Synthesis and characterization of poly(L‐lactide)‐poly(ethylene glycol) multiblock copolymers

Poly(L‐lactide)‐poly(ethylene glycol) multiblock copolymers with predetermined block lengths were synthesized by polycondensation of PLA diols and PEG diacids. The reaction was carried out under mild conditions, using dicyclohexylcarbodiimide as the coupling agent and dimethylaminopyridine as the catalyst. The resulting copolymers were characterized by various analytical techniques, such as GPC, viscometry, ¹H‐NMR, FTIR, DSC, X‐ray diffractometry, and contact angle measurement. The results indicated that these copolymers presented outstanding properties pertinent to biomedical use, including better miscibility between the two components, low crystallinity, and hydrophilicity. Moreover, the properties of the copolymers can be modulated by adjusting the block length of the two components or the reaction conditions. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 1729–1736, 2002; DOI 10.1002/app.10580     

Synthesis and characterization of star‐shaped poly(ethylene glycol)‐block‐poly(L‐lactic acid) copolymers by melt polycondensation

Compared with linear diblock or triblock poly(ethylene glycol)‐block‐poly(L ‐lactic acid) copolymer (PEG‐b‐PLLA), star‐shaped PEG‐b‐PLLA (sPEG‐b‐PLLA) copolymers exhibit smaller hydrodynamic radius and lower viscosity and are expected to display peculiar morphologies, thermal properties, and degradation profiles. Compared with the synthesis routine of PEG‐b‐PLLA form lactide and PEG, the traditional synthesis routine from LA and PEG were suffered by the low reaction efficiency, low purity, lower molecular weight, and wide molecular weight distribution. In this article, multiarm sPEG‐b‐PLLA copolymer was prepared from multiarm sPEG and L ‐lactic acid (LLA using an improved method of melt polycondensation, in which two types of sPEG, that is, sPEG₁ (four arm, Mn = 4300) and sPEG₂ (three arm, Mn = 3200) were chosen as the core. It was found the molecular weight of sPEG‐b‐PLLA could be strongly affected by the purity of LLA and sPEGs, and the purification technology of vacuum dewater and vacuum distillation could help to remove most of the impurities in commercial available LLA. The polymers, including sPEG and sPEG‐b‐PLLA with varied core (sPEG₁ and sPEG₂) and LLA/sPEG feeding ratios, were characterized and confirmed by ¹H‐NMR and ¹³C‐NMR spectroscopy, Fourier transform infrared spectroscopy (FT‐IR) and gel permeation chromatography, which showed that the terminal hydroxyl group in each arm of sPEGs had reacted with LLA to form sPEG‐b‐PLLA copolymers with fairly narrow molecular weight distribution. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

A novel initiating system for ring‐opening polymerization of ε‐caprolactone: Synthesis of triarm star‐shaped poly(ε‐caprolactone)

The rare earth compound, scandium trifluoromethanesulfonate [Sc(OTf)₃], has been used as a water‐tolerant catalyst for the synthesis of star‐shaped poly(ε‐caprolactone)s (SPCLs) with trimethylol propane as trifunctional initiator in solvent at 40°C. Triarm SPCLs have been successfully prepared. The molar mass of SPCLs were determined by end‐group ¹H NMR analyses, which could be well controlled by the molar ratio of the monomer to the initiator, and were independent of the amount of Sc(OTf)₃ used. Differential scanning calorimetry analyses suggested that the maximal melting point, the cold crystallization temperature, and the degree of crystallinities of SPCLs increased with the increasing of the molar mass and were lower than the linear poly(ε‐caprolactone) (LPCL) with similar molar mass. Furthermore, polarized optical microscopy indicated that LPCL showed fast crystallization rate and good spherulitic morphology with apparent Maltese cross pattern, whereas SPCLs exhibit much lower crystallization rate and poor spherulitic morphology. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Crystallization behavior of biodegradable amphiphilic poly(ethylene glycol)‐poly(L‐lactide) block copolymers

