锆合金的晶粒观测与亚结构分析

为了研究锆合金包壳管再结晶退火的程度及合金的晶粒尺寸,用直线截点法、同心圆截点法以及晶粒度软件法分别对经塑性变形后再结晶退火的国产M5、法国产M5以及国产N18锆合金包壳管晶粒尺寸进行了观测,并用透射电子显微分析观察了合金的亚结构.结果表明:法产M5包壳管的晶粒尺寸为(3.73±0.107)μm,位错较少,再结晶退火程度良好;国产M5包壳管的晶粒尺寸为(3.63±0.239)μm,存在混晶,位错密度高,再结晶退火程度不足,国产N18包壳管的晶粒尺寸为(5.37±0.079 2)μm,位错较少,发生了沉淀相变,再结晶退火程度已经过度.     

TiAl＋Ca合金断裂及变形亚结构研究

运用ＳＥＭ和ＴＥＭ等分析手段研究了ＴｉＡｌ＋Ｃａ三元合金的室温断裂行为和变形亚结构，结果表明，少量Ｃａ的添加可以大幅度提高Ｔｉ－３４％Ａｌ合金的室和学性能，合金断裂时不再表现为单纯的穿晶解理断裂而在γ单相中出现的河流状的解理纹，断口上还出现较多的撕裂梭；ＴＥＭ分析表明，Ｃdisplay status     

Cu-Al-Be-B合金马氏体形貌和亚结构

用光学显微镜和透射电镜分析研究了Cu-11.42Al-0.35Be-0.18B(质量分数,%)形状记忆合金的马氏体的组织形态及亚结构.结果表明,Cu-11.42Al-0.35Be-0.18B(质量分数,%)合金的马氏体的形貌组态较复杂,主要有平行状、矛头状和竹节状,亚结构主要为位错、层错.矛头状自协作形态的马氏体的变体呈竹节状.用XRD分析了晶界析出相α相,其化学式为AlCu4.     

激光焊接锆—4合金辅助装置的设计与使用

本文主要介绍为采用大功率二氧化碳激光器焊接锆－４合金而专门保护装置。试验证明，所设计的保护装置完全能达到焊接锆－４合金的要求。     

具有高强度和良好塑性的锆基晶态合金

在非晶材料家族中,锆基非晶以其强度高而成为最具应用前景的结构材料之一.但因其很难制备出大尺寸、很难加工成形及含有有毒的铍元素等原因,使其应用受到限制.Zr-Ti-Al-V系列晶态锆基合金,具有与锆基非晶的强度相当但塑性远远高于非晶态锆基合金的良好力学特性,其抗拉强度和延展性分别可以达到1720 MPa和3.3%.更为重要的是,锆基合金可批量生产、不含有毒的铍元素以及没有尺寸和形状的限制等非晶合金不具备的特性.     

真空自耗熔炼钛锆合金锭的研制及性能研究

采用真空自耗电极电弧熔炼法熔炼钛锆合金铸锭．实验分析了真空自耗熔炼钛锆合金锭的影响因素,并对钛锆合金力学性能分析．结果表明：钛锆合金与纯钛相比具有较高的硬度及良好的抗拉强度．     

微合金化的HP合金中的铌、锆分布及作用

利用宏观、显微组织观察和萃取碳化物的X射线分析,使用电子探针等技术手段,对铌、锆在HP合金中的分布及存在形态进行定性.探讨这两个强碳化物形成元素对HP合金的影响.     

二氧化碳激光焊接工艺条件对锆—4合金接头质量的影响

研究了二氧化碳激光焊接工艺条件对锆－４合金接头质量的影响。结果表明，在适宜的焊接工艺条件下，可以获得焊缝成形系数大，力学性能接近于母材的焊接接头；与氩弧焊相比，其接头质量显著地优于氩弧焊     

热处理工艺对N36锆合金耐腐蚀性能影响的研究

研究热处理工艺对N36锆合金耐府蚀性能的影响。选取N36锆合金材料,进行不同的变形热处理实验,将最终试样放入高压釜中在400℃、10.3 MPa条件下进行水蒸气腐蚀。经过为期310 d的腐蚀后发现,580℃样品的耐腐蚀性能最佳。     

组织对N18新锆合金的碘致应力腐蚀行为的影响

通过两种热试验方法（去应力和再结晶退火）得到的组织不同的两种N18新锆合金板材，研究它们在40℃I2蒸汽介质中，分别为300℃、350℃和400℃的实验温度条件下的应力腐蚀行为，实验过程中动态监测应力腐蚀裂纹的长度，对实验后的试样进行了断口分析，研究表明：支应力状态的N18新锆合金在350℃时的抗碘致应力腐蚀的能力优于300℃时的抗碘致应力腐蚀的能力。而对于再结晶状态的N18新锆合金则是350℃时的抗碘致应力腐蚀的能力优于400℃时的抗碘致应力腐蚀的能力。断口形貌主要是以穿晶准解理扩展为主。     

M5锆合金塑性变形行为

了解锆合金塑性变形行为,为M5合金的工程应用提供数据.试验采用静态拉伸试验方法对国产及法国产M5锆合金核燃料包壳管在室温和400℃下的拉伸性能进行了研究.结果表明,国产及法国产M5合金的拉伸性能无显著差异.在均匀塑性变形阶段,室温拉伸时法国产M5的形变硬化指数稍高于国产M5,400℃拉伸时两种材料的均匀塑性变形阶段均分为两个阶段,前均匀塑性变形阶段(n1)和后均匀塑性变形阶段(n2),法国产M5的n1明显高于国产M5的n1,法国产M5的n2稍高于国产M5的n2.     

