增强型AlGaN/GaN高电子迁移率晶体管高温退火研究

深入研究了两种增强型AlGaN/GaN高电子迁移率晶体管(HEMT)高温退火前后的直流特性变化.槽栅增强型AlGaN/GaN HEMT在500 ℃ N₂中退火5 min后,阈值电压由0.12 V正向移动到0.57 V,器件Schottky反向栅漏电流减小一个数量级.F注入增强型AlGaN/GaN HEMT在 400 ℃ N₂中退火2 min后,器件阈值电压由0.23 V负向移动到-0.69 V,栅泄漏电流明显增大.槽栅增强型器件退火过程中Schottky有效势垒     

AlGaN/GaN异质结Ni/Au肖特基表面处理及退火研究

采用O₂等离子体及HF溶液对AlGaN/GaN异质结材料进行表面处理后，Ni/Au肖特基接触特性比未处理有了明显改善，反向泄漏电流减小3个数量级.对制备的肖特基接触进行200—600℃ 5min的N₂气氛退火，发现退火冷却后肖特基反向泄漏电流随退火温度增大进一步减小.N₂气中600℃退火后肖特基二极管C-V特性曲线在不同频率下一致性变好，这表明退火中Ni向材料表面扩散减小了表面陷阱密度；C-V特性曲线随退火温度增大向右移动，从二维电子气耗尽电压绝对值减小反映了肖特基势垒的提高. 关键词： AlGaN/GaN 肖特基接触 表面处理 退火     

基于凹槽结构抑制AlGaN/GaN高电子迁移率晶体管电流崩塌效应

基于双脉冲技术,研究了GaN缓冲层陷阱对AlGaN/GaN高电子迁移率晶体管电流崩塌效应的影响.结果表明,栅边缘漏侧的电场峰值使得沟道电子跃迁至缓冲层,并被缓冲层中的陷阱俘获是造成电流崩塌的主要原因之一.提出了势垒层局部凹槽结构,降低了栅边缘漏侧的电场峰值,使电场分布更加均匀,改善了器件的电流崩塌效应.与传统AlGaN/GaN高电子迁移率晶体管结构相比,新器件结构对电流崩塌效应的抑制作用至少提升了22.30%.     

AlGaN/GaN 高速电子迁移率晶体管器件电流坍塌效应与界面热阻和温度的研究

本文系统研究了AlGaN/GaN基高速电子迁移率晶体管器件界面热阻和工作温度对器件在高功率下的电流坍塌效应的影响规律.研究发现低漏极电压下热电子是导致负微分输出电导的重要因素,器件工作温度变高会使负微分输出电导减小.高漏极电压下自加热效应是导致电流坍塌的一个重要因素.随着界面热阻的增加,器件跨导降低,阈值电压增大.同时,由于工作环境温度的增高,器件随之温度增高,载流子迁移率会显著降低. 最终这两种因素会引起AlGaN/GaN基高速电子迁移率晶体管器件显著的电流坍塌效应,从而降低了器件整体性能. 关键词： AlGaN/GaN HEMT 器件 热电子效应 自加热效应 电流坍塌效应     

AlGaN/GaN 高电子迁移率晶体管漏电流退化机理研究

本文首先制备了与AlGaN/GaN高电子迁移率晶体管 (HEMT) 结构与特性等效的AlGaN/GaN异质结肖特基二极管, 采用步进应力测试比较了不同栅压下器件漏电流的变化情况, 然后基于电流-电压和电容-电压测试验证了退化前后漏电流的传输机理, 并使用失效分析技术光发射显微镜 (EMMI) 观测器件表面的光发射, 研究了漏电流的时间依赖退化机理. 实验结果表明: 在栅压高于某临界值后, 器件漏电流随时间开始增加, 同时伴有较大的噪声. 将极化电场引入电流与电场的依赖关系后, 器件退化前后的 log(I_FT/E)与√E 都遵循良好的线性关系, 表明漏电流均由电子Frenkel-Poole (FP) 发射主导. 退化后 log(I_FT/E)与√E 曲线斜率的减小, 以及利用EMMI在栅边缘直接观察到了与缺陷存在对应关系的“热点”, 证明了漏电流退化的机理是: 高电场在AlGaN层中诱发了新的缺陷, 而缺陷密度的增加导致了FP发射电流I_FT的增加. 关键词： AlGaN/GaN 高电子迁移率晶体管 漏电流 退化机理     

AlGaN/GaN双异质结F注入增强型高电子迁移率晶体管

理论模拟了不同GaN沟道厚度的双异质结(AlGaN/GaN/AlGaN/GaN)材料对高电子迁移率晶体管(HEMT)特性的影响,并模拟了不同F注入剂量下用该材料制作的增强型器件的特性差异.采用双异质结材料,结合F注入工艺成功地研制出了较高正向阈值电压的增强型HEMT器件.实验研究了三种GaN沟道厚度制作的增强型器件直流特性的差异,与模拟结果进行了对比验证.采用降低的F注入等离子体功率,减小了等离子体处理工艺对器件沟道迁移率的损伤,研制出的器件未经高温退火即实现了较高的跨导和饱和电流特性.对14 nm GaN沟道厚度的器件进行了阈值电压温度稳定性和栅泄漏电流的比较研究,并且分析了双异质结器件的漏致势垒降低效应.     

