Cu-BTC/氧化石墨烯复合材料对刚果红的吸附特性

文章采用溶剂热合成法制备出了金属有机骨架(MOF)1, 3, 5-均苯三羧酸铜,即Cu-BTC,然后将Cu-BTC与氧化石墨烯(GO)进行复合制备Cu-BTC/GO复合材料。利用扫描电子显微镜(SEM)、X射线衍射仪(XRD)、红外光谱(FT-IR)、BET分析仪对材料进行了表征,并研究了复合材料对阴离子染料刚果红(CR)的吸附特性。XRD谱图显示MOF复合材料具有较高的结晶度。SEM表征证实了MOF在GO表面实现了成功生长。复合材料对CR的去除率大于单一MOF的去除率,吸附过程符合准2级动力学和Langmuir吸附等温线模型,吸附容量达到1 491.6 mg/g。总的来说,Cu-BTC/GO可以作为染料废水处理的优良候选材料。     

改性氧化石墨烯/壳聚糖功能材料对刚果红的吸附研究

以氧化石墨烯(GO)和壳聚糖(CS)为前体物,以乙二胺四乙酸二钠(EDTA-2Na)为表面改性剂,制备了一种新型改性氧化石墨烯/壳聚糖功能材料(GEC),并将此材料作为吸附剂用于水中刚果红的吸附去除,探讨了时间、pH值、吸附剂投加量、温度及初始浓度对GEC吸附去除刚果红的影响.结果表明,GEC对水中刚果红具备良好的吸附能力,且在pH=2~12的范围内都具有较佳的吸附效果.GEC对刚果红的吸附动力学可以较好地用伪二级动力学模型进行描述,其吸附数据可应用Langmuir吸附等温模型进行拟合,其吸附过程是自发的吸热反应过程.根据Langmuir模型计算得到GEC室温条件下最大吸附量为175.43 mg·g~(-1).用2 mol·L~(-1)NaOH溶液在60℃水浴条件下对GEC进行脱附再生实验,在重复循环利用6次后,GEC对刚果红的吸附量仅下降了5.89%,刚果红的去除率仍保持在88%以上.以上结果表明,GEC适合作为一种有效的吸附剂去除水中刚果红.     

羟基磷灰石-四氧化三铁-沸石复合材料制备及去除水中刚果红研究

采用可溶性磷酸盐、钙离子、二价铁离子、三价铁离子和天然沸石等材料制备了羟基磷灰石-四氧化三铁-沸石(HAPFe3O4-沸石)复合材料,对该复合材料进行了表征,并考察了该复合材料对水中刚果红的吸附作用.结果表明,HAP-Fe3O4-沸石复合材料对水中的刚果红具备良好的吸附能力.当pH由3增加到4或由7增加到11时,HAP-Fe3O4-沸石复合材料对水中刚果红的去除能力下降;当pH由4增加到7时,对刚果红的吸附能力基本保持不变.HAP-Fe3O4-沸石复合材料对水中刚果红的去除率随吸附剂投加量的增加而增加,而对水中刚果红的单位吸附量则随吸附剂投加量的增加而降低.HAP-Fe3O4-沸石复合材料对水中刚果红的吸附动力学过程可以较好地采用准二级动力学模型加以描述,对刚果红的吸附平衡数据可以采用Langmuir和Freundlich等温吸附模型加以描述.根据Langmuir模型确定的最大吸附容量为117 mg·g-1.(pH 7和303 K).HAP-Fe3O4-沸石复合材料对水中刚果红的吸附是自发吸热并伴随熵增加的过程.当pH为7时,HAP-Fe3O4-沸石复合材料吸附水中刚果红的主要机制包括表面配位作用、氢键作用以及路易斯酸碱反应.采用热再生的方法可以使吸附刚果红后的HAP-Fe3O4-沸石复合材料得到再生,热再生后的复合材料可以循环使用并且对水中刚果红的吸附性能良好.X射线衍射分析结果表明HAP-Fe3O4-沸石复合材料含Fe3O4,磁滞回线结果表明HAP-Fe3O4-沸石复合材料具备较高的磁饱和强度,复合材料吸附刚果红后可以很容易地通过外加磁场的作用快速地与水溶液分离.结果表明,HAP-Fe3O4-沸石复合材料适合作为一种吸附剂去除废水中的刚果红.     

