高固体分环氧涂料的制备与性能研究

将环氧树脂E51、E20与聚天门冬氨酸酯树脂(F420)反应,加入活性稀释剂1,4–环己烷二甲醇二缩水甘油醚(630)调节黏度,得到改性环氧树脂.该改性环氧树脂与腰果酚固化剂配伍可以得到高固体分环氧树脂涂料;采用盐雾试验和3.5％N a C l溶液、10％N a O H溶液浸泡试验,用电化学工作站检测树脂的阻抗,探究了...     

酚醛胺/环氧树脂胶粘剂耐化学介质性能研究

以自制酚醛胺作为环氧树脂(EP)的固化剂,研究了酚醛胺/EP胶粘剂的耐化学介质性能和耐久性。结果表明:酚醛胺/EP胶粘剂在水、10%NaOH和2%NaCl溶液中浸泡48 h时,其剪切强度分别为6.61、4.66、5.12 MPa,其强度保留率分别为87.90%、61.97%、68.09%;酚醛胺/EP胶粘剂既具有良好的耐水性、耐碱性和耐盐性,又具有较好的碱、盐耐久性,可作为特种胶粘剂——水下胶粘剂广泛用于房屋、水利、地下建筑、医疗、仿生和养殖等领域,并具有良好的经济效益和应用前景。     

环氧-酚醛胺体系的增韧研究

在环氧-酚醛胺体系中使用端环氧基聚氨酯醚、聚硫橡胶、液体丁腈橡胶等活性增韧剂,通过对固化物剪切强度、弯曲弹性模量及断裂强度的测试对比,可以看出不同增韧剂效果不同。相比较而言,端环氧基聚氨酯醚海岛结构增韧剂的综合性能较好。     

酚醛环氧改性有机硅树脂防腐耐温涂料的研制

采用酚醛环氧树脂对有机硅树脂进行了共聚改性,以此共聚物为成膜树脂,采用合适的固化剂,添加适当的颜填料制备了防腐耐温涂料,该涂料具有优异的耐高温及防腐性能。     

酚醛环氧导静电涂料的研究

将导电填料添加到常温固化的酚醛环氧涂料体系中,通过研究酚醛树脂相容性、导电填料添加量等要素成功制备了酚醛环氧导静电涂料,其表面电阻率最低可达10~6Ω,通过实验验证其在耐化学介质能力上明显优于市面上的环氧导静电涂料。     

常温固化型酚醛环氧防腐涂料

讨论了常温固化型酚醛环氧防腐涂料的配方设计 ,评价涂层优异的耐热水、耐介质 ,特别是耐小分子介质的渗透性能。该涂料可应用于耐温要求 >10 0℃的食品行业。     

常温固化酚醛环氧涂料的研制

选择环氧官能度适中的酚醛环氧树脂作为基料,以脂环胺作为固化剂,制备了常温固化酚醛环氧涂料.考察了脂环胺的加成改性对其抗发白性和黏度的影响;探讨了3种脂环胺的耐化学品性差异;研究了苯甲醇对酚醛环氧漆膜的固化程度和耐化学品性的影响;分析了偶联剂对涂膜的抗阴极剥离作用.结果表明:选用官能度适中的DEN431作为酚醛环氧树脂;活泼氢当量为65的改性4,4’-二氨基二环己基甲烷作为固化剂;以苯甲醇作为增塑剂,其用量为酚醛环氧树脂的7.5％;以KH-550作为偶联剂,其用量为酚醛环氧树脂的0.5％(质量分数,下同);以DMP-30作为促进剂,其用量为酚醛环氧树脂的0.8％,得到耐化学品性与耐温性优异的常温固化酚醛环氧涂料.     

酚醛环氧防腐涂料的制备及性能研究

采用酚醛环氧树脂以及耐酸性颜填料等原料,制备了可常温固化耐强化学品性的酚醛环氧防腐涂料。进行了配方设计和工艺设计,探讨了涂料指标,助剂的影响、固化剂的反应机理以及施工条件。     

添加剂对酚醛环氧涂层耐磨性的影响

以天然生漆改性酚醛环氧树脂为防腐耐磨涂层的基料，详细讨论了天然生漆、润滑剂、填料及有机胺等添加剂对涂层耐磨寿命的影响。给出了获得优化涂层所需的各种添加剂的最佳添加量。     