Poly(ethylene glycol)‐poly(L ‐lactide) diblock and triblock copolymers were prepared by ring‐opening polymerization of L ‐lactide with poly(ethylene glycol) methyl ether or with poly(ethylene glycol) in the presence of stannous octoate. Molecular weight, thermal properties, and crystalline structure of block copolymers were analyzed by ¹H‐NMR, FTIR, GPC, DSC, and wide‐angle X‐ray diffraction (WAXD). The composition of the block copolymer was found to be comparable to those of the reactants. Each block of the PEG–PLLA copolymer was phase separated at room temperature, as determined by DSC and WAXD. For the asymmetric block copolymers, the crystallization of one block influenced much the crystalline structure of the other block that was chemically connected to it. Time‐resolved WAXD analyses also showed the crystallization of the PLLA block became retarded due to the presence of the PEG block. According to the biodegradability test using the activated sludge, PEG–PLLA block copolymer degraded much faster than PLLA homopolymers of the same molecular weight. © 1999 John Wiley amp; Sons, Inc. J Appl Polym Sci 72: 341–348, 1999     

Synthesis and characterization of ABA type tri‐block copolymers derived from p‐dioxanone,L‐lactide and poly(ethylene glycol)

A series of triblock co‐polymers, consisting of a poly(ethylene glycol) (PEG) central block joined to two blocks of random p‐dioxanone‐co‐L ‐lactide copolymers were synthesized by ring‐opening polymerization of p‐dioxanone (PDO) and L ‐lactide (LLA) initiated by PEG in the presence of stannous 2‐ethylhexanoate catalyst. The resulting copolymers were characterized by various techniques including ¹H and ¹³C NMR and FTIR spectroscopies, gel permeation chromatography, inherent viscosity, wide‐angle X‐ray diffractometry (WAXD) and differential scanning calorimetry (DSC). The conversion of PDO and L ‐lactide into the polymer was studied various mole ratios and at different polymerization temperature from ¹H NMR spectra. Results of WAXD and DSC showed that the crystallinity of PEG macroinitiator was greatly influenced by the composition of PDO and L ‐lactide in the copolymer. The triblock copolymers with low molecular weight were soluble in water at below room temperature. © 2003 Society of Chemical Industry     

Polyethylene‐block‐poly(ε‐caprolactone) diblock copolymers: synthesis and compatibility

A strategy is introduced for the synthesis of polyethylene‐block‐poly(ε‐caprolactone) block copolymers by a combination of coordination polymerization and ring‐opening polymerization. First, end‐hydroxylated polyethylene (PE‐OH) was prepared with a one‐step process through ethylene/3‐buten‐1‐ol copolymerization catalyzed by a vanadium(III) complex bearing a bidentate [N,O] ligand ([PhN?C(CH₃)CHC(Ph)O]VCl₂(THF)₂). The PE‐OH was then used as macroinitiator for ring‐opening polymerization of ε‐caprolactone, leading to the desired nonpolar/polar diblock copolymers. The block structure was confirmed by spectral analysis using ¹H NMR, gel permeation chromatography and differential scanning calorimetry. The unusual topologies of the model copolymers will establish a fundamental understanding for structure–property correlations, e.g. compatibilization, of polymer blends and surface and interface modification of other polymers. © 2014 Society of Chemical Industry     

Influence of semi‐crystalline poly(ε‐caprolactone) and non‐crystalline polylactide blocks on the thermal properties of polydimethylsiloxane‐based block copolymers

Poly(A)‐block‐poly(B), poly(A)‐block‐poly(B)‐block‐poly(A) and B(A)₂ block copolymers were prepared through coordinated anionic ring‐opening polymerization of ε‐caprolactone (CL) and lactic acid (LA) using hydroxy‐terminated polydimethylsiloxane (PDMS) as initiator. A wide range of well‐defined combinations of PDMS‐block‐PCL and PDMS‐block‐PLA diblock copolymers, PCL‐block‐PDMS‐block‐PCL and PLA‐block‐PDMS‐block‐PLA triblock copolymers and star‐PDMS(PCL)₂ copolymers were thus obtained. The number‐average molar masses and the structure of the synthesized block copolymers were identified using various analytical techniques. The thermal properties of these copolymers were established using differential scanning calorimetry. Considering PDMS‐block‐PCL copolymers, the results demonstrate the complex effect of polymer architecture and PCL block length on the ability of the PDMS block to crystallize or not. In the case of diblock copolymers, crystallization of PCL blocks originated from stacking of adjacent chains inducing the extension of the PDMS block that can easily crystallize. In the case of star copolymers, the same tendency as in triblock copolymers is observed, showing a limited crystallization of PDMS when the length of the PCL block increases. In the case of PDMS‐block‐PLA copolymers, melting and crystallization transitions of the PLA block are never observed. Considering the diblock copolymers, PDMS sequences have the ability to crystallize. © 2019 Society of Chemical Industry     

