MgO(111)衬底MgB2 超薄膜的制备和性质研究

利用混合物理化学气相沉积法(HPCVD)在MgO(111)衬底上制备了干净的MgB₂超导超薄膜. 在背景气体压强, 载气氢气流量以及沉积时间一定的情况下, 改变B₂H₆的流量, 制备得到不同厚度系列的MgB₂超导薄膜样品, 并测量了其超导转变温度 T_c, 临界电流密度J_c等临界参量. 该系列超导薄膜沿c轴外延生长, 表面具有良好的连接性, 且有很高的超导转变温度T_c(0) ≈ 35-38 K和很小的剩余电阻率ρ(42 K) ≈ 1.8-20.3 μΩ·cm^-1. 随着膜厚的减小而减小, 临界温度变低, 而剩余电阻率变大. 其中20 nm的样品在零磁场, 5K时的临界电流密度J_c ≈ 2.3×10⁷ A/cm². 表明了利用HPCVD在MgO(111)衬底上制备的MgB₂超薄膜有很好的性能, 预示了其在超导电子器件中广阔的应用前景. 关键词： MgO(111)衬底 2超薄膜')" href="#">MgB₂超薄膜 混合物理化学气相沉积     

Mg/B多层膜退火法中不同制备条件对MgB2超导薄膜性质的影响

用Mg/B多层膜退火的方法制备了一系列MgB₂超导薄膜,研究了退火温度、退火时间和薄膜厚度对于MgB₂薄膜性质的影响.厚度为250 nm的Mg/B多层膜经400 ℃低温退火后已经生成超导相,此厚度薄膜750 ℃下退火20—30 min实现最佳超导转变温度（T_c）.前驱膜分层厚度相同时,随着薄膜厚度减小MgB₂薄膜T_c明显降低,而且较薄的膜T_{c关键词： 2}超导薄膜')" href="#">MgB₂超导薄膜 电子束蒸发 超导成相     

MgB2 超薄膜的制备和性质研究

利用混合物理化学气相沉积法在6H-SiC(001)衬底上制备干净的MgB₂超导超薄膜.在本底气体压强、载气氢气流量等条件一定的情况下,改变B₂H₆流量及沉积时间,制备得到不同厚度的系列MgB₂超薄膜样品,并研究了超导转变温度T_c、剩余电阻率ρ_(42K)、上临界磁场H_c2等与膜厚的关系.该系列超薄膜沿c轴外延生长,随膜厚度的变小,T_c(0)降低,ρ_(42K)升高.膜在衬底上的生长遵循Volmer-Weber岛状生长模式.对于厚度为7.5 nm的MgB₂超薄膜,T_c(0) =32.8 K,ρ_(42K) =118 μΩcm,是迄今为止所观测到的厚度为7.5 nm的MgB₂超薄膜最高的T_c值;对于厚度为10 nm的MgB₂膜,T_c(0)=35.5 K,ρ_(42K)=17.7 μΩcm,上临界磁场μ₀H_c2估算为12 T左右,零磁场、4 K时的临界电流密度J_c=1.0×10⁷ A/cm²,是迄今为止10 nm厚MgB₂超薄膜的最高J_c值,且其表面连接性良好,均方根粗糙度为0.731 nm.这预示MgB₂超薄膜在超导纳米器件上具有广阔的应用前景. 关键词： 2超薄膜')" href="#">MgB₂超薄膜 薄膜生长 氢气流量 混合物理化学气相沉积     

柠檬酸掺杂的MgB2超导体钉扎机理的研究

本文研究了柠檬酸掺杂的MgB₂超导材料的J_c-B行为及其钉扎机理.在纯MgB₂多晶样品中,δT_c钉扎起主要作用,而在掺杂的样品中,则是δl钉扎和δT_c钉扎共同作用,并且δl钉扎机理占主要作用,其贡献比重随着掺杂量的增加而增加.从J_c-B行为和钉扎行为的分析都可以得到 关键词： 柠檬酸 2')" href="#">MgB₂ T_c钉扎')" href="#">δT_c钉扎 l钉扎')" href="#">δl钉扎     