基于脉冲方法的超短栅长GaN基高电子迁移率晶体管陷阱效应机理

陷阱效应导致的电流崩塌是制约GaN基微波功率电子器件性能提高的一个重要因素,研究深能级陷阱行为对材料生长和器件开发具有非常重要的意义.随着器件频率的提升,器件尺寸不断缩小,对小尺寸器件中深能级陷阱的表征变得越发困难.本文制备了超短栅长（L_g=80 nm）的AlGaN/GaN金属氧化物半导体高电子迁移率晶体管（MOSHEMT）,并基于脉冲I-V测试和二维数值瞬态仿真对器件的动态特性进行了深入研究,分析了深能级陷阱对AlGaN/GaN MOSHEMT器件动态特性的影响以及相关陷阱效应的内在物理机制.结果表明,AlGaN/GaN MOSHEMT器件的电流崩塌随着栅极静态偏置电压的增加呈非单调变化趋势,这是由栅漏电注入和热电子注入两种陷阱机制共同作用的结果.根据研究结果推断,可通过改善栅介质的质量以减小栅漏电或提高外延材料质量以减少缺陷密度等措施达到抑制陷阱效应的目的,从而进一步抑制电流崩塌.     

界面处理对AlGaN/GaN MIS-HEMTs器件动态特性的影响

研究不同界面处理对AlGaN/GaN金属-绝缘层-半导体(MIS)结构的高电子迁移率晶体管(HEMT)器件性能的影响。采用N_2和NH_3等离子体对器件界面预处理,实验结果表明,N_2等离子体预处理能够减小器件的电流崩塌,通过对N_2等离子体预处理的时间优化,发现预处理时间10 min能够较好地提高器件的动态特性,30 min时动态性能下降。进一步引入AlN作为栅介质插入层并经过高温热退火后能够有效提高器件的动态性能,将器件的阈值回滞从411 mV减小至111 mV,动态测试表明,在900 V关态应力下,器件的电流崩塌因子从42.04减小至4.76。     

开态应力下电压和电流对AlGaN/GaN高电子迁移率晶体管的退化作用研究

通过采集等功率的两种不同开态直流应力作用下AlGaN/GaN高电子迁移率晶体管(HEMTs)漏源电流输出特性、源区和漏区大信号寄生电阻、转移特性、阈值电压随应力时间的变化, 并使用光发射显微镜观察器件漏电流情况, 研究了开态应力下电压和电流对AlGaN/GaN高电子迁移率晶体管的退化作用. 结果表明, 低电压大电流应力下器件退化很少, 高电压大电流下器件退化较明显. 高电压是HEMTs退化的主要因素, 栅漏之间高电场引起的逆压电效应对参数的永久性退化起决定性作用. 除此之外, 器件表面损坏部位的显微图像表明低电压大电流下器件失效是由于局部电流密度过高, 出现热斑导致器件损伤引起的.     

60Co γ射线辐射对AlGaN/GaN HEMT器件的影响

采用⁶⁰Co γ射线辐射源对非钝化保护的AlGaN/GaN高电子迁移率晶体管(HEMT)器件进行了1 Mrad(Si)的总剂量辐射,实验发现辐射累积剂量越大,器件尺寸越小,器件饱和漏电流和跨导下降越明显,同时辐射后器件栅泄漏电流明显增大,而阈值电压变化很小. 对辐射前后器件的沟道串联电阻和阈值电压变化的分析表明,辐射感生表面态负电荷的产生是造成AlGaN/GaN HEMT器件电特性退化的主要原因之一. 关键词： AlGaN/GaN HEMT器件 γ射线辐射 表面态     

Neutron irradiation effects on A1GaN//GaN high electron mobility transistors

AlGaN/GaN high electron mobility transistors(HEMTs) were exposed to 1 MeV neutron irradiation at a neutron fluence of 1 × 10 15 cm 2.The dc characteristics of the devices,such as the drain saturation current and the maximum transconductance,decreased after neutron irradiation.The gate leakage currents increased obviously after neutron irradiation.However,the rf characteristics,such as the cut-off frequency and the maximum frequency,were hardly affected by neutron irradiation.The AlGaN/GaN heterojunctions have been employed for the better understanding of the degradation mechanism.It is shown in the Hall measurements and capacitance-voltage tests that the mobility and concentration of two-dimensional electron gas(2DEG) decreased after neutron irradiation.There was no evidence of the full-width at half-maximum of X-ray diffraction(XRD) rocking curve changing after irradiation,so the dislocation was not influenced by neutron irradiation.It is concluded that the point defects induced in AlGaN and GaN by neutron irradiation are the dominant mechanisms responsible for performance degradations of AlGaN/GaN HEMT devices.     