AB‐ and ABC‐type di‐ and triblock copolymers of poly[styrene‐block‐(ε‐caprolactone)] and poly[styrene‐block‐(ε‐caprolactone)‐block‐lactide]: synthesis,characterization and thermal studies

Polystyrene terminated with benzyl alcohol units was employed as a macroinitiator for ring‐opening polymerization of ε‐caprolactone and L ‐lactide to yield AB‐ and ABC‐type block copolymers. Even though there are many reports on the diblock copolymers of poly(styrene‐block‐lactide) and poly(styrene‐block‐lactone), this is the first report on the poly(styrene‐block‐lactone‐block‐lactide) triblock copolymer consisting of two semicrystalline and degradable segments. The triblock copolymers exhibited twin melting behavior in differential scanning calorimetry (DSC) analysis with thermal transitions corresponding to each of the lactone and lactide blocks. The block derived from ε‐caprolactone also showed crystallization transitions upon cooling from the melt. In the DSC analysis, one of the triblock copolymers showed an exothermic transition well above the melting temperature upon cooling. Thermogravimetric analysis of these block copolymers showed a two‐step degradation curve for the diblock copolymer and a three‐step degradation for the triblock copolymer with each of the degradation steps associated with each segment of the block copolymers. The present study shows that it is possible to make pure triblock copolymers with two semicrystalline segments which also consist of degradable blocks. Copyright © 2009 Society of Chemical Industry     

Part 7. Effects of poly(L‐lactide‐co‐ϵ‐caprolactone) on morphology,structure, crystallization,and physical properties of blends of poly(L‐lactide) and poly(ϵ‐caprolactone)

Blended films of poly(L ‐lactide) [ie poly(L ‐lactic acid)] (PLLA) and poly(?‐caprolactone) (PCL) without or mixed with 10 wt% poly(L ‐lactide‐co‐?‐caprolactone) (PLLA‐CL) were prepared by solution‐casting. The effects of PLLA‐CL on the morphology, phase structure, crystallization, and mechanical properties of films have been investigated using polarization optical microscopy, scanning electron microscopy, differential scanning calorimetry and tensile testing. Addition of PLLA‐CL decreased number densities of spherulites in PLLA and PCL films, and improved the observability of spherulites and the smoothness of cross‐section of the PLLA/PCL blend film. The melting temperatures (T_m) of PLLA and PCL in the films remained unchanged upon addition of PLLA‐CL, while the crystallinities of PLLA and PCL increased at PLLA contents [X_PLLA = weight of PLLA/(weight of PLLA and PCL)] of 0.4–0.7 and at most of the X_PLLA values, respectively. The addition of PLLA‐CL improved the tensile strength and the Young modulus of the films at X_PLLA of 0.5–0.8 and of 0–0.1 and 0.5–0.8, respectively, and the elongation at break of the films at all the X_PLLA values. These findings strongly suggest that PLLA‐CL was miscible with PLLA and PCL, and that the dissolved PLLA‐CL in PLLA‐rich and PCL‐rich phases increased the compatibility between these two phases. © 2003 Society of Chemical Industry     

Synthesis and characterization of poly(ϵ‐caprolactone)‐b‐poly(ethylene glycol) block copolymers prepared by a salicylaldimine‐aluminum complex

A series of poly(?‐caprolactone)‐b‐poly(ethylene glycol) (PCL‐b‐PEG) block copolymers with different molecular weights were synthesized with a salicylaldimine‐aluminum complex in the presence of monomethoxy poly(ethylene glycol). The block copolymers were characterized by ¹H NMR, GPC, WAXD, and DSC. The ¹H NMR and GPC results verify the block structure and narrow molecular weight distribution of the block copolymers. WAXD and DSC results show that crystallization behavior of the block copolymers varies with the composition. When the PCL block is extremely short, only the PEG block is crystallizable. With further increase in the length of the PCL block, both blocks can crystallize. The PCL crystallizes prior to the PEG block and has a stronger suppression effect on crystallization of the PEG block, while the PEG block only exerts a relatively weak adverse effect on crystallization of the PCL block. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Comparison of micelles formed by amphiphilic poly(ethylene glycol)‐b‐poly(trimethylene carbonate) star block copolymers

