S掺杂形式对TiO2基光催化剂结构和性能的影响

采用改进的Sol-gel法制备了S-TiO₂和TiO₂,用1 mol·L^-1的H₂SO₄对TiO₂进行表面修饰制成的SO₄^2-/TiO₂。采用XRD、IR、UV-Vis、SEM和EDS等技术对催化剂的结构进行了表征,以L酸(1-萘酚-5-磺酸)为目标物,考察了所制备的催化剂的性能．结果表明：S-TiO₂的禁带宽度明显降低,并且对400~650 nm区域的可见光都有一定的吸收,其可见光活性和紫外光活性均高于SO₄^2-/TiO₂和纯TiO₂。     

TiO2/Gd2O3纳米粉体的制备、表征及光催化活性

利用酸催化的溶胶-凝胶法制备了纯TiO₂和Gd³⁺(0.5wt%)掺杂的TiO₂纳米粉体，采用XRD、BET、XPS、紫外-可见漫反射谱(DRS)和表面光电压谱(SPS)等技术进行了表征；以亚甲基蓝(MB)的光催化降解为探针反应，评价了其光催化活性；探讨了Gd³⁺掺杂对TiO₂纳米粉体的光催化活性的影响机制。结果表明，TiO₂/Gd₂O₃纳米粒子对MB溶液的光催化活性提高到纯TiO₂的1.5倍。掺杂Gd³⁺可以强烈抑制TiO₂由锐钛矿相向金红石相的转变；阻碍TiO₂晶粒的生长；提高高温组织稳定性，改善粉体的表面织构特性；形成光生电子的浅势捕获陷阱，抑制e^-/h⁺复合，这些因素共同作用最终导致TiO₂/Gd₂O₃纳米粉体的光催化活性明显提高。XPS分析结果证实，掺杂Gd³⁺导致粉体的表面羟基含量降低。由于产生了量子尺寸效应，复合粉体的紫外吸收带边蓝移，光的吸收能力略有降低。     

TiO2纳米纤维无纺布的制备及光催化性能研究

以聚乙烯吡咯烷酮(PVP)作为配位剂与钛酸正丁酯(Ti(C₄H₉O)₄)反应制得前驱体，再以乙醇为溶剂，CH3COOH作为催化剂，采用静电纺丝法制得PVP/TiO₂复合纳米纤维，经550 ℃、700 ℃和900 ℃焙烧后分别得到以锐钛矿型的TiO₂为主、以金红石型TiO₂为主和完全金红石晶型的TiO₂纳米纤维。对所制得的纳米纤维的结晶度、纯度和形貌，分别采用差热-热重分析(TG-DTA)、红外光谱(IR)、X射线粉末衍射(XRD)、扫描电镜(SEM)等进行了表征。光降解苯酚水溶液的实验结果表明，550 ℃下煅烧得到的以锐钛矿占主体的TiO₂纳米纤维，2 h使浓度为50 mg·L^-1苯酚水溶液的降解率超过85%，这充分说明这种TiO₂电纺纳米纤维具有良好的光催化性能。     

SO42-改性后的TiO2(锐钛和/或金红石)表面上MoO3的分散性质研究

采用红外(IR)、拉曼(Raman)、X-射线衍射(XRD)、程序升温还原(TPR)等方法考察了经硫酸根改性后的金红石(SR)与锐钛矿(SA)的混合比例变化时的负载型催化剂，MoO₃ / TiO₂(SR+SA)，的一些物理化学性质(如活性组分MoO₃的分散行为、表面酸碱性、氧化还原性)的变化规律。结果表明：对于MoO₃ / TiO₂(SR+SA)样品，低含量MoO₃表面分散时倾向于优先与混合载体中的改性金红石(SR)发生作用；TiO₂载体表面SO₄^2-的存在，使得载体表面产生了新的酸性位，导致样品中表面分散的钼物种主要以聚合八面体状态存在。     