YBCO/聚丙烯腈杂化膜及其超导性研究

报告了一种简单制备不依赖于基底结构的柔性YBCO/聚丙烯腈（PAN）厚膜的新方法.研究结果发现,PAN含量从0增加到10wt%的过程中,全部YBCO/PAN样品的超导临界温度T_c在900—920 K区间,表现出较好的超导电性.而且当PAN含量为10wt%时,YBCO/PAN杂化膜即具有一定柔性,膜厚约35 μm,临界电流密度Jc=29×10⁴Acm^-2(1 T, 10 K)和J< 关键词： 超导电性 YBCO 聚丙烯腈（PAN） 杂化膜     

利用电泳法在金属基底上制备MgB2超导厚膜

利用电泳技术在高熔点金属基底Ta，Mo和W上制备MgB₂超导厚膜.厚膜中的MgB2晶粒结合紧密，粒度小于1μm，呈随机取向生长.电阻测量表明沉积在Ta，Mo，W上的MgB₂厚膜的超导起始转变温度分别为36.5K，34.8K，33.4K，对应的转变宽度为0.3K，1.5K和2.0K.三种基底上制备的MgB₂厚膜的临界电流密度在不同温度下随外磁场的变化情况 基本相同，MgB₂/Mo厚膜的临界电流密 关键词： 2超导厚膜')" href="#">MgB₂超导厚膜 电泳 金属基底     

关于MgB2/Al2O3超导薄膜电阻转变和各向异性的研究

利用电子束蒸发方法将MgB₂超导薄膜沉积到Al₂O₃(001)衬底上.采用标准的四引线法研究了磁场平行和垂直超导薄膜ab平面下的电阻转变.一个激活能模型 U(T,H)=U₀(1-T/(T_c+δ))ⁿ(1-H/H 关键词： 2/Al₂O₃')" href="#">MgB₂/Al₂O₃ 超导体 电阻转变 各向异性     

插入二氧化铈薄膜提高MOD-YBa2Cu3O7-x厚膜超导性能的研究

YBa₂Cu₃O_7-x(YBCO)膜存在“厚度效应”: 随着厚度增加, YBCO薄膜的临界电流密度下降, 尤其是YBCO薄膜的厚度超过1 μm时, 它的临界电流密度急剧下降. 本文在YBCO薄膜之间引入极薄的二氧化铈(CeO₂)薄膜, 成功制备出结构为YBCO/YBCO/CeO₂/YBCO的超导厚膜. 所制备的厚度为2 μm的YBCO膜临界电流密度为1.36 MA/cm² (77 K, 自场), 其性能比相同厚度的纯YBCO膜有了较大幅度的提升. 研究表明CeO₂薄膜起到了传递织构、松弛应力的作用.     

混合物理化学气相沉积法制备MgB$lt;sub$gt;2$lt;/sub$gt;单晶纳米晶片的研究

利用混合物理化学气相沉积法在石墨衬底上制备出了晶形为六角结构、厚度不同、径向尺寸不一的MgB₂单晶纳米晶片. 利用纳米定向转移技术将此晶片转移到了碳支持膜铜网上, 以便对其精细结构等物性进行表征. 电输运测量和磁性测量结果都表明晶片具有超导电性: T_conset=38 K, T_c(0)=33 K. 扫描电子显微镜图像表明, 晶片表面平整、厚度分布在几个纳米到200 nm之间, 宽度从几微米到上百微米; 高分辨透射电镜图像显示出晶片具有周期性晶格条纹. 选区电子衍射数据与MgB₂已有的单晶衍射数据相符. 这些测量结果证实了其确为高质量单晶MgB₂超导纳米晶片. 本文不仅提出了一种全新的制备单晶MgB₂的方法, 也观察到了纳米尺度MgB₂单晶的零电阻现象, 为后续的磁通钉扎、纳米力学性能等领域的深入研究提供了合适的素材. 关键词： 2')" href="#">单晶MgB₂ 超导纳米晶片 零电阻 混合物理化学气相沉积法     

不同厚度的MgB_2超薄膜的制备和性质研究

本文报导了利用混合物理化学气相沉积法(Hybrid physical-chemical vapor deposition,HPCVD)在SiC(0001)衬底上制备干净的MgB2超薄膜.在背景气体压强、载气H2流量等条件一定的情况下,改变B2H6流量及沉积时间,制备不同厚度的MgB2超薄膜样品,并研究了超导转变温度Tc、剩余电阻率ρ(42K)、上临界场Hc2等与膜厚的关系.这系列超薄膜生长沿c轴外延,随膜厚度的变小Tc(0)降低,ρ(42K)升高.膜在衬底上的生长遵循Volmer-Weber岛状生长模式.对于10nm厚的膜,Tc(0)~32.4K,ρ(42K)~124.92μΩ·cm,其表面连接性良好,平均粗糙度为2.72nm,上临界磁场Hc2(0K)~12T,零场4K时的临界电流密度Jc~107A/cm2,为迄今为止所观测到的10nm厚MgB2超薄膜的最高Jc值,这也证明了10nm厚的MgB2膜在超导纳米器件上具有很强的应用潜力.     