高固体分环氧饮水设备防腐涂料

介绍了一种低温固化、高固体分环氧饮水设备用防腐涂料的研制。讨论了环氧树脂、固化剂、颜填料、溶剂、助剂、涂膜厚度等对涂膜性能的影响。     

对叔丁基酚改性环氧酚醛涂料的合成与表征

以对叔丁基酚、苯酚、甲醛水溶液为原料，在氨水的催化下，合成了一种对叔丁基酚改性的甲阶酚醛树脂。考察了对叔丁基酚含量对固含量和涂料性能的影响。利用红外光谱、DSC和GPC方法分析了产物的结构，并与环氧树脂混合配制出一种性能优异的非双酚A型食品罐用环氧酚醛涂料。     

双环戊二烯酚型环氧树脂的合成及其结构表征

研究了催化剂用量,反应温度及时间,碱量及浓度因素对双环戊二烯酚型环氧树脂合成反应的影响,并采用ＦＴ－ＩＲ及＾１Ｈ－ＮＭＲ光谱表征了该环氧树脂的化学结构。     

Study on Novel Epoxy Based Poly (Schiff Reagent)s

Abstract

Novel poly(schiff reagent)s from diketo derivative of epoxy resin were synthesised and characterised. A series of epoxy resin based poly(schiff reagent)s were synthesised by reacting an epoxy resin, diglycidyl ether of bisphenol-A (DGEBA) with 4-amino acetophenone (4-AAP) in a 1:2 mole ratio to afford the corresponding diketo derivative, and subsequent reaction with various aliphatic diamines in a presence of a triethyl amino as a catalyst. The resultant poly(schiff reagent)s were characterised by infrared spectroscopy (IR) and number average molecular weight (Mn) of PSs were estimated by non-aqueous conductometric titration. As produced, PSs having amine groups may act for curing of epoxy resins. Differential scanning calorimetric (DSC) curing kinetics of the epoxy resins viz. diglycidyl ether of bisphenol-A(DGEBA) and triglytidyl-p-amino phenol (TGPAP) have been investigated using PSs as a curing agent and triethyl amine as a catalyst. Thermal stability of the cured epoxy systems were studied by thermogravimetric analysis (TGA). The glass fiber reinforced composites of the produced PSs-epoxy system have been fabricated and were characterised by their mechanical properties and chemical resistance.     

端羟基聚二甲基硅氧烷改性环氧树脂的研究

以端羟基聚二甲基硅氧烷(HTPDMS)改性环氧树脂(EP)能将热稳定和柔性的Si-O链引入环氧树脂固化的结构中,提高环氧树脂的综合性能.实验采用2-乙基-4-甲基咪唑作为环氧树脂的固化剂,添加不同质量分数的HTPDMS,实验结果表明:通过增容剂KH550的作用,HTPDMS可与EP发生反应,红外光谱分析表明有Si-O柔...     

紫外光固化环氧树脂涂层性质的研究

以双酚A型环氧树脂紫外光阳离子固化体系为对象，系统研究了光引发剂和各种单体组成对光固化速度及固化膜机械物理性质的影响。结果表明，光引发剂的种类不但可以有效地影响光固化速度，还能对涂层硬度产生影响；环氧稀释剂在降低体系黏度的同时，对光固化速度和硬度产生负面影响；而羟基化合物对光固化速度几乎不产生影响，但是可以大幅度提高涂层的硬度和柔韧性；三元体系中，由于存在加合作用，在光固化速度和物理机械性质两方面都得到了很好的结果。这就使得能够根据具体要求，配制出各种性能都较好的材料，将大大扩展阳离子紫外光固化技术的应用领域。     

环氧树脂防粘涂料的研究

研制了一种以环氧树脂为基料,聚四氟乙烯为防粘剂,二硫化钼为润滑剂的常温固化防粘涂层。通过正交实验与极差分析,对涂层性能作了较为深入的研究,筛选出最优的涂料配方。结果表明,该涂层具有优良的防粘性,硬度和附着力。     

环氧粉末涂料的增韧改性

采用国产增韧剂对市售的环氧树脂进行改性,得到效果良好的增韧环氧粉末涂料。SEM分析表明,增韧剂的加入,在树脂集体内部形成了海岛结构,增韧剂微粒的存在,使得粉末涂料的韧性得到了极大的提高。DMA分析表明,增韧前后粉末涂料的储能模量和玻璃化转变温度均有所升高。DTA分析表明,少量增韧剂的引入有益于树脂的热稳定性能的提高。     

耐黄变木器涂料的研究

基于木器涂料黄变的客观现实,剖析了涂层和基材的黄变机理,以及其它物化性能下降的影响因素,研究出了能够提高木材寿命、延缓涂层老化的涂料.