Gd-N共掺杂SrTiO3/TiO2复合纳米纤维制备及光催化性能

以静电纺丝技术制备的TiO_2纳米纤维为基质和反应物,结合一步水热法制得Gd-N共掺杂SrTiO_3/TiO_2复合纳米纤维光催化剂。利用X射线衍射(XRD)、扫描电子显微镜(SEM)、高分辨透射电镜(HRTEM)、X射线光电子能谱(XPS)、紫外-可见漫反射(UV-Vis DRS)和荧光光谱(PL)等方法对其微观结构、形貌和光学性能进行表征。结果表明:SrTiO_3和TiO_2形成异质结能够使光生电子和空穴得到很好的分离,而Gd-N共掺杂产生新带隙,可以拓宽光谱响应范围至可见光区,并引起晶格缺陷,成为光生电子-空穴对的浅势捕获阱。Gd-N共掺杂与异质结的协同作用有效提高了SrTiO_3/TiO_2复合纳米纤维的可见光催化活性。     

Pt / InVO4 / TiO2可见光催化剂的制备及性能研究

采用溶胶-凝胶法制备了Pt / InVO₄ / TiO₂三元体系可见光催化剂。以乙烯为模拟目标分子，评价其光催化活性并与二元体系催化剂Pt / TiO₂ 和InVO₄ / TiO₂进行比较。用DRS，XRD对催化剂的吸收带边和晶型进行了表征。结果表明：Pt / InVO₄ / TiO₂在可见光区（λ>450 nm）的光催化比活性比Pt / TiO相似文献   

微乳法制备纳米TiO2 /SiO2的结构及光催化研究

Nanosized TiO₂ and TiO₂/SiO₂ particles were prepared by hydrolysis of tetrabutyl titanate (TBOT) and tetraethyl orthosilicate (TEOS) in the TX-100 reverse microemulsion. These particles were characterized by TG-DSC, XRD, FTIR, TEM，N₂ adsorption-desorption. Their photocatalytic activity was tested by degradation of methyl orange. The result shows that TiO₂/SiO₂ nanoparticles are with a monodispersed spherical phase and a uniform size distribution，and TiO₂ particles are dispersed on the surface of SiO₂. The band for Ti-O-Si vibration in FTIR was observed, the Ti-O-Si bond increased the stability of anatase TiO₂, suppressed the phase transformation of titania from anatase to rutile. And due to the addition of SiO₂, the average size of titania decreased from 38 nm in pure TiO₂ to 5 nm in TiO₂/SiO₂. It was found, under UV light irradiation, TiO₂/SiO₂ particles showed higher activity than pure TiO₂, and TiO₂/SiO₂(1/1) particles showed the highest photocatalytic activity on the photocatalytic decomposition of methyl orange, which was influenced by crystal structure, particle size, crystallinity and Surface area Characteristics.     

ZnFe2O4/Ag/TiO2复合材料的制备及其光催化性能

以硝酸银、钛酸四丁酯、无水氯化锌、六水氯化铁为原料,采用溶胶-凝胶法与溶剂热相结合的方法制备了ZnFe₂O₄/Ag/TiO₂复合材料,通过扫描电子显微镜、能谱分析仪、X射线粉末衍射仪、X射线光电子能谱仪、振动样品磁强计、紫外可见分光光度计对样品进行表征及测试。结果表明： ZnFe₂O₄/Ag/TiO₂-10具有最佳的光催化效果,在紫外和可见光下对染料的降解率都能达到90%以上,具有优异的紫外可见光光催化活性。ZnFe₂O₄/Ag/TiO₂具有独特的磁性,能在外部磁场作用下进行回收利用,这使其在实际应用中成为可能。通过磁分离技术重复回收利用5次后仍然保持优良的光催化性能,说明ZnFe₂O₄/Ag/TiO₂-10具有优异的磁性及较高的光催化循环稳定性。     

碱土金属掺杂纳米TiO2催化剂的制备与光催化活性的评价

The nanometer TiO₂ were prepared by the hydrolyze-gel method and fellowed by doping alkaline-earth metals (Mg, Ca, Sr, Ba). XRD, SEM, diffuse reflection spectra were used to investigate their characteristices. The result indicates that the average particles size of the TiO₂ is about 80 nm and keep uniformity in distributing. The product was mainly anatase in 300～400 ℃ calcinations, the einstein shift of absorption spectrum was observed after doping the alkaline-earth metals. The best mole percentages of Mg, Ca, Sr and Ba are 0.5%, 1.0%, 1.5%, 1.5% respectively. Under the same reaction conditions, it is more effective to the UV-catalyed degradation reaction that the catalysts containing Mg and Ca were calcined at 300 ℃ for 1h or containing Sr and Ba were calcined at 400 ℃ for 1 h. The photocatalystic activity is considerably depondent on pH and the concentration of the oxidant. Using the sunlight to do the degradation experimental, the result also show that the doping catalysts has higher degradation efficiency than that of pure TiO₂.     

