动态硫化EPDM/PP/SiO_2共混物的力学性能研究

研究了橡塑比、过氧化物复合硫化体系及KH-570硅烷偶联剂对动态硫化EPDM/PP/SiO2共混物的力学性能的影响。结果表明,随着PP含量的增加,动态硫化EPDM/PP/SiO2共混物的力学性能和硬度增加,但压缩永久变形增加,断裂伸长率却减小。过氧化物复合硫化体系中,当DCP为1.5份时,动态硫化EPDM/PP/SiO2共混物的综合物理力学性能较好。加入KH-570改性的白炭黑,对EPDM/PP/SiO2共混物起到补强的作用;且提高共混物的交联密度,降低压缩永久变形。     

PP／EPDM共混物的力学性能及形貌研究

对PP／EPDM共混物的力学性能进行了研究,并用扫描电子显微镜（SEM）观察了共混物的形貌特征。结果表明,随EPDM含量增加,拉伸强度、拉伸弹性模量、弯曲强度、弯曲弹性模量均下降,但冲击强度在EPDM含量约为30％时出现极大值。除了分散相球粒的粒径和粒间距外,分散相在基体中的形状对共混物的冲击强度也有很大影响。同时,SEM结果表明,EPDM参与了PP的结晶过程。     

动态硫化EPDM/PP/HDPE热塑性弹性体结构与性能的研究

研究了三元乙丙橡胶(EPDM)/聚丙烯(PP)/高密度聚乙烯(HDPE)动态硫化热塑性弹性体(TPV)的力学性能、流变性能和热性能,并用扫描电镜(SEM)扫描其断面形貌.结果表明,随着HDPE的用量增加,TPV的拉伸强度和撕裂强度以及硬度有所下降;在流变性能测试中TPV体系的最大扭矩逐渐增加到最大值,随后趋于稳定;TPV体系的热失重温度和分解温度与不含HDPE的TPV相比变化不大;扫描电镜图片显示体系中EPDM包裹HDPE的壳-核结构随HDPE用量的增加而增多.     

共混对聚丙烯力学性能的影响

研究了不同牌号的聚丙烯共混后的产物的力学性能,并以DCP为硫化剂,TAIC为硫化促进剂,以自制的聚酯型超支化聚合物为流动促进剂,利用动态硫化技术制备了聚丙烯树脂/三元乙丙橡胶(EPDM)热塑弹性体.研究表明:高熔融指数的聚丙烯、共混材料中橡胶的用量以及超支化树脂的比例对共混材料的力学性能和高温流动性有很大影响.     

高抗冲击高强度的PP改性材料的研制

本文用ＨＤＰＥ和ＥＰＤＭ共混改性ＰＰ，通过对其组分配比与共混材料力学性能的考察，研制了既有卓越的韧性，又有较高强度的综合性能优良的系列三元共混材料。本产品加工性能好，成本低，制成母粒便于工业化推广，具有一定的经济效益和社会效益。     

MPP增容PP／PA6共混物的形态结构与增容机理

采用马来酸酐接枝改性聚丙烯(MPP)为增容剂制备了聚丙烯／尼龙6(PP／PA6)共混物，研究了MPP增容PP／PA6共混物的形态结构和热行为，探讨了MPP增容PP／PA6共混物的增容机理。结果表明：PP／PA6共混物为热力学不相容的海岛型两相结构。MPP的加入改善了PA6与PP的相容性，使两相分散均匀，MPP对PP／PA6共混物的增容机理可用界面——分散相表面改性模型来描述。     

辐照交联对HDPE／EPDM体系结构和动态力学性能的影响

利用动态力学说，ＤＳＣ等方法，对辐照交联ＨＤＰＥ／ＥＰＤＭ共混体系的结构和动态力学性能进行了研究。结果发现，辐照能够为ＨＤＰＥ的结晶产度生影响；辐照后聚合物体系学谱３个损耗峰的变化与其形态的结构的变化有关。     