氨基修饰磁性氧化石墨烯吸附离子型染料性能

采用恒温搅拌法和水热法首次制备磁性三乙烯四胺氧化石墨烯（M-T-GO）,并通过SEM和XPS对M-T-GO进行表征.以M-T-GO为吸附剂,分析pH值、吸附时间和初始浓度对阴离子染料酒石黄（TY）和阳离子染料亚甲基蓝（MB）吸附效果的影响.并对吸附动力学和吸附等温线进行拟合.结果表明：M-T-GO对离子型染料的吸附过程符合Langmuir吸附等温式和拟二级反应动力学描述.M-T-GO对TY和MB具有较好的吸附性能,饱和吸附量分别为157.23mg/g和169.49mg/g.与GO相比,M-T-GO对离子型染料的吸附效果更优异,同时具有快速分离和易再生的优点.     

磁性氧化石墨烯同时吸附砷(Ⅴ)和镉的性能研究

用化学方法合成磁性氧化石墨烯(MGO)。X射线衍射(XRD)与振动样品磁强计(VSM)表征结果发现,四氧化三铁粒子均匀分布在MGO表面,其饱和磁化强度达30.2 emu/g。考察As(Ⅴ)和Cd在单独存在体系和共存体系下MGO对其的吸附性能,结果表明,单独存在体系下As(Ⅴ)和Cd的最大吸附量分别为5.857和78.81 mg/g,而共存体系下则分别提高至6.303和91.27 mg/g。     

磁性石墨烯吸附水中Cr(Ⅵ)研究

以氧化石墨和铁盐为原料,采用化学沉淀法制备出磁性石墨烯复合材料,运用静态吸附实验研究了吸附动力学、热力学、等温吸附模型以及不同因素如p H、温度、时间对Cr(Ⅵ)吸附的影响.结果表明,吸附动力学符合假二级动力学模型;与Freundlich模型相比,Langmuir模型更适合描述吸附过程.热力学参数为:ΔHθ=33.89 k J·mol-1,ΔSθ=120.15 J·(mol·K)-1,ΔGθ=-2.51 k J·mol-1(303 K),这表明吸附过程是吸热并且自发的.实验最佳p H值为2,升高温度和延长时间均有利于吸附的进行.初始Cr(Ⅵ)浓度为5 mg·L-1时,重复利用3次后吸附量由3.9 mg·g-1下降到2.1 mg·g-1.在磁铁存在的条件下吸附剂可轻易从溶液中分离出来,利用Na OH可使其再生,因此可作为去除Cr(Ⅵ)的良好吸附剂.     

磁性氧化石墨烯/壳聚糖制备及其对磺胺嘧啶吸附性能研究

采用一步溶剂热法制备磁性氧化石墨烯/壳聚糖三元复合材料(GO/CS/Fe_3O_4).复合材料的表征结果显示,GO/CS/Fe_3O_4含有丰富含氧官能团,氧化石墨烯片层上均匀负载四氧化三铁磁性粒子,分散到水中的磁性复合材料在外加磁场的作用下,具有良好的磁分离效果.选择磺胺嘧啶为目标污染物考察复合材料吸附性能.结果表明,吸附动力学符合拟二级动力学模型,吸附等温线符合Langmuir模型,在295、303、313 K温度下最大吸附量分别为53.30、60.56、79.23 mg·g~(-1),吸附热力学参数表明GO/CS/Fe_3O_4对磺胺嘧啶的吸附是以物理吸附为主的自发吸热反应.通过不同pH条件下吸附量和Zeta电位分析吸附机理,证明π-π电子共轭效应及静电吸附是复合材料吸附磺胺嘧啶过程中的主导作用力.     