N 掺杂TiO2光催化剂的制备及其可见光活性研究

A visible-light-active photocatalyst was prepared by calcination of the hydrolysis product of tetrabutyl titanate with ammonia as precipitant. The photocatalyst was characterized by X-ray diffraction (XRD), UV-Vis diffuse reflection spectra (DRS), thermal gravimetric-differential thermal analysis (TG-DTA), X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM). The color of the photocatalyst was yellow and could absorb light wavelength under 550 nm as measured by DRS. The catalyst calcined at higher temperature will give lower absorbance for visible light. Structures of the sample were characterized mainly to be anatase by XRD except for the sample calcined at 700 ℃ which gave mixtures of anatase and rutile. TG-DTA results showed that temperature for anatase formation was 415 ℃. XPS results showed that doped-nitrogen was presented in the sample, they are important to show visible-light absorbency. The photocatalytic activities were evaluated using methyl orange and phenol as model pollutants, the results showed that over 90% of phenol could be degraded under visible light using N/TiO₂ as the catalyst after 4 hours reaction. Almost the same activity was found for the TiO₂ photocatalyst calcined at different temperature under sunlight but activities were different when the treatment was under UV light.     

Cu掺杂TiO2及其纳米管的制备、表征与光催化性能

通过溶胶-凝胶法和水热法制备了Cu掺杂TiO₂纳米粉末及其纳米管,并通过XRD、TEM、FE-SEM、EDS、UV-Vis/DRS等手段分析了样品的结构。发现以Cu掺杂TiO₂纳米粉末为水热反应原料制备的纳米管中不含Cu,对其原因进行了分析讨论并通过Zn掺杂TiO₂纳米粉末证实：以金属掺杂TiO₂纳米粉末为原料,通过水热法制备TiO₂纳米管中不含有相应金属离子,这是由于金属离子在强碱水热条件下形成金属配离子,使金属离子溶解于水中而不能形成金属掺杂TiO₂纳米管。对所得样品进行了光催化性能测试,发现：Cu掺杂TiO₂粉末的光催化产氢效率为0.75 μmol·(g·h)^-1,高于由其本身及P25通过水热法制备的TiO₂纳米管(分别为：0.42 μmol·(g·h)^-1,0.25 μmol·(g·h)^-1)的光催化产氢效率。     

纳米复合固体超强酸SO42-/CoFe2O4的制备和表征

采用纳米化学制备技术合成了新型的纳米复合固体超强酸催化剂ＳＯ４＾２－／ＣｏＦｅ２Ｏ４。用ＸＲＤ、ＴＥＭ、ＸＰＳ、红外光谱和比表面测定等技术研究了该催化剂的结构形态,结果表明：所研制的ＳＯ４＾２－／ＣｏＦｅ２Ｏ４２催化剂为晶态纳米粒子（〈５０ｎｍ）,比表面积很大（１５７ｍ＾２．ｇ＾－１）,ＳＯ４＾２－与氧化物的金属离子呈无机齿螯合状配位化合物的结合形式。以乙酸乙酯合成为模型反应考究了该催化剂的催化活     

锐钛相介孔SO42-/TiO2的声化学制备及结构和催化酯化性能

不使用有机模板剂,采用超声化学法一步水解制得吸附硫酸根的介孔偏钛酸,500℃焙烧得到介孔SO2-4/TiO2固体超强酸.用XRD、TFEM、FTIR、低温氮吸附-脱附等手段对催化剂结构进行了表征.结果表明,硫酸根在焙烧过程中与前驱体介孔偏钛酸孔壁上自由羟基的键合起到了孔结构导向及支撑作用,500℃焙烧后样品具有161 m2·g-1的比表面积及4.1 nm的平均孔径,酸强度H0介于-14.52与-16.02之间,硫含量为2.8%,晶型全部为锐钛矿相,介孔SO2-4/TiO2具有较大比表面、强酸特性和稳定性.催化合成富马酸二甲酯的最佳条件为:n(甲醇):n(富马酸)=6:1,催化剂用量为1.0%(反应物总质量),带水剂苯用量为10 mL,反应时间为3 h,催化剂重复使用7次,酯化率大于90%.     

