Ag/SBA-15材料的制备及其CO催化氧化性能研究

采用2种不同方法将金属Ag浸渍在SBA-15上制备Ag/SBA-15复合材料,通过SEM、UV-Vis、XRD对Ag/SBA-15复合材料进行表征,并对Ag/SBA-15进行CO气体催化氧化实验,评价Ag/SBA-15复合材料的催化性能。结果表明,去除模板剂后浸渍合成的Ag/SBA-15的催化性能较好,其中金属负载量为1%的产品催化性能最好,催化所需的温度最低,CO转化率最高。     

MCM-41和SBA-15动态吸附VOCs特性和穿透模型

采用模板剂法制备了具有规整孔道的MCM-41和SBA-15介孔分子筛,考察了两种介孔分子筛动态吸附甲苯、邻二甲苯、均三甲苯的特性.结果表明,MCM-41平均孔径小,孔壁叠加作用力强,更适合吸附中、低浓度的VOCs,对芳烃类VOCs为典型的I型吸附等温线;SBA-15具有微孔和介孔共存的特点,平均孔径大,对大分子和高浓度...     

NiY/MCM-41催化剂的制备及催化氧化脱硫研究

采用后合成法制备复合分子筛Y/MCM-41,并以其为载体,用活性组分硝酸镍对其改性,制备Ni-Y/MCM-41催化剂,并利用XRD、BET、N2吸附-脱附对其进行表征。结果表明,复合分子筛同时具有微孔分子筛Y沸石和介孔材料MCM-41分子筛的特征。以硫质量分数为300μg/g的模拟油进行催化氧化脱硫实验,考察了Ni离子的负载量、反应温度、反应时间、催化剂用量、氧化剂用量等工艺条件对脱硫率的影响。结果表明:硝酸镍的负载量为10%,模拟油用量为20 m L,反应温度为70℃,反应时间为80 min,剂油比(催化剂与模拟油的质量比)为1∶70,V(H2O2)/V(油)=0.03时,脱硫率可达86.53%。     

MPc/SBA-15负载型催化剂催化氧化巯基乙醇

采用浸渍法制备了α-八异戊氧基酞菁铜(锌、镍、钴)/SBA-15(α-PcCu/SBA-15,α-PcZn/SBA-15,α-PcNi/SBA-15,α-PcCo/SBA-15)4种SBA-15负载型金属酞菁催化剂.在可见光照射下,研究了溶液的pH值、催化剂中心金属离子、催化剂用量、温度等因素对催化氧化巯基乙醇的影响,...     

环己烷催化氧化制环己酮的MCM-41催化剂研究

以十六烷基三甲基溴化铵为模板剂,正硅酸乙酯为硅源,采用水热合成法制备纯MCM-41分子筛和掺杂不同金属离子的MCM-41分子筛,并采用等体积浸渍法将一定量的金属离子负载在纯MCM-41分子筛内表面上,制备了负载型和掺杂型2类不同的MCM-41分子筛催化剂.分别考察了负载和掺杂的金属种类、金属Cr负载和掺杂量等对环己烷氧化制环己酮中的催化活性和选择性的影响.研究表明:采用掺杂制备的MCM-41分子筛催化剂活性明显高于负载型MCM-41分子筛催化剂;Cr掺杂量增加,虽然环己烷氧化转化率增加,但产物选择性下降;掺杂Cr的MCM-41分子筛催化剂,用于环己烷氧化制环己酮,在Si与Cr摩尔比为50以下、反应温度75℃、H2O2与环己烷摩尔比为1.2的条件下,环己烷的转化率可达60%左右,环己酮和环己醇的总选择性可达94%以上.     