氧化石墨烯制备及其结构表征

本文以不同类型的石墨为原料,采用密闭氧化法制备了氧化石墨,并通过超声剥离得到氧化石墨烯,利用氨肼还原法将氧化石墨烯还原得到石墨烯。讨论了不同类型石墨原料对所制备氧化石墨烯微观形貌的影响,并且利用高分辨率扫描电子显微镜(SEM)和X射线衍射仪(XRD)对所制备的氧化石墨烯和石墨烯进行了结构表征,结果表明,在以不同类型石墨为原料所制备的氧化石墨烯中,50目天然鳞片制备的氧化石墨烯的微观形貌最好,呈波浪褶皱状。     

磁性GO复合材料对水溶液中Cu(Ⅱ)的去除研究

该研究利用简单的化学合成法合成新型Fe_3O_4@SiO_2/PEI修饰的氧化石墨烯磁性复合材料,并用于去除水中的Cu(Ⅱ)离子,通过Box-Behnken响应面法对pH、Cu(Ⅱ)离子的初始浓度和反应温度3个变量进行优化,得到MSPG对Cu(Ⅱ)离子吸附的最优吸附条件为初始p H为5、初始浓度80 mg/L、反应温度为40℃时,最大理论吸附量为61.48 mg/g。而在最佳条件下进行验证实验,实验值为61.55 mg/g,与理论值相近。吸附动力学研究和等温线研究表明吸附过程在6 h达到平衡,分别符合准二阶动力学模型与Freundlich等温模型,粒子内扩散并不是整个过程中唯一的速率控制步骤。热力学研究证明MSPG对Cu(Ⅱ)的吸附过程是吸热的自发过程。     

氧化石墨烯改性污泥基生物炭对培氟沙星的去除机理研究

为获得培氟沙星废水高效去除的环境友好型吸附剂,以城市剩余污泥为原料制备了SBC（污泥基生物炭）,并采用氧化石墨烯（GO）对其改性得到GO-SBC（氧化石墨烯改性生物炭）,利用SEM和FTIR对其进行表征,通过静态吸附试验探讨了生物炭对培氟沙星的去除效果,并通过吸附模型和FTIR、XPS表征技术进一步探究了GO-SBC对培氟沙星的吸附机理.结果表明:①改性后的GO-SBC表面更加粗糙,生物炭表面含氧官能团数量增加.②动力学吸附研究表明,GO-SBC对培氟沙星的最大吸附容量为137.51 mg/g,比SBC对培氟沙星的吸附容量提高了40.32%,且GO-SBC对培氟沙星的吸附更符合伪二级动力学模型,表明吸附过程主要以化学吸附为主.③GO-SBC对培氟沙星的吸附符合Freundlich等温吸附模型,表明该吸附过程为多层吸附.④热力学研究表明,吸附过程为自发吸热反应.⑤GO-SBC对培氟沙星的吸附机制主要有两种作用,一种是π-π相互作用,另一种是GO-SBC的N—H与培氟沙星的C—H相互作用.研究显示,GO-SBC是一种高效去除培氟沙星的吸附剂,这为城市剩余污泥的资源化利用提供了出路,也为抗生素废水治理提供了方法.      

Removal of heavy metal ions from aqueous solution using red loess as an adsorbent

The adsorption behaviors of heavy metals onto novel low-cost adsorbent, red loess, were investigated. Red loess was characterized by X-ray diffraction, scanning electron microscopy and Fourier transform infrared spectra. The results indicated that red loess mainly consisted of silicate, ferric and aluminum oxides. Solution pH, adsorbent dosage, initial metal concentration, contact time and temperature significantly influenced the efficiency of heavy metals removal. The adsorption reached equilibrium at 4 hr, and the experimental equilibrium data were fitted to Langmuir monolayer adsorption model. The adsorption of Cu(II) and Zn(II) onto red loess was endothermic, while the adsorption of Pb(II) was exothermic. The maximum adsorption capacities of red loess for Pb(II), Cu(II) and Zn(II) were estimated to be 113.6, 34.2 and 17.5 mg/g, respectively at 25°C and pH 6. The maximum removal efficiencies were 100% for Pb(II) at pH 7, 100% for Cu(II) at pH 8, and 80% for Zn(II) at pH 8. The used adsorbents were readily regenerated using dilute HC1 solution, indicating that red loess has a high reusability. All the above results demonstrated that red loess could be used as a possible alternative low-cost adsorbent for the removal of heavy metals from aqueous solution.     