硅烷偶联剂对复合沥青混合料路用性能的影响

针对胶浆与集料界面粘附对沥青混合料性能的影响,采用“三步”成型工艺制备复合沥青混合料试件,研究了KH-550硅烷偶联剂对其路用性能的影响,并借助IR和SEM等微观设备,分析了硅烷偶联剂在复合沥青混合料中的偶联机理。结果表明,随硅烷偶联剂用量增加,复合沥青混合料在7d和28d龄期的路用性能先提高后降低,当用量为乳化沥青质量分数的0．6％时,混合料冻融劈裂强度比、马歇尔稳定度和抗压回弹模量等路用性能提高了10％～30％。硅烷偶联剂改性后的花岗岩集料引入了偶联剂分子结构的Si-O键,在胶浆与集料界面有Si-O-Si键的生成;掺加偶联剂后的水泥乳化沥青胶浆表面变得凹凸不平,结构致密性提高;水泥乳化沥青胶浆能够较好地粘附于花岗岩集料表面,胶浆与集料界面结构得到改善。     

PP／EVA共混物相转变对力学性能的影响

本文借助ＳＥＭ及力学性能测试考察了ＰＰ／ＥＶＡ共混物的相转变过程，实验结果表明：Ｗ同观结构形态随ＥＶＡ含量的变化有一从“海－岛”结构向“海－海”结构的转化，且相转变对共混物的力学性能有较大影响，本文对此进行了分析讨论。     

OMMT对EPDM止水带耐H2S腐蚀性能的影响

采用有机蒙脱土(OMMT)与三元乙丙橡胶(EPDM)进行共混改性,制备了OMMT改性EPDM(EPDM/OM-MT)止水带。利用X射线衍射(XRD)对EPDM/OMMT止水带的结构进行了表征,并研究了EPDM/OMMT止水带在H2S气体和H2S溶液中的耐腐蚀性能。结果表明,5phr和10phr的OMMT与EPDM止水带形成了剥离型纳米复合结构,15phr的OMMT与EPDM止水带则形成了插层型纳米复合结构。EPDM/OMMT止水带在H2S气体和H2S溶液中的拉伸强度保留率、扯断伸长率保留率和撕裂强度保留率均远高于EPDM止水带,经OMMT改性的EPDM止水带的耐H2S腐蚀性能得到明显提高,这可归因于EPDM与OMMT形成的剥离或插层型纳米复合材料具有很好的气液阻隔性能。     

Effects of Silane Coupling Agent on Microstructure and Mechanical Properties of EPDM/Carbonyl Iron Microwave Absorbing Patch

The effects of types and amounts of silane coupling agent on mechanical properties of vuleanized rubber microwave absorbing patch （VRMAP） were studied. The mechanisms of silane coupling agent＇s effects on mechanical properties of rubber microwave absorbing patch （ RMAP ） and microvave absorbing patch＇s （MAP＇s） mierostrueture were also discussed by using SEM and FT-IR. The experimental results show that the tensile strength of RMAP could be increased through adding the filler of carbonyl iron powder （CIP） modified by silane coupling agent. RMAP fiUed with CIP, which was treated by silane coupling agent KH550, possessed a high tensile strength of 11.5 MPa, which was 448% more than that of MAP whose filler wus not modified by any coupling agent. It was found that the optimal amount of KH550 was 1.0 phr to 100.0 phr carbonyl iron powder. The effects of different modifying techniques on RMAP＇s mechanical properties were also inrestigated. It is indieated that MAP whose filler is modified by the wet process has the highest tensile strength, but it is not the optimal modiifying technique due to complieated wet process. On the contrary, the dry process was very simple, and VRMAP possessed fairly high mechanical properties, therefore, it was the perfect modifying process.     

硅烷偶联剂处理对玄武岩单丝拉伸性能的影响

用硅烷偶联剂KH-550对不同品种的玄武岩纤维进行表面改性处理,采用单丝拉伸试验,结合扫描电镜和SPSS统计分析的方法,研究了硅烷偶联剂处理对玄武岩单丝拉伸性能的影响.结果表明:表面处理前后,玄武岩纤维品种2和3的拉伸强度和断裂伸长率均没有显著变化;玄武岩纤维品种1的拉伸强度和断裂伸长率明显增大,其拉伸强度提高32.8%,断裂伸长率增大31.79%.这证明用硅烷偶联剂KH-550对玄武岩纤维进行表面改性处理,可以达到表面处理的目的且不损伤玄武岩单丝的拉伸性能,一定程度上可以弥补玄武岩纤维生产工艺的不足.     

