CMK-5负载Pt-Ni合金催化剂及其甲醇电化学氧化性能

采用NaBH₄还原法将不同原子比的铂镍负载于CMK-5(由SBA-15模板所得的碳载体)表面. X射线衍射(XRD)和X射线光电子能谱(XPS)测试结果表明, 所得催化剂是以铂镍合金的形式存在, 相对于Pt/CMK-5而言, 这种合金化的催化剂中Pt表现出更多的金属态. 电化学测试结果显示, 在催化剂中主要以化合态存在的镍(包括NiO、Ni(OH)₂和NiOOH)可能更有利于甲醇的吸附和氧化产物从催化剂表面的脱附. 另外, 从循环伏安测试结果可知, Pt-Ni/CMK-5 (5:1)(原子比)具有较大的比表面活性, 其电化学活性面积高达63.9 m²·g^-1, 且与Pt/CMK-5相比抗CO中毒能力有明显改善.     

SBA-15负载高分散纳米NiO的丙烷氧化脱氢制丙烯催化性能

采用浸渍法通过改变焙烧气氛制备了系列NiO/SBA-15 (w_NiO=20%)催化剂, 并考察了催化剂的丙烷氧化脱氢(ODHP)反应性能. 实验结果表明, 与在静止和流动空气中焙烧的催化剂相比, 在1%NO/He (V_NO/V_He=1:99)气氛中焙烧的NiO/SBA-15-NO具有优异的低温丙烷氧化脱氢制丙烯性能, 在350 ℃时, 丙烷的转化率和丙烯收率分别约达29%和13%. 反应温度升至450 ℃时, 丙烯的选择性仍保持在45%左右. X射线粉末衍射(XRD)和透射电镜(TEM)测试结果表明, 1%NO/He气氛可有效抑制焙烧过程中NiO纳米颗粒的团聚, 使NiO物种高分散于SBA-15 的孔道中. H₂-程序升温还原(H₂-TPR)和O₂-程序升温脱附(O₂-TPD)测试结果表明, 随着NiO在SBA-15上分散度的提高, 催化剂的抗还原性增强, ODHP活性氧物种O-的含量增加, 进而使1%NO/He气氛中焙烧的NiO/SBA-15-NO在较宽的温度范围内(350-450 ℃)均具有良好的丙烯选择性, 并显著提高了催化剂的低温活性.     

B助剂对Ni2P/SBA-15催化剂结构及其加氢脱硫性能的影响

以介孔分子筛SBA-15为载体, 磷酸氢二铵为磷源, 硝酸镍为镍源, 硼酸为硼源, 采用共浸渍法制备了B-Ni₂P/SBA-15催化剂前驱体, 然后采用程序升温氢气还原法, 制备了n_P/n_Ni=0.8, B含量为0.35%-2.10%(w)的一系列B-Ni₂P/SBA-15催化剂. 用X射线衍射(XRD)、N₂吸附脱附、透射电子显微镜(TEM)和氨气程序升温脱附(NH₃-TPD)等表征技术对催化剂的结构进行了研究, 以1%(w)二苯并噻吩(DBT)/十氢萘溶液为模型化合物, 在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价. 结果表明, B-Ni₂P/SBA-15催化剂仍具有介孔结构, Ni₂P为主要的活性物相. 适量B助剂的加入可促使Ni₂P晶粒减小, 催化剂比表面积增加. 此外, 随着B含量的增加, B-Ni₂P/SBA-15催化剂的总酸量也增加. 当反应压力为3.0 MPa, 反应温度由300 ℃升高至360 ℃时, B含量对Ni₂P/SBA-15催化剂活性有明显的影响, B含量为1.40%(w)的B-Ni₂P/SBA-15催化剂加氢脱硫活性最高. B-Ni₂P/SBA-15催化剂上二苯并噻吩的加氢脱硫的反应机理以直接脱硫为主.     

