压力注胶对硅烷接枝Ni/CFRP粘接的影响

针对复合材料(Carbon fibre reinforced plastics, CFRP)叶片镍包边粘接强度不足,稳定性不高的问题,提出压力注胶强化KH550接枝Ni/CFRP粘接方法。通过气缸压力推动注胶活塞,将胶粘剂注入密封处理后的待粘接区域,完成充填后在压力作用下实现初步固化粘合,以增强Ni/CFRP的粘接性能。通过单搭接剪切试验测试试样剪切强度,利用扫描电子显微镜(Scanning electronmicroscope,SEM)、X射线能谱(X-rayenergyspectroscopy,EDS)和傅里叶红外光谱(Fouriertransforminfrared spectroscopy, FTIR)表征镍板表面和粘接界面的形貌变化和化学成分变化,采用分子动力学方法分析压力作用对粘接界面分子间化学反应的影响。结果表明,1%KH550接枝处理可提高Ni/CFRP粘接试样剪切强度15.7%,压力注胶工艺可进一步提升剪切强度4.8%,提升粘接稳定性29.3%。压力作用有效减少气泡、胶层裂纹的产生,促进胶粘剂微结构渗透,减小界面处胶粘剂/偶联剂分子距离,增强界面相互作用,同时促进胶粘...     

精密仪表用铝合金瓷质阳极氧化表面粘接性能研究

铝合金瓷质阳极氧化工艺是精密仪表制造中的一种特殊且关键的技术应用，但该氧化表面的胶粘连接常常出现脱粘、泄漏等失效问题。为此，通过探究瓷质阳极氧化表面的微纳形貌与润湿性特征以及高低温下的胶接强度与失效模式，并与自然氧化表面及磷酸阳极氧化表面进行对比分析，阐明瓷质阳极氧化表面胶接失效的影响机理。结果表明，磷酸阳极氧化虽未在微米尺度上显著改变表面粗糙度，但其纳米级多孔氧化膜结构，可显著提高表面润湿性与界面粘接作用力；而瓷质阳极氧化膜在50 000×的SEM形貌下较为致密、平滑，显示出不利于胶粘剂润湿与吸附的物理特征；在-30～80℃下，温度与氧化方法均对胶接强度影响显著，胶接强度随着温度的升高而降低；磷酸阳极氧化表面的强度最高(36.75～20.54 MPa)，其次为自然氧化，最差为瓷质阳极氧化(24.79～17.10 MPa)。热红外与能谱分析表明，瓷质阳极氧化表面的粘附强度低于胶粘剂的内聚强度，失效模式为粘附失效，而磷酸阳极氧化表面的失效模式为胶粘剂的内聚失效。因此，瓷质阳极氧化表面由于氧化膜的致密性，缺少类似磷酸阳极氧化膜的纳米级多孔结构，不利于表面润湿吸附，降低了胶粘剂与基底表面的机...     

阳极化处理对铝箔网与树脂基复合材料粘接性能的影响

采用磷酸阳极化工艺对铝箔网进行了表面处理,研究了阳极化工艺参数对其与树脂基复合材料粘接性能的影响,并对优化后工艺处理的铝箔网表面形貌及粘接性能进行了分析。结果表明:最佳工艺参数的去氧化时磷酸体积分数为16%,处理时间为6min,氧化时磷酸体积分数为16%,处理时间为23min;磷酸阳极化后,铝箔网表面生成一层疏松多孔的氧化膜,可以增大铝箔网表面与复合材料的粘接界面面积,并有良好的界面效应,有效地提高了粘接强度,与处理前的抗拉剪强度相比,提高了14.66%;同时铝箔网的耐蚀性也得到了较大提高。     

阳极化处理对铝合金表面粘接性能的影响

对铝合金进行了磷酸阳极化处理,测试了阳极化各阶段铝合金的力学性能和粘接性能,考察了阳极化铝合金粘接副在不同环境下的拉剪强度及其耐久性。结果表明：阳极化处理对铝合金力学性能影响较小;阳极化后铝合金的粘接性能大幅度提高,与铝合金粘接时拉剪强度提高了238％,与复合材料粘接时拉剪强度提高了近1049／6。阳极化铝合金粘接副具有较好的耐候性,经过100h碱液浸泡后,铝合金／铝合金粘接副的拉剪强度降低了8．1％,经过60d的室外放置后,铝合金／复合材料粘接副的拉剪强度基本保持不变;楔形试验结果表明阳极化铝合金粘接副具有较佳的耐久性,水分存在会加速楔形试样的失效。     

