免煅烧磷石膏—矿渣复合胶凝材研究

磷石膏-矿渣胶结材是以未经煅烧的磷石膏和矿渣为主要原料配制的新型石膏基胶凝材.它具有比其他品种石膏高的强度和耐水性能.对影响磷石膏-矿渣胶结材的矿物改性剂单个因素进行了试验研究,得出各因素单独作用时胶结材强度的发展规律.在此基础上,通过正交试验得到磷石膏-矿渣胶结材的最佳复合矿物改性剂配比.对最佳配比的石膏基胶凝材料进行抗冻融实验.结果表明磷石膏-矿渣材料抗冻性能良好.     

发泡剂对石膏基复合墙板热工参数及固化特性的影响

以硬石膏、矿渣、改性剂和发泡剂为原材料,配制石膏基复合墙板胶结料,研究发泡剂对石膏基复合墙板胶结材硬化体的面密度、导热系数以及胶结材的凝结时间、吸水率及其硬化体的耐水性、强度、干燥收缩等性能的影响.结果表明,发泡剂可使石膏基复合墙板形成轻质多孔结构,提高保温隔热性能.随着发泡剂掺量的增加,胶结材的水化硬化进程加快,胶结材硬化体的吸水率增大、软化系数逐渐变小、抗压强度和抗折强度均逐渐变小、干燥收缩率逐渐增大.当发泡剂S的掺量范围为0.2％～0.8％、发泡剂T的掺量范围为0.4％～0.6％时,石膏基复合墙板的物理性能指标可同时满足GB/T 23451-2009《建筑用轻质隔墙条板》中软化系数≥0.60、抗压强度≥3.5MPa、干燥收缩值≤0.6mm/m的技术规定.     

新型脱硫石膏砌块的制备及性能研究

以脱硫石膏为主要胶凝材料,以粉煤灰为填料,通过掺加复合激发剂激发脱硫石膏-粉煤灰胶结材的活性,达到改善石膏砌块性能的目的;通过掺加蜡-醇复合防水剂,提高石膏砌块的耐水性能.试验结果表明,当粉煤灰填充量为脱硫石膏质量的20％时,对石膏强度影响最小;当复合激发剂B掺量为1.75％时,脱硫石膏-粉煤灰胶结材的活性得到最大激发程度;当蜡-醇复合防水剂掺量为0.4％时,新型脱硫石膏砌块的耐水性能达到最佳状态.     

矿渣-粉煤灰-氟石膏胶结材激发及毒性

研究了激发剂对氟石膏的激发效果和机理,复合氟石膏胶结材的强度、软化系数和浸出毒性.通过NaOH、Na2 SO4和NaF对氟石膏激发试验,确定最优掺量均为1％.在此基础上,采用矿渣、粉煤灰、熟料对用量80％以上氟石膏进一步改性,发现Na2 SO41％、矿渣2.5％、粉煤灰5％和氟石膏89％复合胶结材性能最好,28 d抗压...     

矿渣-脱硫石膏-水泥复合胶凝材料的性能研究

制备了矿渣-脱硫石膏-水泥复合胶凝材料,通过抗压强度试验确定了其最佳配合比,并进行了微观机理分析。抗压强度结果表明：相同水泥掺量(10%)下,随着脱硫石膏掺量的增加,试件的28 d抗压强度先增大后减小;相同m_矿渣∶m_脱硫石膏(8.0∶1.0)下,随着水泥掺量的增加,试件的28 d抗压强度先增大后减小;最佳m_矿渣∶m_脱硫石膏∶m_水泥为75.5∶9.5∶15.0。28 d微观结果表明：随着脱硫石膏掺量的增加,水化产物生成量增多,AFt由针状变为粗棒状,但同时CaSO₄·2H₂O量也较多;随着水泥掺量的增加,CaSO₄·2H₂O和矿渣颗粒减少,无胶结性的SiO₂增多,AFt由针状先变为粗棒状再变为针状和粗棒状共同存在。     

复合激发剂对脱硫石膏-粉煤灰胶结材抗压强度的影响

研究了燃煤电厂两大固体废物脱硫石膏和粉煤灰在空气自然养护条件下胶结反应特性,以粉煤灰改性未经煅烧脱硫石膏配制的新型石膏基胶结材,对影响脱硫石膏-粉煤灰胶结材的碱激发各因素进行了试验研究,得出了各因素单独作用时胶结材强度的发展规律.在此基础上,通过正交试验得到脱硫石膏-粉煤灰胶结材的最佳复合激发剂配比.此外,还研究了各激...     