In this article, we describe the synthesis and solution properties of PEG‐b‐PTMC star block copolymers via ring‐opening polymerization (ROP) of trimethylene carbonate (TMC) monomer initiated at the hydroxyl end group of the core PEG using HCl Et₂O as a monomer activator. The ROP of TMC was performed to synthesize PEG‐b‐PTMC star block copolymers with one, two, four, and eight arms. The PEG‐b‐PTMC star block copolymers with same ratio of between hydrophobic PTMC and hydrophilic PEG segments were obtained in quantitative yield and exhibited monomodal GPC curves. The amphiphilic PEG‐b‐PTMC star block copolymers formed spherical micelles with a core–shell structure in an aqueous phase. The mean hydrodynamic diameters of the micelles increased from 17 to 194 nm with increasing arm number. As arm number increased, the critical micelle concentration (CMC) of the PEG‐b‐PTMC star block copolymers increased from 3.1 × 10^?3 to 21.1 × 10^?3 mg/mL but the partition equilibrium constant, which is an indicator of the hydrophobicity of the micelles of the PEG‐b‐PTMC star block copolymers in aqueous media, decreased from 4.44 × 10⁴ to 1.34 × 10⁴. In conclusion, we confirmed that the PEG‐b‐PTMC star block copolymers form micelles and, hence, may be potential hydrophobic drug delivery vehicles. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Preparation of drug‐loaded microspheres of linear and star‐shaped poly(D,L‐lactide)s and their drug release behaviors

Linear (1‐arm) and star‐shaped (4‐, 6‐, and 16‐arm) poly(D,L ‐lactide)s (PDLLs) were synthesized by ring‐opening polymerization in bulk of D,L ‐lactide monomer. Hydroxyl end‐group compounds and stannous octoate were used as the initiator and catalyst, respectively. The intrinsic viscosity and glass transition temperature (T_g) of the PDLLs decreased steadily as the branch arm number increased for similar molecular weights. However, the intrinsic viscosity and T_g values of the linear PDLL were less than the star‐shaped PDLL for similar each PDLL arm lengths. Ibuprofen, a poorly water soluble model drug was entrapped in the PDLL microspheres. All drug‐loaded PDLL microspheres were prepared by the oil‐in‐water emulsion solvent evaporation method, were spherical in shape, and had a smooth surface with fine dispersibility. In vitro drug release behaviors indicated that the drug release from the microspheres with higher branch arm number was faster than from those with lower branch arm number. Moreover, the drug release from the star‐shaped PDLL microspheres was slower than that of the linear PDLL microspheres for similar PDLL arm lengths. The drug release behavior could be adjusted through both the branch arm number and arm length of PDLL. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Synthesis and characterization of poly(ε‐caprolactone)‐b‐poly(ethylene glycol)‐b‐poly(ε‐caprolactone) triblock copolymers with dibutylmagnesium as catalyst

Two series of poly(ε‐caprolactone)‐b‐poly(ethylene glycol)‐b‐poly(ε‐caprolactone) triblock copolymers were prepared by the ring opening polymerization of ε‐caprolactone in the presence of poly(ethylene glycol) and dibutylmagnesium in 1,4‐dioxane solution at 70°C. The triblock structure and molecular weight of the copolymers were analyzed and confirmed by ¹H NMR, ¹³C NMR, FTIR, and gel permeation chromatography. The crystallization and thermal properties of the copolymers were investigated by wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry (DSC). The results illustrated that the crystallization and melting behaviors of the copolymers were depended on the copolymer composition and the relative length of each block in copolymers. Crystallization exothermal peaks (T_c) and melting endothermic peaks (T_m) of PEG block were significantly influenced by the relative length of PCL blocks, due to the hindrance of the lateral PCL blocks. With increasing of the length of PCL blocks, the diffraction and the melting peak of PEG block disappeared gradually in the WAXD patterns and DSC curves, respectively. In contrast, the crystallization of PCL blocks was not suppressed by the middle PEG block. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Multicarboxylic aromatic acid core initiator for the synthesis of star‐shaped poly(ϵ‐caprolactone) with carboxyl end groups