Ru 前驱体对 Ru/MgO-CeO2 氨合成催化剂性能的影响

 分别以 K₂RuO₄, Ru(Ac)₃ 和 RuCl₃ 为 Ru 前驱体, 制备了 Ru/MgO-CeO₂ 催化剂, 并运用 X 射线衍射、X 射线荧光光谱, CO 吸附、N₂ 物理吸附和 H₂程序升温还原等技术对催化剂进行了表征, 考察了 Ru 前驱体对 Ru/MgO-CeO₂ 催化剂氨合成性能的影响. 结果表明, Ru 前驱体对载体 MgO-CeO₂ 和 Ru 的还原性能、氯残留量和催化剂比表面积的影响都很大, 从而导致催化剂的氨合成性能的不同. 其中以 K₂RuO₄ 为 Ru 前驱体制备的催化剂的载体和 Ru 容易还原, 无氯离子, 且比表面积较高, 因而催化剂活性和氨合成转换频率较高. 在 10 MPa, 425 °C, 10 000 h^-1 条件下, K₂RuO₄, Ru(Ac)₃ 和 RuCl₃ 作前驱体制备的催化剂上氨合成转换频率比为 1.33:1.05:1.     

串联双釜连续反应装置中Ru-Co-B/ZrO2上苯选择加氢制环己烯

采用化学还原法制备了苯选择加氢制环己烯催化剂Ru-B/ZrO₂,考察了Cr,Mn,Fe,Co,Ni,Cu和Zn等过渡金属的添加对Ru-B/ZrO₂催化剂性能的影响.结果表明,这些过渡金属的添加均可提高Ru-B/ZrO₂催化剂中的B含量.B的修饰及第二种金属或金属氧化物的集团效应和配位效应导致Ru-B/ZrO₂催化剂活性降低和环己烯选择性升高.当Co/Ru原子比为0.06时,Ru-Co-B/ZrO₂催化剂上反应25min苯转化率为75.8%时,环己烯选择性和收率分别为82.8%和62.8%.在双釜串联连续反应器中和优化反应条件下,Ru-Co-B/ZrO₂催化剂使用419h内苯转化率稳定在40%左右,环己烯选择性和收率分别稳定在73%和30%左右.     

一种制备碳载高合金化Pt-Ru催化剂的方法

提出了在四氢呋喃(THF)和H₂O混合溶液中用一般的化学还原法在室温下制备碳载Pt-Ru(Pt-Ru/C)催化剂的新方法。与在纯水中制得的Pt-Ru/C催化剂相比，其Pt-Ru粒子的合金化程度高、平均粒径较小且相对结晶度低，因此，该催化剂对甲醇氧化的电催化活性远高于在纯水中制得的Pt-Ru/C催化剂。高合金化程度的原因是H₂PtCl₆和RuCl₃在THF和H₂O混合溶液中的起始还原电位相近。此外，在THF和H₂O混合溶液中，THF和H₂O的体积比的改变并不影响制得的Pt-Ru/C催化剂中Pt-Ru粒子的合金化程度，但对Pt-Ru粒子的粒径以及相对结晶度有较大影响。     

在一维ZnO表面可控构建Co3Mn1纳米晶及其催化CO氧化性能

利用热分解法制备了结构明确的负载型纳米晶催化剂。在纳米晶成核和生长过程中加入一维ZnO纳米棒作为晶种,调控不同组分的纳米晶在 ZnO纳米棒表面均匀生长,从而获得了结构明确的 MnO/ZnO、Co₃O₄/ZnO、Co₃Mn₁/ZnO催化剂。透射电子显微镜(TEM)与 X 射线粉末衍射(XRD)结果显示,不同组分纳米颗粒都均匀分散在 ZnO 纳米棒表面。相对于 MnO/ZnO 和Co₃O₄/ZnO催化剂,Co₃Mn₁/ZnO催化剂在CO氧化反应中具有最佳的催化性能。在200 L·g_cat^-1·h^-1的气时空速下,Co₃Mn₁/ZnO催化剂起活温度为 50 ℃,其 T100(CO 转化率达到 100% 时的温度)为 200 ℃;利用 X 射线光电子能谱(XPS)对不同催化剂进行了分析,结果显示,Co₃Mn₁/ZnO催化剂的氧空位比MnO/ZnO催化剂提高了30%以上,从而使其具有较高的CO氧化催化性能。更为重要的是,Co₃Mn₁/ZnO复合纳米晶催化剂的活化能(39.4 kJ·mol^-1)远低于其它负载型纳米晶催化剂。     

