无卤含磷阻燃剂协效氢氧化镁阻燃乙烯-醋酸乙烯酯共聚物的研究

采用新型阻燃剂9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)和双马来酰亚胺(BMI)反应,合成了一种无卤含磷阻燃剂(DB).以乙烯-醋酸乙烯酯共聚物(EVA)为基体树脂,KH550硅烷偶联剂改性氢氧化镁(MH)为主阻燃剂(KH550-MH),DB为协效阻燃剂,制备了EVA复合材料,研究了DB含量对复合材料的力学性能、加工性能、垂直燃烧性、吸水率的影响.结果表明:添加少量DB可提高EVA复合材料的阻燃性能和改善加工性能.     

偶联剂改性SiO2对PEO基电解质导电性能的影响

采用硅烷偶联剂KH-550对SiO2进行表面改性,并加入聚氧化乙烯/高氯酸锂复合物[(PEO)8LiClO4]中,制备了(PEO)8LiClO4/KH550-SiO2复合聚合物电解质,通过红外光谱(IR),热重分析法(TGA)和交流阻抗方法研究了偶联剂改性SiO2的结构、表面改性程度和复合电解质的离子导电性能.结果表明加入表面改性SiO2的聚合物电解质体系电导率明显提高,当SiO2含量为10%时,(PEO)8LiClO4/KH 550-SiO2体系电导率达到最大值1.99×10-5S·cm-1(20℃).     

硅烷偶联剂处理对剑麻及其复合材料性能的影响

用KH -550硅烷偶联剂对剑麻纤维 (SF)进行表面处理 ,再制备剑麻/酚醛树脂复合材料 ,研究了SF表面处理对复合材料性能的影响 ,探讨了复合体系的界面粘合性 ,并借助偏光显微镜 (POM)和扫描电子显微镜 (SEM)观察了复合材料的形态结构。结果表明 ,经过KH -550硅烷偶联剂处理后 ,复合材料的界面粘合性较好 ,提高了其综合性能。     

硅烷偶联剂对介电弹性体复合材料电-机转化敏感度的影响

利用硅烷偶联剂KH550、KH570对无机纳米TiO2粒子进行表面改性,经机械共混及压延成型方法制备出3种界面结构的TiO2/室温硫化硅橡胶(RTV)介电弹性体复合材料。利用FTIR及DSC研究TiO2纳米粒子的表面改性情况,并研究不同硅烷偶联剂对复合材料介电性能和力学性能的影响。结果表明:KH550改性TiO2掺杂的复合材料较纯TiO2或KH570改性掺杂的复合材料其功能性明显提高。采用KH550改性TiO2使得复合材料拥有更高的介电常数,更低的弹性模量,使电-机转化敏感度较未改性前提高了57.4%。     

无卤阻燃高密度聚乙烯/乙烯-醋酸乙烯酯共聚物体系的性能研究

以乙烯-醋酸乙烯酯共聚物(EVA)、高密度聚乙烯(HDPE)为基体树脂,硅烷偶联剂KH- 550改性氢氧化镁(KH550- MH)为主阻燃剂,无卤含磷阻燃剂(DB)作为协效阻燃剂,制备了复合材料,对比了不同含量的EVA、HDPE对复合材料力学性能、加工性能、燃烧性能、吸水性的影响.结果表明:当EVA、HDPE含量分别占...     

硅微粉/气相SiO_2/环氧树脂复合材料的制备与力学性能研究

采用γ-氨丙基三乙氧基硅烷(KH-550)对硅微粉、气相SiO2进行表面改性后,分别使用单一的硅微粉、气相SiO2及复配的硅微粉/气相SiO2作为填料,对环氧树脂电子灌封胶进行改性,制得二元或三元体系的复合材料,并对其力学性能进行比较分析。结果表明:与采用单一填料改性的二元体系相比,采用硅微粉和气相SiO2组合填料改性的三元体系环氧复合材料的力学性能较好;当m(环氧树脂)∶m(硅微粉)∶m(气相SiO2)=100∶120∶3时,复合材料的弯曲强度达到最大值161.44MPa。     

