热处理工艺对工程机械用1000MPa级高强钢组织与性能的影响

对工程机械用1 000MPa级高强钢进行不同温度的淬火和回火热处理,研究了热处理工艺对其力学性能和显微组织的影响,并得到了试验钢较佳的淬火和回火温度。结果表明:随着淬火温度升高,试验钢的强度先增大后降低,并在900℃时达到最大;830℃以下淬火后,组织中存在未溶铁素体,组织为铁素体和板条马氏体;900℃以上淬火后,组织为板条马氏体;随着回火温度的升高,试验钢的强度下降,塑、韧性提高,当回火温度达到450℃以上时,组织转变为回火索氏体,冲击韧性大幅提高;较优的热处理工艺为900℃淬火后在500℃回火。     

S460G1钢特厚板在调质过程中的组织演变与强韧化机制

通过严格控制轧制参数对S460G1钢进行热轧,得到厚度150 mm的特厚板,然后进行870～960℃淬火和550～660℃回火处理,研究了钢板的组织演变和强钢化机制.结果表明:热轧钢板由表面向心部的组织依次为针状铁素体→粒状贝氏体→铁素体+珠光体;淬火后,表面组织主要为板条马氏体,1/4板厚处以粒状贝氏体为主,1/2板...     

等温淬火时间对铁道机车用SAE8620轴承钢接触疲劳性能的影响

将表面渗碳处理的SAE8620轴承钢在855℃奥氏体化后,在225℃盐浴中进行等温淬火处理,再在225℃下进行回火处理,研究了等温淬火时间(7,21 h)对试验钢显微组织、物相组成、硬度和接触疲劳性能的影响。结果表明：等温淬火7 h时试验钢表层组织为贝氏体铁素体、残余奥氏体、马氏体和碳化物,等温淬火21 h后表层组织中的马氏体消失,贝氏体板条平均宽度增加,针状贝氏体铁素体含量增加,残余奥氏体含量减少;与等温淬火21 h相比等温淬火7 h试验钢的表层硬度更大,接触疲劳寿命也更长,这主要与其表层残余奥氏体含量更高、贝氏体板条平均宽度更小、表层硬度更大,可以更好地抵抗塑性变形有关。     

调质工艺对C95石油套管用钢组织的影响

利用光学显微镜(OM)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和电子背散射衍射仪(EBSD)等研究了不同调质工艺对C95级石油套管用钢组织的影响。结果表明:直接淬火后试验钢的奥氏体沿着轧制方向拉长,呈扁平状,再加热淬火后试验钢组织则为等轴状;随着调质回火温度的升高,马氏体板条合并,尺寸变宽,板条边界模糊,同时析出的碳化物也明显粗化,相邻晶粒小角度晶界比例降低;直接淬火试验钢与再加热淬火试验钢相比,其板条更细小、位错密度更高、相邻晶粒小角度晶界比例更高。     

电脉冲调质处理对齿套用35CrMo钢显微组织和 力学性能的影响

在不同回火温度(550～640℃)、不同脉冲次数(1,2次)和脉冲持续时间(60～180ms)下对热轧态35CrMo钢分别进行传统淬火+传统回火、电脉冲淬火+传统回火、传统淬火+电脉冲回火处理,对比研究了处理后的显微组织和力学性能。结果表明:电脉冲淬火+550℃传统回火、传统淬火+1次电脉冲回火以及传统淬火+2次电脉冲60ms回火处理后,试验钢的组织与传统淬火+传统回火处理后的相似,均由马氏体和碳化物组成;随着回火温度的升高,电脉冲淬火+传统回火处理后的组织中出现层片状索氏体,试验钢的抗拉强度和硬度降低,伸长率增大;电脉冲淬火或回火均能提高试验钢的强塑性,电脉冲淬火+580℃传统回火处理后的强塑性最佳。     

不同工艺渗碳淬火和深冷处理后20CrNi2Mo轴承钢的组织与性能

对正火态20CrNi2Mo轴承钢分别进行渗碳油淬+回火、二次渗碳油淬+回火、渗碳气淬+渗碳油淬+回火等3种渗碳淬火+回火处理以及在上述工艺的回火前增加深冷处理的渗碳淬火+深冷+回火处理,研究了不同工艺处理后轴承钢的显微组织、力学性能和耐磨性能。结果表明：渗碳淬火+回火后轴承钢的组织均为针状马氏体+残余奥氏体+碳化物,渗碳气淬+渗碳油淬+回火后的马氏体更细小,残余奥氏体更少,此工艺下轴承钢的硬度、抗拉强度和断后伸长率均高于其他2种渗碳淬火+回火工艺,磨痕宽度和深度较小;与渗碳淬火+回火相比,渗碳淬火+深冷+回火处理后轴承钢中奥氏体含量减少,硬度提高,磨痕宽度和深度减小,并且在200 N载荷下的磨损质量损失明显减少;较优的工艺是渗碳气淬+渗碳油淬+深冷+回火。     