Pt 改性的高结晶度 TiO2 晶须的光催化性能

 以二钛酸钾 (K₂Ti₂O₅) 为前驱体, 通过离子交换和 800^oC 焙烧制备了 TiO₂晶须 (TiO₂(800^oC)), 并采用乙二醇胶体法, 在 TiO₂(800^oC) 样品上负载 1% Pt 纳米颗粒制成了 Pt/TiO₂(800^oC 催化剂. 采用 X 射线衍射、扫描电镜、透射电镜、X 荧光光谱和低温 N2 吸附-脱附等技术对催化剂进行了表征, 并考察了该催化剂光催化降解苯酚活性及稳定性. 结果表明, TiO₂(800^oC)样品为结晶度较高的纯锐钛矿 TiO₂, 载 Pt 后催化活性提高到原来的 2.3 倍, 具有很高的单位比表面积活性. 催化剂经 10 次重复使用后, Pt 流失量仅为 6%, 活性为新鲜催化剂的 91%. 而低结晶度的纯锐钛矿或混晶的 TiO₂ 负载 Pt 催化剂的活性和稳定性均不及 Pt/TiO₂(800^oC).     

SO42-/SnO2-Fe2O3固体酸催化下的环酮Baeyer-Villiger氧化反应及缩合反应

采用共沉淀的方法制备了不同Fe 掺杂量的SO₄^2-/SnO₂-Fe₂O₃固体超强酸催化剂. 利用傅里叶变换红外(FTIR)光谱, 粉末X射线衍射(XRD), N₂吸附-脱附实验(BET), 热重(TG)分析和扫描电镜(SEM)等方法对样品进行了表征. 考察了所得催化剂对4-叔丁基环己酮与乙二醇缩合反应的催化性能. 实验结果表明, 与未经过掺杂改性的SO₄^2-/SnO₂固体酸催化剂相比, 改性后催化剂的催化性能得到了改善. 研究了以Fe/Sn 摩尔比为0.5的SO₄^2-/SnO₂-Fe₂O₃固体酸为催化剂, 部分醛酮类化合物与乙二醇及1,2-丙二醇的缩合反应. 考察了反应时间、催化剂用量等因素对反应的影响. 同时, 将所得催化剂应用于环酮Baeyer-Villiger 氧化反应中, 催化剂表现出良好的催化活性, 且催化剂具有一定的循环使用性.     

不同载体对负载型氧化钨催化剂在己二酸合成反应中的结构及性能影响

以SBA-15、六角介孔二氧化硅（HMS）和SnO₂为载体,通过浸渍法合成了含钨负载型催化剂,并考察了三种催化剂在环氧环己烷选择氧化制备己二酸反应中的催化性能. 通过X射线衍射（XRD）,透射电镜/场发射透射电镜（TEM/FETEM）,紫外-可见漫反射光谱（UV-Vis DRS）,拉曼（Raman）光谱,X射线光电子能谱（XPS）以及傅里叶变换红外（FTIR）光谱等手段对各种催化剂的结构进行表征. 结果表明,载体与催化剂的性能有密切的关系. 以SnO₂为载体的WO₃/SnO₂催化剂活性最高,其次是WO₃/HMS催化剂,WO₃/SBA-15 催化剂的活性最差.XRD 分析显示WO₃/SnO₂催化剂中氧化钨物种的晶化程度最低,TEM 和XPS 结果表明氧化钨物种在WO₃/SnO₂催化剂表面高度分散并且粒径尺寸很小（约2 nm）,UV-Vis DRS结果表明在WO₃/SnO₂催化剂中存在孤立[WO₄]四面体和低聚态的钨物种,这些物种的存在可能是WO₃/SnO₂催化剂具有高活性的主要原因. 此外,WO₃/SnO₂催化剂可以重复使用多次,6 次反应后己二酸（AA）得率仍然保持在80%以上,说明氧化钨物种与SnO₂载体间存在强烈的相互作用,从而提高了催化剂的稳定性.     

Ultrasound-assisted synthesis of monodisperse Ru–B amorphous alloys with enhanced catalytic activity in maltose hydrogenation

Monodisperse Ru–B amorphous alloy catalysts were synthesized by ultrasound-assisted chemical reduction of (NH₄)₂RuCl₆ with BH ₄ ^? . With the characterization of X-ray diffraction (XRD), selective area electronic diffraction (SAED), X-ray photoelectron spectroscopy (XPS), differential scanning calorimetry (DSC), and transmission electron microscopy (TEM), the resulting Ru–B nanoparticles were identified to be amorphous alloys ranging in size from 2.4 to 4.9 nm. During liquid-phase maltose hydrogenation, the as-synthesized Ru–B catalyst was extremely active compared to the regular Ru–B obtained via the reduction of RuCl₃ with BH ₄ ^? . The Ru–B sample prepared under ultrasonication with 60 W was proven to be the most active catalyst. Its catalytic activity was nearly 11 times that of industrial Raney Ni, and could be used repetitively for more than six times without significant deactivation.     