纳米SiO2表面KH550接枝密度对改性纤维素绝缘纸力学性能与热稳定性的影响

为提升纤维素绝缘纸的力学性能与热稳定性,利用KH550对纳米SiO2进行表面改性,将其掺杂到纤维素绝缘纸中,通过分子模拟建立不同接枝密度的纳米SiO2/纤维素复合模型,并对各模型的力学性能、均方位移、内聚能密度、溶解度参数和径向分布函数进行计算和分析.结果表明:KH550接枝密度为12.5％的纳米SiO2/纤维素复合模型抗形变能力最佳,并具有较大的内聚能密度和溶解度参数,改性效果最佳.     

可分散性纳米二氧化硅改性高压绝缘用环氧树脂的研究

选用CCl4作分散介质将DNS-2型可分散性SiO2纳米微粒充分分散在环氧树脂中改性环氧树脂,并与平高电气的具体生产工艺相结合制得具有高力学性能的高压绝缘复合材料。对复合材料的冲击性能、拉伸性能、弯曲性能和耐压性能进行了测试研究;利用透射电镜(TEM)和扫描电镜(SEM)考察了SiO2纳米微粒在环氧树脂中的分散性和复合材料冲击断面形貌。结果表明,SiO2纳米微粒在环氧树脂里得到了较好的分散,在不影响绝缘复合材料电性能的前提下使冲击性能、拉伸性能、弯曲性能得到了明显的改善。     

可应用于带电作业装备防护的高导热绝缘复合材料的制备

高分子基体与高导热填料复合的导热绝缘复合材料是解决带电作业机器人等机械设备绝缘防护、电子电气设备散热问题的良好解决方案.本研究采用硅烷偶联剂KH550对微米级氧化铝(A12O3)表面进行修饰,混合高导热的碳纳米管(CNT)作为导热填料,选用耐受温度范围广和耐腐蚀的硅橡胶(SR)作为高分子基体,制备了硅橡胶复合材料,并对其性能进行测试.结果表明:A1203/CNT混合填料总含量在10％,CNT占比为0.3％时,SR复合材料的热导率高达0.268 W/(m·K),相比SR提升了103.1％,体积电阻率为10.5x1012 Ω·cm,相对介电常数几乎不变,邵氏A硬度和杨氏模量略微增大.     

可陶瓷化PE/EVA/MH/PCS复合材料阻燃性能与绝缘性能研究EI北大核心CSCD

低烟无卤阻燃聚烯烃材料已成为保护人类生命及财产安全、保障生产生活正常进行的重要材料而得到广泛的应用,但因无机阻燃剂阻燃效率低而需要高添加量,使其阻燃材料综合性能降低,影响在高端领域的应用。该文采用聚碳硅烷协同氢氧化镁阻燃改性聚乙烯/乙烯–醋酸乙烯酯共聚物复合材料,研究聚碳硅烷(polycarbosilane,PCS)与氢氧化镁(magnesium hydroxide,MH)之间的协同作用及阻燃剂微观相分布对复合材料阻燃性能、燃烧行为及电性能的影响。实验结果表明,当阻燃剂总添加量为40%时,复合材料的极限氧指数达到28.3,热释放速率峰值降低了38%,总热释放降低39%,燃烧性能得到改善;PCS不影响复合材料的热降解行为,在燃烧过程中形成无定形相将氢氧化镁分解生成的MgO颗粒粘结在一起形成致密的陶瓷化炭层;两步混制备方法影响MH的分布,有利于提高复合材料电性能,体积电阻率提升26%,电击穿性能提升22%。研究结果可为低烟无卤阻燃聚烯烃材料的开发及在高端领域应用提供理论支撑及实践基础。     