磷石膏复合材料制备和性能研究

在激发剂的作用下,利用矿渣改性磷石膏(PG)制备磷石膏基胶凝材料(PGS),然后研究掺入钢渣和粉煤灰制备磷石膏复合材料的性能情况。结果表明:当激发剂掺量在3%时,在20℃(湿度大于70%)养护下PGS固化体28d的抗压强度和抗折强度(41.9MPa和7.1MPa)分别较未掺激发剂的提高了47.3%和42.3%,28d软化系数为0.94;当钢渣比例在1:1时,磷石膏砂浆性能最佳,28d抗压强度和抗折强度分别为57.1MPa和4.8MPa;粉煤灰掺量在20%时,磷石膏砂浆抗压强度和抗折强度分别为22.1MPa和3.4MPa,吸水率和软化系数分别为4.9%和0.94,质量损失率、抗压强度损失率和抗折强度损失率分别为1.5%、4.5%和4.3%。     

磷石膏蒸压砖制备工艺及强度机理研究

以经低压(0.12 MPa,120℃)蒸汽预处理后的磷石膏为原料制备墙砖.研究表明,以磷石膏掺量(质量分数,余同)为40%,消石灰掺量为15%,复合外加剂掺量为1%,石硝和粉煤灰质量比为2:1制备的墙砖,其抗折强度达到4 MPa以上,抗压强度达到23 MPa以上,抗冻性优良,可用作承重墙材.对该墙砖进行了XRD,SEM分析,结果表明,墙砖强度主要来源于高强托勃莫来石结晶相,其包裹着磷石膏和骨料,形成了致密的结构.     

粉煤灰矿渣建筑胶结料的研制

在以粉煤灰为主的胶结料中掺入适量的矿渣能大幅度提高其强度,矿渣掺量以控制在15%￣25%为宜;石灰对粉煤灰和矿渣都起激发剂的作用,在本试验范围内,石灰适宜掺量为15%￣25%;粉磨细度与强度成正比关系,综合考虑产量、质量与电耗的关系,胶结料的比表面积控制在420￣450m2/kg。以粉煤灰、矿渣、石灰和石膏配置的胶结料,后期强度能大幅增长,凝结时间可调,抗大气稳定性较好。若采用蒸养技术,可得到3d抗压强度达45MPa以上,后期抗压强度能继续增长的硅酸盐制品。     

盐激发对大掺量固废胶凝材料及其制备混凝土性能的影响

为了大规模消纳钢铁冶炼渣,实现其高附加值利用,激发钢渣潜在活性,在m(钢渣)∶m(矿渣)∶m(水泥)=36∶54∶10时,研究了Na₂SO₄和Na₂SiO₃两类常用激发剂单掺及复掺对钢渣-矿渣复合胶凝材料性能的影响。结果表明,Na₂SiO₃和Na₂SO₄复掺的激发效果要优于单掺,最佳复合激发剂掺量为3%Na₂SiO₃+1%Na₂SO₄。复掺激发剂时,钢渣-矿渣复合胶凝体系除了出现新相黝帘石外,其它水化产物种类基本相同,均为AFt、CH和无定形的C-(A)-S-H凝胶,其中SO₄^2-能够加速钢渣和矿渣玻璃体结构的解聚,而SiO₃^2-水解形成H₃SiO₄^-和OH^-     

Effects of the law reforming public works contracts on the Italian building process

The Italian construction industry was rocked by the scandals regarding procurement by the public sector during the early 1990s. Although not confined to construction, the role of the state in construction demand meant that it was one of the most heavily implicated sectors. Known as 'tangentopoli', the scandals have prompted a major reform of public sector procurement in the Italian industry which, combined with changes required to conform with EU directives, is leading to a profound cultural change in the industry. This paper provides an authoritative review of the changes in the procurement codes and the roles and relationships within the construction industry. It shows how the project management of public sector programmes is being strengthened, and how the procurement of the design and construction processes is being separated to provide greater transparency in the process. Although it is too soon to tell what the actual impact of these changes will be upon construction industry practice, some suggestions are made in the concluding comments. En Italie, le secteur de la construction a ete secoue par les scandales concernant les approvisionnements par le secteur public au debut des annees 1990. Bien que n'etant pas limitee a la construction, la part de l'Etat dans la demande pour les travaux de construction temoignait que c'etait bien l'un des secteurs les plus impliques. Connus sous l'appellation de 'tangentopoli', ces scandales ont declenche une vague de reformes qui a touche les approvisionnements par le secteur public qui, combines aux changements necessaires pour se conformer aux directives de l'UE, conduisent a un profond changement culturel de cette industrie. La presente communication constitue une etude documentee des changements qui affectent les codes d'approvisionnement ainsi que les roles et les relations qui s'etablissent au sein de l'industrie de la construction. Elle montre comment la gestion de projets, lorsqu'il s'agit de programmes du secteur public, se trouve renforcee et comment la fourniture de prestations d'etudes et de travaux de construction joue en faveur d'une plus grande transparence du procede. Bien qu'il soit trop tot pour dire quel impact auront ces changements sur les pratiques dans le secteur de la construction, l'auteur conclut en faisant certaines recommandations.