不锈钢阳极氧化

一、工艺参数: 介质:20～30%硫酸 0.1%钼酸钠;电流密度:10～20毫安/厘米~2;处理时间:10～20分钟;处理温度:室温;阳极:不锈钢;阴极:铅板。二、处理效果: 1.阳极氧化处理后的不锈钢,其显著的特点是大大地提高了它的耐蚀性。例如1Cr18Ni9Ti钢在沸腾的5%硫酸中是不耐蚀的,腐蚀速率大于10毫米/年。我们将该钢种试样进行阳极氧化处理后,在同样的条件下经过805小时试验后仍未发生腐蚀,试样表面仍光亮如新。图1表示阳极氧化处理后的1Cr18Ni9Ti钢和未经阳极氧化处理的1Cr18Ni12Mo2钢在各种浓度的硫酸中的耐蚀性。图2表示阳极氧化和未经阳极氧化的1Cr18Ni9Ti钢在硫酸中的腐蚀速率。     

磷酸阳极化工艺对铝合金粘接质量的影响

针对航空用2024铝合金单搭接头胶接修补试验件进行了二维有限元粘接模型的模拟计算,利用标准力学性能试验进行了有效性的验证,并在此基础上,对比论证了磷酸阳极化表面处理工艺对粘接质量的影响。对比论证结果表明:裸铝合金板材粘接质量差,强度低,破坏形式不理想;经磷酸阳极化处理后的铝合金板材粘接表面变得粗糙,浸润效果显著,去除了氧化物等松散结构,有效提高了边界层的强度,改善了铝合金的表面活性,促进了粘接过程中化学键的形成,使得粘接质量明显提升,强度趋于理想值,破坏形式更为合理。所得结果对铝合金粘接修补工艺及粘接质量优化具有指导意义。     

不同胶接参数对CFRP层合板单搭胶接结构强度的影响及优化设计

对于碳纤维增强基复合材料(Carbon fibre-reinforced polymer,CFRP)层合板单搭胶接结构的优化问题,首先利用连续损伤力学模型、三维Hashin准则和内聚力模型研究不同胶接参数对CFRP层压板单搭胶接结构力学性能的影响,其次采用拉丁超立方试验设计方法和响应面法构建了拉伸强度代理模型,最后基于遗传算法和代理模型进行联合优化.结果 表明,仿真与试验吻合较好,数值结果与试验结果的误差均低于10％,验证了有限元模型的精确性.随着搭接长度的增大,拉伸强度和层合板层间分层损伤程度逐渐增大,剪切强度和胶层自身剪切失效程度逐渐减小;胶接结构的力学性能及失效形式随着铺层方式的不同而改变.最佳铺层顺序、胶接长度、胶层厚度和搭接宽度分别为[03/903]2s、20 mm、0.0607 mm和10 mm.与常规单搭胶接结构相比,拉伸强度和剪切强度分别提高了25.92％和25.88％.采用遗传算法对CFRP层合板单搭胶接结构进行优化,对提高单搭接接头的力学性能具有重要意义.     

激光烧蚀铝合金表面对其胶接接头耐腐蚀性能的影响

采用激光对5052铝合金进行表面烧蚀处理,对其表面物化特性进行观察分析,并测试了其胶接接头在盐雾环境腐蚀后的剪切强度与失效模式。实验结果发现,经激光表面处理后,接头的剩余强度在盐雾环境腐蚀后强度增大了40%,并且失效模式由几乎完全界面失效变成内聚失效。经分析测量,处理后的铝合金表面粗糙度从0.09μm增大到1.77μm,并且在其表面形成了凹凸不平的多孔结构,胶接时发现胶粘剂渗入其中增强了胶接界面的粘接;同时,经过表面元素能谱分析,发现氧元素含量增加,铝合金表面生成氧化铝,也有利于增强铝合金基体的抗腐蚀性能,证明激光表面处理可以提高胶接接头的耐腐蚀性能。      

254—2铜粉导电胶

264-2铜粉导电胶,性能稳定,效果良好,经济效益显著。一、基本性能 1.电性能:体积电阻率为10~(-3)10~(-4)欧·厘米,在-20～80℃范围内无明显变化。 2.机械性能:硬铝与硬铝粘接时,其粘接表面经砂纸打毛或经化学处理后,剪切强度≥100千克力/厘米~2(-60～60℃);如仅用酒精等溶剂除油处理,其剪切强度为≥30千克力/厘米~2。其不均匀扯离强度为≥10千克力/厘米~2。二、工艺性能 1.状态:甲组分为棕红色糊状物,乙组分为淡黄色液体,甲、乙混合后,为浆糊状。     