We successfully carried out the ring‐opening polymerization of ?‐caprolactone with 1,3,5‐benzenetricarboxylic acid and 1,2,4,5‐benzenetetracarboxylic acid as the core initiators at 225°C in bulk, and three‐armed and four‐armed star poly(?‐caprolactone)s [poly(?‐CL)s] with carboxyl end groups were obtained. No transesterification, which would have led to a decrease in the molecular weight of poly(?‐CL), was found. The effects of the polymerization conditions on the polymerization are discussed; the poly(?‐CL)s were characterized by ¹H‐NMR, gel permeation chromatography, and thermogravimetric analysis in detail. A mechanism of alkyl–oxygen bond scission by the nucleophilic attack of the carboxyl anions via hydrogen proton transfer is presented for this system. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 3713–3717, 2006     

Preparation and dispersibility of poly(L‐lactide)‐grafted silica nanoparticle

To improve dispersibility of silica nanoparticle in organic solvents, the grafting of poly(L ‐lactide) (PLLA) onto silica nanoparticle surface by ring‐opening polymerization of L‐lactide (LA) was investigated in the presence of an amidine base catalyst. The ring‐opening polymerization of LA successfully initiated in the presence of silica having amino groups (silica‐NH₂) and an amidine base catalyst to give PLLA‐grafted silica, but not in the presence of untreated silica (silica‐OH). In the absence of the amidine base catalyst no ring‐opening polymerization of LA even in the presence of silica‐NH₂ and no grafting of PLLA onto silica were observed. It became apparent that the amidine base catalyst acts as an effective catalyst for the ring‐opening graft polymerization of LA from the surface of silica‐NH₂. In addition, it was found that the percentage of PLLA grafting onto silica could be controlled according to the reaction conditions. The average particle size of PLLA‐grafted silica was smaller than that of silica‐NH₂. Therefore, it was considered that the aggregation structure of silica nanoparticles was considerably destroyed by grafting of PLLA onto the surface. The PLLA‐grafted silica gave a stable dispersion in polar solvents, which are good solvents for PLLA. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Electrospun poly(L‐lactide)/poly(ε‐caprolactone) blend fibers and their cellular response to adipose‐derived stem cells

Polymer blending is one of the most effective methods for providing new, desirable biocomposites for tissue‐engineering applications. In this study, electrospun poly(L ‐lactide)/poly(ε‐caprolactone) (PLLA/PCL) blend fibrous membranes with defect‐free morphology and uniform diameter were optimally prepared by a 1 : 1 ratio of PLLA/PCL blend under a solution concentration of 10 wt %, an applied voltage of 20 kV, and a tip‐to‐collector distance of 15 cm. The fibrous membranes also showed a porous structure and high ductility. Because of the rapid solidification of polymer solution during electrospinning, the crystallinity of electrospun PLLA/PCL blend fibers was much lower than that of the PLLA/PCL blend cast film. To obtain an initial understanding of biocompatibility, adipose‐derived stem cells (ADSCs) were used as seed cells to assess the cellular response, including morphology, proliferation, viability, attachment, and multilineage differentiation on the PLLA/PCL blend fibrous scaffold. Because of the good biocompatibility and nontoxic effect on ADSCs, the PLLA/PCL blend electrospun fibrous membrane provided a high‐performance scaffold for feasible application in tissue engineering using ADSCs. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Biodegradable poly(L‐lactide) and polycaprolactone block copolymer networks

New biodegradable block copolymer networks were synthesized from methacrylate‐terminated poly(L ‐lactide) (mLA) and polycaprolactone (mCL) macromers. This allowed the realization of a series of materials in which the macromer ratio can be used to tailor the physical and mechanical properties of the materials. The synthesis of the macromers was characterized using Fourier transform infrared (FTIR) spectroscopy and ¹H NMR spectroscopy. Poly(mCL) and poly(mLA) networks were prepared by photopolymerization of the macromers, and copolymers were also prepared from the two macromers in various proportions. The phase microstructure of the new systems and the network architecture were investigated using differential scanning calorimetry, FTIR spectroscopy, dynamic mechanical analysis and thermogravimetry studies. Copyright © 2010 Society of Chemical Industry     

Confined crystallization morphology of poly(ϵ‐caprolactone) block within poly(ϵ‐caprolactone)–poly(l‐lactide) copolymers