High critical current density YBa2Cu3O7−δ tapes prepared by the surface-oxidation epitaxy method

YBa₂Cu₃O_7−δ (YBCO) films with high critical current density (J_c) were successfully fabricated on nickel tapes buffered with epitaxial NiO. NiO was prepared on the textured nickel tape by the surface-oxidation epitaxy (SOE) method. We have reported so far a critical temperature (T_c) of 87 K and J_c=4–6×10⁴ A/cm² (77 K, 0 T) for the YBCO films on NiO/Ni tapes. To enhance the superconducting properties of the YBCO films on the SOE-grown NiO, depositions of thin oxide cap layers such as YSZ, CeO₂, and MgO on NiO were investigated. These oxide cap layers were epitaxially grown on NiO and provided the template for the epitaxial growth of YBCO films. Substantially improved data of T_c=88 K and J_c=3×10⁵ A/cm² (77 K, 0 T) and 1×10⁴ A/cm² (77 K, Hc, 4 T) were obtained for YBCO film on NiO, by using a MgO cap layer with a thickness of 50 nm. The method described in this paper is a simple way to produce long YBCO tape conductors with high-J_c values.     

Laser ablated bismuth cuprate thin films preparation and effect of oxygen nonstoichiometry upon superconductivity

Thin films of Bi₂Sr₂CaCu₂O₈ and (Bi, Pb)₂Sr₂Ca₂Cu₃O₁₀ have been prepared on monocrystalline (100) MgO substrates, using a laser ablation method with post annealing treatment. The influence of substrate temperature and oxygen pressure during deposition were investigated. SEM observations, EDS analysis, electric and magnetic measurements have been used to characterize the films. Superconducting “2212” films, with T_c(R = 0) at 80–83 K and J_c (50 K) up to 5 × 10⁵ A/cm², have been currently achieved, while Pb-doped “2223” films exhibit T_c as high as 110 K with J_c = 5 × 10⁴ A/cm² at 77 K. The effect of annealing at low temperature (350°C) in an argon flow has been studied for the 2212 phase, it shows the influence of the oxygen non-stoichiometry, i.e. of the hole carrier density upon T_c's which can be measured up to 89 K (zero resistance).     

Synthesis of YBa2Cu3O7−x superconducting thin films on LaAlO3 by means of PAMOCVD

High-T_c superconducting thin films have been deposited in situ by means of a plasma assisted metal-organic chemical vapour deposition (PAMOCVD) process on LaAlO₃. An EMCORE high-speed rotating disc reactor was used to deposit the films at a substrate temperature of 600°C to 800°C. The system is equipped with a (remote) 120 W microwave plasma generator. The oxidising plasma gas is N₂O and/or O₂ while Ar was used as the inert carrier gas for the different metal-organics. The influence of different process parameters (such as the temperatures of the metal-organics, substrate temperature, and plasma gas composition) on the superconductive properties and on the morphology of the films was investigated. Surface morphology and composition were studied by SEM/EDX or EPMA, and AC susceptibility measurements were used to investigate the superconductive properties (T_c and J_c). X-ray diffraction measurements indicated that single-phase YBa₂Cu₃O_7−x films were epitaxially grown with the 00l orientation perpendicular to the substrate surface. The critical temperature (T_c) of the films is about 90 K and the critical current density (J_c) is higher than 10⁶ A/cm² at 77 K and zero field.     