V/SBA-15的制备及催化氧化性能研究

以柠檬酸处理过的偏钒酸铵为钒源,采用后合成法制备出了V/SBA-15负载型催化剂,研究其在氧化苯乙烯制苯甲醛反应中的催化性能.结果表明,在钒负载量低于15％时,V/SBA-15仍保持SBA-15的高度有序的二维六方孔道结构,且具有较大的比表面积和孔体积,负载的活性组分金属钒氧化物均匀分布在介孔分子筛表面;在优化条件下催化氧化苯乙烯制苯甲醛,苯乙烯转化率达65.62％,苯甲醛的选择性81.21％,且V/SBA-15具有较好的催化剂稳定性.     

Mn/Al-SBA-15催化剂的制备及其催化氧化甲苯的性能研究

以凹凸棒土为原料,采用原位晶化法制备Al-SBA-15分子筛,负载Mn制备出一系列Mn/Al-SBA-15催化剂,利用XRD、SEM、TEM、H₂-TPR等表征催化剂物化性质,并考察了催化剂催化氧化甲苯性能。结果表明,Al的掺杂能够使Mn活性物种在Al-SBA-15分子筛表面与孔道中高度分散,进一步提升催化剂氧化还原能力。Mn元素质量分数为8%时,催化剂活性最佳,当甲苯浓度为2 000 ppm、空速为60 000 mL/（g·h）时,8%Mn/Al-SBA-15能够将甲苯的T₅₀和T₉₀分别降至201℃和278℃;8%Mn/SBA-15能够将甲苯的T₅₀和T₉₀分别降至223℃和298℃。     

复合氧化物催化剂催化氧化甲苯性能

以γ-Al2O3为催化剂载体,铜、锰为活性组分,稀土元素铈为助催化剂,采用浸渍法制备复合氧化物催化剂5%Cu/γ-Al2O3、5%Mn/γ-Al2O3、5%Cu-5%Mn/γ-Al2O3和5%Cu-5%Mn-1.6%Ce/γ-Al2O3,并考察其催化氧化甲苯性能。研究表明,复合氧化物催化剂催化氧化甲苯具有显著的效果,5%Cu-5%Mn/γ-Al2O3催化剂和5%Cu-5%Mn-1.6%Ce/γ-Al2O3催化剂表现出良好的低温活性和催化性能,对甲苯的完全燃烧温度分别为340℃和285℃。采用SEM和BET对催化剂进行表征,结果表明,催化剂的催化活性与活性组分在催化剂表面的分散度和催化剂的孔结构相关。     

Sn修饰SBA-15、MCM-41催化剂的制备及顺酐酯化性能

以SBA-15和MCM-41分子筛为载体,负载无水四氯化锡,制备了SnCl4-SBA-15和SnCl4-MCM-41催化剂,考察了不同锡与硅物质的量比对催化顺酐与正丁醇酯化反应的影响。结果表明,SnCl4-SBA-15表现出比SnCl4-MCM-41更高的催化性能,顺酐转化率为99.8%,副产物较少,马来酸二丁酯的产率最高可达91.3%。采用X射线衍射、N₂物理吸附、傅立叶红外光谱和紫外-可见漫反射技术对催化剂进行表征,结果显示, SnCl₄-SBA-15具有较高的比表面积,较大的孔容和孔径,更有利于催化反应的进行。     

高分散的Ir/SBA-15的制备及其催化性能

采用一锅法将P123、TEOS、HCl和H2IrCl6溶液混合,酸性条件下得到高度分散的Ir/SBA-15催化剂.使用X射线衍射、透射电镜和N2吸附-脱附等对样品进行表征.结果表明,一步合成的Ir/SBA-15依然保持高度有序的介孔孔道结构、较大比表面积和孔容,而且Ir在SBA-15孔道内高度分散.CO的催化氧化反应结...     