Plasma-Catalytic Oxidation of Toluene on MnxOy at Atmospheric Pressure and Room Temperature

Mn_xO_y/SBA-15 catalysts were prepared via the impregnation method and utilized for toluene removal in dielectric barrier discharge plasma at atmospheric pressure and room temperature. The catalysts were characterized by X-ray diffraction, N₂ adsorption–desorption, Raman spectroscopy, X-ray photoelectron spectroscopy, H₂ temperature-programmed reduction, and O₂ temperature-programmed desorption methods. The characterization results indicated that manganese loading did not influence the 2D-hexagonal mesoporous structure of SBA-15. The catalyst had various oxidation states of manganese (Mn²⁺, Mn³⁺, and Mn⁴⁺), with Mn³⁺ being the dominant oxidation state. Toluene removal was investigated in the environment of pure N₂ and 80 % N₂ + 20 % O₂ plasma, showing that the toluene removal efficiency and CO₂ selectivity were noticeably increased by Mn_xO_y/SBA-15, especially in the presence of 5 % Mn/SBA-15. This activity was closely related to the high dispersion of 5 % Mn on SBA-15 and the lowest reduction temperature exhibited by this catalyst. Mn loading increased the yield of CO₂ in the N₂ plasma and promoted the deep oxidation of toluene. During toluene oxidation, oxygen exchange might follow a pathway, wherein bulk oxygen was released from the Mn_xO_y/SBA-15 surface; gas-phase O₂ subsequently filled up the vacancies created on the oxide. Each of the manganese oxidation states played an important role; Mn₂O₃ was considered as a bridge for oxygen exchange between the gas phase and the catalyst, and Mn₃O₄ mediated transfer of oxygen between the catalyst and toluene.     

SBA-15负载Pd催化剂的制备及其在Heck反应中的应用研究

利用水热反应制备了表面离子液体功能化的SBA-15介孔材料,在丙酮溶液中与氯化钯反应,然后使用水合肼在乙醇中还原.测试了这种催化剂在Mizoroki-Heck反应中的催化活性.与直接负载在SBA-15上的钯催化剂相比,这种表面修饰的介孔SBA-15负载催化剂表现出更高的催化活性、可回收性和反应稳定性.氮气吸脱附实验和小角XRD衍射实验表明,在合成中,材料的介孔性能并没有被破坏.透视电镜也表征了该材料的表面形貌.最后,Mizoroki-Heck反应表明该催化剂具有很高的催化活性,且循环五次后,其催化活性降低并不明显.     

Aqueous-Phase Nitrile Hydration Catalyzed by an In Situ Generated Air-Stable Ruthenium Catalyst

RuCl₂(PTA)₄ (PTA=1,3,5-triaza-7-phosphaadamantane) is an active, recyclable, air-stable, aqueous-phase nitrile hydration catalyst. The development of an in situ generated aqueous-phase nitrile hydration catalyst (RuCl₃⋅3 H₂O+6 equivalents PTA) is reported. The activity of the in situ catalyst is comparable to RuCl₂(PTA)₄. The effects of [PTA] on the activity of the reaction were investigated: the catalytic activity, in general, increases as the pH goes up, which shows a positive correlation with [PTA]. The pH effects were further explored for both the in situ and RuCl₂(PTA)₄ catalyzed reaction in phosphate buffer solutions with particular attention given to pH 6.8 buffer. Increased catalytic activity was observed at pH 6.8 versus water for both systems with turnover frequency (TOF) up to 135 h⁻¹ observed for RuCl₂(PTA)₄ and 64 h⁻¹ for the in situ catalyst. Catalyst loading down to 0.001 mol % was examined with turnover numbers as high as 22 000 reported. Similar to the preformed catalyst, RuCl₂(PTA)₄, the in situ catalyst could be recycled more than five times without significant loss of activity from either water or pH 6.8 buffer.     

