Phase Relations and Stability Studies in the Si3N4-SiO2-Y2O3 Pseudoternary System

Composite powders were hot-pressed to determine the phase relations in the Si₃N₄-SiO₂-Y₂O₃ pseudoternary system. Four quaternary compounds, Si₃Y₂O₃N₄, YSiO₂N, Y₁₀Si₇O₂₃N₄, and Y₄Si₂O₇N₂, were identified. Studies of polyphase and single-phase materials in this system showed that these 4 compounds are unstable under oxidizing conditions. Materials within the Si₃N₄-Si₂N₂O-Y₂Si₂O₇ compatibility triangle precluded the unstable compounds, and are extremely resistant to oxidation.     

Sintering of Si3N4-Y2O3-Al2O3

Sintering kinetics of the system Si₃N4-Y2O₃-Al₂O3 were determined from measurements of the linear shrinkage of pressed disks sintered isothermally at 1500° to 1700°C. Amorphous and crystalline Si₃N₄ were studied with additions of 4 to 17 wt% Y₂O₃ and 4 wt% A1₂O₃. Sintering occurs by a liquid-phase mechanism in which the kinetics exhibit the three stages predicted by Kingery's model. However, the rates during the second stage of the process are higher for all compositions than predicted by the model. X-ray data show the presence of several transient phases which, with sufficient heating, disappear leaving mixtures of β ' -Si₃N₄ and glass or β '-Si₃N₄, α '-Si₃N₄, and glass. The compositions and amounts of the residual glassy phases are estimated.     

Sintering of Si3N4-Y2O3 Under Nitrogen Pressure

This study shows that the amount ofAl₂O₃ needed to form high density Si₃N₄-15Y₂-O₃ samples can be reduced by using high surface area Si₃N₄ powder and high N₂ overpressure (high sintering temperatures) during the sintering process. The reduction in AI₂O₃ content results in improved oxidation resistance of the sintered samples.     

Phase Equilibria in the System Si3N4-SiO2-BeO-Be3N2

The 1780°C isothermal section of the reciprocal quasiternary system Si₃N₄-SiO₂-BeO-Be₃N₂ was investigated by the X-ray analysis of hot-pressed samples. The equilibrium relations shown involve previously known compounds and 8 newly found compounds: Be₆Si³N₈, Be₁₁Si₅N₁₄, Be₅Si²N₆, Be₉Si₃N₁₀, Be₈SiO₄N₄, Be₆O₃N₂, Be₈O₅N₂, and Be₉O₆N₂. Large solid solubility occurs in β-Si₃N₄, BeSiN₂, Be₉Si₃N₁₀, Be₄SiN₄, and β-Be₃N₂. Solid solubility in β-Si₃N₄ extends toward Be₂SiO₄ and decreases with increasing temperature from 19 mol% at 1770°C to 11.5 mol% Be₂SiO₄ at 1880°C. A 4-phase isotherm, liquid +β-Si₃N₄ ( ss )Si₂ON₂+ BeO, exists at 1770°C.     

Oxidation of Si3N4 Alloys: Relation to Phase Equilibria in the System Si3N4-SiO2-MgO

The oxidation resistance at 1400°C of silicon nitride alloys hot-pressed with magnesia was investigated as a function of the phase content of the alloys. The extent of oxidation, the products of oxidation, their stratification, and the continuity of the oxide scale are all dependent on the initial composition. Also, the compositions of the alloys themselves change during oxidation. The findings can be interpreted on the basis of compositional paths in the equivalence phase diagram. Reasons for the outward diffusion of Mg and impurities are given and the effect of the secondary phase on oxidation kinetics is discussed.     

Densification of Si3N4-Y2O3/Al2O3 by a Dual N2 Pressure Process

Sintering studies of Si₃N4-Y₂O3/Al₂O₃ compositions indicated that increased densification could be produced using a dual N₂ pressure process. RT modulus of rupture values and microstructures were found to be similar to hot-pressed material. The technique should be adaptable to complex shaped Si₃N₄ bodies where high density and strength are required .     

Characteristics of Si3N4-SiO2-Ce2O3 Compositions Sintered in High-pressure Nitrogen

Full-density Si₃N₄-SiO₂-Ce₂O₃ compositions were prepared by sintering with 2.5 MPa nitrogen pressure at temperatures of 1900° and 2090°C. Room-temperature flexural strengths near 700 MPa for sintered material compared favorably with the strength of hot-pressed material. At 1370°C, where flexural strengths as high as 363 MPa were obtained, it was observed that the coarsest structure was the strongest and the finest structure was the weakest. One of the compositions tested, Si₃N₄-8.7 wt% SiO₂-8.3 wt%-Ce₂O₃, was found to have excellent 200-h oxidation resistance at 700°, 1000°, and 1370°C, without incidence of 700° to 1000°C phase instability and cracking.     

