变曲线、荷载-残余位移曲线和骨架曲线.结果表明:截面直径较小的试件发生剪切破坏,截面直径较大的试件发生环向破坏,最终内部混凝土被压溃,各试件截面规整且均未发生扭曲破坏;玻璃纤维空管的承载力相对较低,破坏时属于脆性破坏;随着试件直径的增大,试件的轴压承载力和刚度逐渐增大;玻璃纤维管再生混凝土柱极限承载力相比玻璃纤维空管显著提高,在重复荷载作用下,玻璃纤维管再生混凝土柱具有较好的延性和耗能能力.     

复合砂浆钢丝网加固RC受弯构件的试验研究

本文对用无机材料钢丝网复合砂浆加固的钢筋混凝土梁进行了正截面抗弯试验研究,研究了这种新的加固技术对钢筋混凝土梁的抗弯承载力的影响和作用。试验包括13根用钢丝网加固的试件和两根未加固的对比试件。加固的形式包括U形三面加固及一面加固两种。试验的主要目的是研究采用该加固方法后,试件可能产生的破坏形式,正截面抗弯承载力的提高程度等等。试验中测量了受弯构件的开裂荷载、极限荷载、钢筋应变及钢丝网应变。试验结果表明,钢丝网复合砂浆薄层可以明显地提高钢筋混凝土梁的抗弯承载力,提高抗裂性能,增强构件的抗弯刚度。试验结果说明该技术是一种有效的加固方法。     

预应力钢绞线-角钢复合加固预损混凝土柱轴压性能试验研究

基于预应力钢绞线加固法和外包钢加固法的原理,提出一种新型加固方法:预应力钢绞线-角钢复合加固法.通过12根钢筋混凝土方柱(其中2根为对比柱,2根预应力钢绞线加固柱,8根4组不同损伤程度的预应力钢绞线-角钢复合加固柱)的轴压试验,研究了预应力钢绞线加固方法和预应力钢绞线-角钢复合加固方法的加固效率以及不同受损程度下预应力钢绞线-角钢复合加固后钢筋混凝土柱破坏特征、受力性能和破坏机理.试验结果表明:预应力钢绞线-角钢复合加固方法充分发挥了两种材料的优点,两种材料协同工作性能良好.极限承载力大幅提高,延性也得到明显的改善.结合受损混凝土柱特征,提出考虑损伤折减指标的轴压承载力计算公式,理论计算结果与实际值吻合较好,可为相关研究提供理论支持.     

外包钢与碳纤维布复合加固钢筋混凝土偏压柱试验研究

通过14根被加固钢筋混凝土柱的偏心受压试验,研究了碳纤维布和角钢以及两者复合加固后混凝土柱的破坏特征、受力性能和破坏机理。分别对不同含碳纤维布率、含角钢率、长细比和偏心距下被加固混凝土柱的极限承载力、应力-应变关系以及刚度和延性等方面进行了研究和分析。研究结果表明:复合加固混凝土柱充分发挥了碳纤维布和角钢加固混凝土柱的各自优点,并使它们能协调工作、共同作用,获得优良的力学性能,同时复合加固柱的承载力和延性均优于碳纤维布和角钢单一加固柱。长细比越小、偏心距越小、含CFRP率和含角钢率越高,则柱承载力越高,延性提高效果越好。     

Experimental study on GFRP pipes under axial compression

Fiber reinforced polymer (FRP) is suitable for structures in corrosive environment and long-span lightweight structures due to its high-strength, light-weight, and anti-corrosive qualities. The behavior of pultruded glass fiber reinforced polymer (GFRP) pipes, which are the members of long-span lattice structures, under axial compression was investigated by tests. Short GFRP pipes were first tested to determine the basic mechanical properties. Then the stability of long GFRP pipes was studied by axially compressive tests in four groups with different slenderness ratios, twelve specimens totally. Based on the results of the tests and literature, the formula of the buckling load of composite pipes under axially compressive load was presented based on Perry formula. It can well predict the buckling failure load GFRP pipe under axial compression. __________ Translated from Journal of Tianjin University, 2007, 40(1): 19–23 [译自: 天津大学学报]     

Experimental study on GFRP pipes under axial compression

Fiber reinforced polymer (FRP) is suitable for structures in corrosive environment and long-span light-weight structures due to its high-strength, light-weight, and anti-corrosive qualities. The behavior of pultruded glass fiber reinforced polymer (GFRP) pipes, which are the members of long-span lattice structures, under axial compression was investigated by tests. Short GFRP pipes were first tested to determine the basic mechanical properties. Then the stability of long GFRP pipes was studied by axially compressive tests in four groups with different slenderness ratios, twelve specimens totally. Based on the results of the tests and literature, the formula of the buckling load of composite pipes under axially compressive load was presented based on Perry formula. It can well predict the buckling failure load GFRP pipe under axial compression.     