T700和T300碳纤维增强环氧树脂基复合材料耐湿热老化性能的对比

在温度为70℃、相对湿度为85%的湿热环境下,分别对T700碳纤维/环氧树脂基复合材料、T300碳纤维/环氧树脂基复合材料以及两种复合材料/金属胶接结构进行了70 d的加速老化试验,并对老化前后的试样进行了力学性能试验和无损检测.结果表明:湿热环境没有改变两种复合材料的破坏模式,但使复合材料的纵、横向压缩强度和剪切强度略有降低;对复合材料/金属胶接结构,湿热老化环境不会导致胶接界面产生损伤,但会使胶接强度下降;老化前两种复合材料的力学性能基本相当,老化70 d后T700碳纤维/环氧树脂基复合材料的性能保持率略优.     

High strain rate compression of titanium and some titanium alloys

A modified Hopkinson bar was used to compress specimens of commercially-pure titanium, IMI 125 and titanium alloys, AMS 4911B and AMS 4916B, at natural strain rates of between 3 × 10³ s⁻¹ and 3 × 10⁴ s⁻¹. All three materials deformed in a viscous manner with a linear increase of flow stress with strain rate and a macroscopic viscosity of 4·5 kPa s, 5·7 kPa s and 9·2 kPa s, respectively. At strain rates above about 1 × 10⁴ s⁻¹ there was a decrease in macroscopic viscosities to 0·9 kPa s and 2·5 kPa s for the titanium and 4911B alloy respectively, which is attributed to changes in the dislocation drag mechanisms. The results for the 4916B alloy at the higher strain rates were too scattered to give a definite trend. It is suggested that the increase in the macroscopic viscosity with alloying is due to an increase in the dislocation drag coefficient by solution hardening and to a reduction in the density of mobile dislocations by dislocation pinning.

It is also proposed that the susceptibility of these materials to catastrophic shear failure which occurs without prior linear work-softening is due to the higher propensity for titanium and titanium alloys to shear failure as a consequence of their thermo-mechanical properties. The decrease of strain at which shear occurred with increasing strength is in accord with this suggestion.     

形变时效改善超高强度钢应力腐蚀抗力的研究

本文对比了15CrMnMoV低碳马氏体型高强度钢的形变时效处理和三种中碳马氏体型超高强度钢40iMnCrNiMoV（300M）,45CrMnMoV（D6AC）和28Cr3SiMnCrNiMoWV（28Cr3）常规热处理的强韧化效果。同时其回火脆性和低温韧性也得到显著改善。SEM、TEM和织构反极图分析结果发现,15CrMnMoV钢形变时效除综合利用了固溶、马氏体相变、时效和加工硬化因素外,强烈板织构形成的大量潜在解理面具有异常突出的强韧化作用。这是使15CrMnMoV钢的强韧性,特别是水质应力腐蚀断裂门槛值远高于同等强度水平的300M、D6AC和28Cr3的主要原因。冷轧后的时效虽强化效果不大,但韧化作用很显著。     

The effect of different nanoparticles and open time on bonding strength of poly (vinyl acetate) adhesive

Nanotechnology is one of the major technologies through in this century. Nano particles are an important part of this technology. Properties of many traditional materials can be changed by using the nanoparticles. Open time is one of key processing parameters for adhesive applications. Many adhesion failures are caused by exceeding of the open time. The main objective of this study is to improve the adhesion performance of PVAc adhesive by increasing open time through application of nanoparticles, specifically silicium dioxide (SiO₂) and titanium dioxide (TiO₂). For this reason, nano SiO₂ and nano TiO₂ were blended with PVAc at the open time 0, 5, 10 and 15 min. Effect of the nanoparticles and open time was determined by lap shear joint strength tests. Tests were carried out according to DIN EN 302-1. The results indicate that nanoparticles can considerably improve the bonding strength of PVAc at open-time of 5 and 10 min.     