高铬铸铁耐磨球热处理工艺研究

研究了一种添加微量合金元素Mo、V、Nb的高铬铸铁耐磨球的热处理工艺。采用在980℃淬火、400℃和600℃回火的热处理工艺。通过显微组织分析可知淬火后基体组织为淬火马氏体,400℃回火后基体组织为回火托氏体,600℃回火后基体组织为回火索氏体。经硬度分析和耐磨性分析可知：仅淬火处理时试样硬度为65HRC,磨损量也最小;400℃回火后硬度下降为62.8HRC,磨损量比淬火态增加18.2%;600℃回火后硬度下降为57.6HRC,磨损量比淬火态增加30.3%。结合磨球实际应用状态最佳热处理工艺应采用980℃淬火、400℃回火。     

双淬火+深冷处理工艺对Cr12Mo1V1模具钢组织和性能的影响

对退火态Cr12Mo1V1模具钢分别进行一次淬火+回火、双淬火+回火、一次淬火+深冷+回火、双淬火+深冷+回火等工艺处理,其中一次淬火工艺为1 030℃×0.5 h油淬,双淬火工艺为1 050℃×0.5 h油淬+1 030℃×0.5 h油淬,深冷处理工艺为-60℃×1 h+-120℃×1 h,对比研究了双淬火+深冷处理对试验钢显微组织和力学性能的影响。结果表明:与一次淬火+回火工艺相比,双淬火+回火工艺可以改善共晶碳化物分布均匀性,使碳化物形态趋于球状;增加深冷处理对改善共晶碳化物形态和均匀度的效果不明显,但可降低残余奥氏体含量。双淬火+回火工艺处理后试验钢的硬度与一次淬火+回火处理后相近,但冲击吸收能量和抗弯强度分别提升22%和12%;增加深冷处理对试验钢硬度、冲击韧性和抗弯强度影响不大。     

不同淬回火组织GCr15轴承钢球的性能对比分析

对GCr15钢球实施马氏体淬火后常规回火、240℃高温回火和等温贝氏体淬火3种热处理工艺,分别得到常规马氏体、高温回火马氏体和下贝氏体3种组织,试验研究了这3种组织的性能。结果表明,10 mm的GCr15钢球,高温回火马氏体组织与下贝氏体组织的压碎载荷值相当,且明显高于常规马氏体组织的压碎载荷值;下贝氏体组织的抗回火性能明显优于常规马氏体组织的抗回火性能。     

回火工艺对H13模具钢渗氮层的影响

用光学显微镜、扫描电镜及X射线衍射仪等研究了淬火+不同回火工艺处理H13模具钢再经相同气体渗氮处理后的渗层组织,用显微硬度计测试了渗层横截面的硬度,分析了回火工艺对渗氮层的影响.结果表明:经淬火+两次350℃回火的试样再渗氮后渗层较致密,硬度变化较平缓,但渗层厚度低于淬火+两次600℃回火后渗氮试样的;淬火+两次600...     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

活塞销孔加工工艺的改进

我公司于８０年代末引进Aspera公司年产８０万台冰箱（冷柜）压缩机生产线及软件技术，在压缩机加工中，活塞销孔（如图１所示）的加工是难点之一。用镗床加工，质量一直难以达到要求，废品率很高。后来我们将Aspera公司的加工工艺即精镗后滚光改为精镗后用金刚石铰刀粗、精铰孔，由此解决了这个技术难题。（１）原意大利Aspera公司工艺简述其工艺流程为：钻６．５通孔→扩孔至７＋０．１→粗镗７．４７３＋０．０３６、圆柱度０．０１→精镗至７．９３５＋０．００６、圆柱度０．００２→滚光７．９３８＋０．００６、圆柱度０…     

广州地铁APM列车制动机理分析

根据广州市珠江新城旅客自动运输系统(APM)列车的运行特点,介绍APM列车制动系统的制动方式及其特点,分析APM列车动态制动和摩擦制动的工作机理及其区别和联系,阐明APM列车制动系统的电控制过程和气控制过程,从而为APM列车制动系统的维护和管理提供一定的依据.     

盘丝极心偏对三爪自定心卡盘找标精度影响的分析

三爪自定心卡盘作为机床的主要附件,已有一百多年的发展历史,尽管目前随着数控技术的不断发展,越来越多地需求高速动力卡盘,但三爪自定心卡盘目前仍有一定的市场。 要保证卡盘可靠地夹紧工件,必须使其有可靠的夹持精度;要保持卡盘的精度,必须要严格控制各零部件公差及误差,如盘丝的极心偏。 　　极心偏是形成圆的渐开线的基圆圆心 (极心 )与盘丝内孔中心不同心所造成的偏差值。它对卡盘精度的影响分两种情况,一是卡爪夹持弧采用配磨,二是卡爪夹持弧采用单磨。本文主要探讨配磨时的影响。 　　卡爪夹持弧采用配磨,即每台卡盘整体…     

Development of sclerometric method of studying activation of parameters of damage and fracture of friction deformable surfaces

The article presents a brief review of the wear models based on the kinetic thermofluctuation approach. The materials were developed using SamGTU sclerometric programming software and a set of instruments developed at Samara Engineering University for assessing the parameters of kinetic thermoactivation for surface fracture deformed by friction. The first obtained results of assessments and the estimated prediction of wear resistance exemplified by tribocouple of the aircraft chassis are presented.     

圆柱面素线的直线度公差带解析

详细分析了圆柱面素线的直线度公差带在新旧标准中定义和解释的区别，并从对圆柱面素线实际要素检测的角度，提出了推行新标准的实际意义。     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。