外套钢管自密实混凝土加固钢筋混凝土中长圆柱轴压性能试验研究

对9根外套钢管自密实混凝土加固钢筋混凝土中长圆柱和未加固钢筋混凝土中长圆柱进行轴心受压试验研究,研究长径比、钢管壁厚和后浇自密实混凝土强度对复合加固中长圆柱受力性能的影响。研究结果表明:未加固中长圆柱破坏形态属于局部强度破坏而复合加固中长圆柱的破坏属于弹塑性失稳破坏。长径比越小,复合加固柱承载力提高越大;随着后浇自密实混凝土强度的提高,复合加固柱极限承载力略有提高,但延性逐渐降低;钢管壁厚的增加能够显著提高复合加固柱的极限承载力和延性。在试验研究的基础上,提出外套钢管自密实混凝土加固钢筋混凝土中长圆柱的承载力简化计算公式,计算结果与试验结果吻合较好。     

开孔钢板加劲的矩形钢管钢纤维高强混凝土柱轴压试验研究

为探明加劲肋类型、开孔钢板（PBL）开孔间距、钢纤维体积掺量、混凝土强度等级等对矩形钢管钢纤维高强混凝土（SFRHC）柱轴压破坏模式的影响规律,对10根柱进行了轴压性能试验,得到了其荷载-压缩变形曲线、位移延性系数、耗能指标和破坏模式。研究结果表明：与PBL加劲试件相比,钢板加劲试件和未加劲试件的位移延性系数分别降低11.9%和10.4%,耗能指标分别降低8.3%和5.6%, PBL加劲肋能有效加强钢管与核心混凝土的组合作用。掺入体积率为0.8%钢纤维的PBL加劲试件,其位移延性系数和耗能指标分别提高12.5%和42.3%,钢纤维体积率为0.8%~1.2%时,试件位移延性系数和耗能指标明显提高。加劲SFRHC柱为肋间管壁局部外鼓破坏,PBL加劲柱的破坏位置均位于PBL开孔处,未加劲SFRHC柱为管壁外鼓破坏,对应钢板屈曲处核心混凝土表现为压碎破坏,钢纤维被整体拔出;加劲SFRHC柱沿高度方向破坏位置明显下移,钢板加劲肋和PBL加劲肋均能有效分担轴向荷载。     

外套钢管自密实混凝土加固钢筋混凝土圆形截面短柱轴压性能试验研究

提出外套钢管自密实混凝土加固钢筋混凝土柱的复合加固方法。通过11个加固钢筋混凝土圆形截面短柱试件（其中2个为增大截面加固柱试件、9个为复合加固柱试件）和2个未加固钢筋混凝土圆形截面短柱试件的轴压试验,对不同方法加固的钢筋混凝土圆形截面短柱承载力、刚度和延性进行研究,分析加载方式、含钢率、后浇自密实混凝土强度、界面处理方式等因素对复合加固柱轴压性能的影响。试验结果表明：复合加固柱试件的承载力和延性均优于未加固钢筋混凝土圆柱试件和增大截面加固柱试件。仅核心混凝土受压的试件承载力略大于全截面受压的试件;随着含钢率的增大,复合加固柱试件的承载力和延性提高显著;随着后浇自密实混凝土强度的提高,复合加固柱试件的承载力略有提高,但延性有所下降;界面处理方式对复合加固柱试件轴压性能影响不显著。在试验研究的基础上,提出复合加固钢筋混凝土圆形截面短柱的承载力计算式,得出的计算结果与试验结果吻合良好。     

高强不锈钢绞线网-渗透性聚合砂浆加固梁抗弯裂缝试验研究

高强不锈钢绞线网-渗透性聚合砂浆加固技术是一项新型加固工艺,具有耐火、耐腐蚀、耐老化等优点。针对采用该工艺加固的河北沧州某大桥,采用缩尺比例模型,进行了4根该工艺加固的钢筋混凝土T形梁和1根对比梁的抗弯性能试验研究,分析了加固对梁裂缝的影响以及裂缝的发展情况。结果表明,采用该材料加固梁,可有效降低梁裂缝宽度,并延迟裂缝的出现。在试验研究的基础上。给出了此类加固梁最大裂缝宽度计算公式,可用于实际工程计算。     

碳纤维布加固轴心受压钢筋混凝土圆柱的研究

通过对9根混凝土圆柱的轴心受压试验,研究了碳纤维布加固混凝土柱后的破坏特征和受力性能。试验结果表明,用碳纤维布加固可以获得优良的力学性能,可使加固试件的极限荷载大幅度提高、混凝土的变形能力大大提高,混凝土柱的延性得到显著改善。     

高强不锈钢绞线网-渗透性聚合砂浆抗剪加固的试验研究

高强不锈钢绞线网-渗透性聚合砂浆加固法是一种新型加固工艺,它具有耐火、耐腐蚀、耐老化的优点。本文对4根 用该工艺加固的钢筋混凝土梁和1根对比梁进行了受剪性能试验研究。试验结果表明,利用这种新型材料进行加固,梁的 受剪承载力得到了显著提高,剪切刚度有一定程度的提高,同时加固措施对斜裂缝的发展有良好的约束作用。在试验研究 的基础上,本文给出了利用这种方法进行加固的受剪承载力及剪切刚度的设计计算公式,并给出了最大斜裂缝宽度的计 算方法,公式计算结果与试验结果吻合良好。