Bi2O3 /TiO2复合纳米颗粒的可见光光催化性能

采用溶胶与水热相结合的方法合成了具有可见光光催化活性的复合纳米颗粒Bi2O3/TiO2,并对其进行了X射线衍射、透射电镜、X射线光电子能谱、紫外-可见漫反射谱、红外光谱、低温N2吸附脱附及电子顺磁共振分析。结果表明,复合少量的氧化铋可显著抑制TiO2由锐钛矿到金红石的相转移过程,并将光吸收范围扩展到可见光区。可见光照射下(λ>420 nm),利用电子顺磁共振技术检测到明显的羟基自由基(.OH)信号。铋的最佳掺杂量为Bi/Ti质量比2.0%,适量铋的掺入能显著改善锐钛矿TiO2的结晶度,抑制光生电子-空穴对的复合,提高光催化量子效率。通过可见光照射下,4-氯酚的降解实验测试Bi2O3/TiO2复合纳米颗粒的可见光光催化活性。同时,利用气-质联用仪对4-氯酚降解过程的中间产物进行了测定,并提出可见光照射下的Bi2O3光敏化机理。     

阳极氧化法制备TiO2纳米管及其光催化性能

纳米TiO₂对诸多环境污染物有显著的光催化降解作用,光催化已发展成为新型环境污染治理技术。本文采用阳极氧化法制备出TiO₂纳米管,对比了四种电解液组成(A氟化铵+硫酸铵+水;B氟化铵+硫酸铵+乙酸+水;C氟化铵+硫酸铵+甘油+水;D氢氟酸+二甲基亚砜(DMOS)+乙醇)对催化剂表面形貌及光催化性能的影响。结果表明,电解液A和C都制备出了形貌清晰的TiO₂纳米管,管径约为60~74 nm。样品经400 ℃煅烧,TiO₂晶型主要为锐钛矿相;经500 ℃煅烧,出现少量金红石相;经700 ℃煅烧,晶型全部为金红石相。具有良好形貌的TiO₂纳米管同时具有良好的紫外光吸收能力。当亚甲基蓝初始浓度为10 mg·L^-1,经500 ℃煅烧的TiO₂纳米管光催化活性最佳,光照30 min亚甲基蓝的降解率达89.98%。亚甲基蓝光催化降解反应符合一级反应动力学,反应速率常数为0.079 30。     

纳米复合固体超强酸SO42-/ZnFe2O4的制备与催化合成癸二酸二乙酯的研究

以硫酸盐为原料,添加NaOH和NaHCO₃以制备出碱式碳酸盐前驱体,合成出新型的纳米固体超强酸催化剂SO₄^2-/ZnFe₂O₄,经XRD、BET、IR等检测,粒径为35nm,比表面积很大(137m^2-1),粒度均匀。首次以该固体酸为催化剂,癸二酸和无水乙醇为原料合成癸二酸二乙酯,考察了影响反应的因素。结果表明,醇酸摩尔比为4.0∶1,催化剂用量为1.0g(癸二酸0.1mol),带水剂苯15mL,反应时间2.5h是最佳反应条件,酯化率可达91%,并推断出该催化剂的酸强度-16.02< H_o< -14.52.     

TiO_2光催化失活复活特性与表面NO_3~-浓度的关系

以乙醛作为活性标的,通过人为控制表面附着NO3-浓度,检测TiO2对乙醛的吸附能力和光催化降解能力,得出了TiO2光催化失活复活特性和表面附着NO3-浓度的定量关系。结果表明,表面附着NO3-浓度达到4.24wt%时,光催化降解能力降低50%;表面附着NO3-浓度达到10.50wt%时,TiO2的吸附能力降低50%;通过溢流状态下水洗2h,可除去98%的表面附着NO3-,使TiO2光催化活性复活。