增韧剂对环氧树脂/酚醛胺体系力学性能的影响

用Q S-2增韧剂、聚硫橡胶、液体丁睛橡胶增韧环氧-改性胺固化物,通过对其剪切强度、弯曲强度和弯曲弹性模量及扫描电镜照片的对比,可以看出选用合适的复合增韧剂对环氧树脂固化物体系的力学性能有着显著影响。     

端氨基丁腈橡胶增韧环氧-聚酰胺胶粘剂的研究

通过DSC,扫描电镜分析及剪切和剥离强度性能测试研究了端氨基液体丁腈橡胶(ATBN)改性环氧-聚酰胺体系的固化动力学,粘接性能及增韧相态。结果表明,根据Ellerstein法和峰值法计算得到的固化反应活化能分别为为73.6 kJ/mol和65.7 kJ/mol,体系最佳固化温度为41～97℃。固化体系中橡胶相粒径大小对胶粘剂性能有较大影响,60℃和室温固化体系分散相粒子平均粒径分别为1～2μm,0.5μm。粒径1～2μm时体系的增韧效果最佳,粘接性能优异。     

增韧剂对干式变压器用环氧浇注料性能的影响

通过力学性能、热性能、电性能测试及电镜分析研究了自制改性增韧剂对干式变压器用环氧浇注料性能的影响.结果 表明,增韧剂用量为树脂质量的15％时,固化体系的力学性能最好.增韧剂加入量增大,固化体系的玻璃化温度降低,表面电阻、体积电阻率略有下降,介质损耗因子明显升高.     

环氧-低分子聚酰胺-银粉导电胶体系研究

本文着重从银粉的粒度、添加量和固化剂的种类、用量以及固化条件等方面研究和探讨了环氧-低分子聚酰胺-银粉导电胶体系的导电性及强度。     

新型聚酰胺/环氧固化体系性能的研究

采用部分国产多元胺替代进口多元胺研制出新型低粘度、低分子质量聚酰胺系列固化剂。通过热失重(Tg)、FT-IR及力学性能等分析方法研究其与环氧树脂E-51固化体系的性能。结果表明该类聚酰胺固化剂具有较普通聚酰胺固化剂粘度低、粘接强度大、韧性大及耐热性好等优点。     

环氧-酚醛胺体系的增韧研究

在环氧-酚醛胺体系中使用端环氧基聚氨酯醚、聚硫橡胶、液体丁腈橡胶等活性增韧剂,通过对固化物剪切强度、弯曲弹性模量及断裂强度的测试对比,可以看出不同增韧剂效果不同。相比较而言,端环氧基聚氨酯醚海岛结构增韧剂的综合性能较好。     

一种中温固化高强度环氧胶粘剂的研制

以E-51、E-44为主体树脂,加入奇士增韧剂研制出一种中温固化高强度环氧胶粘剂.该胶粘剂在加入占粘料质量分数30%左右的增韧剂后,选用自制固化剂SL-1,在50 ℃×1 h+80 ℃×1 h条件下固化,其拉伸剪切强度可达42.1 MPa.     

端羧酸丁腈橡胶环氧基酯增韧剂的合成与应用

采用端羧酸丁腈橡胶(CTBN)来合成1种新型的CTBN环氧基酯增韧剂。介绍了该增韧剂的合成工艺路线和条件。并通过应用实例阐述了该增韧剂在环氧固化体系中的应用效果。结果表明:加入一定量的催化剂可有效地提高酯化反应的速率;该增韧剂对环氧树脂固化体系有显著增韧效果。     

新型环氧树脂增韧剂的合成与研究

以聚醚和酸酐反应，再与环氧树脂反应，合成了一种新型的以环氧基封端的内增韧活性增韧剂，讨论了该增韧剂的固化特性和最佳掺合比例，在100份环氧树脂中加入10份这种增韧剂，环氧树脂固化物综合力学性能较好，剪切强度为23．6MPa，压缩强度达70．2Mpa。     

新型增韧剂在建筑结构胶中的应用

一种新型环氧树脂增韧剂——KH—07被成功地用于建筑结构胶。考查了KH-07的用量对胶粘剂综合性能的影响,结果表明,KH-07增韧剂能大幅提高胶粘剂的粘接剪切强度、冲击剥离强度和胶体自身强度,而且耐湿热老化性能也优于其他对照的增韧剂。另外,对KH-07增韧剂所产生的相分离现象也进行了初步探讨。     

活性硅微粉对不饱和树脂力学性能的影响

向不饱和树脂体系中添加不同质量的活性硅微粉,用以改善固化物的力学性能.实验结果表明,添加活性硅微粉30phr(每百份树脂中的份数),改性聚酯树脂固化物剪切强度最大;添加75phr,改性聚酯树脂固化物弯曲弹性模量最佳.     