Extraction of Ultra Trace Amounts of Palladium on 9-Acridinylamine Functionalized SBA-15 and MCM-41 Nanoporous Silica Sorbents

The application of the modified MCM-41 and SBA-15 nanporous silicas in extraction of trace amounts of palladium is investigated and developed. Surface of nanoporous silicas, MCM-41 and SBA-15, were modified with 9-acridinylamine ligand and then utilized as solid-phase sorbents for the extraction of palladium. Different experimental conditions such as pH, flow rates of the sample, and eluent solution were studied. The type and the smallest amount of eluent for elution were optimized and the breakthrough volume and the influence of various cationic interferences on the adsorption was investigated. The recovery values in this method are greater than 95% and 98.5%. The obtained limits of detections (LOD) are lower than 0.17 ng mL^?1 and 0.15 ng mL^?1 for SBA-15 and MCM-41, respectively. The pre-concentration factors were calculated to be more than 193 and 187.5 for SBA-15 and MCM-41, respectively. The relative standard deviations (RSD) of the method are lower than 4% and 1.5%, and the adsorption capacities were also obtained to be more than 170 mg g^?1 and 195 mg g^?1 for SBA-15 and MCM-41, respectively. The proposed procedure was applied on real samples and the amount of palladium was successfully derived.     

Catalytic aerobic oxidation of ethylbenzene over Co/SBA-15

Co(II)O was highly dispersed in the mesopores of SBA-15 by alcoholic impregnation method and characterized by XRD, TEM, UV–VIS DRS, TPR, and XRF techniques. It was found that tetrahedral coordinated Co(II)O was stabilized by SBA-15 at low Co-loading. Co/SBA-15 showed much higher activity than Co(OAc)₂ or Co₃O₄ in the liquid-phase aerobic oxidation of ethylbenzene under solvent-free condition.     

SBA -15负载铁基氧化物催化剂上丙烷选择氧化催化性能的研究

用等体积浸渍法制备了SBA - 15负载铁基和钾修饰的Fe基氧化物催化剂,使用紫外-拉曼光谱对催化剂结构进行表征,并评价催化剂对丙烷的选择氧化活性与选择性.结果表明,介孔结构SBA - 15对丙烷选择氧化活性优于常规的SiO2;对于负载K- Fe/SBA - 15系列催化剂,低Fe负载量时,隔离的四配位Fe氧化物是丙烷...     

用于氧化反应的改性介孔分子筛MCM-41研究进展

主要从金属掺杂、杂多酸负载和有机官能化等方面详细介绍了改性的MCM-41分子筛作为催化剂在氧化反应中的应用情况,分析了其优缺点。今后的研究重点将是进一步提高改性材料MCM-41分子筛的活性,解决活性组分溶脱现象以及水热稳定性等问题。     

Y-Beta/MCM-41复合分子筛的合成和性能

在酸性水热条件下,通过附晶生长法合成Y-Beta/MCM-41复合分子筛,并对其结构、形貌、水热稳定性及催化性能进行研究。结果表明,合成的Y-Beta/MCM-41复合分子筛比表面积高和水热稳定性好,对α-甲基萘的催化裂解性能明显优于机械混合物,表现出良好的催化性能。     

分子筛SBA-15对有机气体的吸附-脱附性能

以聚乙二醇-聚丙三醇-聚乙二醇为模板剂,正硅酸乙酯为硅源,在不同晶化温度下制备了比表面积和晶化不同的SBA-15介孔分子筛,用穿透曲线和程序升温脱附考察了分子筛对甲苯和乙酸乙酯的吸脱附性能。实验结果表明,随着晶化温度从80 ℃升高到135 ℃,SBA-15分子筛对有机气体吸附量减少,脱附温度降低。通过比较发现,分子筛对甲苯的吸附容量比对乙酸乙酯的吸附容量小,SBA-15分子筛呈现亲乙酸乙酯和憎甲苯的性能。     

W、Mn和Ce改性V-MCM-41/堇青石催化剂的制备及其脱硝性能

以采用水热法合成的介孔分子筛MCM-41为栽体,V为主催化剂,添加W、Mn和Ce等助剂,通过涂覆法在蜂窝堇青石(CC)上涂覆制备催化剂,考察助剂对V-MCM-41催化剂采用尿素选择性催化还原NO性能的影响.结果表明,W和Mn能提高催化剂的低温活性,Ce能促进催化剂的高温活性.制备的催化剂V-W-Mn-Ce-MCM-41...