Neutron irradiation effects on AlGaN/GaN high electron mobility transistors

AlGaN/GaN high electron mobility transistors (HEMTs) were exposed to 1 MeV neutron irradiation at a neutron fluence of 1 × 10¹⁵ cm^-2. The dc characteristics of the devices, such as the drain saturation current and the maximum transconductance, decreased after neutron irradiation. The gate leakage currents increased obviously after neutron irradiation. However, the rf characteristics, such as the cut-off frequency and the maximum frequency, were hardly affected by neutron irradiation. The AlGaN/GaN heterojunctions have been employed for the better understanding of the degradation mechanism. It is shown in the Hall measurements and capacitance-voltage tests that the mobility and concentration of two-dimensional electron gas (2DEG) decreased after neutron irradiation. There was no evidence of the full-width at half-maximum of X-ray diffraction (XRD) rocking curve changing after irradiation, so the dislocation was not influenced by neutron irradiation. It is concluded that the point defects induced in AlGaN and GaN by neutron irradiation are the dominant mechanisms responsible for performance degradations of AlGaN/GaN HEMT devices.     

中子辐照对AlGaN/GaN高电子迁移率晶体管器件电特性的影响

本文采用能量为1 MeV的中子对SiN钝化的AlGaN/GaN HEMT(高电子迁移率晶体管)器件进行了最高注量为1015cm-2的辐照.实验发现:当注量小于1014cm-2时,器件特性退化很小,其中栅电流有轻微变化(正向栅电流IF增加,反向栅电流IR减小),随着中子注量上升,IR迅速降低.而当注量达到1015cm-2时,在膝点电压附近,器件跨导有所下降.此外,中子辐照后,器件欧姆接触的方块电阻退化很小,而肖特基特性退化却相对明显.通过分析发现辐照在SiN钝化层中引入的感生缺陷引起了膝点电压附近漏电流和反向栅泄漏电流的减小.以上结果也表明,SiN钝化可以有效地抑制中子辐照感生表面态电荷,从而屏蔽了绝大部分的中子辐照影响.这也证明SiN钝化的AlGaN/GaN HEMT器件很适合在太空等需要抗位移损伤的环境中应用.     

Influence of Schottky drain contacts on the strained AlGaN barrier layer of AlGaN/AlN/GaN heterostructure field-effect transistors

Rectangular Schottky drain AlGaN/AlN/GaN heterostructure field-effect transistors (HFETs) with different gate contact areas and conventional AlGaN/AlN/GaN HFETs as control were both fabricated with same size. It was found there is a significant difference between Schottky drain AlGaN/AlN/GaN HFETs and the control group both in drain series resistance and in two-dimensional electron gas (2DEG) electron mobility in the gate-drain channel. We attribute this to the different influence of Ohmic drain contacts and Schottky drain contacts on the strained AlGaN barrier layer. For conventional AlGaN/AlN/GaN HFETs, annealing drain Ohmic contacts gives rise to a strain variation in the AlGaN barrier layer between the gate contacts and the drain contacts, and results in strong polarization Coulomb field scattering in this region. In Schottky drain AlGaN/AlN/GaN HFETs, the strain in the AlGaN barrier layer is distributed more regularly.     

Impact of oxygen in electrical properties and hot-carrier stress-induced degradation of GaN high electron mobility transistors

The role of the oxygen in AlGaN/GaN high electron mobility transistors (HEMTs) before and after semi-on state stress was discussed. Comparing with the electrical characteristics of the devices in vacuum, air, and oxygen atmosphere, it is revealed that the oxygen has significant influence on the electric characteristics and the hot-carrier-stress-induced degradation of the device. Comparing with the situation in vacuum, the gate leakage increased an order of magnitude in oxygen and air atmosphere. Double gate structure was used to separate the barrier leakage and surface leakage of AlGaN/GaN HEMT it is found that surface leakage is the major influencing factor in gate leakage of SiN-passivated devices before and after semi-on state stress. During semi-on state stress in the oxygen atmosphere, the electric-field-driven oxidation process promoted the oxidation of the nitride layer, and the oxidation layer in the SiN/AlGaN interface leads to the decreasing of the surface leakage.     

Determination of the series resistance under the Schottky contacts of AlGaN/AlN/GaN Schottky barrier diodes

Rectangular AlGaN/AlN/GaN heterostructure field-effect transistors (HFETs) were fabricated, and the gate and the source of the HFETs consisted of AlGaN/AlN/GaN Schottky barrier diodes (SBDs). Based on the measured forward current-voltage and the capacitance-voltage characteristics of the AlGaN/AlN/GaN SBDs, the series resistance under the Schottky contacts (R_S) was calculated using the method of power consumption, which has been proved to be valid. Finally, the method of power consumption for calculating R_S was successfully used to study the two-dimensional electron gas electron mobility for a series of circular AlGaN/AlN/GaN SBDs. It is shown that the series resistance under the Schottky contacts cannot be neglected and is important for analysing and characterizing the AlGaN/AlN/GaN SBDs and the AlGaN/AlN/GaN HFETs.