改性氰酸酯树脂体系力学性能的研究

采用环氧树脂(E-51)与氰酸酯树脂共聚以改善氰酸酯树脂的韧性，研究了环氧树脂的加入量，后处理温度、湿热老化以及紫外光老化等条件对改性后树脂体系力学性能的影响规律，采用扫描电子显微镜对断口形貌进行了分析。结果表明环氧树脂可以明显改善氰酸酯树脂的韧性，环氧树脂含量为30％(质量百分数，下同)的体系的冲击强度和弯曲强度分别比改性前提高了100％和50％随环氧树脂用量的增加，改性树脂的冲击强度和弯曲强度提高，树脂表现为明显的韧性断裂；改性体系经2000℃、后处理2h的力学性能最佳；湿热老化和紫外光老化都使改性树脂体系的冲击强度和弯曲强度降低，而后者的影响较弱，当环氧树脂用量低于30％时冲击强度和弯曲强度的保持率均高于95％。     

新型环氧固化剂的合成与研究

合成一系列二乙烯三胺和三乙烯四胺与三种丙烯酸酯加成物——新型环氧固化剂，采用红外光谱法证实了反应主要发生在丙烯酸酯的双键与多乙烯多胺的氨基上；并对固化后环氧树脂的冲击强度和剪切强度进行了测定，结果表明：环氧树脂的抗冲性能及粘接性能均有所改善。     

Contrast on tensile and flexural properties of glass powder reinforced epoxy composites: Pilot study

Epoxy resin was filled with glass powder to optimize the tensile and flexural strength of the composite for structural applications by a research center in the University of Southern Queensland (USQ). To reduce costs, the center wishes to fill as much glass microspheres as possible subject to maintaining sufficient strength of the composites in structural applications. This project varies the percentage by weight of the glass powder in the composites. After casting the composites to the molds, they were cured at ambient conditions for 24 h. They were then postcured in a conventional oven and subjected to tensile and flexural tests. The contribution of the study was that if tensile and flexural properties were the most important factors to be considered in the applications of the composites, the maximum amount of glass powder can be added to the resin will be five (5) percent. It was also found that the fractured surfaces examined under scanning electron microscope were correlated with the tensile and flexural strength It is also hoped that the discussion and results in this work would not only contribute toward the development of glass powder reinforced epoxy composites with better material properties, but also useful for the investigations of tensile and flexural properties in other composites. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Study on sepiolite‐reinforced polymeric nanocomposites

Epoxy nanocomposites reinforced by nano‐sized sepiolite are investigated. Sepiolite particles and the nanocomposites were characterized by SEM, TEM, XRD, and IR. The level of reinforcement is assessed from impact strength and flexural strength. It is shown that significant improvement in mechanical property is obtained for all reinforced nanocomposites and the addition of 1% sepiolite appears to be an optimum blend ratio. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci, 2006     

MCM-41的孔径和添加量对环氧树脂力学性能的影响

以1,3,5三甲苯(TMB)为扩孔剂,水热合成了5种不同孔径(2.7～5.9 nm)的介孔二氧化硅MCM-41粉体,采用溶液共混法制备了MCM-41环氧树脂复合材料,研究了MCM-41孔径和添加质量对复合材料力学性能的影响。结果表明,添加1%最大孔径的MCM-41时,复合材料的力学性能达到最佳,拉伸强度、弯曲强度、弯曲模量分别比纯环氧树脂提高了54.6%、30.1%、68.3%。     

CFRP界面胶接性能的研究

本文主要对碳纤维增强树脂基复合材料与金属铝的界面胶接问题进行了研究。对胶粘剂中的环氧树脂、增韧剂及胶接工艺方法进行了一系列的对比试验，从而选择出适用于实际工艺生产的胶粘剂。     

环氧树脂覆铜板（CCL）耐热老化的研究

采用不同温度的加速老化试验方法，分别以拉伸强度、弯曲强度为指标，评估了环氧树脂覆铜板的热指数。结果表明，按照拉伸强度为指标，环氧树脂覆铜板的热指数为141℃；按照弯曲强度为指标，环氧树脂覆铜板的热指数为135℃。