一次热带低压“弱回波”的短时强降水特征分析

使用常规天气、自动站、3D云图、单站雷达回波、Web GIS雷达拼图和风廓线雷达等资料,采用统计、对比分析和特征提取等方法,对影响江西宜春的2013年第7号强台风"苏力"(热带低压)短时强降水进行分析。结果表明:①"苏力"(热带低压)短时强降水期间,宜春处于低压中心偏东,并受台风眼南侧大片云系影响,螺旋雨带自北向南气旋式移动,强降水中心也表现为自西北向东南方移动特征。②0714过程表现为"弱回波"特征,回波结构紧密,呈带絮状,回波强度只有35~45dBz。③短时强降水影响前后,单站气象要素表现为温度平稳,湿度饱和,气压较低且随强降水产生而平缓上升,2min平均风速较小,强降水期间出现风向切变,具有典型暴雨特点,降水持续时间较长,并伴随超短时强降水出现。④"苏力"台风低压在短时强降水影响期,风廓线雷达产品水平风向风速上,高层为西北风,低层为西南风,整体风速均匀,为大范围12~20m/s的风区,并探底到600m高度,高低层存在风向风速垂直切变,但切变强度要小于其他强对流天气;径向速度为正速度,最大达8m/s,出现在最强雨强阶段;速度谱宽高低层中大小值交替出现;信噪比SNR达60~70dB;垂直风速受雨滴末速度影响,达到8m/s;大气折射率结构常数C2n因台风系统降水雨滴大和雨滴数量密集而表现出极大值-15~-14m-2/3。     

仿树蛙足垫粘性材料制备及其粘附性能

利用MEMS加工技术制备了表面具有柔性阵列结构的仿生粘性材料,并选取钛板、铝板、有机玻璃板碧。接磐妻;进行了粘附性能测试。实测结果表明：材料表面微观结构、材料自身性能、接触表面形貌对材料的粘附性能均有影响,粘性材料在钛板表面的法向粘附强度可达5．93×10^-2N／mm^2。     

基于ABAQUS的切削钛合金的数值模拟分析

基于ABAQUS仿真软件,模拟了切削加工钛合金TC4(Ti6Al4V)的过程。预测出切屑的形状和剪切角的大小,验证了通过剪切失效和单元删除模型实现切屑分离符合切削理论。     

铬（Ⅵ）-鲁米诺-过氧化氢流动注射化学发光法测定对苯二酚

基于对苯二酚与铬（Ⅵ）的还原反应产生的铬（Ⅲ）催化鲁米诺-过氧化氢的化学发光,建立了一种快速测定对苯二酚的新方法。该方法线性范围为6.0×10-9～8.0×10-6 mol/L,检出限为1.0×10-10 mol/L。对1.5×10-6 mol/L扑热息痛平行测定8次,其标准偏差为3.1%。该法用于废水中对苯二酚含量的测定,结果令人满意。     

高效液相色谱法测定寡肽LT58的含量及其有关物质

建立寡肽LT58含量测定和有关物质检查的方法。采用Diamonsil C18（4.6mm×250mm,5μm）色谱法；以0.1mol/L磷酸二氢钠（用稀磷酸调节pH至2.96）-甲醇-乙腈（75：15：10）为流动相；柱温为40℃；流速为1.0mL/min；检测波长为210nm。在该色谱条件下，LT58与有关物质能够得到很好的分离，分离度大于1.5,理论板数按LT58计大于5000；     

快速溶剂萃取-高效液相色谱法测定鸡肉中磺胺类药物残留

目的利用快速溶剂萃取（ASE）,反相高效液相色谱-紫外检测技术,建立了鸡肉中5种磺胺类药物残留的定量分析方法。方法选择乙腈作为萃取溶剂,优化了快速溶剂萃取法的条件,快速溶剂萃取仪在l0.0MPa、120℃条件下萃取10 min,萃取液经正己烷去脂净化,减压干燥后用流动相溶解定容。选择C18分析柱,体积比为25∶2∶73的乙腈-乙酸-水溶液作为流动相,在柱温为30℃,流动相流速为1.0 mL/min,进样量为10μL,于268nm波长处,用紫外检测器检测,外标法定量。结果当添加水平为500μg/kg时,鸡肉中5种磺胺类药物的加标回收率在86.0%～101.7%,加标回收率的相对标准偏差在3.1%～4.3%（n=5）,检出限为3～9μg/kg。     

多级时效对新型高强铸造铝合金组织和性能的影响

本文主要讨论多级时效工艺对新型高强铸造铝合金微观组织和力学性能的影响。试验结果表明：在100℃×10 h＋120℃×10 h＋140℃×25 h多级时效条件下,该新型合金的性能相当稳定,平均抗拉强度σb=485 MPa、延伸率5δ=8.4%。