Preparation, Characterization and Catalytic Performance of La-SO4/SBA-15 in Esterification of Acetic Acid with n-Butanol

La-SO42-/SBA-15 was synthesized with various amounts of lanthanum via incipient-wetness impregnation. Characterization was done by X-ray diffraction（XRD）, transmission electron micrographs（TEM）, nitrogen adsorption, FTIR spectroscopic analysis, thermogravimetric analysis, and the total amount of acidity of catalyst was estimated by TPD of NH3. The results indicate that lanthanum has been incorporated into SBA-15 molecular sieve. The prepared materials（La-SO42-/SBA-15） keep the highly ordered mesoporous two-dimensional hexagonal structure and do not change the mesoporous channel structure of the support SBA-15. The catalyst showed best catalytic activity in the synthesis of n-butyl acetate. The optimum conditions of the esterification by orthogonal experiments were studied： the molar ratio of n-butanol to acetic acid 1：1.2, the amount of catalyst 7.5%, reaction time 80 min. The yield of n-butyl acetate could reach 93.2% under the optimum conditions. The catalyst was recyclable, cost effective and environmental friendly.     

Ag/SBA-15低温气相选择性催化氧化苯甲醇合成苯甲醛

以SBA-15为载体,采用浸渍法制备了不同Ag含量的Ag/SBA-15,通过N₂吸附-脱附、X射线衍射、扫描电子显微镜、高分辨透射电子显微镜、X射线光电子能谱和电感耦合等离子体质谱对催化剂进行了表征。将Ag/SBA-15用于苯甲醇气相选择性催化氧化合成苯甲醛,研究了反应条件对转化率和选择性的影响。结果表明,Ag/SBA-15具有均一的一维孔道结构、较厚的孔壁（3-5 nm）及较大的比表面积（411-541 m²/g）,其规整纳米空间的限域作用使一定负载量的Ag以纳米尺寸均匀分散于介孔SBA-15孔道内,增加了活性组分的比表面积。亲核性氧物种从Ag到SBA-15表面的氧溢流,提高了低温下Ag/SBA-15对苯甲醇气相选择性氧化合成苯甲醛的催化性能。5.3% Ag/SBA-15中的Ag粒径为5-6 nm,且均匀分散于载体孔道中,反应温度为220℃时,苯甲醇转化率为87%,苯甲醛选择性为95%;240℃时,苯甲醇转化率和苯甲醛选择性分别高达94%和97%;并在240-300℃范围内,其催化活性和选择性保持不变,表现出了良好的温度耐受能力。催化剂经活化再生可以连续使用40 h,选择性基本保持不变。     

Silicotungstic acid-derived WO3 composited with ZrO2 supported on SBA-15 as a highly efficient mesoporous solid acid catalyst for the alkenylation of p-xylene with phenylacetylene

Highly dispersed silicotungstic acid-derived WO₃ composited with ZrO₂ supported on SBA-15（WZ/SBA-15） as an ordered mesoporous solid acid catalyst was prepared via a facile incipient wetness impregnation（IWI） method that active ingredients,ZrO₂ and WO₃,were impregnated into the channels of SBA-15 simultaneously with a subsequent calcination process.The relationship between catalyst nature and performance was explored by high resolution transmission elec...     

SBA-15负载的Cu(Ⅱ)席夫碱配合物催化的苯乙烯氧化反应制备苯甲醛

采用一步法将原硅酸四乙酯与3-氨丙基三乙氧基硅烷在表面活性剂P123作用下,酸性共水解制备出氨基功能化的介孔分子筛SBA-15(NH2-SBA-15),再利用其中氨基与水杨醛的缩合反应制备SBA-15固载的席夫碱,该席夫碱与Cu(NO3)2溶液反应最终制成固定于SBA-15的Cu(II)席夫碱配合物多相催化剂Cu-SBA-15.采用X射线衍射、红外光谱仪、紫外可见分光光度计、场发射电镜、透射电镜、N2吸附-脱附、元素分析、原子发射光谱和热重分析对催化剂进行了表征,并将此催化剂用于无有机溶剂条件下催化氧化苯乙烯制备苯甲醛,考察了反应时间、反应温度、H2O2用量、水的用量、催化剂用量对反应的影响.当反应温度为100°C,反应时间8 h,H2O2与苯乙烯的摩尔比为2:1,不额外添加溶剂,且催化剂用量为3.8 wt%时,苯乙烯的转化率最高为84.4%,苯甲醛选择性为83.9%,催化剂的TOF值为261.1 h–1,并且重复使用3次后活性没有明显下降.规则的孔道、较大的比表面积以及分布均匀的活性中心可能是催化剂活性提高的原因.