新型Ag(I)选择性吸附材料的制备及吸附性能研究

将壳聚糖（CTS）、氧化石墨烯（GO）、3-巯基丙基三甲氧基硅烷（MPTMS）交联制得巯基改性壳聚糖-氧化石墨复合材料（SFCG）.采用傅里叶变换红外光谱仪、扫描电子显微镜、元素分析仪对改性前后和吸附前后的材料进行表征.研究吸附剂投加量、温度、时间、初始浓度对吸附效果的影响.实验结果表明,SFCG与CTS相比结构发生很大变化,呈现薄层状结构,表面有褶皱.SFCG能够在短时间内选择性高效吸附Ag（I）,最大吸附量为578.41 mg·g^-1.通过吸附等温线、吸附动力学、吸附热力学的研究发现,其吸附等温线符合Langumir吸附模型,为单层吸附;吸附过程符合准二级动力学模型,以化学吸附为主,同时吸附过程是自发的、放热的.另外,银是一种贵金属,因此,SFCG将在废水处理和回收贵金属等方面均表现出良好的应用前景.     

磁性吸附剂MZFS吸附偶氮染料中性红的性能及机理

利用正硅酸乙酯水解制备得到"核-壳"结构的磁性吸附剂MZF@SiO₂（MZFS），采用X射线衍射（XRD）、透射电子显微镜（TEM）、振动样品磁强计（VSM）和傅利叶变换红外光谱（FT-IR）对MZFS的结构和性能进行表征，并研究MZFS对偶氮染料中性红（NR）的吸附性能.结果表明，拟二级动力学和Freundlich模型均能较好地描述该吸附过程，吸附过程的速率控制步骤为化学吸附；吸附自由能E为0.472-0.773kJ/mol，△G为-20~0kJ/mol，△H为37.5kJ/mol，表明该过程是以物理吸附为主的自发吸热过程.FT-IR结果表明吸附的主要作用力为分子间氢键，MZFS可采用15% wt H₂O₂进行原位再生.研究结果能为偶氮染料废水处理方法的革新提供基础理论数据.     

Shellac-coated iron oxide nanoparticles for removal of cadmium(II) ions from aqueous solution

This study describes a new effective adsorbent for cadmium removal from aqueous solution synthesized by coating a shellac layer, a natural biodegradable and renewable resin with abundant hydroxyl and carboxylic groups, on the surface of iron oxide magnetic nanoparticles. Transmission Electron Microscopy (TEM) imaging showed shellac-coated magnetic nanoparticle (SCMN) adsorbents had a core-shell structure with a core of 20 nm and shell of 5 nm. Fourier Transform Infrared Spectroscopic analysis suggested the occurrence of reaction between carboxyl groups on the SCMN adsorbent surface and cadmium ions in aqueous solution. Kinetic data were well described by pseudo second-order model and adsorption isotherms were fitted with both Langmuir and Freundlich models with maximum adsorption capacity of 18.80 mg/g. SCMN adsorbents provided a favorable adsorption capacity under high salinity conditions, and cadmium could easily be desorbed using mild organic acid solutions at low concentration.     

Adsorption removal of phosphate from aqueous solution by active red mud

Red mud is the waste of alumina industry and has high TiO_2 and Fe_2O_3 content which are active components for the adsorption of anion pollutants.In this study,the uptake of phosphate by red mud activated by heat treatment and acid-heat treatment was investigated. The factors influencing the adsorption were also investigated.The result showed that the red mud sample treated using acid-heat method at 80℃with 0.25 mol/L HC1 for 2 h achieved the highest phosphate removal.For the heat-activated red mud,the sample heated at 700℃for 2 h preformed better than the other heat treatment.Phosphate removal by the activated red mud was significantly pH dependent,and pH 7 was the optimal pH for phosphate removal.The adsorption fits Langmuir isotherm model well and the maximum adsorption capacities of the acid-heat activated red mud and the heat activated samples were 202.9 mgP/g and 155.2 mgP/g,respectively.