Substrate dependent growth studies of MgB2 films by electrocrystallization

The comparative study of MgB₂ film growth on Al₂O₃ and glass substrate by electrocrystallization technique is discussed. The precursor magnesium films were deposited by vacuum evaporation method. These magnesium films were then used as electrode for the growth of MgB₂ films by electrocrystallization. The structural, morphological and superconducting properties of the electrocrystallized MgB₂ films on Al₂O₃ substrate were examined by using XRD, SEM and electrical resistivity measurement techniques and compared with that of MgB₂ films grown on glass substrate. The films deposited on Al₂O₃ substrates showed enhanced crystallinity and relatively higher T_c value compared to films deposited on glass substrates.     

Induction of superconductivity in pulsed laser ablated La2CuO4 thin films by post-deposition fluorination

Pulsed laser ablation has been used to fabricate La₂CuO₄ thin films. Superconducting properties have been successfully induced in the films by an ex-situ, post-ablation annealing process in F₂ gas resulting in a T_c (onset) of 36 K. The presence of two slightly different c-axis expanded phases in the X-ray diffraction data of the fluorinated films implies a degree of inhomogeneity in F₂ uptake. Critical current densities (J_c) and the irreversibility line have been established from hysteresis cycles. A J_c of 10⁶ A cm⁻² for a typical film was observed at 10 K in zero field.     

MgB2超导薄膜的变温拉曼光谱研究

MgB₂作为迄今为止超导转变温度最高的合金超导体,由于其具有结构简单、相干长度长、晶界间不存在弱连接、上临界场很高、电-声散射时间短等特点,MgB₂超导薄膜在电子学领域有着广阔的的应用前景。拉曼光谱是研究电-声子相互作用和超导能带的一种有效方法,且已广泛用于分析MgB₂材料的电子、声子特征以及超导体能带结构,研究表明,样品质量、晶粒尺寸以及测试条件对MgB₂拉曼峰的峰位和峰形影响很大,其中拉曼光谱随温度的变化也是一个研究重点,但目前关于MgB₂变温拉曼光谱的研究,测试的温度范围相对较小,局限在83 K到室温区域或是转变温度附近。研究了大范围温度区间内MgB₂薄膜的拉曼光谱变化,采用混合物理化学沉积法在(0001)SiC衬底上制备了MgB₂多晶薄膜,薄膜的晶粒尺寸约为300 nm,超导转变温度为39.3 K,对其在10～293 K之间的拉曼光谱进行了测试,测量的波数范围为20～1 200 cm-1。变温拉曼光谱的测试结果显示,在高频620 cm-1附近以及低频80和110 cm-1附近存在MgB₂的拉曼峰。经分析,低频区域出现的两个拉曼峰的频率与超导能隙宽度相对应,表明MgB₂的双能隙特性。考虑到MgB₂中四种声子模式的拉曼活性,高频620 cm-1附近的拉曼峰应是由E_2g振动模所贡献的,且随着测试温度的降低,该拉曼峰的峰位未发生明显的偏移,但半高宽显著变小,从293 K时的380.7 cm-1减小到10 K时的155 .7 cm-1,分析表明E_2g声子与电子系统的非线性耦合所引起的非简谐效应可能是拉曼峰半高宽线性变小的主要原因。     

Magnetic and transport properties of YBa2Cu3Oy superconductor foams

The recently reported superconducting YBa₂Cu₃O_y (Y123) foams are highly interesting and promising for variety of applications. In this report we present first magneto-transport measurements of the superconducting properties of these foams. The investigations reveal the superconducting properties being similar to those of bulk melt processed materials. The 123 foams reveal a T_c of 92 K and have a magnetization J_c of 40,000 A/cm² at 77 K and 0 T. The measurements of magnetic hysteresis versus field show a high anisotropy of the critical current density up to J_c^ab/J_c^c7.     

硼膜制备工艺、微观结构及其在硼化镁超导约瑟夫森结中的应用

MgB_2材料具备临界转变温度较高、相干长度大、临界电流和临界磁场高等优点,被认为有替代Nb基超导材料的潜力.研究了不同温度下以化学气相沉积法制备的硼(B)薄膜的微观结构.实验结果表明:较低温度沉积的B先驱薄膜为无定形B膜,可以与Mg蒸气反应生成MgB_2超导薄膜;当沉积温度高于550?C时,所得硼薄膜为晶型薄膜;以晶型硼薄膜为先驱膜在镁蒸气中退火,不能生成硼化镁超导薄膜.利用晶型B膜的这一特点,成功制备了以晶型硼薄膜为介质层的硼化镁超导约瑟夫森结.