High-Temperature Failure Mechanisms of Hot-Pressed Si3N4 and Si3N4/Si3N4-Whisker-Reinforced Composites

The high-temperature flexural strength of hot-pressed silicon nitride (Si₃N₄) and Si₃N₄-whisker-reinforced Si₃N₄-matrix composites has been measured at a crosshead speed of 1.27 mm/min and temperatures up to 1400°C in a nitrogen atmosphere. Load–displacement curves for whisker-reinforced composites showed nonelastic fracture behavior at 1400°C. In contrast, such behavior was not observed for monolithic Si₃N₄. Microstructures of both materials have been examined by scanning and transmission electron microscopy. The results indicate that grain-boundary sliding could be responsible for strength degradation in both monolithic Si₃N₄ and its whisker composites. The origin of the nonelastic failure behavior of Si₃N₄-whisker composite at 1400°C was not positively identified but several possibilities are discussed.     

The System Bi2O3-SiO2

The Bi₂O₃-rich side of the system Bi₂O₃-SiO₂ was studied with powder X-ray diffraction and differential thermal analysis. In the composition 6Bi₂O₃. x SiO₂, the metastable γ phase (bcc) was observed to exist over the range of 0 < x ≤ 1. In most of the compositions studied, metastable phases of water-quenched melts transformed into another metastable phase before reaching stable phases. A modification of the phase diagram is proposed.     

Hot Isostatic Pressing of Si3N4 Powder Compacts and Reaction-Bonded Si3N4

Hot isostatically pressed silicon nitride was produced by densifying Si₃N₄ powder compacts and reaction-bonded Si₃N₄ (RBSN) parts with yttria as a sintering additive. The microstructure was analyzed using scanning electron microscopy, X-ray diffraction, and density measurements. The influence of the microstructure on fracture strength, creep, and oxidation behavior was investigated. It is assumed that the higher amount of oxygen in the Si₃N₄ starting powder compared with the RBSN starting material leads to an increased amount of liquid phase during densification. This results in grain growth and in a larger amount of grain boundary phase in the hot isostatically pressed material. Compared with the hot isostatically pressed RBSN samples therefore, strength decreases whereas the creep rate and the weight gain during oxidation increase.     

Phase Relations in the Si3N4-Rich Portion of the Si3N4–AlN–Al2O3–Y2O3

The phase relations in the Si₃N₄-rich portion of the Si₃N₄–AlN–Y₂O₃ rystem were investigated using hot-pressed bodies. The one-phase fields of β3 and α, the twophase fields of β+α, β+M (M=melilite), and α+M, and the three-phase fields of β+α+M were observed in the Si₃N₄-rich portion. The α- and β-sialons are not two different compounds but an allotropic transformation phase of the Si–Al–O–N system, and an α solid solution expands and stabilizes with increasing Y₂O₃ content. Therefore, the formulas of the two sialons should be the same.     

Compressive Creep and Oxidation Resistance of an Si3N4 Material Fabricated in the System Si3N4-Si2N2O-Y2Si2O7

The compressive creep behavior and oxidation resistance of an Si₃N₄/Y₂Si₂O₇ material (0.85Si₃N₄+0.10SiO₂+0.05Y₂O₃) were determined at 1400°C. Creep re sistance was superior to that of other Si₃N₄ materials and was significantly in creased by a preoxidation treatment (1600°C /120 h). An apparent parabolic rate constant of 4.2 × 10⁻¹¹ kg²·m-⁴·s⁻¹ indicates excellent oxidation resistance.     

Oxidation and Strength Retention of Monolithic Si3N4 and Nanocomposite Si3N4-SiC with Yb2O3 as a Sintering Aid

The oxidation behaviors of monolithic Si₃N₄ and nanocomposite Si₃N₄-SiC with Yb₂O₃ as a sintering aid were investigated. The specimens were exposed to air at temperatures between 1200° and 1500°C for up to 200 h. Parabolic weight gains with respect to exposure time were observed for both specimens. The oxidation products formed on the surface also were similar, i.e., a mixture of crystalline Yb₂Si₂O₇ and SiO₂ (cristobalite). However, strength retention after oxidation was much higher for the nanocomposite Si₃N₄-SiC compared to the monolithic Si₃N₄. The SiC particles of the nanocomposite at the grain boundary were effective in suppressing the migration of Yb³⁺ ions from the bulk grain-boundary region to the surface during the oxidation process. As a result, depletion of yttribium ions, which led to the formation of a damaged zone beneath the oxide layer, was prevented.