粘结NdFeB磁体表面纳米TiO_2/氟碳复合涂层的耐腐蚀性能

将硅烷偶联剂KH-550改性的纳米TiO2颗粒与氟碳乳液混合涂覆于粘结NdFeB磁体表面形成复合防蚀涂层。研究了纳米TiO2/氟碳复合涂层对粘结NdFeB磁体耐腐蚀性能的影响,利用扫描电镜、接触角测定仪和电化学工作站对涂层表面形貌、疏水性和耐腐蚀性进行了表征。结果表明,经过硅烷偶联剂KH-550改性的纳米TiO2颗粒在涂层中的分散性较好,可以有效减少涂层中的微裂纹和孔洞。粘结NdFeB磁体表面为亲水性,而涂刷纳米TiO2/氟碳复合涂层后,磁体表面转变为疏水性。电化学测试表明复合疏水涂层可以有效提高磁体的耐腐蚀性能。     

Nafion212/SiO2复合膜水的表观扩散系数研究

通过在线溶胶-凝胶法制备了不同SiO2含量的Nafion212/SiO2复合膜,测量了Nafion212膜及不同SiO2含量的Nafion212/SiO2复合膜的水平衡吸附值,通过稳态渗透法测量了不同干空气流速和温度下透过Nafion212膜及不同SiO2含量的Nafion212/SiO2复合膜的水的通量.结果表明,随...     

原位复合SiO2对聚合物电解质导电性能的影响

以正硅酸乙酯(TEOS)为前驱体,LiClO4为添加盐原位复合制得了PEO基聚合物电解质,并在原位复合的同时加入硅烷偶联剂KH560对生成的纳米SiO2表面改性,制得改性聚合物电解质.交流阻抗测试结果表明,原位复合SiO2的聚合物电解质,导电性能明显改善,而原位复合偶联剂改性SiO2的聚合物电解质,导电性能的改善更加明显.扫描电子显微镜(SEM)和X射线衍射分析(XRD)测试结果从不同的方面解释了导电性能改善原因.     

Study on the technology and performance of the degradation of nitrogen oxides according to the outdoor large cement concrete barrier

ABSTRACT

In terms of the study about the decontamination of nitrogen oxides by the outside barrier made of cement concrete, in order to purify NO_x produced by auto exhaust, studies had utilized different spray-finishing technology to make the urban concrete barrier have the function of purification NO_X. This paper has shown the improvements of how to make the photocatalytic materials on barrier surface maintain long-term stability and the effectiveness, and further optimize the ratio of photocatalytic slurry. The results show that the content of surfactant (sodium dodecylbenzenesulfonate) is 3.5% of that of ST (TiO₂ acidified by H₂SO₄); actual concentration of the ST slurry is 2.0 g/L; the best content of the penetrant (silane coupling agent KH550) is 2% of the photocatalytic slurry; within the wear range of less than 2 mm, ST photocatalytic materials showed good purification effect.     

硅烷偶联剂对Nd-Fe-B磁体有机涂层附着强度和阻挡性能的影响

利用打底法和掺混法在烧结Nd-Fe-B磁体上制备出含有不同KH-550硅烷浓度偶联剂的环氧树脂涂层.分析了硅烷浓度对涂层与基体附着强度和涂层阻挡性能的影响,揭示了其影响机理.实验结果表明,合适浓度的KH-550硅烷偶联剂能显著提高环氧树脂涂层的附着强度和阻挡性能;打底法比掺混法更有利于环氧树脂涂层性能的提高;在硅烷浓度约7.5%时涂层的综合性能较佳.     

Preparation and Properties of a Thermal Insulating Layer and a Buffer Layer for Multilayer Pyroelectric Film Infrared Detector

A thermal insulating layer and a buffer layer play a key role in the multilayer pyroelectric thin film infrared detector. In this work, a porous SiO 2 film serving as thermal insulating layer and a dense SiO 2 film serving as buffer layer were prepared by sol-gel method. The porosities of the porous film and the dense film are about 50% and 6%, respectively. Maximum thickness values of a single layer porous film and that of a single layer dense film all come up to 1.5 w m. Rms (root-mean-square) surface roughness of the porous film is about 40 nm and that of the dense film is about 1.5 nm. Experimental result shows 0.4 w m dense SiO 2 film can flatten rough surface of the porous SiO 2 film, and the rms surface roughness is less than 5 nm. The composite SiO 2 film can effectively block thermal diffusion.     