不同偶联剂对秸秆／PP复合材料力学性能的影响研究

通过对秸秆粉的质量分数、偶联剂的种类及其含量等因素的控制,研究上述因素变化对PP／秸秆粉基木塑复合材料的各项力学性能的影响．研究结果表明：四种不同偶联剂中马来酸酐接枝聚丙烯（MAPP）的效果最好;当秸秆粉质量分数达到30％时,木塑复合材料的抗弯强度、抗拉强度、抗冲击强度均为最佳;采用MAPP作为偶联剂且含量为秸秆粉的4％时,材料的抗弯、抗拉强度、抗冲击强度均为最佳,当MAPP含量超过4％时,材料的力学性能会有所下降．     

偶联剂对B_4C／PP共混体系的增容作用

Ｂ４Ｃ／ＰＰ共混纤维是重要的防中子辐射材料。通过Ｂ４Ｃ／ＰＰ共混体系流变性能及纤维的形态结构性能的研究，分析了钛酸酯偶联剂在Ｂ４Ｃ／ＰＰ共混体系中的增容作用，表明了最佳偶联剂的品种和用量分别为ＮＤＺ－１０１和１．５～２．５％．     

聚丙烯/纳米SiO2 复合材料的制备和表征

使用熔融共混法制备了聚丙烯（PP）／纳米SiO2复合材料。研究发现，硅烷偶联剂对纳米SiO2在PP中的分散起一定的作用，但不是非常有效。添加马来酸酐接枝聚丙烯（PP—g—MAH）相容剂后，可以使纳米SiO2均匀地分散于PP中。当纳米SiO2的质量分数为2％时性能较优，与纯PP相比，V形缺口冲击强度提高了90％，拉伸强度提高了5％，弯曲强度提高了23％。最后，对PP—g—MAH大幅度改善纳米SiO2在PP中分散效果的机理作了初步推断。     

单分散疏水SiO2改性苯丙乳液的制备及其性能

采用种子-半连续乳液聚合法,以硅烷偶联剂KH-560表面改性的单分散二氧化硅为改性材料,制得单分散疏水性SiO2改性的复合苯丙乳液.对乳液及涂膜性能进行了红外光谱、粒径分析、接触角和热失重表征.考察了不同含量的SiO2对转化率、凝胶率、化学稳定性、机械稳定性和涂膜的硬度、耐盐雾时间的影响.结果表明,SiO2用量为单体质量的2.0％,改性后的乳液及涂膜各项性能明显提高.     

纳米ZnO/PP复合材料性能研究

以钛酸酯偶联剂对不同粒径的纳米ZnO粒子进行表面处理 ;采用熔融共混工艺制备了纳米ZnO/PP复合材料 ;并对复合材料力学性能及其结晶性能进行研究。结果表明 :偶联剂改善了复合材料的力学性能 ;平均粒径为 80nm的纳米ZnO质量分数为 4 %时 ,其复合材料的综合性能相对较好 ,复合材料的冲击强度、拉伸强度和弯曲强度均得到不同程度的提高 ;纳米ZnO具有异相成核作用 ,能够起到细化PP球晶的作用。     

硅烷接枝聚丙烯对聚丙烯复合材料性能的影响

目的研究硅烷接枝聚丙烯（PP－g－Si）对不同填料如滑石粉（Ta）、碳酸钙和硫酸钡填充的PP复合材料性能的影响,方法分别制备经PP－g－Si偶联的滑石粉、CaCO3和BaSO4填充的PP复合材料,并测试其机械性能和结晶熔融行为,结果与未经偶联的体系相比,在一定PP－g－Si含量范围内,PP－g－Si可使T3／PP体系力学性能提高,但拉伸模量降低;而对PP／CaCO3和PP／BaSO4体系的力学性能影响不大或使其性能有所降低,同时,PP－g－Si对这3种填料填充的PP体系中PP的结晶熔融行为也有较大影响,结论在实验范围内,PP－g－Si对聚丙烯和滑石粉界面有增容作用,可作为PP／Ta材料的大分子偶联剂,而对PP／CaCO3和PP／BaSO4体系则没有增容作用。     

溅射条件对SiO2膜力学特性的影响