体心立方Fe—17Cr合金晶界的原子探针分析

通过原子探针（AP）对体心立方Fe-17Cr合金的深度分析,在原子尺度上获得紧靠晶界40nm区域内Cr元素的分布。结果表明敏化Fe-17Cr合金在该区域存在贫Cr区,证实了Fe-Cr合金晶间腐蚀的贫Cr理论。在距晶界约30nm内,出现比较平稳的Cr分布平台,并且Cr浓度低于相同Cr含量的敏化Fe-Cr-Ni合金Cr浓度。     

Mechanism and Inhibition of Grain Coarsening of Al-Mg-Si Alloy in Hot Forming

A high-Ti 6061 alloy was rolled with strains up to 0.8-2.0 and at 350-550 ℃. Microstructures that developed during deformation and subsequent solution heat treatment (SHT) were observed by using optical and transmission electron microscopy. Microstructure evolution during SHT depends mainly on the initial rolling temperature, and it was found that the higher this temperature is, the coarser the grains are. After rolling at 400 ℃, well-defined cells and subgrains were formed, which induced further sites for recrystallization nucleation during subsequent SHT. The recrystallization mechanism was found to be subgrain rotation, with a final grain size smaller than 200 μm. Increasing the rolling temperature to 500 ℃ results in a low density of dislocations distributed uniformly in the deformed matrix and fewer nucleation sites during subsequent SHT. The recrystallization mechanism is grain boundary bulging, while the final grain size approaches several millimeters. Finally, a hot forming process of high-Ti 6061 alloy for inhibiting grain coarsening was proposed, and verified by experiments.     

AZ31镁合金板材复合形变的孪晶组织及晶粒尺寸

研究了复合形变对镁合金AZ31板材性能的影响规律,比较了不同变形齿间比、温度和压下量对镁合金板材微观组织的影响。研究结果表明,在复合变形条件下,随着齿间比的增大,板材孪晶体积分数逐渐减小,平均晶粒尺寸有先减小后增大的趋势。随着压下量的逐渐增大,板材的孪晶体积分数逐渐增大,平均晶粒尺寸也有先减小后增大的趋势。同时过大的压下量容易导致板材断裂。随着变形温度的提高,板材能完成较大的变形量,但是孪晶体积分数逐渐减少,晶粒尺寸先减小后增大。     

ZA27合金的铸态组织及晶界共晶体

研究分析了ＺＡ２７合金（锌－铝合金）的铸态组织及其分布特点。电子探针分析表明ＺＡ２７合金的初生α相和β相晶内偏析十分严重；在电镜下观察可见α相和β相已转变成层片相间的（α＋η）共析体，并从差热分析，微区分析等四个方面着重讨论了ＺＡ２７合金的晶界不平衡组织是共晶体（由α，β，η相组成），而不是共析体。退火处理可以消除晶界不平衡共晶体，并使成分均匀化，从而使ＺＡ２７合金的塑性得到明显提高。     

加载路径对铝合金疲劳位错结构的影响

目的研究铝合金材料在相同等效应力幅、不同非比例加载路径下的多轴疲劳寿命以及疲劳失效试件位错结构,从而明确加载路径对位错结构的影响.方法利用透射电镜分析了不同加载路径下疲劳试样的位错结构特征.结果铝合金多轴非比例加载疲劳寿命变化规律为:圆形路径<正方形路径<矩形路径<椭圆形路径,圆形路径下位错以交叉滑移为典型特征,正方形路径下以单方向的滑移线以及拉长的位错环为典型特征,矩形和椭圆形路径下均以三方向的多滑移为典型结构特征.结论加载路径对疲劳寿命有明显影响,不同加载路径下疲劳试样位错结构不同,质点对位错有较强的钉扎作用,位错以线形平行排列塞积在质点前.     

Al—Cu合金凝固冷却曲线及晶粒组织特征的计算机模拟

利用宏观－微观耦合的模型和热焓法处理结晶潜热,用外节点直接差分法数值计算技术,模拟了Ａｌ－２ｗｔ％Ｃｕ合金凝固过程的冷却曲线和晶粒组织特征,并与实验结果进行了比较。结果表明：冷却速率越大的凝固区域,再辉出现得越早,平台凝固段越短。模拟所得冷却曲线和晶粒组织特征同实测值吻合较好。     

GH4169合金等温条件下晶粒长大数学模型研究

本文研究了GH4169合金在不同加热温度和不同保温时间下的晶粒长大规律.结果表明,晶粒尺寸随着保温时间的增加和加热温度的升高而长大.但该合金晶粒尺寸受温度影响更为显著,当温度高于1050℃时晶粒长大速度明显加快,同时计算了晶粒长大激活能,而且建立了晶粒长大模型.