低介电常数绝缘纸的制备及其击穿性能

为提高油浸式变压器绕阻中纸-油-纸复合绝缘系统的击穿电压,实验室制备了能降低绝缘纸介电常数的微纳米级SiO2空心微球以及含不同质量分数SiO2(wSiO2)空心微球的实验用绝缘纸手抄片。测量浸油后的含不同质量分数SiO2空心微球绝缘纸的介电常数,wSiO2=5%空心微球的绝缘纸介电常数最低,比未加SiO2空心微球的绝缘纸介电常数低34%。用双层电介质场强公式分析绝缘纸介电常数以及复合绝缘系统中油隙厚度对油、纸中场强分配的影响。设计纸-油-纸复合绝缘系统模型,用COMSOL仿真软件对模型进行计算,得出模型中纸、油中电场为均匀电场,双层电介质场强公式可用于纸-油-纸模型的理论分析。最后,用含不同质量分数SiO2空心微球的绝缘纸组成纸-油-纸复合绝缘系统进行电击穿实验,介电常数越低的绝缘纸组成的纸-油-纸复合绝缘系统击穿电压越高,介电常数最低的wSiO2=5%空心微球的绝缘纸组成的纸-油-纸复合绝缘系统比未加SiO2空心微球的绝缘纸组成的纸-油-纸复合绝缘系统的击穿电压高15.5%。     

正交实验研究硼铝硅玻璃的介电性能

利用正交实验法,以降低玻璃的介电常数和介质损耗为目标,对硼铝硅玻璃(SiO2-Al2O3-B2O3-RO)组份进行了优化研究.极差分析表明:在选定的水平下,CaO对玻璃的介电常数影响最大,最终得到所选影响因素水平为SiO2 53.5%、Al2O314.5%、CaO 4%时玻璃的介电性能最好.通过对优化后的玻璃分析表明,该玻璃具有很好的热稳定性,不易分相和析晶,并指出要降低玻璃的介电常数可以在保持SiO2含量不变的情况下,适当减少碱土金属的含量.     

原位制备P(VDF-HFP)/SiO_2复合聚合物电解质及其性能研究

通过倒相法原位制备P(VDF-HFP)/SiO_2复合聚合物电解质膜,将其于1.0 mol/L LiPF_6/(EC+DMC+EMC)中浸泡30 min即得复合聚合物电解质。采用扫描电子显微镜法(SEM)、X射线衍射光谱法(XRD)、线性扫描法(LSV)和交流阻抗法(EIS)分别对复合电解质的形貌、结晶度和电化学性能进行表征。SEM结果表明SiO_2溶胶原位制备的P(VDF-HFP)/SiO_2复合膜的膜层表面微孔丰富且相互连通,XRD表明其结晶度较纯P(VDF-HFP)膜减小;LSV和EIS结果表明复合膜的电化学稳定窗口为5.0 V,室温离子电导率高达3.134×10~(-3) S/cm,且其界面阻抗较直接添加SiO_2粉末制备的复合膜的920Ω下降至850Ω。     

溶剂分子与Nafion膜、SiO2/Nafion复合膜的相互作用

用溶胶-凝胶法把SiO2复合到Nafion膜的亲水相中,研究了甲醇、乙醇和水在Nafion膜及SiO2/Nafion复合膜中的溶解情况。衰减全反射(ATR)FT-IR、XRD分析结果显示:甲醇、乙醇分子容易渗透到Nafion膜的疏水区,引起渗透,导致膜的溶胀;水分子容易与Nafion膜的亲水区相互作用,与疏水区的相互作用不明显。SiO2/Nafion复合膜在醇、水中具有与Nafion膜相似的性质,但具有阻醇作用和良好的吸水、保水功能。加入15%的SiO2有助于降低Nafion膜的渗透问题。