The confined crystallization of poly(?‐caprolactone) (PCL) block in poly(?‐caprolactone)–poly(l ‐lactide) (PCL‐PLLA) copolymers was investigated using differential scanning calorimetry, polarized optical microscopy, scanning electronic microscopy and atomic force microscopy. To study the effect of crystallization and molecular chain motion state of PLLA blocks in PCL‐PLLA copolymers on PCL crystallization morphology, high‐temperature annealing (180 °C) and low‐temperature annealing (80 °C) were applied to treat the samples. It was found that the crystallization morphology of PCL block in PCL‐PLLA copolymers is not only related to the ratio of block components, but also related to the thermal history. After annealing PCL‐PLLA copolymers at 180 °C, the molten PCL blocks are rejected from the front of PLLA crystal growth into the amorphous regions, which will lead to PCL and PLLA blocks exhibiting obvious fractionated crystallization and forming various morphologies depending on the length of PLLA segment. On the contrary, PCL blocks more easily form banded spherulites after PCL‐PLLA copolymers are annealed at 80 °C because the preexisting PLLA crystal template and the dangling amorphous PLLA chains on PCL segments more easily cause unequal stresses at opposite fold surfaces of PCL lamellae during the growth process. Also, it was found that the growth rate of banded spherulites is less than that of classical spherulites and the growth rate of banded spherulites decreases with decreasing band spacing. © 2019 Society of Chemical Industry     

Synthesis of star‐shaped poly(ϵ‐caprolactone) by samarium‐based tetrafunctional initiator and its dilute‐solution properties

An in situ–generated tetrafunctional samarium enolate from the reduction of 1,1,1,1‐tetra(2‐bromoisobutyryloxymethyl)methane with divalent samarium complexes [Sm(PPh₂)₂ and SmI₂] in tetrahydrofuran has proven to initiate the ring‐opening polymerization of ?‐caprolactone (CL) giving star‐shaped aliphatic polyesters. The polymerization proceeded with quantitative conversions at room temperature in 2 h and exhibited good controllability of the molecular weight of polymer. The resulting four‐armed poly(?‐caprolactone) (PCL) was fractionated, and the dilute‐solution properties of the fractions were studied in tetrahydrofuran and toluene at 30°C. The Mark–Houwink relations for these solvents were [η] = 2.73 × 10^?2M_w^0.74 and [η] = 1.97 × 10^?2M_w^0.75, respectively. In addition, the unperturbed dimensions of the star‐shaped PCL systems were also evaluated, and a significant solvent effect was observed. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 175–182, 2006     

Synthesis,characterization and biocompatibility of novel biodegradable poly[((R)‐3‐hydroxybutyrate)‐block‐(D,L‐lactide)‐block‐(ε‐caprolactone)] triblock copolymers

BACKGROUND: Biodegradable block copolymers have attracted particular attention in both fundamental and applied research because of their unique chain architecture, biodegradability and biocompatibility. Hence, biodegradable poly[((R )‐3 ‐hydroxybutyrate)‐block‐(D ,L ‐lactide)‐block‐(ε‐caprolactone)] (PHB‐PLA‐PCL) triblock copolymers were synthesized, characterized and evaluated for their biocompatibility. RESULTS: The results from nuclear magnetic resonance spectroscopy, gel permeation chromatography and thermogravimetric analysis showed that the novel triblock copolymers were successfully synthesized. Differential scanning calorimetry and wide‐angle X‐ray diffraction showed that the crystallinity of PHB in the copolymers decreased compared with methyl‐PHB (LMPHB) oligomer precursor. Blood compatibility experiments showed that the blood coagulation time became longer accompanied by a reduced number of platelets adhering to films of the copolymers with decreasing PHB content in the triblocks. Murine osteoblast MC3T3‐E1 cells cultured on the triblock copolymer films spread and proliferated significantly better compared with their growth on homopolymers of PHB, PLA and PCL, respectively. CONCLUSION: For the first time, PHB‐PLA‐PCL triblock copolymers were synthesized using low molecular weight LMPHB oligomer as the macroinitiator through ring‐opening polymerization with D ,L ‐lactide and ε‐caprolactone. The triblock copolymers exhibited flexible properties with good biocompatibility; they could be developed into promising biomedical materials for in vivo applications. Copyright © 2008 Society of Chemical Industry